• Journal of Powder Materials
• /
• v.26 no.4
• /
• pp.319-326
• /
• 2019

Additive manufacturing (AM) is a highly innovative method for joining dissimilar materials for industrial applications. In the present work, AM of STS630 and Ti-6Al-4V powder alloys on medium entropy alloys (MEAs) NiCrCo and NiCrCoMn is studied. The STS630 and Ti64 powders are deposited on the MEAs. Joint delamination and cracks are observed after the deposition of Ti64 on the MEAs, whereas the deposition of STS630 on the MEAs is successful, without any cracks and joint delamination. The microstructure around the fusion zone interface is characterized by scanning electron microscopy and X-ray diffraction. Intermetallic compounds are formed at the interfacial regions of MEA-Ti64 samples. In addition, Vicker's hardness value increased dramatically at the joint interface between MEAs and Ti-6Al-4V compared to that between MEAs and STS630. This result is attributed to the brittle nature of the joint, which can lead to a decrease in the joint strength.

• Transactions of Materials Processing
• /
• v.22 no.3
• /
• pp.165-170
• /
• 2013

High temperature deformation behavior of a heat-resistant duplex stainless steel, used as a retort in the Pidgeon process for Mg production, was investigated in this study. 25Cr-8Ni based duplex stainless steels were cast into rectangular ingots, with dimensions of $350mm{\times}350mm{\times}100mm$. Nitrogen and yttrium were added at 0.3wt.% each to enhance the heat-resistance of the steel. Phase equilibrium was calculated using the thermodynamic software FactSage$^{(R)}$ and the database of FSStel. For comparison, cast 310S steel, a widely used heat-resistant austenitic stainless steel, was also examined in this study. Dilatometry was conducted on the as-cast ingots for the temperature range from RT to $1200^{\circ}C$ and the thermal expansion coefficients were evaluated. The nitrogen addition was found to have an effect on the thermal expansion behavior for temperatures between 800 and $1000^{\circ}C$. High temperature tensile and compression tests were conducted on the ingots for temperatures ranging from 900 to $1230^{\circ}C$, which is the operation temperature employed in Mg production by the Silico-thermic reduction process. The steel containing both N and Y showed much higher strength as compared to 310S.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.2
• /
• pp.99-107
• /
• 1999

The graphitization is affected by the addition of small amount of the elements(such as Si, Al, Ni, B, Cr and Mn etc.) and the pre-treatment(such as cold rolling). Boron is well known element to accelerate the graphitization of cementite in high carbon steels. Also, cold rolling is known to accelerate the graphitization. But the graphitization nucleation mechanism by cold rolling is few reported. Therefore the effect of cold rolling in Fe-0.5%C-1.0%Si-0.47%Mn-0.005%B steel on the graphitization is investigated quantitatively using hardness test, optical microscope and scanning electron microscope, neutron induced microscopic radiography. The nucleation of graphite in cold-rolled Fe-0.5%C-1.0%Si-0.47%Mn-0.005%B steel is formed at void which is formed at pearlite/pearlite boundary by cold rolling. But the effect of cold rolling on graphitization in boron addition steel is more effective than that of no boron addition steel due to segregation of BN at void in boron addition steel.

• Journal of the Korean Society for Heat Treatment
• /
• v.23 no.5
• /
• pp.263-268
• /
• 2010

This investigation was focused on the low temperature tensile properties, phase change, changes in nitrogen content and corrosion resistance in the 22Cr-5Ni-3Mo duplex stainless steel after high temperature gas nitriding and solution annealing (HTGN-SA). From the HTGN-SA treatment, the duplex (ferrite + austenite) phase changed into austenite single phase. The nitrogen content of austenite single-phase steel showed a value of ~0.54%. For the HTGN-SA treated austenitic steel, tensile strength increased with lowering test temperature, on the other hand elongation showed the maximum value of 28.2% at $-100^{\circ}C$. The strain-induced martensitic transformation gave rise to lead the maximum elongation. After HTGN-SA treatment, corrosion resistance of the austenite single-phase steel increased remarkably compared with HTGN- treated steel.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.109-109
• /
• 2018

