• Proceedings of the Korean Vacuum Society Conference
• /
• 2001.07a
• /
• pp.147-148
• /
• 2001

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.27-32
• /
• 2006

[$YBa_2Cu_3O_{7-x}$] thin films were deposited on various buffered-templates by a metal organic chemical vapor deposition(MOCVD). Three different templates of $CeO_2/YSZ/CeO_2/pure-Ni(CYC),\;CeO_2/YSZ/Y_2O_3/Ni-3at.%W(YYC)$ and $CeO_2/IBAD-YSZ$/stainless steel were used. The Ni and Ni-W alloy tapes were biaxially textured by cold rolling and annealing heat treatment. The dense YBCO films were grown on both the IBAD and YYC templates with no microcrack, while the YBCO films on the CYC templates were grown with the formation of microcracks and NiO. The YBCO film on the YYC template showed the higher $I_c$ than that on CYC template. Especially, the IBAD templates with a thin $CeO_2$(type I) and thick $CeO_2$(type II) top layer were used to compare the deposition nature of the YBCO on them. Comparing the current property of the YBCO films on IBAD templates, the YBCO film deposited on thick $CeO_2$ layer was better than the film on thin $CeO_2$ layer.

• Journal of Powder Materials
• /
• v.19 no.5
• /
• pp.338-342
• /
• 2012

A novel chemical method was evaluated to fabricate the ultrafine tungsten heavy alloy powders with bater-base solution made from the ammonium metatungstate (AMT), iron(II) chloride tetrahydrate ($FeCl_2{\cdot}4H_2O$), nickel(II) chloride hexahydrate ($NiCl_2{\cdot}6H_2O$) as source materials and the sodium tungstate dihydrate ($NaWO_4{\cdot}2H_2O$) as Cl-reductant. In the preparation of mixtures the amounts of the source components were chosen so as to obtain alloy of 93W-5Ni-2Fe composition(wt.%). The obtained powders were characterized by X-ray diffraction, XRF, field-emission scanning microscope (FESEM), and chemical composition was analyzed by EDX.

• Journal of Powder Materials
• /
• v.13 no.4 s.57
• /
• pp.285-289
• /
• 2006

Co-Fe-Ni-B-Si-Cr based amorphous strips containing nitrogen were manufactured via melt spinning, and then devitrified by crystallization treatment at the various annealing temperatures of $300^{\circ}C{\sim}540^{\circ}C$ for up to 30 minutes in an inert gas $(N_2)$ atmosphere. The microstructures were examined by using XRD and TEM and the magnetic properties were measured by using VSM and B-H meter. Among the alloys, the amorphous ribbons of $Co_{72.6}Fe_{9.8}Ni_{5.5}B_{2.4}Si_{7.1}Cr_{2.6}$ containing 121 ppm of nitrogen showed relatively high saturation magnetization. The alloy ribbons crystallized at $540^{\circ}C$ showed that the grain size of $Co_{72.6}Fe_{9.8}Ni_{5.5}B_{2.4}Si_{7.1}Cr_{2.6}$ alloy containing 121 ppm of nitrogen was about f nm, which exhibited paramagnetic behavior. The formation of nano-grain structure was attributed to the finely dispersed Fe4N particles and the solid-solutionized nitrogen atoms in the matrix. Accordingly, it can be concluded that the nano-grain structure of 5nm in size could reduce the core loss within the normally applied magnetic field of 300A/m at 10kHz.

• Korean Journal of Materials Research
• /
• v.10 no.8
• /
• pp.532-539
• /
• 2000

Co-0.5C-(15~20)Cr-20Ni-8W-(2~7)Fe alloy bond in diamond-impregnated abrasive tool was synthesized by ball-milling and mechanical alloying process. When the powders were mechanical alloyed for 6h, micro-welding in most metal powders was observed irrespective of addition of stearic acid. Without stearic acid in metal powders, partial-ly coarse powders were obtained, which could be unfaverable to the densification of composite of composite powders. The hot-pressed compacts showed rupture strength of 1100MPa and hardness of about $46H_{RC}$, respectively.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.1
• /
• pp.19-22
• /
• 2006

