• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.5
• /
• pp.239-249
• /
• 2015

Various amount of NbC carbide was intentionally formed in a matrix-type cold-work tool steel by controlled amount of Nb and C addition. And the effect of NbC addition on the mechanical properties was investigated. Four alloys with different Nb and C contents were cast by vacuum induction melting, then hot forging and spheroidizing annealing were conducted. The machinability of the annealed specimens was examined with 3 different cutting tools. And tensile tests at room temperature were conducted. After quenching and tempering, hardness and impact toughness were measured, while wear resistance was evaluated by disk-on-plate type wear test. The increasing amount of NbC addition resulted in degraded machinability with increased strength, whereas the absence of NbC also led to poor machinability due to high toughness. After quenching and tempering, the additional NbC improved wear resistance with increasing hardness, whereas it deteriorated impact toughness. Therefore, it could be found that a moderate addition of NbC was desirable for the balanced combination of mechanical properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.496-499
• /
• 2000

In order to investigate the effect of Ge addition to the Cu Matrix on the microstructure and the critical current density, four kinds of internal tin processed Nb$_3$Sn strands with pure Cu and Cu 0.2, 0.4, 0.6 wt％ Ge alloy were drawn to 0.8 mm diameter. The microstructure and critical current of internal tin processed Nb$_3$Sn wires that were heat treated at temperatures ranging from 68$0^{\circ}C$ to 74$0^{\circ}C$ for 240 h were investigated. The Ge addition to the matrix did not make workability worse. A Ge rich layer in the Cu-Ge matrix suppressed the growth of the Nb$_3$Sn layer and promoted grain coarsening. The greater the Ge content in the matrix, the lower the net Jc result after Nb$_3$Sn reaction heat treatment. There was no significant variation in Jc observed with heat treatment temperature ranging from 68$0^{\circ}C$ to 74$0^{\circ}C$.

• Journal of Magnetics
• /
• v.14 no.4
• /
• pp.150-154
• /
• 2009

The effect of Ga and, Nb addition on the kinetics and mechanism of the disproportionation of a Nd-Fe-B alloy were investigated by isothermal thermopiezic analysis (TPA) using $Nd_{12.5}Fe_{(81.1-(x+y))}B_{6.4}Ga_xNb_y$ (x=0 and 0.3, y= 0 and 0.2) alloys. The addition of Ga and Nb retarded the disproportionation kinetics of the Nd-Fe-B alloy significantly, and increased the activation energy of the disproportionation reaction. The disproportionation kinetics of the $Nd_{12.5}Fe_{(81.1-(x+y))}B_{6.4}Ga_xNb_y$ alloys measured under an initial hydrogen pressure of 0.02 MPa were fitted to a parabolic rate law. This suggested that during the disproportionation of $Nd_{12.5}Fe_{(81.1-(x+y))}B_{6.4}Ga_xNb_y$ alloys with an initial hydrogen pressure of 0.02 MPa, a continuous disproportionation product is formed and the overall reaction rate is limited by the diffusion of hydrogen atoms (or ions).

• Journal of Magnetics
• /
• v.10 no.1
• /
• pp.28-32
• /
• 2005

The magnetic properties and ordering behavior of Nb-doped FePt alloy films prepared by dc-magnetron sputtering were investigated. It was found that Nb addition retarded the ordering reaction from the disordered face-centered-cubic (fcc) Al phase to the ordered face-centered-tetragonal (fct) L1₀ phase. The tetragonality (c/a ratio) of the ordered fct L1₀ phase increased with the Nb concentration. Nb addition hampered c-axis contraction during ordering, probably because the larger Nb atoms occupy Pt sites. Consequently, the coercivity and magnetocrystalline anisotropic energy of Nb-doped FePt alloy films are lower than those of un-doped FePt film under equivalent annealing conditions.

• Korean Journal of Materials Research
• /
• v.4 no.6
• /
• pp.669-680
• /
• 1994

Oxidation behaviour of TiAl intermetallic compounds with the addition of Cr, V, Si, Mo, or Nb was investigated at 900~$1100^{\circ}C$ under the atmospheric environment. The reaction products were examined by XRD, SEM equipped with WDX. The weight gain by continuous oxidation increased with the addition of Cr or V, but there was less weight gain when Mo, Si or Nb was added individually. he oxidation rate of Cr- or V-added TiAl was always larger than that of TiAI. However, oxidation rate of Si-, Mo- or Nb-added TiAl was almost same or smaller than that of TiAI. Thus, it is concluded that the addition of Cr or V did not improve the oxidation resistance, whereas the addition of Si, Mo or Nb improved the oxidation resistance. Oxides formed on TiAl with Mo, Si, and Nb were found to be more protective, resulting from the decrease in diffusion rate of the alloying elements and oxygen. Nb strengthened the tendency to form $AI_{2}O_{3}$ in the early stage of oxidation, due to the continuous $AI_{2}O_{3}$ layer formation and dense $Tio_{2}+AI_{2}O_{3}$ layer. According to the Pt-marker test of TiAI- 5wt%Nb, oxygen diffused mainly inward while oxides were formed on the substrate surface. Upon thermal cyclic oxidation at $900^{\circ}C$, it is shown that the addition of Cr or Nb improved the adherence of oxide scale to the substrate.

