• Journal of the Korean Magnetics Society
• /
• v.18 no.2
• /
• pp.49-53
• /
• 2008

Magnetic and crystallographic properties of patterned media fabricated by nanoimprint lithography and Co-Pt electroplating were studied. Thin films of Ru(20 nm)/Ta(5 nm)/$SiO_2$(100 nm) were deposited on Si(100) wafer and then 25 nm hole pattern was fabricated by nanoimprint lithography on substrate. The electroplated Co-Pt nano-dots have the diameter of 35 nm and the height of 27 nm. Magnetic dot patterns of Co-Pt alloy were created using electroplated Co-Pt alloy and then their properties were measured by MFM, SQUID, SEM, TEM and AFM. We observed single domain with perendicular anisotropy for each dot and achieved optimum coercivity of 2900 Oe. These results mean that patterned media fabricated by nanoimprint lithography and electroplating have good properties in view of extending superparamagnetic limit while satisfying the writability requirements with the present write heads.

• Polymer(Korea)
• /
• v.36 no.3
• /
• pp.357-363
• /
• 2012

Surface-modified poly(L-lactic acid) (PLLA) films and scaffolds were treated with plasma discharge in oxygen gas and subsequently subjected to $in$ $situ$ grafting of acrylic acid (AA) in order to increase the cell compatibility. The surface of AA-grafted PLLA was converted to hydroxyapatite (HA)-deposited PLLA in stimulated body fluid (SBF). After the samples were immersed in phosphate-buffered saline (PBS), fetal bovine serum (FBS), normal saline, or cell medium, the water contact angles were significantly reduced on the surface of HA-deposited PLLA. Chondrocyte and osteoblast showed a higher attachment and cell proliferation on HA-deposited surfaces and in particular, it was confirmed that chondrocyte was considerably influenced by HA. However, osteoblast showed better cell proliferation on the surfaces immersed in FBS, cell medium or HA-deposited surface. In addition, the cell proliferation in 3D scaffolds was much higher than that on film type, irrespective of chondrocyte and osteoblast. Therefore, such surface-modified PLLAs are expected to be useful as organic-inorganic hybrid scaffolds in the regeneration of cartilage and bone.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.3
• /
• pp.77-81
• /
• 2020

Commercialization of flexible OLED displays, such as rollable and foldable displays, has attracted tremendous interest in next-generation display markets. However, during bending deformation, cracking and delamination of thin films in the flexible display panels are the critical bottleneck for the commercialization. Therefore, measuring mechanical properties of the fragile thin films in the flexible display panels is essential to prevent mechanical failures of the devices. In this study, tensile properties of the metal and ceramic nano-thin films were quantitatively measured by using a direct tensile testing method on the water surface. Elastic modulus, tensile strength, and elongation of the sputtered Mo, MoTi thin films, and PECVD deposited SiN_x thin films were successfully measured. As a result, the tensile properties were varied depending on the deposition conditions and the film thickness. The measured tensile property values can be applied to stress analysis modeling for mechanically robust flexible displays.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.148-148
• /
• 2000

