• The Korean Journal of Ceramics
• /
• v.5 no.3
• /
• pp.239-244
• /
• 1999

Ultrafine lead magnesium niobate $Pb(Mg_{1/3}Nb_{2/3}) O_3$ (PMN) powders have been successfully prepared via a micro-emulsion processing technique. By stepwise hydrolysis using aqueous as the precipitant, hydroxide precursor was obtained from nitrate solutions dispersed in the nanosized aqueous domains of a microemulsion consisting of cyclohexane, non-ionic surfactant (NP5+NP9) and an aueous phase. Upon calcination of the microemulsion-derived precursor at $800^{\circ}C$, PMN powders with 100% perovskite phase was obtained.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.7
• /
• pp.473-478
• /
• 2001

Ferroelectric P $b_{0.99}$［(Z $r_{0}$ 6S $n_{0.4}$)/0.9/ $Ti_{0.1}$］0.98/N $b_{0.02}$ $O_3$(PNZST) thin films were deposited by a RF magnetron sputtering on L $a_{0.5}$S $r_{0.5}$Co $O_3$(LSCO)/Pt/Ti/ $SiO_2$/Si substrate using a PNZST target with excess PbO of 10 mole%. The crystallinity and electrical properties of the thin films annealed at various temperature and time were investigated. The thin films deposited at the substrate temperature of 500 $^{\circ}C$ and the power of 80 W were crystallized to a perovskite phase after rapid thermal annealing(RTA). The thin films annealed at 650 $^{\circ}C$ for 10 seconds in air exhibited the good crystal structures. The remanent polarization and coercive field of the PNZST capacitor were about 20 $\mu$C/$\textrm{cm}^2$ and 50 kV/cm, respectively. The reduction of the polarization after 2.2$\times$10$^{9}$ switching cycles was less than 10 %..10 %......

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.869-873
• /
• 2004

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient, piezoelectric, and a photo refractive properties. In this study, SBN60(x=0.6) thin film was manufactured by ion beam sputtering technique. Using the prepared SBN60 target in $Ar/O_2$ atmosphere as-deposited SBN60 thin film on Pt(100)/$TiO_2/SiO_2/Si$ substrate crystallization and orientation behavior as well as electric properties of SBN60 thin film were examined. SBN60 deposition up to $3000{\AA}$ in thickness, SBN60 thin film was heat-treated at $650^{\circ}C{\sim}800^{\circ}C$. The orientation was shown primarily along (001) plane from XRD pattern where working pressure was $4.3{\times}10^{-4}$ torr. The deposited layer was uniform, preferred orientatin and crystallization behavior resulted in the change of $O_2$ ratio was observed. In electric propertie of Pt/SBN60/Pt thin film capacitor remnant polarization (2Pr) value was $10{\mu}C/cm^2$, the coercive filed (Ec) 50 kV/cm, and the dielectric constant 615, respectively.

• The Journal of the Petrological Society of Korea
• /
• v.8 no.2
• /
• pp.57-70
• /
• 1999

The volcanic rocks of Ulleungdo reveal very high alkali element abundances and most of them have high K20/Na20 ratios and belong to potassium-series. Ulleungdo volcanics show very wide range of variation in their composition from basalts to trachytic basalt, basaltic trachyandesite, trachyandesite, and finally to trachyte on total alkali-silica diagram. Such a general trend of compositional variation can be explained well by differentiation due to fractional crystallization of various minerals. Olivine, clinopyroxene, plagioclase, ilmenite, and apatite are suggested as the major fractionated minerals. Ulleungdo volcanics show Nb/U and PbICe ratios similar to oceanic volcanics such as MORB and OIB, but significantly different .from volcanic rocks of island arc environments, which suggest that they are not directly related with subduction along the Japanese arc. LREE abundances of Ulleungdo volcanics are highly enriched compared with HREE abundances ((La)N=193-420, (L~)~=7.5-19.5).O nly trachyte-1 show appreciable negative Eu anomalies among various rock types, which suggests significant amount of plagioclase were fractionated. However, trachyte-2, trachyte-3, phonolite, and pumice reveal quite different variation trend of trace and rare earth element abundances from trachyte-1, which suggest that they have originated from different magma batches and have experienced different differentiation processes. A prominent bimodal distribution, thus lacking of intermediate composition, is observed from the Ulleundo volcanics.

• Asian Pacific Journal of Cancer Prevention
• /
• v.13 no.8
• /
• pp.3791-3794
• /
• 2012

CD44v, especially splice variants containing exon v6, has been shown to be related closely to development of different tumors. High levels of CD44v6/v7 have been reported to be associated with invasiveness and metastasis of many malignancies. The objective of this study was to detect expression of CD44v6-containing variants in patients with acute promyelocytic leukemia (APL) and evaluate the potential of CD44v6/v7 for risk stratification. Reverse transcription polymerase chain reaction (RT-PCR) followed by PCR product purification, ligation into T vectors and positive clone sequencing were used to detect CD44 v6-containing variant isoforms in 23 APL patients. Real-time quantitative PCR of the CD44v6/v7 gene was performed in patients with APL and in NB4 cells that were treated with all-trans retinoic acid (ATRA) or arsenic trioxide ($As_2O_3$). Sequencing results identified four isoforms (CD44v6/v7, CD44v6/v8/v10, CD44v6/v8/v9/v10, and CD44v6/v7/v8/v9/v10) in bone marrow mononuclear cells of 23 patients with APL. The level of CD44v6/v7 in high-risk cases was significantly higher than those with low-risk. Higher levels of CD44v6/v7 were found in three patients with central nervous system relapse than in other patients inthe same risk group. Furthermore, in contrast to ATRA, only $As_2O_3$ could significantly down-regulate CD44v6/v7 expression in NB4 cells. Our data suggest that CD44v6/v7 expression may be a prognostic indicator for APL.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.327-328
• /
• 2006

