• Applied Chemistry for Engineering
• /
• v.20 no.5
• /
• pp.565-569
• /
• 2009

Nano-sized green and blue phosphor powders were synthesized by liquid phase method to confirm the size and morphology. By using that process, the particle sizes of green and blue phosphor particles were 80 nm and 60 nm, respectively. The characteristic comparison of $Zn_2SiO_4$ : Mn and BAM : Eu was carried out and as a result, $Zn_2SiO_4$ : Mn powders showed an higher PL performance compared to BAM : Eu.

• Journal of Powder Materials
• /
• v.25 no.4
• /
• pp.309-315
• /
• 2018

In the present work, we synthesize nano-sized ZnO, $SnO_2$, and $TiO_2$ powders by hydrothermal reaction using metal chlorides. We also examine the energy-storage characteristics of the resulting materials to evaluate the potential application of these powders to dye-sensitized solar cells. The control of processing parameters such as pressure, temperature, and the concentration of aqueous solution results in the formation of a variety of powder morphologies with different sizes. Nano-rod, nano-flower, and spherical powders are easily formed with the present method. Heat treatment after the hydrothermal reaction usually increases the size of the powder. At temperatures above $1000^{\circ}C$, a complete collapse of the shape occurs. With regard to the capacity of DSSC materials, the hydrothermally synthesized $TiO_2$ results in the highest current density of $9.1mA/cm^2$ among the examined oxides. This is attributed to the fine particle size and morphology with large specific surface area.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.7
• /
• pp.1047-1054
• /
• 2001

Atomic Force Microscope (AFM) was used to study cross sectional profiles and dimensions of fatigue striations in 2017-T351 aluminum alloy. Their widths(SW) and heights (SH, SH(sub)h, SH(sub)ι) were measured from the cross sectional profiles of three-dimension AFM images. The following results that will be helpful to understand the fatigue crack growth mechanism were obtained. (1) The relation of SH=$\alpha$(SW)(sup)1.2 was obtained. (2) The ratio of the striation height to its width SH/SW, SH(sub)h/SW and SH(sub)ι/SW did not depend on the stress intensity factor range ΔK and the stress ratio R( =P(sub)min/P(sub)max = K(sub)min/K(sub)max). (3) Effect of precipitate on the morphology of striation was changed by the relative dimensional difference between the striation width SW and the precipitates. From these results, the applicability of the AFM to nano-fractography is discussed.

• The Journal of Korea Institute of Information, Electronics, and Communication Technology
• /
• v.1 no.2
• /
• pp.27-32
• /
• 2008

A current research basically diverted towards an increase in the operational output with the minimization of the materials used, which ultimately scaled down the dimensions of ceramic electronic components. In this direction the nano-technology pave the revolutionary changes in particular the electronic industries. The applications of nano-sized particles or nano-sized materials are hence, playing a significant role for various purposes. The PZT(lead, zirconium, titanium) based ceramics which, are reported to be ferroelectric materials have their important applications in the areas of surface acoustic waves (SAW), filters, infrared detectors, actuators, ferroelectric random access memory, speakers, electronic switches etc. Moreover, these PZT materials possess the large electro mechanical coupling factor, large spontaneous polarization, low dielectric loss and low internal stress etc. Hence, keeping in view the unique properties of PZT piezoelectric ceramics we also tried to synthesize indigenously the small sized PZT ceramic powder in the laboratory by using the modified sol-gel approach. In this paper, propyl alcohol based sol-gel method was used for preparation of PZT piezoelectric ceramic. The powder obtained by this sol-gel process was calcined and sintering to reach a pyrochlore-free crystal phase. The characterization of synthesized material was carried out by the XRD analysis and the surface morphology was determined by high resolution scanning electron microscopy.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.471-474
• /
• 2005

This study investigates the nano/microstructure, the aging response, and the mechanical/tribological properties of the eutectic regions in rheoformed A356 alloy-T5 parts using nano/micro-indentation and mechanical scratching, combined with optical microscopy and atomic force microscope (AFM). Most eutectic Si crystals in the A356 alloy showed a modified morphology as fine-fibers. The loading curve for the eutectic region was more irregular than that of the primary Al region due to the presence of various particles of varying strength. The aging responses of the eutectic regions in the rheoformed A356 alloys aged at $150^{\circ}C$ for different times (0, 2, 4, 8, 10, 16, 24, 36, and 72 h) were investigated. Both Victors hardness $(H_v)$ and indentation $(H_{IT})$ test results showed a similar trend of aging curves, and the peak was obtained at the same aging time of 10 h. A remarkable size-dependence of the tests was found.

