• Journal of the Korean Ceramic Society
• /
• v.41 no.6
• /
• pp.450-455
• /
• 2004

NiCr thin films were fabricated by thermal evaporation method using NiCr alloy as evaporating source. NiCr thin films were annealed at various temperatures in air atmosphere in order to investigate effects of annealing conditions on phase change, composition, and microstructures of NiCr films. Typical multilayer was formed after annealing in air atmosphere. This results from the diffusion and oxidation of Cr toward surface during annealing. In the case of annealing at 700$^{\circ}C$, large columnar grains of NiO were formed on Cr-oxide layer through the diffusion and oxidation of Ni over Cr-oxide layer. Especially, NiO layer was formed additionally on surface, sustaining the underlayer structure with the formation of porous Ni layer.

• Journal of Sensor Science and Technology
• /
• v.1 no.1
• /
• pp.23-34
• /
• 1992

In order to fabricate magnetoresistive sensor, Fe-Ni and Co-Ni alleys were evaporated on the slide glass and the silicon wafers. Saturation magnetic induction($B_{s}$), coercive field strength($H_{c}$) and magnetoresistance were measured for fabricated samples. The evaporated Fe-Ni thin films show that the saturation magnetic induction was 0.65 T, and coercive field strength was 0.379 A/cm, and this value was changed to 0.370 A/cm(//), 0.390 A/cm(${\bot}$), respectively after magnetic annealing. For the measurement of coercive field strength, magnetizing frequency of 1 kHz was used. For the fabricated sensor element, the change of magnetoresistance (${\Delta}R/R$) was excessively unstable due to oxidation in the process of fabrication. The evaporated Co-Ni alloy thin films show that saturation magnetic induction was 0.66 T, and coercive field strengthes were 5.895 A/cm(//), 5.898 A/cm(${\bot}$), respectively, after magnetic annelaing. The change of magnetoresistance(${\Delta}R/R$) was $3.6{\sim}3.7%$ of which value was excessively stable to room temperature. Fe-Ni thin film could have many problems due to large affinity in the process of fabrication of magnetoresistance sensor, but Co-Ni thin film could be a suitable material for fabrication of magnetoresistance sensor, because of its small affinity and definite magnetoresistance effects.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.27-32
• /
• 2006

[$YBa_2Cu_3O_{7-x}$] thin films were deposited on various buffered-templates by a metal organic chemical vapor deposition(MOCVD). Three different templates of $CeO_2/YSZ/CeO_2/pure-Ni(CYC),\;CeO_2/YSZ/Y_2O_3/Ni-3at.%W(YYC)$ and $CeO_2/IBAD-YSZ$/stainless steel were used. The Ni and Ni-W alloy tapes were biaxially textured by cold rolling and annealing heat treatment. The dense YBCO films were grown on both the IBAD and YYC templates with no microcrack, while the YBCO films on the CYC templates were grown with the formation of microcracks and NiO. The YBCO film on the YYC template showed the higher $I_c$ than that on CYC template. Especially, the IBAD templates with a thin $CeO_2$(type I) and thick $CeO_2$(type II) top layer were used to compare the deposition nature of the YBCO on them. Comparing the current property of the YBCO films on IBAD templates, the YBCO film deposited on thick $CeO_2$ layer was better than the film on thin $CeO_2$ layer.

• Journal of Sensor Science and Technology
• /
• v.4 no.1
• /
• pp.9-14
• /
• 1995

To fabricate low field magnetic sensors using magnetoresistance(MR) effects, we deposited thin layers of $600{\AA}$ in thickness of Ni-Co(0.7Ni-0.3Co) alloy on slide glasses. In the layers we ordered 4 arms of the fullbridge sensors in the shape of grid structure to be inclined at an angle of $45^{\circ}$ to main axis and made the areal rate increase to 67%. While the response characteristics of the fabricated sensors had good linearity in the magnetic field of ${\pm}0.5mT$ ranges, the white noise was 0.2 nV and the voltage sensitivity was 7.6 $nV/{\mu}T$.

