Stainless steel is widely applied in many industrial fields due to its excellent anti-corrosion and durability characteristics. However, stainless steel is very vulnerable to cavitation attack caused by high speed flow of fluid in the chloride environments such as marine environment. These conditions promote intergranular corrosion and cavitation-erosion, leading to degradation of the structural integrity and service life. In order to prevent these problems, the stabilized stainless steel is applied to the offshore and shipbuilding industries. In this study, Ti was added to 19%Cr-9%Ni as the stabilizer element with different concentrations (0.26%, 0.71%), and their durabilities were evaluated with cavitation-erosion experiment by a modified ASTM G32 method. The microstructural change was observed with the stabilizer element contents. The result of the observation indicated that the amount of carbide precipitation was decreased and its size became finer with increasing Ti content. In the cavitation-erosion experiment, both weight loss and surface damage depth represented an inverse proportional relationship with the amount of Ti element. Consequently, the stainless steel containing 0.71% of Ti had excellent durability characteristics.
Cu-P계, 4종의 Cu-P-Pn계 및 3종의 Cu-P-Sn-Ag계 용가재를 사용해 Ar분위기 하에서 1003 및 1033K로 1.2Ks동안 노브레이징한 ST304, STS430 및 저탄소강과 동 접합체들을 전단시험 및 조직시험하였다. 계면에서의 미세조직은 제 종류 즉 첫째,균열을 포함하는 반응층 둘째, 분산층 세째, 균열을 포함하는 반응층과 분산층으로 분류된다. 분산층만이 존재할때 40-60MPa 이상의 상대적으로 높은 전단강도가 얻어지며, 동모재파단을 일으킨다. 이 반응층이 형성되었을때는 반드시 균열이 형성되며, 낮은 전단강도를 나타내고 접합부파단을일으킨다. 이 반응층은 Fe-P계의 화합물이다. 이러한 미소조직 및 강도 경향은 용가재내 Sn의 존재 및 모재내 Ni(또한 Cr)의 존재 유무에 따라 변화한다.
In order to evaluate the corrosion resistance at the anode side separator for molten carbonate fuel cell, STS316 and SACC-STS316 (chromium and aluminum were simultaneously deposited by diffusion into STS316 authentic stainless steel substrate by pack-cementation process) were applied as the separator material. In case of STS316, corrosion proceeded via three steps ; a formation step of corrosion product until stable corrosion product, a protection step against corrosion until breakaway occurs, a advance step of corrosion after breakaway. Especially, STS316 would be impossible to use the separator without suitable surface modification because of rapid corrosion rate after formation of corrosion product, occurs the severe problem on stability of cell during long-time operation. Whereas, SACC-STS316 was showed more effective corrosion resistance than the present separator, STS316 due to the intermetallic compound layer such as NiAl, Ni3Al formed on the surface of STS316 specimen. And it is anticipated that, in order to use SACC-STS316 alternative separator at the anode side, coating process, which can lead to dense coating layer, has to be developed, and by suitable pre-treatment before using it, very effective corrosion resistance will be achieved.
The experimentally determined mechanical behavior of the material under the prescribed service conditions is the basis of advanced engineering optimum design. To allow experimental data on the behavior of the material considered, uniaxial stress tests were made. The aforementioned tests have enabled the determination of mechanical properties of material at different temperatures, then, the material's resistance to creep at various temperatures and stress levels, and finally, insight into the uniaxial high cyclic fatigue of the material under different applied stresses for prescribed stress ratio. Based on fatigue tests, using modified staircase method, fatigue limit was determined. All these data contributes the reliability of the use of material in mechanical structures. Data representing mechanical properties are shown in the form of engineering stress-strain diagrams; creep behavior is displayed in the form of creep curves while fatigue of the material is presented in the form of S-N (maximum applied stress versus number of the cycles to failure) curve. Material under consideration was 18CrNi8 (1.5920) steel. Ultimate tensile strength and yield strength at room temperature and at temperature of $600^{\circ}C$: [${\sigma}_{m,20/600}=(613/156)MPa$; ${\sigma}_{0.2,20/600}=(458/141)MPa$], as well as endurance (fatigue) limit at room temperature and stress ratio of R = -1 : (${\sigma}_{f,20,R=-1}=285.1MPa$).
In this paper, We studied the change of surface and variation of elements on both electrodes of hydrogen generator of alkaline electrolysis in use of FE-SEM and SIMS. We used the stainless steel 316(600 ${\mu}m$) as electrode in condition of 25%KOH, $60^{\circ}C$ Temperature. The results show that the intensity of elements (C, Si, P, S, Ti, Cr, Mn, Fe, Ni, Mo) of Positive Electrode are decreased as much as about $10^1{\sim}10^3 $than the original electrode. Thickness of Positive Electrode is decreased about 40 ${\mu}m$ after chemical reaction. The negative electrode, however, shows a slight variation in the intensity of elements (C, Si, P, Fe, Ni, Mn, Mo) but Change of thickness and surface' shape of electrode show nothing after chemical reaction. The change in thickness and variation of Stainless Steel 316 cause the lifetime of electrode to be shorted. We also observed hydrogen, oxygen, potassium in both electrodes. Especially, The potassium is increased in proportional with depth of positive electrode. this means the concentration of alkali solutions is changed. and so we have to supply alkaline solution to generator in order to produce same quantity of hydrogen gas continuously. we hope that this study gives a foundation to develop the electrode for hydrogen generator of alkaline electrolysis.