본 연구에서는 0-3 타입의 압전 세라믹 - 고분자 복합소재를 제조하기 위해서 $Pb(Zr_{0.54}Ti_{0.48})O_3$ + 0.2 wt% $Cr_2O_3$ + 1 wt% $Nb_2O_5$ 조성을 기본 조성으로 하여, 세라믹-고분자 첨가량에 따른 복합소재의 전기적 특성과 여러 분극조건, 즉 분극온도, 분극시간, 분극전압 변화에 의한 압전 특성을 고찰하였다. 세라믹 첨가비율이 증가함에 따라 유전상수와 압전상수($d_{33}$)는 증가하였으며, 전압상수($g_{33}$)는 급격히 감소하는 경향을 보였으며, 분극시간과 분극전압도 전기적 특성에 영향을 주는 것을 확인하였다. 분극전압 5KV 인가한 고분자 15% 첨가한 복합 소재에서 유전상수 13, 압전상수 $d_{33}$ 23(${\ast}10^{-12}C/N$), 전압상수 $g_{33}$ 170($10^{-3}v.m/N$)의 우수한 특성을 나타내었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.8
• /
• pp.601-604
• /
• 2010

In this study, the piezoelectric energy harvester was investigated employing the pillar structure with the diameter size of 50~500 um. Usually, the aspect ratio between the height and diameter was related with the piezoelectric performance. High aspect ratio was showed the low electric noise and high piezoelectric properties than low aspect ratio. Therefore, we have selected the Su-8 photo-resist and modified lithography process to manufacture the pillar structure with height above the 250 ${\mu}m$. In this presentation, we will report the process and properties of micro pillar structure based on the PMN-PZT (Pb$(Mg_{1/3}Nb_{2/3})O_3$-PbZrTiO$_3$) materials.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.4
• /
• pp.232-240
• /
• 1999

In this study, the $(1-\chi)Ba(Mg_{\fraction one-third}Ta_{\fraction two-thirds}O_3-\chiBa(Co_{\fraction one-third}\Nb_{\fraction two-thirds})O_3$ ceramics($\chi$=0.3,0.4,0.5,0.6) were prepared by the conventional mixed oxide method. The ceramics were sintered at the temperature of $1500~1575^{\circ}C$ for5 hours in air. The BMT-BCN ceramics have a complex perovskite structure, and have peaks of (101), (102), (201), (202) and (212). Increasing the sintering temperature, dielectric constant was increased. Temperature coefficients of resonant frequency of the specimens were decreasing with increasing BCN content. In the case of the 0.7BMT-0.3BCN ceramics sintered at $1575^{\circ}C$ for 5 hours, dielectric constant, quality factor and temperature coefficient of resonant frequency for microwave dielectrics application were a good value of 28, 235500 at ㎓ and -$1.2 ppm/^{\circ}C$, respectively.

• ETRI Journal
• /
• v.31 no.6
• /
• pp.688-694
• /
• 2009

In this paper, we present the results of a preliminary study on the piezoelectric energy harvesting performance of a Zr-doped $PbMg_{1/3}Nb_{2/3}O_3-PbTiO_3$ (PMN-PZT) single crystal beam. A novel piezoelectric beam cantilever structure is used to demonstrate the feasibility of generating AC voltage during a state of vibration. The energy-harvesting capability of a PMN-PZT beam is calculated and tested. The frequency response of the cantilever device shows that the first mode resonance frequency of the excitation model exists in the neighborhood of several hundreds of hertz, which is similar to the calculated value. These tests show that several significantly open AC voltages and sub-mW power are achieved. To test the possibility of a small scale power source for a ubiquitous sensor network service, energy conversion and the testing of storage experiment are also carried out.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.11
• /
• pp.892-897
• /
• 2001

Variations of dielectric and piezoelectric properties and associated phase transformation of <001> -oriented rhombohedral 0.92Pb (Zn$\sub$1/3/Nb$\sub$2/3/)O$_3$-0.08PbTiO$_3$ single crystals were investigated. The longitudinal strain level was found to abruptly increase at 15 kV/cm, corresponding to that where an induced phase appears within a multidomain matrix. Drastic decreases in the dielectric constant, transverse coupling, and transverse piezoelectric coefficient associated with the E-field induced phase were the result of increased crystal anisotropy in PZN-PT crystals. By contrast, the thickness coupling increased from 53 % at 0 kV/cm to 64 % at 45 kV/cm, also associated with this phase transition under the E-field. The measured dielectric and piezflelectric properties found for the induced phase state were nearly identical to those of <001> poled tetragonal (1-x)PZN-xPT (x>0.1) crystals. Based on these results, it is evident that the symmetry of induced phase is tetragonal.