• Journal of Powder Materials
• /
• v.29 no.4
• /
• pp.297-302
• /
• 2022

This study compares the characteristics of a compact TiO₂ (c-TiO₂) powdery film, which is used as the electron transport layer (ETL) of perovskite solar cells, based on the manufacturing method. Additionally, its efficiency is measured by applying it to a carbon electrode solar cell. Spin-coating and spray methods are compared, and spray-based c-TiO₂ exhibits superior optical properties. Furthermore, surface analysis by scanning electron microscopy (SEM) and atomic force microscopy (AFM) exhibits the excellent surface properties of spray-based TiO₂. The photoelectric conversion efficiency (PCE) is 14.31% when applied to planar perovskite solar cells based on metal electrodes. Finally, carbon nanotube (CNT) film electrode-based solar cells exhibits a 76% PCE compared with that of metal electrode-based solar cells, providing the possibility of commercialization.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.46 no.4
• /
• pp.1-10
• /
• 2014

In papermaking industry, inorganic fillers are widely used for the purpose of improving opacity, brightness, printability, uniformity and dimensional stability. They are also useful for production costs and energy savings. In the past, inorganic fillers in papermaking industry only focused on micro-scale but recently, new trials on nano-powdered technology are applying. Even nano-powdered fillers are rapidly utilized for improving the optical and surface properties in coating and surface sizing, there still have some problems in wet-end process due to poor dispersibility and retention. In this study, nano-particled calcium carbonate was produced by milling the PCC and its applicability between micro sized and nano sized calcium carbonated was compared in wet-end process, and finally the sheet properties were evaluated. Nano-PCC was not retained in sheet structure without applying retention system, but with retention system nano-powdered PCC was absorbed on fiber surface with expanding the fiber networks. The application of PAM-bentonite system has resulted in high ash retention and bulky structure for copier paper, and good optical properties in brightness and opacity. However, it required to solve the weakness of low tensile property due to interruption of hydrogen bonding by nano fillers.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.177.2-177.2
• /
• 2015

Nano-mechanics 연구는 기판의 나노표면에 대하여 indenter tip을 직접 인가하여 측정함으로써 기존 분광학 연구에서는 불가능했던 박막의 기계적 특성 연구가 가능하다. 그러나 박막분석 특성상 박막의 표면, 기판 또는 하부 박막에 의한 영향으로 인해 박막의 고유한 물성특성 연구에 제약이 있다. 박막 표면에 의한 영향인 표면효과는 nano-indentation을 실행 할 때 tip의 압입으로 발생되는 표면의 스트레스로 인해 표면 변형이 나타나는 현상이다. 반면에 하부 박막과 기판에 의한 오류는 nano-indentation 실행 시 tip의 압입 깊이가 깊어질수록 하부박막 또는 기판과 가까워지기 때문에 박막 고유의 특성이 아닌 하부박막과 기판에 의한 영향이 같이 나타나는 현상이다. 이러한 오류를 최소화 하고자 많은 연구에서는 박막의 강도에 따라 nano-indentation의 실행 깊이를 박막 총 두께의 최소7%에서 최대 50%까지 삽입하는 방법을 도입하였다. 이를 기반으로 본 연구는 Zirconium nitride (ZrN) 박막의 증착된 두께 깊이만큼 nano-indentation 분석을 실행 하였으며 박막 고유의 nano-mechanics 특성을 연구 하였다. ZrN 박막은 hard coating 분야에 많이 사용되는 물질로 박막 고유의 hardness를 연구하는 것이 큰 의미가 있다. 연구 결과 모든 박막은 두께 30% 깊이 측정에서 박막 표면과 기판효과가 최소화된 박막의 물성 측정이 가능 하였고, 증착 시 질소를 0.5, 1, 2 sccm 흘려준 박막들은 총 두께 30% 깊이에서 hardness가 각각 23.2, 8.6, 18 GPa이었다. 따라서 nano-indenter 측정 시 유효한 측정 깊이에서 측정을 실시하는 것이, 박막의 물성분석에 있어서 대단히 중요함을 확인 하였다.