지금까지 반도체 표면에 대한 연구는 주로 (1000, (111) 표면 등 낮은 밀러 지표를 가진 표면에 대해 이루어져 왔다. 이에 반해 밀러 지표가 높은 Si 면은 불안정하고, 가열하면 다른 표면, 즉 지표가 낮은 면으로 재배열하는 경향이 있는 것으로 알려져 있는데 아직 이들 높은 밀러 지표를 가진 표면에 대한 연구는 미미한 상태이다. 그러나, Si(113)면은 밀러 지표가 높으면서도 안정하기 때문에 Si(113)의 구조를 정확하게 알 수 있다면 밀러 지표가 낮은 Si 표면이 안정한 이유를 이해할 수 있을 것이다. 따라서 본 연구에서는 TOF-CAICISS 장치(Time of Flight - CoAxial Impact Collision Ion Scattering Spectroscopy) 장비와 RHEED(Reflection High Energy Electron Diffrction)를 이용하여 Si(113) 표면의 구조와 Si(113) 표면의 온도에 따른 구조 변화를 관찰하였다. TOF-CAICISS 실험결과를 보면 (3$\times$2)에서 (3$\times$1)으로 상변환하면서 Si(113) 표면에 오각형을 이루는 dimer 원자들과 adatom 원자들간의 높이차가 작아짐을 알 수 있다. RHEED 실험결과와 전산 모사 결과로부터 상온에서 Si(113)(3$\times$2) 구조를 가지다가 45$0^{\circ}C$~50$0^{\circ}C$에서 Si(113) (3$\times$1) 구조로 상변환한다는 것을 알 수 있다. 그러나, 아직 상전이 메카니즘은 명확하게 밝혀지지 않았다. 실험결과를 전산 모사와 비교함으로써 Si(113) 표면에 [33]방향으로 이온빔을 입사시켰을 경우 dabrowski 모델과 Ranke AI 모델이 적합하지 않다는 것을 알 수 있다./TEX>, shower head의 온도는 $65^{\circ}C$로 설정하였다. 증착된 Cu 박막은 SEM, XRD, AFM를 통해 제작된 박막의 특성을 비교.분석하였다. 초기 plasma 처리를 한 경우에는 그림 1에서와 같이 현저히 증가한 초기 구리 입자들이 관측되었으며, 이는 도상 표면에 활성화된 catalytic site의 증가에 기인한다고 보여진다. 이러한 특성은 Cu films의 성장률을 향상시키고, 또한 voids를 줄여 전기적 성질 및 surface morphology를 향상시키는 것으로 나타났다. 결과 필름의 잔류 응력과 biaxial elastic modulus는 필름의 두께가 감소함에 따라 감소하는 경향을 나타냈으며, 같은 두께의 필름인 경우, 식각 깊이에 따른 biaxial elastic modulus 의 변화를 통해 최적의 식각 깊이를 알 수 있었다.도의 값을 나타내었으며 X-선 회절 data로부터 분석한 박막의 변형은 증온도에 따라 7.2%에서 0.04%로 감소하였고 이 이경향은 유전손실은 감소경향과 일치하였다.는 현저하게 향상되었다. 그 원인은 SB power의 인가에 의해 활성화된 precursor 분자들이 큰 에너지를 가지고 기판에 유입되어 치밀한 박막이 형성되었기 때문으로 사료된다.을수 있었다.보았다.다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(nano)화하여 나노 입자를 제조, 기존의 기능성 안료에 대한 비용 절감 효과등을 유도 할 수 있다. 역시 기술적인 측면에서도 특수소재 개발에 있어 최적의 나노 입자 제어기술 개발 및 나노입자를 기능성 소재로 사용하여 새로운 제품의 제조와 고압 기상 분사기술의 최적화에 의한 기능성 나노 입자 제조 기술을 확립하고 2차 오염 발생원인 유기계 항균제를 무기계 항균제로 대체할 수 있다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.433-433
• /
• 2012

As the requirement in patterning geometry continuously shrinks down, the termination of etch process at the exact time became crucial for the success in nano patterning technology. By virtue of real-time optical emission spectroscopy (OES), etch end point detection (EPD) technique continuously develops; however, it also faced with difficulty in low open ratio etching, typically in self aligned contact (SAC) and one cylinder contact (OCS), because of very small amount of optical emission from by-product gas species in the bulk plasma glow discharge. In developing etching process, one may observe that coupon test is being performed. It consumes costs and time for preparing the patterned sample wafers every test in priority, so the coupon wafer test instead of the whole patterned wafer is beneficial for testing and developing etch process condition. We also can observe that etch open area is varied with the number of coupons on a dummy wafer. However, this can be a misleading in OES study. If the coupon wafer test are monitored using OES, we can conjecture the endpoint by experienced method, but considering by data, the materials for residual area by being etched open area are needed to consider. In this research, we compare and analysis the OES data for coupon wafer test results for monitoring about the conditions that the areas except the patterns on the coupon wafers for real-time process monitoring. In this research, we compared two cases, first one is etching the coupon wafers attached on the carrier wafer that is covered by the photoresist, and other case is etching the coupon wafers on the chuck. For comparing the emission intensity, we chose the four chemical species (SiF2, N2, CO, CN), and for comparing the etched profile, measured by scanning electron microscope (SEM). In addition, we adopted the Dynamic Time Warping (DTW) algorithm for analyzing the chose OES data patterns, and analysis the covariance and coefficient for statistical method. After the result, coupon wafers are over-etched for without carrier wafer groups, while with carrier wafer groups are under-etched. And the CN emission intensity has significant difference compare with OES raw data. Based on these results, it necessary to reasonable analysis of the OES data to adopt the pre-data processing and algorithms, and the result will influence the reliability for relation of coupon wafer test and whole wafer test.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2002.11a
• /
• pp.477-480
• /
• 2002

