• 한국표면공학회지
• /
• 제44권2호
• /
• pp.68-73
• /
• 2011

A Ni-W thin-film was synthesized by electrodeposition, and its corrosion resistance and electrical surface conductivity were investigated. Amount of tungsten in the Ni-W thin-film increased linearly with current density during the electrodeposition, and crack-free and low-crystalline Ni-21 at.%W coating layer was obtained. Corrosion resistances of the Ni-W thin-films were examined with an anodic polarization method and a storage test in a strong sulfuric acid solution. As a result, the Ni-21 at.%W thin-film exhibited the greatest corrosion resistance, and maintained the electrical surface conductivity even after the severe corrosion test, which could be applicable as a surface treatment for advanced metallic bipolar plates in fuel cell or redox flow battery systems.

• 한국재료학회지
• /
• 제8권10호
• /
• pp.898-904
• /
• 1998

10-50wt% 범위의 W을 함유하는 Ni-W 합금을 전기도금에 의해 제조하였다. 합금 중의 W 량은 전류밀도가 증가함에 따라 증가하였다. 전류밀도가 50mA/${cm}^2$이하인 경우 Ni-W합금은 미세한 결정립을 갖는 Ni의 고용체이었으며, 전류밀도가 50mA/${cm}^2$이상인 경우 비정질상으로 변화하였다. 이들의 결정질$\longrightarrow$비정질 천이는 W량이 40-46wt%인 구간에서 일어났으며 반각폭이 3배이상으로 증가하였다. 결정질 합금의 격자상수는 평형상태도 상의 W의 고용한계(약 30wt%)를 초과하는 40wt%까지 연속적으로 증가하는 것으로 나타나 Ni이 W을 과고용하고 있는 상태인 것으로 밝혀졌다. 비정질 Ni-W 합금은 $400^{\circ}C$이상의 온도에서 열처리하면 강한 [111]방향성을 가지며 재결정하였으며, $800^{\circ}C$이상의 온도에서는 과고용된 W이 석출하였다. 합금조성 및 결정구조의 전류밀도 의존성을 이용하여 Ni-30%W과 Ni-50%W 합금층이 반복되는 결정질/비정질의 다층도금을 제조하였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 1999년도 추계학술발표회 초록집
• /
• pp.39-39
• /
• 1999

• Corrosion Science and Technology
• /
• 제11권6호
• /
• pp.275-279
• /
• 2012

Ni-W alloy deposits have lately attracted the interest as an alternative surface treatment method for hard chromium electrodeposits because of higher wear resistance, hardness at high temperature, and corrosion resistance. This study deals with influences of process variables, such as electodeposition current density, plating temperature and pH, on the internal stress of Ni-W nanocrystalline deposits. The internal stress was increased with increasing the applied current density. With increasing applied current density, the grain size of the deposit decreases and concentration of hydrogen in the deposit increases. The subsequent release of the hydrogen results in shrinkage of the deposit and the introduction of tensile stress in the deposit. Consequently, for layers deposited at high current density, cracking occurs readily owing to high tensile stress value. By increasing the temperature of the electrodeposition from $60^{\circ}C$ to $80^{\circ}C$, the internal stress was decreased. It seems that an increase in the number of active ions overcoming the activation energy at elevated temperature caused a decline in the concentration polarization and surface diffusion. It decreased the level of hydrogen absorption due to the lessened hydrogen evolution reaction. Therefore, the lower level of hydrogen absorption degenerated the hydride on the surface of the electrode, resulting in the reduction of the internal stress of the deposits. By increasing the pH of the electrodeposition from 5.6 to 6.8, the internal stress in the deposits were slightly decreased. It is considered that the decrease in internal stess of deposits was due to supply of W complex compound in cathode surface, and hydrogen ion resulted from decrease of activity.

• Journal of Magnetics
• /
• 제16권2호
• /
• pp.97-100
• /
• 2011

Bilayers of soft NiFe (150 nm-420 nm) on hard Ni (150 nm) were prepared by electrodeposition. The process of magnetization reversal in the NiFe/Ni bilayers was then investigated. The hysteresis loop generated by a magnetization reversal of soft NiFe under a positive saturation state of a hard Ni layer shows a shift along the negative field axis, which is clear evidence for the exchange spring effect in the NiFe/Ni bilayers. The dependence of the coercive field $H_c$ and exchange bias field Hex on the thickness of the NiFe layer was also investigated. As the NiFe thickness increases from 150 nm to 420 nm, both $H_c$ and $H_{ex}$ decrease rapidly from $H_c$= 51.7 Oe and $H_{ex}$ = 12.2 Oe, and saturate to $H_c$ = 5.8 Oe and $H_{ex}$ = 3.5 Oe.

