• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.552-557
• /
• 2004

Thin Ni-B films, 1 ${\mu}m$ thick, were electrolessly deposited on Cu bus electrode fabricated by electro deposition. The purpose of these films is to encapsulate Cu electrodes for preventing Cu oxidation and to serve as a diffusion barrier against copper contamination of dielectric layer in AC-plasma display panel. The layers were heat treated at $580^{\circ}C$(baking temperature of dielectric layer) with and without pre-annealing at $300^{\circ}C$($Ni_{3}B$ formation temperature) for 30 minutes. In the layer with pre-annealing, amount of Cu diffusion was lower about 5 times than that in the layer without pre-annealing. The difference of Cu concentration could be attributed to Cu diffusion before $Ni_{3}B$ formation at grain boundaries. However, the diffusion behavior of the layer with pre-annealing was similar to that of the layer without pre-annealing after $Ni_{3}B$ formation. With increasing annealing time, Cu concentration of both layers increased due to grain growth.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.4
• /
• pp.495-503
• /
• 2011

The sealed nickel-metal hydride (Ni-MH) secondary battery are primarily used as energy storage for the HEV. But, the research on Ni-MH battery has focused on anode materials. In the present study, we investigate to improve the electrochemical characteristics of Ni-MH batteries using the surface treatment of $Ni(OH)_2$ cathode by CoOOH. Surface treated $Ni(OH)_2$ cathode showed significant improvement in the activation behavior, rate capability, charge retention, and cycle life of the batteries were significantly improved. In addition, the surface treated electrode exhibited the higher overvoltage for oxygen evolution than the untreated electrode. This phenomenon indicates that the charge efficiency can be improved by suppressing the oxygen evolution on cathode.

• Journal of the Korean Ceramic Society
• /
• v.43 no.12 s.295
• /
• pp.764-767
• /
• 2006

Ni/YSZ $(Y_2O_3-stabilized\;ZrO_2)$ composite as an electrode component for High Temperature Electrolysis (HTE) was fabricated by mechanical alloying method using Ni and YSZ powders. Characterization of the synthesized composite was investigated with various analysis tools, including XRD, SEM and PSA, and a self-supporting planar unit cell prepared with the Ni/YSZ composite was prepared to study the electrochemical reactions for the production of hydrogen. The Ni/YSZ cermet is composed of crystalline Ni and YSZ, in a sub-micro scale, and has an even distribution without aggregated particles. In addition, under an electrochemical reaction, the unit cell showed an $H_2$ evolution rate from steam of 14 Nml/min and $600mA/cm^2$ of current density at the electrode.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.1
• /
• pp.37-42
• /
• 2021

Electrodeposition is a synthetic method that allows fine control of the nucleation and growth factors of metals and is a suitable method for studying the nucleation and growth of Ni(OH)2. Hexa-methylenetetramine (HMT) helps to form Ni(OH)2 nanosheets by increasing the OH- of the nickel precursor solution and helps to improve the electrochemical properties of the electrode. In this study, the structural properties of Ni(OH)2 nanosheets according to the HMT concentration change using electrodeposition were studied. As the concentration of HMT increased, the size and thickness of the Ni(OH)2 nanosheet adsorbed on the surface increased and porosity increased. Also, the Scharifker-Hills nucleation theory model and experimental data were compared. In conclusion, the nanosheet shape of the HMT 7.5 mM sample electrodeposited with -0.85 V vs. Ag/AgCl grew most uniformly, and the best result was obtained as an electrode material for a pseudocapacitor.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1993.11a
• /
• pp.69-71
• /
• 1993

Fluoride compound potentiometric cell oxygen sensors were fabricated for the measurement of oxygen pressure in the low temperature range (300。K-500。K). The disk type sensors consist of a reference Air(0$_2$):Ag, a solid electrolyte SrF$_2$, and a sensing metel Ag electrode. And the buried reference electrode type sensor have a NiO/Ni reference electrode. The open circuit emf of the cell showed high sensivity to oxygen gas (60mv) at the measuring temperature 20$0^{\circ}C$. Also, The buried reference electrode type sensor showed 30mv from 1% to 10% oxygen pressure range.