Cr-Mo 합금강은 고온 환경 하에서 높은 크리이프 강도와 우수한 내식성 때문에 발전설비, 석유 화학, 그리고 해양산업과 같은 여러 산업분야에서 널리 사용되고 있다. 특히, Cr-Mo 강의 내식성은 합금 내 Cr 함량에 크게 의존한다. 이는 고온에서 Cr과 O가 화학적 반응을 일으킴에 따라 보호성의 Cr 산화스케일을 형성하기 때문이다. 그러나 화석연료를 사용하는 발전설비의 경우, $SO_2$가 포함된 강한 부식성의 연소 가스가 배출되며, 이에 노출된 금속의 표면에서는 산화와 황화가 동시에 발생한다. 황화스케일은 산화스케일에 비해 매우 빠르게 성장하며, 그 특성이 매우 취약하기 때문에 황화 환경에서 금속의 내식성 및 기계적 물성치는 보다 크게 저하된다. 따라서 본 연구에서는 화력 발전소의 증기발생용 튜브 재료인 9Cr-1MoVNb 강을 선정하였으며, $SO_2$ 가스 환경 하에서의 부식 및 기계적 물성치 저하 특성을 평가하고자 하였다. 본 연구에서 사용된 9Cr-1MoVNb강의 화학 성분 조성은 0.1 C, 0.38 Si, 0.46 Mn, 0.25 Ni, 8.38 Cr, 0.93 Mo, 0.18 V, 0.09 Nb, 그리고 나머지는 Fe이다. 부식시험은 가공된 미소시험편과 인장시험편을 전기열처리로에 장입한 후, $650^{\circ}C$에서 $N_2+O_2+O_2+SO_2$ 조성의 가스를 분당 50 CC로 흘려주었다. 제작된 시험편에 대한 부식거동은 무게 증가량, optical microscope, scanning electron microsope, 그리고 energy dispersive x-ray spectrum을 통해 평가하였다. 그리고 기계적 물성치 평가를 위한 인장시험은 분당 2mm 변위제어를 통해 실시하였다. 그 결과, 9Cr-1MoVNb 강은 $SO_2$ 가스 환경 하에서 비 보호적인 Fe-풍부상의 산화 스케일층이 두껍게 형성됨에 따라 열악한 내식성을 나타냈다. 그에 따라 기계적 물성치는 저하되는 경향을 나타내었다.

• Journal of the Korean institute of surface engineering
• /
• v.20 no.2
• /
• pp.49-59
• /
• 1987

The properties of $Cr_2O_3-Al_2O_3-SiO_2$ composite oxide coatings on steel surface were investigated. The results obtained were as follows: The microhardness of oxide coating layer increased with increasing heat-treatment temperature and $Cr_2O_3$ content in coating layer. The hardness showed the highest value (850Hv) treated at 700$^{\circ}C$ for $SiO_2:Al_2O_3:Cr_2O_3$=1:1:4. Increasing heat-treatment temperature, corrosion current density became lower and coating layer became denser. The corrosion current density showed the lowest value $(6.5{\times}10^{-5}\;Acm^2)$ treated at 750$^{\circ}C\;for\;SiO_2:Al_2O_3:Cr_2O_3$=1:1:3. These results were explained by protective layer which was formed during heat-treatment. The bonding between matrix and coating layer is expected to be made mechanically and chemically by the inter diffusion of Ni and Fe. The composite oxide coating was formed by softening of the binder with increasing heat-treatment temperature. The strengthening of coating layer is to be resulted from the dispersion of major oxide particles.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.4
• /
• pp.344-348
• /
• 2016