• 한국표면공학회지
• /
• 제32권6호
• /
• pp.686-694
• /
• 1999

Insoluble anodes of the Ta/Ir mixed metal oxide for electrodeposition of Ni-W alloy in ammoniacal citrate bath were prepared by thermal decomposition method. Ti plate was etched in boiling oxalic acid solution and coated with ethanol solution of $TaCl_{5}$ and $IrCl_4$ mixed in a fixed ratio, followed by drying and treating at various temperatures. The coating layer of these insoluble anode was characterized by SEM, EDX, XRD and DSC. The decomposition rate of citric acid in plating bath was determined by measuring the $CO_2$ gas evolved at the anodes with Gas Chromatography. Evolution of $CO_2$ gas from Ta/Ir oxide anodes decreased about 5% compared with that of Pt. The $CO_2$ gas evolution was increased with the amount of Ir-oxide in the coatings. The coatings which have more than 40% ratio of Ta content and heat-treated at the temperature higher than $400^{\circ}C$ showed better efficiency

• Corrosion Science and Technology
• /
• 제12권4호
• /
• pp.185-190
• /
• 2013

In the present study, $Ni-TiO_2$ composite coatings were electrodeposited in a sulfamate bath containing $TiO_2$ particles. The influence of the ultrasonic treatment on the co-deposition of $TiO_2$ particles in the coating and the hardness of the electrodeposited $Ni-TiO_2$ composite has been investigated. Three different ultrasonic treatments (pretreatment before the electrodeposition (pre-UT), pretreatment + applied during the electrodeposition (UT), and the electrodeposition without the ultrasonic treatment (w/o UT)) were performed. The $Ni-TiO_2$ composite coatings are characterized using scanning electron microscopy (SEM), image analyzer, and hardness tester. Comparison of results indicates that the volume fraction is more important factor than the agglomerated particle size in terms of the strength improvement, and the strength of the electrodeposited $Ni-TiO_2$ composite coatings is enhanced with pre-UT condition.

• 한국표면공학회지
• /
• 제36권6호
• /
• pp.430-436
• /
• 2003

The nanoocrystalline Ni-l5W(at.%) coating electrodeposited on the high carbon steel was oxidized at 700 and $800^{\circ}C$ in air, and the resultant oxidation properties were investigated using XRD, EPMA, TGA and TEM. The oxidation resistance of the coating was not so good that most of the coating was oxidized after oxidation at $800^{\circ}C$ for 5 hrs. The oxidation led to the formation of the outer, thin NiO oxide scale and the inner, porous, rather thick ($NiWO_4$＋NiO) mixed layer containing a bit of $WO_2$. During oxidation, substrate elements such as Fe and Cr diffused outwardly toward the coating, according to the concentration gradient.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2014년도 추계학술대회 논문집
• /
• pp.178-179
• /
• 2014

In this study, $Ni-W-Si_3N_4$ alloy composite coatings were prepared by pulse electrodeposition method using nickel sulfate bath with different contents of tungsten source, $Na_2WO_4.2H_2O$, and dispersed $Si_3N_4$ nano particles. The structure and microstructure ofcoatings was separately analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). Results indicated that nano $Si_3N_4$ and W content in alloy had remarkable effect on microstructure, microhardness and scratch resistant properties. Tungsten content in Ni-W and $Ni-W-Si_3N_4$ alloy ranged from 7 to 14 at.%. Scratch test results suggest that as compared to Ni-W only, $Ni-W-Si_3N_4$ prepared from Ni/W molar ratio of 1:1.5 dispersed with 20 g/L $Si_3N_4$ has shown the best result among different samples.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.171-172
• /
• 2015

$Ni-W-Si_3N_4$ alloy composite coatings were prepared by pulse electro-deposition method using nickel sulfate bath with different contents of tungsten source, $Na_2WO_4.2H_2O$, and dispersed $Si_3N_4$ nano-particles. The structure and micro-structure of coatings was separately analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). Results indicated that nano $Si_3N_4$ and W content in alloy had remarkable effect on micro-structure, micro-hardness and scratch resistant properties. Tungsten content in Ni-W and $Ni-W-Si_3N_4$ alloy ranged from 7 to 14 at.%. Scratch test results suggest that as compared to Ni-W only, $Ni-W-Si_3N_4$ prepared from Ni/W molar ratio of 1:1.5 dispersed with 20 g/L $Si_3N_4$ has shown the best result among different samples.