• Journal of the Korean Society of Industry Convergence
• /
• v.19 no.4
• /
• pp.198-205
• /
• 2016

For the study on the ion exchange of nickel hexacyanoferrate(NiHCNFe) electrode with the several cations, the film of hexacyanoferrate was prepared on the bare nickel surface by the electrochemical and chemical methods in the solution composed with 5mM K3Fe(CN)6 and 100mM KNO3. To compare the capability of the ion exchange of NiHCNFe film electrode, the repeated cyclic voltammograms were measured in the 0.5M cation nitrate solutions at $25^{\circ}C$ and pH7. It was found that the capacity of the electrochemically derivatized NiHCNFe reduced in the rate of 0.5~0.7%/cycle and was nearly exhausted at the 150th potential cycle. Better result was obtained from that the capacity loss of the chemically assembled NiHCNFe was less than 0.02%/cycle for 5,000cycles. Furthermore, the residual capacity was more than 30% at the 5,000th cycle.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.12
• /
• pp.83-89
• /
• 1996

The electrochemical spike oscillations at the nickel (Ni) electrode/(0.05M KHC$_{8}$H$_{4}$O$_{4}$) buffer solution (pH 9) interface have been studied using voltammetric and chronoamperometric methods. The nature of the periodic cathodic current spikes is the activation controlled currents due to the hydrogen evolution reaction and depends onthe fractioanl surface coverage of the adsorbed hydrogen intermediate or the cathodic potential. There is two kinds of the waveforms corresponding to two kinds of the cathodic current spike oscillations. The widths, periods, and amplitudes of the cathodic current spikes are 4 ms or 5ms, 151 ms or 302 ms, and < 30 mA or < 275 mA, respectively. The fast discharge and recombination reaction steps are 1.5 times and twice and faster than the slow discharge and recombination reaction steps. The fast and slow discharge and recombination reaction steps are 1.5 times and twice faster than the slow discharge and recombination reaction steps. The fast and slow discharge and recombination reactions corresponding to the fast and slow adsorption sites at the Ni cathode.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.2
• /
• pp.88-93
• /
• 2007

Nano-sized Sn particles were coated with Ni-P layer using an electroless deposition method and their anodic performance was tested for lithium secondary batteries. Uniform coating layers were obtained, of which the thickness was controlled by varying the $Ni^{2+}$ concentration in the plating bath. It was found that the Ni-P layer plays two important roles in improving the anodic performance of Sn powder electrode. First, it prevents the inter-particle aggregation between Sn particles during the charge/discharge process. Second, it provides an electrical conduction pathway to the Sn particles, which allows an electrode fabrication without an addition of conductive carbon. A pseudo-optimized sample showed a good cyclability and high capacity ($>400mAh\;g^{-1}$) even without conductive carbon loading.

• Journal of Advanced Marine Engineering and Technology
• /
• v.31 no.6
• /
• pp.729-735
• /
• 2007

AC cold arc welding process with AWS E Ni-CI and NiFe-CI is sometimes used to repair damaged cast iron parts in diesel engine room. But if some difference in hardness on welding zones, repaired parts would be cracked in a short. To overcome this default. this study is performed on varying preheating temperature of welding parts, selecting welding rod etc. Experimental results showed that difference in hardness on welding zones at $200^{\circ}C$ was less than $100^{\circ}C$ and less low current than high current. From this study we could conclude that repair welding at $200^{\circ}C$ preheating and low current as possible as welding in damaged cast iron parts was a little difference in hardness on welding zones.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.11a
• /
• pp.283-287
• /
• 2004

Arc welding is sometimes used to repair damaged cast iron parts in diesel engine for driving a ship. In this case cola arc welding. is good for. saving the time and results in good repairing. But if some difference in hardness on welding zones made with AWS E Ni-CI and NiFe-CI. happen, repaired parts would be cracked in a short. In order to overcome this default, the study is performed on varying preheating temperature of welding parts, selecting welding rod and welding work way. The result will be used on ship's repair working shop.