Si-O-C(-H) thin film with a tow dielectric constant were deposited on a P-type Si(100) substrate by an inductively coupled plasma chemical vapor deposition (ICPCVD). Bis-trimethylsilymethane (BTMSM, H$_{9}$C$_3$-Si-CH$_2$-Si-C$_3$H$_{9}$) and oxygen gas were used as Precursor. Hybrid type Si-O-C(-H) thin films with organic material have been generated many voids after annealing. Consequently, the Si-O-C(-H) films can be made a low dielectric material by the effect of void. The surface characterization of Si-O-C(-H) thin films were performed by SEM(scanning electron microscope). The characteristic analysis of Si-O-C(-H) thin films were performed by X-ray photoelectron spectroscopy (XPS).

• Journal of the Korean Magnetics Society
• /
• v.22 no.2
• /
• pp.37-41
• /
• 2012

The Ag nanoparticles attached $La_{0.7}Sr_{0.3}Co_{0.3}Fe_{0.7}O_{3-{\delta}}$ (LSCF) perovskites were prepared by plasma method. The Ag nanoparticles with size of several nanometers deposited from the Ag target were coated on the surface of LSCF powders with size range from 0.2 to 3 ${\mu}m$. The agglomeration of Ag particles annealed at $800^{\circ}C$ under inert gas of Ar were rarely observed. The inter-diffusion between surface Ag and core LSCF is effectively strong to prevent aggregation of Ag nanoparticles. The wave number of FT-IR spectra for LSCF were largely shifted as the concentration of Ag on LSCF up to 2.11 wt.%. The ionic states of irons in LSCF were measured by M$\ddot{o}$ssbauer spectroscopy. The small amount of $Fe^{4+}$ ions are converted to $Fe^{3+}$ ions after Ag nanopartcles were coated on LSCF.

• Polymer(Korea)
• /
• v.36 no.4
• /
• pp.542-548
• /
• 2012

Morphological characteristics and formation of symmetric polystyrene-block-poly(1,4-butadiene) copolymer (PS-b-PBD) in thin films upon solvent-annealing were investigated by using atomic force microscopy (AFM). The thin films solvent-annealed in cyclohexane revealed the perforated lamellae of poly(1,4-butadiene) in the matrix of polystyrene while those solvent-annealed in n-hexane exhibited highly disordered patterns. Interestingly, when the thin films of PS-b-PBD were solvent-annealed with binary mixtures of cyclohexane and n-hexane, the morphological transition from the perforated lameallae to the perpendicularly-oriented lamellae of poly(1,4-butadiene) could be induced by changing the mixing ratio of both solvents. We also demonstrated that after microdomians of poly(1,4-butadiene) were successfully degraded by UV-$O_3$, linear poly(dimethyl siloxane) chains were back-filled into the etched regions of the thin film and then converted to silica nano-objects by oxygen plasma treatments.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.96-96
• /
• 1999