• Korean Journal of Materials Research
• /
• v.25 no.8
• /
• pp.376-385
• /
• 2015

The effects of Nb and Cr addition on the microstructure, corrosion and oxide characteristics of Zr based alloys were investigated. The corrosion tests were performed in a pressurized water reactor simulated-loop system at $360^{\circ}C$. The microstructures were examined using OM and TEM, and the oxide properties were characterized by low-angle X-ray diffraction and TEM. The corrosion test results up to 360 days revealed that the corrosion rates were considerably affected by Cr content but not Nb content. The corrosion resistance of the Zr-xNb-0.1Sn-yCr quaternary alloys was improved by an increasing Nb/Cr ratio. The crystal structure of the precipitates was affected by a variation of the Nb/Cr ratio. The Zr-Nb beta-enriched precipitates were mainly formed in the high Nb/Cr ratio alloy while $Zr(NbCr)_2$ precipitates were frequently observed in the low Nb/Cr ratio alloy. The studies of oxide characteristics revealed that the corrosion resistance was related to the crystal structure of the precipitate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.104-107
• /
• 2001

In order to investigate the effect of Ge addition to the Cu matrix on the microstructure and the critical current density, four kinds of internal tin processed Nb$_3$Sn strands with pure Cu and Cu 0.2, 0.4, 0.6 wt % Ge alloys were drawn to 0.8 mm diameter. The microstructure and critical current of internal tin processed Nb$_3$Sn wires that were heat treated at temperatures ranging from 68$0^{\circ}C$ to 74$0^{\circ}C$ for 240h were investigated. The Ge addition to the matrix did not make workability worse. A Ge rich layer in the Cu-Ge matrix suppressed the growth of the Nb$_3$Sn layer and promoted grain coarsening. The greater the Ge content in the matrix, the lower the net Jc result after Nb$_3$sn reaction heat treatment. There was no significant variation in Jc observed with heat treatment temperature ranging from 68$0^{\circ}C$ to 74$0^{\circ}C$. The values of AC loss of Ge added wires were decreased to 40 % compare with no addition wire. Low AC loss was due to segregation of Ge rich layer in the Cu-Ge matrix. If Ge added wire with thin Nb filaments were fabricated, slow diffusion rate of Sn would be overcome and decreased AC loss that is weak Point of internal tin method.

• Journal of Mechanical Science and Technology
• /
• v.14 no.8
• /
• pp.830-835
• /
• 2000

The thermodynamical estimation of the interfacial reaction and the impact properties of $Nb/MoSi_2$ laminate composites containing SiC, $NbSi_2$ or $ZrO_2$ particles are investigated. Laminate composites, which comprise alternating layers of $MoSi_2$ with the particle and Nb foil, were fabricated by the hot press process. It is clearly found out that the interfacial reaction of $Nb/MoSi_2$ can be controlled by the addition of $ZrO_2$ particle to the $MoSi_2$ phase. The addition of $ZrO_2$ particle increases both the impact value and the sintered density of Nb/McSij, The suppression of the interfacial reaction is caused by the formation of $ZrSiO_2$ in $MoSi_2-ZrO_2$ matrix mixture.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.5
• /
• pp.346-354
• /
• 2000

Effect of Nb addition on the phase transformation behavior was studied through continuous cooling transformation tests after reheating(reheating CCT) and deforming(deforming CCT) the 0.07%C-1.3%Mn-0.015%Ti-(0~0.08)% Nb steels. Transformation temperatures for deforming CCT were lower than those for reheating CCT, and the critical cooling rate for bainite transformation during deforming CCT was lower than that during reheating CCT. These enhanced hardenability for deforming CCT was considered to come from the sufficient solid solution of Nb in austenite during high temperature reheating before deformation. With Nb addition, the phase transformation temperature decreased, the bainite formation was enhanced, and the hardness of steel increased. Furthermore, these phenomena were more remarkable for deforming CCT than for reheating CCT. From the results, Nb-Ti bearing low carbon steel was considered to be a very favorable alloy system with good strength/toughness balance by recrystallization control rolling process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.8
• /
• pp.717-723
• /
• 2006

Lead free $(Na_{0.5}K_{0.47}Cd_x)NbO_3$ ceramics (x=0.015-0.005) were prepared by the conventional mixed oxide route. The effects of CdO addition on the sintering, dielectric and piezoelectric properties of the samples were examined. The addition of CdO greatly enhanced the sinterability of ceramics and the sample has a lower dielectric loss. The $k_p\;and\;Q_m$ of the samples with 0.02 mol CdO addition are 0.35 and 125, respectively, The $(Na,K)NbO_3$ ceramics show a large degradation of $k_p$ due to the deliquescence when exposed to humidity, while the $(Na,K,Cd)NbO_3$ ceramics have no a significant degradation of it.