• Journal of Welding and Joining
• /
• v.11 no.1
• /
• pp.62-72
• /
• 1993

Recently there is an increased interest in joining of ceramics to metals and brazing now an accepted method of joining for a wide variety of ceramic to metal combination. The present research work is aimed at establishing the basis of the metal-ceramic joining of $Al_{2}$O$_{3}$ to STS 304 with using Cu-7.5wt% Zr insert metals. Also the microstructures of the brazed joints were observed by using optical microscope and SEM and the reaction products were analyzed by using EDX, WDX and XRD. As a result, the following findings were obtained. The reaction layers of the brazed joints of $Al_{2}$O$_{3}$ to STS 304 are composed of four layers at the bonded interlayer. Double reaction layers are formed at the interface of $Al_{2}$O$_{3}$ insert metal. Layer I was composed of ZrO$_{2}$ particles, Fe-Cr-Ni compounds in Cu matrix, while layer II ZrO$_{2}$ band phase containing Fe-Cr-Ni compounds.

• Transactions of the Korean hydrogen and new energy society
• /
• v.27 no.3
• /
• pp.306-310
• /
• 2016

In Na-base Battery for ESS, ${\alpha}-Al_2O_3$ and metal bonding was used to prevent direct reaction between electrolyte and electrode. The hard metal was metalized at $1600^{\circ}C$ in a flowing hydrogen gas for high bonding strength. In this study, instead of hard metal metalizing, Ni was plated on ${\alpha}-Al_2O_3$ by electroless Ni plating technique and then bonded with metal. To enhance the bonding strength, surface of ${\alpha}-Al_2O_3$ was treated with $H_3PO_4$. The effects of strength and leakage of joining as a function of acid treatment time on ${\alpha}-Al_2O_3$ are described.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.3
• /
• pp.50-61
• /
• 1995

In recent years, many ceramic researchers have discoved various methods of joining ceramic to metal. However, most of these joining methods are perfomed under vacuum and pressured circumstances. So, when we join ceramic to metal,the proceedings are very complicated and require a very high cost. The purpose of this study is to develop a new joining method of an alumina ceramic to an aluminum metal in air atmosphere. The joining condition, such as copper metallizing, nickel plating, brazing, etc. was investigated through the shear strength test of the trial joint. The results obtained from the above experimenta are summarized as follows : 1) In the case of the $Al_2O_3$/$Al_2O_3$joint, the shear strength of the joint was affected by the various foctor such as kaolin content, copper metallizing thickness, firing temperature, firing time. 2) The better shear strength of the $Al_2O_3$/Al joint was obtained when Ni plating was conducted under higher current density than existing plating condition. 3) The shear strength of the $Al_2O_3$/Al joint increases with the Ni plating thickness is confined to the range of this paper. 4) The shear strength of the thermal-shocked specimen($Al_2O_3$/Al joint) was far more deteriorated than that of the as-bonded specimen.

• Journal of Welding and Joining
• /
• v.10 no.3
• /
• pp.63-72
• /
• 1992

The joining methods of ceramics to metals which can be expected to obtain high temperature strength are mainly classified into the solid-state diffusion bonding method and the active brazing method. Between these two, the solid-state diffusion bonding method is given attentions as substituting method for active brazing method due to being capable of obtaining higher bonding strength at high temperature and accurate bonding. In this paper, the solid-state diffusion bonding of $Al_{2}$O$_{3}$ ceramics to Ni-Cr-Mo alloy steel (SNCM21) using insert metal was carried out. The insert metal employed in this study was experimentally home-made, Ag-Cu-Ti alloy. Influence of several bonding parameters of $Al_{2}$O$_{3}$SNCM21 joint was quantitatively evaluated by bonding strength test, and microstructural analyses at the interlayer were performed by SEM/EDX. From above experiments, the optimum bonding condition of the solid-state diffusion bonding of $Al_{2}$O$_{3}$/SNCM21 using Ag-Cu-Ti insert metal was determined. Futhermore, high temperature strength and thermal-shock properties of $Al_{2}$O$_{3}$/SNCM21 joint were also examined. The results obtained are as follows. 1. The maximum bonding strength was obtained at the temperature of 95% melting point of insert metal. 2. The high temperature strength of $Al_{2}$O$_{3}$/SNCM21 joint appeared to bemaximum value at test temperature 500.deg.C and the bonding strength with increasingtemperature showed parabolic curve. 3. The strength of thermal-shocked specimens was far deteriorated than those of as-bonded specimens. Especially, water-quenched specimen after heated up to 600.deg. C was directly fractured in quenching.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.117.2-117.2
• /
• 2007

• Journal of Welding and Joining
• /
• v.18 no.3
• /
• pp.51-59
• /
• 2000

Sink roll has been used in molten 55%Al-Zn alloy bath of continuous galvanizing line for sinking and stabilizing working steel strip in molten metal bath. In the process, the sink roll body inevitably build up dross compounds and pitting on the sink roll surface during 55%Al-Zn alloy coated strip production, and the life time of the sink roll is shorten by build up dross compounds and pitting. The present study examined the application of thermally sprayed ceramic coatings method on sink roll body for improving erosion resistance at molten 55% Al-Zn pool. In this experiment, the stainless steels such as STS 316L and STS 430F were used as the substrate materials. The CoNiCr and WE-Co powder were selected as bond coating materials. Moreover $Al_2O_3-ZrO_2-SiO_2 and ZrO_2-SiO_2$ powders selected as the top coating materials. Appearances of the specimens before and after dipping to molten 55%Al-Zn pool were compared and analyzed. As a result of this study, STS430F of substrate, WC-Co of bond spray coatings, $ZrO_2-SiO_2$ power of top spray coatings is the best quality in erosion resistance test at molten 55%Al-Zn pool

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.114-116
• /
• 2003

The multi function sprayed coating is used for direct-heating, wear resistance and high bonding strength. The merits of surface direct-heating coatings are short warming time, low power consumption and better wear resistance that can be used in many organization parts. In this study, the surface direct-heating and wear resistance can be improved by spraying the proper materials on the surface $Al_2$O$_3$40%TiO$_2$ powder and Ni-20%Cr powder that had the properties of conduction and high wear resistivity are used in order to improve wear resistance, electrical properties and bonding strength.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2008.05a
• /
• pp.42.1-42.1
• /
• 2008

• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.134-146
• /
• 1995

Aluminium nitride(AlN) is currently under investigation as potential candidate for replacing alumium oxide(Al$_{2}$ $O_{3}$) as a substrate material for for electronic circuit packaging. Brazing of aluminium nitride(AlN) to Cu with Ag base active alloy containing Ti has been investigated in vacuum. Binary Ag$_{98}$ $Ti_{2}$(AT) and ternary At-1wt.%Al(ATA), AT-1wt.%Ni(ATN), AT-1wt.% Mn(ATM) alloys showed good wettability to AlN and led to the development of strong bond between brate alloy and AlN ceramic. The reaction between AlN and the melted brazing alloys resulted in the formation of continuous TiN layers at the AlN side iterface. This reaction layer was found to increase by increase by increasing brazing time and temperature for all filler metals. The bond strength, measured by 4-point bend test, was increased with bonding temperature and showed maximum value and then decreased with temperature. It might be concluded that optimum thickness of the reaction layer was existed for maximum bond strength. The joint brazed at 900.deg.C for 1800sec using binary AT alloy fractured at the maximum load of 35kgf which is the highest value measured in this work. The failure of this joint was initiated at the interface between AlN and TiN layer and then proceeded alternately through the interior of the reaction layer and AlN ceramic itself.