• Korean Journal of Materials Research
• /
• v.6 no.11
• /
• pp.1099-1106
• /
• 1996

니켈-수소화물전지의 음극재료로서 주목을 받고 있는 다원계 Zr기 Laves 합금의 조성에 따른 결정구조, 방전특성등을 조사하였다. 전극은 아크 용해한 합금을 분쇄한 분말과 PVA를 다공성니켈 foam에 충진하여 제작하였고 충방전시험은 6M KOH 용액중에서 수행하였다. 대상 합금은 ZrNi2를 기본조성으로 하여 이중 Ni의 일부를 V, Mn, Cr, Mo 또는 W로 치환한 삼원계 및 사원계 합금이었다. 이들 합금의 충방전 실험결과 ZrV0.5Mn0.5Ni1.0의 경우가 260 mAh/g로 가장 높은 방전용량을 나타내었다. 이 합금의 방전용량은 방전전류밀도의 영향을 크게 받았으며 10 mA/g과 200mA/g의 방전전류에서 각각 300mAh/g와 150mAh/g이었다. 이 합금을 110$0^{\circ}C$에서 열처리한 경우 저율방전시에는 방전용량의 변화가 거의 없었으나 수소의 확산이 율속이 될 것으로 생각되는 고율 방잔시에서는 방전용량이 현저하게 감소하였다. 이러한 현상은 열처리에 의해 수소의확산을 용이하게 해주는 격자결함이 감소하기 때문이 아닌가 생각된다.

• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.787-796
• /
• 2009

The fracture toughness improvement of Ni-Mn-Ga-Fe ferromagnetic shape memory alloys containing ductile particles was explained by direct observation of microfracture processes using an in situ loading stage installed inside a scanning electron microscope (SEM) chamber. The Ni-Mn-Ga-Fe alloys contained a considerable amount of ductile particles in the grains after the homogenization treatment at $800{\sim}1100^{\circ}C$. ${\gamma}$ particles were coarsened and distributed homogeneously along {$\beta}$ grain boundaries as well as inside {$\beta}$ grains as the homogenization temperature increased. The in situ microfracture observation results indicated that ${\gamma}$ particles effectively acted as blocking sites of crack propagation, and provided stable crack growth that could be confirmed by the R-curve analysis. This increase in fracture resistance with increasing crack length improved overall fracture properties of the alloys containing ${\gamma}$ particles.

• Korean Journal of Materials Research
• /
• v.33 no.2
• /
• pp.77-86
• /
• 2023

High-temperature oxidation of a Ni-based superalloy was analyzed with samples taken from gas turbine blades, where the samples were heat-treated and thermally exposed. The effect of Cr/Ti/Al elements in the alloy on high temperature oxidation was investigated using an optical microscope, SEM/EDS, and TEM. A high-Cr/high-Ti oxide layer was formed on the blade surface under the heat-treated state considered to be the initial stage of high-temperature oxidation. In addition, a PFZ (γ' precipitate free zone) accompanied by Cr carbide of Cr₂₃C₆ and high Cr-Co phase as a kind of TCP precipitation was formed under the surface layer. Pits of several ㎛ depth containing high-Al content oxide was observed at the boundary between the oxide layer and PFZ. However, high temperature oxidation formed on the thermally exposed blade surface consisted of the following steps: ① Ti-oxide formation in the center of the oxide layer, ② Cr-oxide formation surrounding the inner oxide layer, and ③ Al-oxide formation in the pits directly under the Cr oxide layer. It is estimated that the Cr content of Ni-based superalloys improves the oxidation resistance of the alloy by forming dense oxide layer, but produced the σ or µ phase of TCP precipitation with the high-Cr component resulting in material brittleness.

• Progress in Superconductivity
• /
• v.7 no.1
• /
• pp.69-76
• /
• 2005

Complex single buffer composed of yttrium and samarium oxide was deposited on the metallic substrates by MOCVD (metal organic chemical vapor deposition) method using single liquid source. Two different types of the substrates with in-plane textures of about $8{\sim}10$ degree of Ni and $3at.\%W-Ni$ alloy were used. Y(tmhd: 2,2,6,6-tetramethyl-3,5-heptane dionate)$_3$:Sm(tmhd)$_3$ of liquid source was adjusted to 0.4:0.6 to minimize the lattice mismatch between the complex single buffer and the YBCO. The epitaxial growth of $(Y_{x}Sm_{1-x})_{2}O_3$ was achieved at the temperature higher than $500^{\circ}C$ in $O_2$ atmosphere. However, it was found that the formation of NiO accelerated with increasing deposition temperature. By supplying $H_{2}O$ vapor, this oxidation of the substrate could be suppressed throughout the deposition temperatures. We could get the epitaxial growth on pure Ni substrate without the formation of NiO. The competitive (222) and (400) growths were observed at the deposition temperatures of $650\~750^{\circ}C$, but the (400) growth became dominant above $800^{\circ}C$. The $(Y_{x}Sm_{1-x})_{2}O_3$-buffered metallic substrates can be used as the buffer for YBCO coated conductor.