• Journal of the Korean Ceramic Society
• /
• v.42 no.1
• /
• pp.43-49
• /
• 2005

YSZ layer containing nano-sized particles has been deposited on the commercial A1203 substrate by Electron Beam Physical Vapor Deposition (EB-PVD). The role of coating rnjcrostructures of YSZ to indentation damage is studied. The different coating microsouctures are prepared by varying the substrate temperatures from $600^{circ}C$ to $800^{circ}C$ during the deposition. Microhardness test and Hertzian indentation are conducted on the $YSZ/Al_{2}O_{3}$ layered systems. The damage and flilure behaviors have been investigated according to the effect of microstructures and indentation loads. With increasing the substrate temperature during EB-PVD, the overall grain sizes are coarser and more faceted, which microsoucture ultimately influences on the indentation behavior, thus, YSZ/Al_{2}O_{3}$ layered system prepared at the substrate temperature of $800^{circ}C$ shows relatively higher damage tolerance.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2005.09a
• /
• pp.201-212
• /
• 2005

[ $Epoxy/BaTiO_3$ ] composite embedded capacitor films (ECFs) were newly designed fur high dielectric constant and low tolerance (less than ${\pm}15\%$) embedded capacitor fabrication for organic substrates. In terms of material formulation, ECFs are composed of specially formulated epoxy resin and latent curing agent, and in terms of coating process, a comma roll coating method is used for uniform film thickness in large area. Dielectric constant of $BaTiO_3\;&\;SrTiO_3$ composite ECF is measured with MIM capacitor at 100 kHz using LCR meter. Dielectric constant of $BaTiO_3$ ECF is bigger than that of $SrTiO_3$ ECF, and it is due to difference of permittivity of $BaTiO_3\;and\;SrTiO_3$ particles. Dielectric constant of $BaTiO_3\;&\;SrTiO_3$ ECF in high frequency range $(0.5\~10GHz)$ is measured using cavity resonance method. In order to estimate dielectric constant, the reflection coefficient is measured with a network analyzer. Dielectric constant is calculated by observing the frequencies of the resonant cavity modes. About both powders, calculated dielectric constants in this frequency range are about 3/4 of the dielectric constants at 1 MHz. This difference is due to the decrease of the dielectric constant of epoxy matrix. For $BaTiO_3$ ECF, there is the dielectric relaxation at $5\~9GHz$. It is due to changing of polarization mode of $BaTiO_3$ powder. In the case of $SrTiO_3$ ECF, there is no relaxation up to 10GHz. Alternative material for embedded capacitor fabrication is $epoxy/BaTiO_3$ composite embedded capacitor paste (ECP). It uses similar materials formulation like ECF and a screen printing method for film coating. The screen printing method has the advantage of forming capacitor partially in desired part. But the screen printing makes surface irregularity during mask peel-off, Surface flatness is significantly improved by adding some additives and by applying pressure during curing. As a result, dielectric layer with improved thickness uniformity is successfully demonstrated. Using $epoxy/BaTiO_3$ composite ECP, dielectric constant of 63 and specific capacitance of 5.1nF/cm2 were achieved.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.1
• /
• pp.62-67
• /
• 2011

Nanoparticles-coated and impact-damaged carbon-fiber reinforced plastics(CFRP) laminates were tested under compression-after-impact(CAI) mode and the propagation of damage due to compressive loading has been monitored by acoustic emission(AE). The impact damage was induced not by mechanical loading but by a simulated lightning strike. CFRP laminates were made of carbon prepregs prepared by coating of conductive nano-particles directly on the fibers and the coupons were subjected to simulated lightning strikes with a high voltage/current impulse of 10~40 kA within a few microseconds. The effects of nano-particles coating and the degree of damage induced by the simulated lightning strikes on the AE activities were examined, and the relationship between the compressive residual strength and AE behavior has been evaluated in terms of AE event counts and the onset of AE activity with the compressive loading. The degree of impact damage was also measured in terms of damage area by using ultrasonic C-scan images. From the results assessed during the CAI tests of damaged CFRP showed that AE monitoring appeared to be very useful to differentiate the degree of damage hence the mechanical integrity of composite structures damaged by lightning strikes.

• Korean Journal of Materials Research
• /
• v.17 no.8
• /
• pp.447-451
• /
• 2007