Desirable substrates for $YBa_2Cu_3O_{7-\delta}$ coated conductor are highly cube textured Ni or Ni-alloy tapes, which can be produced by cold rolling and recrystallization annealing. We have fabricated hi-axially textured pure Ni tapes for the application of coated conductors. The sintered Ni rod was cold-rolled into the thin tapes of $50{\mu}m$ thickness and the tapes were heat-treated for texture development with line-focused infrared heater. The temperature was maintained at $800\sim1050^{\circ}C$, using 1kW double ended linear halogen lamp in $96%Ar-4%H_2$ atmosphere The biaxially tortured Ni tapes were successfully formed by line-focused infrared heat treatment The texture of the annealed Ni tapes was analysed using the GADDS (general area detector diffraction system). The full width at half maximum values of phi and omega scan for the Ni tapes were less than $10^{\circ}$ and the grain size was $20-50{\mu}m$.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.02a
• /
• pp.37-59
• /
• 2004

In the case of Ni/Au finished pad on the package side, the solder joint of SnAgCu system can bring brittle fracture under impact load such as drop test. Therefore, it's difficult to prevent the brittle fracture of lead-free solder, by controlling Cu content. The failure locus existing on the interface between $(Ni,Cu)_3Sn_4\;and\;(Cu,Ni)_6Sn_5$ IMC layers must be changed to other site in order to avoid brittle fracture due to impact load. It was not found any clear evidence that there were two IMC layers exist. But it was strongly assumed these were two layers which have different Cu-Ni composition. From the above analysis it was assumed that Cu atom in the solder alloy or substrate seemed to affect IMC composition and cause to IMC brittle fracture.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.1
• /
• pp.65-74
• /
• 1995

This research was performed to investigate the effect of ageing on grain refinement of 82wt%Cu-13.5wt%Al-4.5wt%Ni-0.1wt% misch metal alloy with ageing temperature and time. The results obtained in this study are as follows; The variation of transformation temperature with ageing temperature had very influence on ageing time at $300^{\circ}C$. But it had not influence on ageing time at $100^{\circ}C$. The variation of transformation temperature after second reversed transformation cycle was not occured in martensitic phase ageing, but $M_s$ point was appeared equally with third reversed transformation cycle in parent phase ageing. The variation of $M_s$ point was not nearly with ageing time at $100^{\circ}C$ ageing temperature. But it was decreasing with ageing time at $300^{\circ}C$ ageing temperature and $A_s$ point was increasing with ageing time. Structure of parent phase ageing was being M18R martensitic and N2H martensitic phase. It was found that ${\alpha}$ and ${\gamma}_2$ phase were created by ageing of long time at $300^{\circ}C$ ageing temperature.

• Transactions of Materials Processing
• /
• v.26 no.4
• /
• pp.216-221
• /
• 2017

Recently, interest in multifunctional energetic structural materials (MESMs) has grown due to their multifunctional potential, especially in military applications. However, there are few studies about extrinsic factors that govern the reactivity of MESMs. In this paper, a shock compaction process was performed on the nano Ni/Al-mixed powder to investigate the effect of particle size on the shock reaction condition. Additionally, heating the statically compacted specimen was also performed to compare the mechanical properties and microstructure between reacted and unreacted material. The results show that the agglomerated structure of nanopowders interrupts the reaction by reducing the elemental boundary. X-ray diffraction analysis shows that the NiAl and $Ni_3Al$ intermetallics are formed on the reacted specimen. The microhardness results show that the $Ni_3Al$ phase has a higher hardness than NiAl, but the portion of $Ni_3Al$ in the reacted specimen is minor. In conclusion, using Ni/Al composites as a reactive material should focus on energetic use.

• Korean Journal of Materials Research
• /
• v.6 no.9
• /
• pp.871-877
• /
• 1996

가스터빈용 단결정 주조 블레이드는 기포 및 Freckle등과 같은 주조결함이 없어야 하며, 수지상, ${\gamma}$'크기와 모양에 따라 화학조성이 다르며, 기지와 공정조직을 각각 2영역 및 3영역으로 분류할 수 있었다. 또한, Ti는 첨가원소호서 조직제어에 매우 중요한 역할을 하였다.