CdTe는 일반적으로 광전 소자나 Xtjs 및 λ선 감지 소자로서 많은 연구가 되어지고 있는 물질이다. 특히 적외선 감지 소자로 쓰이고 있는 HgCdTe 물질의 기판으로서도 많은 연구가 진행되고 있다. 이러한 여러 가지 목적으로 사용함에 있어서 CdTe 내에 가지고 있는 여러 가지 불순물에 의한 영향으로 각종 결함밴드들이 형성됨으로서 소자로서의 응용에 많은 지장을 주고 있다. 이러한 이유로 여러 가지 방법으로 불순물 및 결합에 의한 준위에 관한 연구들이 진행되고 있다. 본 실험에서는 MBE 법으로 성장된 In 도핑된 CdTe 박막의 광학적 성질을 관찰하기 위하여 수소화 및 열처리를 하여 PL 법을 이용하여 관찰하여 보앗다. 열처리는 Cd 분위기의 50$0^{\circ}C$에서 5시간 동안 수행하였으며 수소화는 rf plasma 장치를 이용하여 8$0^{\circ}C$에서 50mW/c2의 출력으로 1시간동안 수행하여 주었다. 열처리한 시료의 경우 PL 신호는 갓 성장한 시료와 비교하여 깊은 준위에 관련된 신호들만 변화가 있었을뿐 그리 큰 변화가 있지는 않았다. 그러나 수소화시킨 시료의 경우 전체적으로 피크의 크기가 5배정도 감소하는 것을 볼 수 있었는데 이것은 수소에 의하여 passivation된 효과로 볼 수 있다. 정량적인 passivation 효과를 보기 위하여 온도의존성 PL 측정을 하여 보았다. 측정에서 관측된 (D,h) emission lines의 FWHM을 비교하여 본 결과 FWHM 온도가 증가함에 따라 선형적으로 증가하는 것이 아니라 급격한 증가를 q이는 구간을 관착할 수 있었다. 이것은 CdTe내에 존재하는 전하를 띠고 있는 주게와 받게의 결합의 결과로 나타나는 현상으로 보여진다. 이러한 결과를 통하여 얕은 준위에 있는 주게 불순물의 농도를 계산해 보았고 Hall 측정을 얻은 결과와 비교하여 보았다.판단된다. 따라서 이 기술은 기존의 광소자 제작을 위한 IFVD 방법의 문제점을 해결할 뿐만 아니라 결정 재성장 없이 도일한 기판상에 국부적으로 상이한 bandgap 영역을 만들 수 있기 때문에 광소자 제작에 적극 이용될 수 있다.나지 않았으며 BST 박막에서는 약 1.2V의 C-V이력현상이 보였다.를 이용하였으며, 이온주입후 열처리 온도에 따른 활성화 정도의 관찰을 위하여 4-point probe와 Hall measurement를 이용하였다. 증착된 다결정 SiGe의 두게를 nanospec과 SEM으로 분석한 결과 Gem이 함량이 적을 때는 높은 온도에서의 증착이 더 빠른 증착속도를 나타내었지만, Ge의 함량이 30% 되었을 때는 온도에 관계없이 일정한 것으로 나타났다. XRD 분석을 한 결과 Peak의 위치가 순수한 Si과 순수한 Ge 사이에 존재하는 것으로 나타났으며, ge 함량이 많아짐에 따라 순수한 Ge쪽으로 옮겨가는 경향을 보였다. SEM, ASFM으로 증착한 다결정 SiGe의 morphology 관찰결과 Ge 함량이 높은 박막의 입계가 다결정 Si의 입계에 비해 훨씬 큰 것으로 나타났으며 근 값도 증가하는 것으로 나타났다. 포유동물 세포에 유전자 발현벡터로써 사용할 수 있음으로 post-genomics시대에 다양한 종류의 단백질 기능연구에 맡은 도움이 되리라 기대한다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(nano)화하여 나노 입자를 제조, 기존의 기능성 안료에 대한 비용 절감 효과등을 유도 할 수 있다. 역시 기술적인 측면에서도 특수소재 개발에 있어 최적의 나노 입자 제어기술 개발 및 나노입자를 기능성 소재로 사용하여 새로운 제품의 제조와 고압 기상 분사기술의 최적화에 의한 기능성 나노 입자 제조 기술을 확립하고 2차 오염 발생원인 유