We investigated the dependence of the various annealing conditions and thickness ($6\sim45nm$) of the Ti-doped $Al_2O_3$ coating on the electrochemical properties and the capacity fading of Ti-doped $Al_2O_3$ coated $LiCoO_2$ films. The Ti-doped-$Al_2O_3$-coating layer and the cathode films were deposited on $Al_2O_3$ plate substrates by RF-magnetron sputter. Microstructural and electrochemical properties of Ti-doped-$Al_2O_3$-coated $LiCoO_2$ films were investigated by transmission electron microscopy (TEM) and a dc four-point probe method, respectively. The cycling performance of Ti-doped $Al_2O_3$ coated $LiCoO_2$ film was improved at higher cut-off voltage. But it has different electrochemical properties with various annealing conditions. They were related on the microstructure, surface morphology and the interface condition. Suppression of Li-ion migration is dominant at the coating thickness >24.nm during charge/discharge processes. It is due to the electrochemically passive nature of the Ti-doped $Al_2O_3$ films. The sample be made up of Ti-doped $Al_2O_3$ coated on annealed $LiCoO_2$ film with additional annealing at $400^{\circ}C$ had good adhesion between coating layer and cathode films. This sample showed the best capacity retention of $\sim92%$ with a charge cut off of 4.5 V after 50 cycles. The Ti-doped $Al_2O_3$ film was an amorphous phase and it has a higher electrical conductivity than that of the $Al_2O_3$ film. Therefore, the Ti-doped $Al_2O_3$ coated improved the cycle performance and the capacity retention at high voltage (4.5 V) of $LiCoO_2$ films.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.375-379
• /
• 2014

Nanocrystalline TiAlN coatings were prepared by reactively sputtering TiAl metal target with $N_2$ gas. This was done using a magnetron sputtering system operated in DC and ICP (inductively coupled plasma) conditions at various power levels. The effect of ICP power (from 0 to 300 W) on the coating microstructure, corrosion and mechanical properties were systematically investigated using FE-SEM, AFM and nanoindentation. The results show that ICP power has a significant influence on coating microstructure and mechanical properties of TiAlN coatings. With increasing ICP power, the coating microstructure evolved from the columnar structure typical of DC sputtering processes to a highly dense one. Average grain size of TiAlN coatings decreased from 15.6 to 5.9 nm with increasing ICP power. The maximum nano-hardness (67.9 GPa) was obtained for the coatings deposited at 300 W of ICP power. The smoothest surface morphology (Ra roughness 5.1 nm) was obtained for the TiAlN coating sputtered at 300 W ICP power.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.3
• /
• pp.133-140
• /
• 2002

The Ti-Si-N coating layers were synthesized on SKD 11 steel substrate by a DC reactive magnetron co-sputtering technique with separate Ti and Si targets. The high resolution transmission electron microscopy (HRTEM) and X-ray photoelectron spectroscopy (XPS) analyses for the coating layers revealed that microstructure of Ti-Si-N layer was nanocomposite, consisting of nano-sized TiN crystallites surrounded by amorphous $Si_3$$N_4$ phase. The highest hardness value of about 39 GPa was obtained at the Si content of ~11at.%, where the microstructure had fine TiN crystallites (about 5nm in size) dispersed uniformly in amorphous matrix. As the Si content in Ti-Si-N films increased, the TiN crystallites became from aligned to randomly oriented microstructure, finer, and fully penetrated by amorphous phase. Free Si appeared in the layers due to the deficit of nitrogen source at higher Si content. Friction coefficient and wear rate of the Ti-Si-N coating layer significantly decreased with increase of relative humidity. The self-lubricating tribe-layers such as $SiO_2$ or (OH)$Si_2$ seemed to play an important role in the wear behavior of Ti-Si-N film against steel.

• Korean Journal of Materials Research
• /
• v.26 no.5
• /
• pp.271-280
• /
• 2016

When a single inorganic precursor is used for the synthesis of a sol-gel coating, there is a problem of cracking on the surface of coating layer. In order to solve this problem of surface cracking, we synthesized inorganic-organic coatings that have hybrid properties of inorganic and organic materials. Sols of various ratios (1:0.07, 0.2, 0.41, 0.82, 1.64, 3.26, 6.54, 13.2) of an inorganic precursor of Tetrabutylorthotitanate ($Ti(OBu)_4$, TBOT) and an organic precursor of ${\gamma}$-Methacryloxy propyltrimethoxysilane (MAPTS) were prepared and coated on stainless steels (SUS316L) by dip coating method. The binding structure and the physical properties of the synthesized coatings were analyzed by FT-IR, FE-SEM, FIB (Focused Ion Beam), and a nano-indenter. Dynamic polarization testing and EIS (electrical impedance spectroscopy) were carried out to evaluate the micro-defects and the corrosion properties of the coatings. The prepared coatings show hybrid properties of inorganic oxides and organic materials. Crack free coatings were prepared when the MAPTS ratio was above a critical value. As the MAPTS ratio increased, the thickness and the corrosion resistance increased, and the hardness decreased.