This paper reports the results of field evaluation to determine the levels of heavy metals in major industrial complexes in Korea over a seven year period (2007~2013). The measurement of heavy metal was conducted using quartz fiber filter sampling and ICP-AES analysis. In order to validate the analytical performance of these methods, studies were also carried out to investigate data quality control(QC) parameters, such as the method detection limit (MDL), repeatability, and recovery efficiencies. The average concentrations of total suspended particulates (TSP) for the nine industrial complexes in Korea were $104{\sim}169{\mu}g/m^3$, which was higher than other industrial complexes and urban areas. The Sihwa and Banwol industrial complexes were shown to be the biggest contributing sources to high TSP emission ($159{\mu}g/m^3$ and $169{\mu}g/m^3$, respectively). The concentrations of heavy metals in TSP were higher in the order of Fe>Cu>Zn, Pb, Mn>Cr, Ni, As and Cd. It was observed that Fe was the highest in the Gwangyang and Pohang steel industrial complexes. The concentrations of Zn and Pb were high in Onsan, Sihwa and Banwol industrial complexes, and this was attributed to the emission from the nonferrous industry. Additionally, Cr and Ni concentrations were high in the Sihwa and Banwol industrial complexes due to plating industry. On the other hand, Ulsan and Onsan industrial complexes showed high Cr and Ni concentrations as a response to the emission of metal industry related to automobile. The correlation analysis revealed the high correlation between Cr and Ni in plating industry from Sihwa and Banwol industrial complexes. Adding to this, components related to coal combustion and road dust showed high correlation in Pohang and Gwangyang industrial complexes. Then Onsan and Ulsan industrial complexes showed high correlation among components related to the nonferrous metals.
Journal of Advanced Marine Engineering and Technology
/
제27권6호
/
pp.704-713
/
2003
The effect of partial substitution of tungsten for molybdenum on the microstructure and corrosion resistance in 22Cr-5Ni-3Mo duplex stainless steel(DSS) aging heat treated in a temperature range of 600~$1000^{\circ}C$ has been investigated. Electrochemical tests were carried out for the evaluation of corrosion resistance. Aging treatment had hardly influenced the general corrosion resistance. With the increase of aging time, the pitting corrosion resistance of the DSS had decreased, After aging for 2min at 700~$900^{\circ}C$, the pitting potential of the 3Mo steel decreased remarkably, while that of the W-substituted steel hardly changed. During aging. the intermetallic $\sigma$ and secondary austenite ($\gamma_2$) phases were precipitated. and the pitting corrosion and intergranular corrosion resistance were significantly decreased after aging at 700~$750^{\circ}C$ for 10 h, which could be caused by the $\gamma_2$ formation. The ${\gamma}$$_2$ phase could affect the depletion of molybdenum and chromium in the $\gamma_2/\alpha and \gamma_2/\sigma$ boundaries.
시간분해 레이저 유도 파열 분광분석 (TRELIBS) 시스템을 구성하여 원자력발전소 계통재질의 성분을 정성 분석하는 데 응용하였다. 본 연구에서는 탄소강 (A106 Gr. B, A336 P11, A335 P22), 스텐인레스강 (type 304, type 316) 및 인코넬 계열 합금(인코넬 600, 인코넬 690, 인코넬 800) 시료를 사용하였다. 탄소강의 종류는 485~575 nm 파장영역에서 나타난 Cr/Fe과 Mo/Fe의 TRELIBS 피크 비에 의해서 서로 구분 가능하였다. type 304와 type 316 스텐인레스강은 485~575 nm 파장영역에서 나타나는 Mo의 TRELIBS 피크 존재 여부에 의해서 쉽게 구분 가능하였다: type 304는 어떤 Mo의 피크도 나타내지 않지만, type 316은 Mo의 피크를 보여준다. 인코넬 계열 합금강 종류는 420~510 nm 파장영역에서 나타난 Cr/Fe과 Ni/Fe의 TRELIBS 피크비에 의해서 서로 구분 가능하였다. TRELIBS는 시료의 전처리 없이 빠르고 쉽게 합금을 분석할 수 있는 효과적인 분석 기술임이 입증되었다.
Carburizing treatments are the important way to developing fatigue strength and wear resistance. It is well known that the case depth is one of the most significant parameters determining fatigue strength. In this study, 3-point bending fatigue test was conducted to evaluate fatigue strength for the carburized depth with 18CrNiMo7-6 steel. As a result, fatigue strength increased with effective case depth decreased. It is shown that hardness in case hardened layer played principal role in the fatigue strength.
The 316LVM stainless steel that is widely used in surgical implant has been studied. The objective of this study is to develop the domestic production of the surgical implant materials. In the work, the metalllirgical phenomena, physical and chemical properties and biocompatibility of the materials are investigated. According to the experimental observation, corrosion resistance is strongly depended on the -ferrite structure and passive film, and mechanical properties are mainly depended on the cold reduction ratio. The -ferrite structure is minimized in the 16.651 Cr and 14%Ni contents, and yield strength is 104 kg/mm$^2$ at 45% cold reduction. Biocompatibility is excellent in the mouse body test for six weeks.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.