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.159-159
• /
• 1999

니켈 산화물 박막을 전자비임 증착법으로 기판온도는 RT~25$0^{\circ}C$의 범위에서 제작하였다. 제작시 초기 베이스 압력은 2$\times$10-6mbar로 하고 산소주입후 작업진공도를 3$\times$10-4mbar로 유지하여 증착하였다. 제작시 기판온도에 따라 제작된 시료들은 각각 X선회절장치(XRD)로 막의 구조과 그림과 같이 입방체 구조 또는 팔면체구조를 갖음을 알 수 있었으며 막의 표면형상은 SEM을 이용하여 분석하였다. 각각의 여러 기판온도에 따라 제작된 니켈 산화물 박막의 전기 화학적인 특성을 분석하기 위해 순환전압전류법을 이용하였다. 또한, 전기적인 광학소자로써의 특성을 분석하기 위해 UV-Vis 광분광기를 사용하여 투과율을 측정하여 그 특성을 알아보았다. 순환전압전류법에 의한 각 시료에 대한 박막의 전기화학적 특성은 0.5M KOH 전해질 수용액에서 기판온도가 150~20$0^{\circ}C$로 제작된 니켈 산화물 박막이 다른 온도에서 제작된 시료들보다 높은 전기화학적 안정성을 보임을 알 수 있었다. 마찬가지로 광학적 특성에서 착색과 탈색의 순환과정시 분광광도계에서 나타나는 광투과율을 비교해 보면 100~20$0^{\circ}C$에서 제작된 니켈 산화물 박막이 가역적인 착탈색의 색변화가 현저하게 나타남을 알 수 있었다. 결과적으로 광학적 특성 및 전기화학적 안정성 분석으로 인해 막의수명과 전기적착색 물질의 특성면에서 증착시 기판온도가 150~20$0^{\circ}C$에서 제작된 시료가 가장 내구성면에서 막의 이온 누적이 적고 활성적인 광투과율의 성질을 갖는다는 것이다. 이와같이 니켈산화물 박막제작시 기판온도가 전기적착색물질의 특성과 내구성에 큰 영향을 미침을 분석할 수 있었다.electron Microscopy)과 AFM(Atomim Force microscopy)으로 증착박 표면의 topology와 roughness를 관찰하였다. grain의 크기는 10nm에서 150nm이었고 증착막의 roughness는 4.2nm이었다. 그리고 이 산화막에 전극을 형성하여 유전 상수와 손실률 등을 측정하였다. 이와 같이 plasma를 이용한 3-beam에 의한 증착은 금속의 산화막을 얻는데 유용한 기술로 광학 재료 및 유전 재료의 개발 및 연구에 많이 사용될 것으로 기대된다.소분압 조건에서 RuO2의 형성을 관찰하였으며, 이것은 열역학적인 계산을 통해서 잘 설명할 수 있었다.0$\mu\textrm{m}$, 코일간의 간격은 100$\mu\textrm{m}$였다. 제조된 박막 인덕터는 5MHz에서 1.0$\mu$H의 인덕턴스를 나타내었으며 dc current dervability는 100mA까지 유지되었다. CeO2 박막과 Si 사이의 결함때문이라고 사료된다.phology 관찰결과 Ge 함량이 높은 박막의 입계가 다결정 Si의 입계에 비해 훨씬 큰 것으로 나타났으며 근 값도 증가하는 것으로 나타났다. 포유동물 세포에 유전자 발현벡터로써 사용할 수 있음으로 post-genomics시대에 다양한 종류의 단백질 기능연구에 맡은 도움이 되리라 기대한다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(nano)화하여 나노 입자를 제조, 기존의 기능성 안료에 대한 비용 절감 효과등을 유도 할 수 있다. 역시 기술적인 측면에서도 특수소재 개발에 있어 최적의 나노 입자 제어기술 개발 및 나노입자를 기능성 소재로 사용하여 새로운 제품의 제조와 고압 기상 분사기술의 최적