Stainless steel is widely applied in many industrial fields due to its excellent anti-corrosion and durability characteristics. However, stainless steel is very vulnerable to cavitation attack caused by high speed flow of fluid in the chloride environments such as marine environment. These conditions promote intergranular corrosion and cavitation-erosion, leading to degradation of the structural integrity and service life. In order to prevent these problems, the stabilized stainless steel is applied to the offshore and shipbuilding industries. In this study, Ti was added to 19%Cr-9%Ni as the stabilizer element with different concentrations (0.26%, 0.71%), and their durabilities were evaluated with cavitation-erosion experiment by a modified ASTM G32 method. The microstructural change was observed with the stabilizer element contents. The result of the observation indicated that the amount of carbide precipitation was decreased and its size became finer with increasing Ti content. In the cavitation-erosion experiment, both weight loss and surface damage depth represented an inverse proportional relationship with the amount of Ti element. Consequently, the stainless steel containing 0.71% of Ti had excellent durability characteristics.

• Korean Journal of Materials Research
• /
• v.3 no.6
• /
• pp.668-677
• /
• 1993

The microstructural and shear tests of STS304/, STS430/ and low-C steel/Cu joints brazed using Cu-P, Cu-P-Sn(four type) and Cu-P-Sn-Ag(three type) filler metals at 1003 and 1033K for 1.2ks in Ar atomsphere were performed. Interfacial microstructures were divided into three type ; first, reaction layer contained cracks second, dispersed layer without cracks third, dispersed layer and reaction layer contained cracks. The joints composed only of dispersed layer without cracks have the high shear strength of above 40-60 MPa and result in failure in copper base metal. Low shear strength and joint failure result from the formation of reaction layer which induced cracks. The reaction layer is a Fe-P compound. This tendency of microstructure and shear strength depends on the existence and/or nonexistence of Sn in filler metals as well as Ni (and Cr) in base metals.

• Korean Journal of Materials Research
• /
• v.13 no.2
• /
• pp.126-132
• /
• 2003

In order to evaluate the corrosion resistance at the anode side separator for molten carbonate fuel cell, STS316 and SACC-STS316 (chromium and aluminum were simultaneously deposited by diffusion into STS316 authentic stainless steel substrate by pack-cementation process) were applied as the separator material. In case of STS316, corrosion proceeded via three steps ; a formation step of corrosion product until stable corrosion product, a protection step against corrosion until breakaway occurs, a advance step of corrosion after breakaway. Especially, STS316 would be impossible to use the separator without suitable surface modification because of rapid corrosion rate after formation of corrosion product, occurs the severe problem on stability of cell during long-time operation. Whereas, SACC-STS316 was showed more effective corrosion resistance than the present separator, STS316 due to the intermetallic compound layer such as NiAl, Ni3Al formed on the surface of STS316 specimen. And it is anticipated that, in order to use SACC-STS316 alternative separator at the anode side, coating process, which can lead to dense coating layer, has to be developed, and by suitable pre-treatment before using it, very effective corrosion resistance will be achieved.

• Structural Engineering and Mechanics
• /
• v.72 no.2
• /
• pp.245-256
• /
• 2019

The experimentally determined mechanical behavior of the material under the prescribed service conditions is the basis of advanced engineering optimum design. To allow experimental data on the behavior of the material considered, uniaxial stress tests were made. The aforementioned tests have enabled the determination of mechanical properties of material at different temperatures, then, the material's resistance to creep at various temperatures and stress levels, and finally, insight into the uniaxial high cyclic fatigue of the material under different applied stresses for prescribed stress ratio. Based on fatigue tests, using modified staircase method, fatigue limit was determined. All these data contributes the reliability of the use of material in mechanical structures. Data representing mechanical properties are shown in the form of engineering stress-strain diagrams; creep behavior is displayed in the form of creep curves while fatigue of the material is presented in the form of S-N (maximum applied stress versus number of the cycles to failure) curve. Material under consideration was 18CrNi8 (1.5920) steel. Ultimate tensile strength and yield strength at room temperature and at temperature of $600^{\circ}C$: [${\sigma}_{m,20/600}=(613/156)MPa$; ${\sigma}_{0.2,20/600}=(458/141)MPa$], as well as endurance (fatigue) limit at room temperature and stress ratio of R = -1 : (${\sigma}_{f,20,R=-1}=285.1MPa$).