• Journal of Hydrogen and New Energy
• /
• v.9 no.4
• /
• pp.169-176
• /
• 1998

An experimental study on effect of vapor-cooled heat stations in a 5.5 liter cryogenic vessel has been performed. The cryogenic vessel is made of stainless steel of thickness of 1mm and insulated by the combined insulation of vacuum, MLI(multi-layer insulation) and vapor-cooled radiation shield. Vapor-cooled heat stations are also constructed based on the 1-dimensional thermal analysis to reduce the heat inleak through a filling tube. Thermal analysis indicates that the vapor-cooled heat stations can substantially enhance the performance of vessel for cryogenic fluids with high $C_p/h_{fg}$ where $C_p$ the specific heat and $h_{fg}$ the heat of vaporization, such as $LH_2$ and LHe. The experimental results for $LN_2$ shows that the total heat inleak into inner vessel consists of 14% radiation and 86% conduction through the filling tube. Therefore, it is expected that the conduction heat in leak of the vessel for high $C_p/h_{fg}$ cryogenic fluids can be significantly reduced. powders. The amount of copper coating was 20wt%. In order to examine corrosion behavior of the electrodes, the corrosion current and the current density, in 6M KOH aqueous solution after removal of oxygen in the solution, were measured by potentiodynamic and cyclic voltamo methods. The results showed that Co in the alloy increased corrosion resistance of the electrode whereas Ni decreased the stability of the electrode during the charge-discharge cycles. The electrode used Si sealant as a binder showed a lower corrosion current density than the electrode used PTFE and the electrode used Cu-coated alloy powders showed the best corrosion resistance.

• Archives of design research
• /
• v.17 no.4
• /
• pp.241-250
• /
• 2004

In this research, the copper alloy plates C2200, C5210, C7701, C8113 were selected to make datum and to identify further usage of metal craft experimentation. For its experimentation, the general welding and TIG welding methods were researched; for 2nd experimentation, the Reticulation and Electroforming skill's differences in color and temperature were researched. With these methods 3 different kinds of works are introduced for sample studies. For this research, Dr. Lee, Dong-Woo who works in Poongsan Metal Co, supported 4 kinds of copper alloy metals. Which are Commercial bronze (Cu-Zn), Deoxidiged Copper(Cu-Sn-P), Nickel Silver (Cu-Ni-Zn), and White Bronze (Cu-Ni); they were applied partly and wholly by the method of Laminatin, Reticulation, Fusing, and Electroforming skills. In case of C2200, the brass, the A. C. TIG welding method is better under 2mm slight plate; the D.C. TIG welding is better upper 2mm plate; and 250~300$^{\circ}C$ is recommended for remain heat treatment. In case of C5210, not having Hydrogen in high temperature return period, doesn't need Oxygen in high temperature and hardening in comparative high temperature neither, it is good for welding. It contains Sn 2-9% ad P 0.03-0.4% generally; and in accordance with the growth rate of Sn contain amount, the harden temperature boundary become broad. In case of cold moment after welding, they are recommended that higher speed TIG welding, smaller melting site and less than 200$^{\circ}C$ for pre-heating temperature. In case of C7701, the 10-20% Ni, 15-30% Zn are widely used.. If it is upper 30% Zn, it become (${\alpha}+{\beta}$) system and adhesive power rate become lower, and the productivity become lower in low temperature but the productivity become higher in high temperature. Nickel Silver's resistance of electricity is well; and the heatproof and incorrodibility is good, too. Lastly, in case of C8113, good at persistence in salty and grind; high in strength of high temperature. In case of white brass, contain 10-30% Nickel and hardened in high temperature and become single phrase. For these reason, the crystallization particles easily become large, if the resistance become higher small amount of Pb, P, S separation rate become higher.