• Journal of Surface Science and Engineering
• /
• v.40 no.2
• /
• pp.70-76
• /
• 2007

Ni-P-SiC composite coating layers were prepared by electroless plating method and their deposition rate, codeposition of SiC, morphology, surface roughness, hardness, wear and friction properties were investigated. The deposition rate was kept almost constant independent of the concentration of SiC in the plating solution and the codeposition of SiC in the composite coating layer increased with increased concentration of SiC in the plating solution except the early stage. Vickers microhardness increased with respect to the increased codeposition of SiC and the heat treatment at $300^{\circ}C$ in air for 1 hour. It was found that the wear volume decreased with increased up to 50 wt.% of SiC codeposition, and that friction coefficient increased gradually with increased codeposition of SiC. Considering the wear and the friction behaviors, the composite coating layer obtained by using 50 wt.% of SiC codeposition is desirable for the practical application for anti-wear and anti-friction coatings.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.28 no.1
• /
• pp.214-224
• /
• 2002

High concentrated $TiO_2$ nano colloids were synthesized by sol-gel method. Reactions were performed in $TiCl_4$/HCl/$H_2O$ aqueous solution and the conditions of particles such as shape, size and aggregation, etc. were controlled by polymerization and adsorption of acrylamide in surface of $TiO_2$ nano particles. And also, aminopropyltriethoxysilane was added instead of acrylamide and compared each other. The prepared colloids were well dispersed and showed the strong absorption peaks at 350nm-370nm which is blue shifted to 20-30nm, compared to macro particles. The obtained techniques from $TiO_2$ nato colloids synthesis were utilized in coating on boron nitride powders which are nonpolar and isoelectronic materials of carbon. Their surface morphology, structure, thermal stability and U. V absorption chracteristics were examined by SEM(Scanning Electron Microscopy), XRD(X-ray diffraction), TG/DTA(Thermogravimetric and Differential Thermal Analysis), UV-VIS(Ultraviolet-Visible Spectroscopy).

• Journal of Species Research
• /
• v.12 no.2
• /
• pp.158-164
• /
• 2023

In March 2021, marine sediment from East Sea samples were suspended in a 2% NaCl solution, and serial dilution was performed in fresh marine and Reasoner's 2A agar. Isolated bacterial strains were identified based on 16S rRNA gene sequences, and showed at least 98.7% sequence similarity with previously reported bacterial species. Finally, seven bacterial strains which were validly published but not reported in Korea, were obtained. These isolates were allocated to the orders Bacillales and Flavobacteriales. The three Flavobacteriales strains are classified into the family Flavobacteriaceae. The other four Bacillales belong to the families Bacillaceae and Paenibacillaceae. The seven unrecorded bacterial strains in this study are classified into seven different genera, which are assigned to Mesobacillus, Paenibacillus, Gramella, Gillisia, Arenibacter, Fictibacillus, and Brevibacillus. During the investigation, the possibility of excavation of various unrecorded species in domestic marine sediment was confirmed. Gram-staining, cell morphology, physiological and basic biochemical characteristics, and phylogenetic analysis were performed in this study and provided in the description of each strain.

• Journal of Industrial Technology
• /
• v.43 no.1
• /
• pp.1-6
• /
• 2023

TiO₂ is a versatile metal oxide material that is frequently used as a photo-catalyst for organic pollutant oxidation and a functional material for ultraviolet-ray protection. To improve its chemical/physical properties and widen the range of industrial application, it is demanded to control the crystalline feature and morphology precisely by applying advanced nano-synthesis methods. In this study, we prepared TiO₂ nanoparticles using the water-in-oil (W/O) microemulsion method and compared them with the particles synthesized by the conventional precipitation method. Also, we tried to find the optimum conditions for obtaining nano-sized, anatase-rich TiO₂ particles by the W/O microemulsion method. We analyzed the crystalline feature and particle size of the prepared samples using X-ray diffraction (XRD) and Transmission electron microscopy (TEM). In summary, we found the W/O microemulsion is more effective than precipitation in obtaining nano-sized TiO₂. The best result was derived when the microemulsion was formed using AOT surfactant, hydrolysis was performed under basic condition and the sample was calcined at 200℃.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.98-98
• /
• 2010

Ion beam irradiation has been extensively used for surface modification of polymers, glassy metals and amorphous and crystalline materials at micron and submicron scales. The surface structures created by exposure to an ion beam range from dots, steps and one-dimensional straight wrinkles to highly complex hierarchical undulations and ripples. In general, the morphology of these nanoscale features can be selected by controlling the ion beam parameters (e.g. fluence and acceleration voltage), making ion beam irradiation a promising method for the surface engineering of materials. In the work, we presented that ion beam irradiation results in creation of a peculiar nanoscale dimple-like structure on the surface of polyimide - a common polymer in electronics, large scale structures, automobile industry, and biomedical applications. The role of broad Ar ion beam on the morphology of the structural features was investigated and insights into the mechanisms of formation of these nanoscale features were provided. Moreover, a systematic experimental study was performed to quantify the role of ion beam treatment time, and thus the morphology, on the coefficient of friction of polyimide surfaces covered by nanostructure using a tribo-experiment. Nano-indentation experiment were performed on the ion beam treated surfaces which shows that the hardness as well as the elastic modulus of the polyimide surface increased with increase of Ar ion beam treatment time. The increased of hardness of polyimide have been explained in terms of surface structure as well as morphology changes induced by Ar ion beam treatment.