• 한국재료학회지
• /
• 제17권4호
• /
• pp.236-238
• /
• 2007

[ 0-3PbTiO_3/P$ ](VDF/TrFE) nanocomposites thin films for passive pyroelectric infrared sensor have been fabricated by two-step spin coating technique. 65 wt% VDF and 35 wt% TrFE was formed to a P(VDF/TrFE) poder Nano size $PbTiO_3$ powder was used. 0-3 connectivity of $PbTiO_3$(VDF/TrFE) composites film is achieved and also observed by SEM photography successfully. The dielectric constant, and pyroelectric coefficient measured and compared with P (VDF/TrFE). A very low dielectric constant (13.48 at 1 kHz) and high enough pyroelectric coefficient (3.101 $nC/cm^2$.k at $50^{circ}C$) neasured. This nanocomposites can be used for a new pyroelectric infrared sensor for better performance.

• 폴리머
• /
• 제31권5호
• /
• pp.379-384
• /
• 2007

본 연구는 열안정성을 향상시킨 무기나노 분말충전 나노복합재료를 우레탄 중합방법으로 제조하였다. 나노복합재료의 구조와 표면 특성은 XRD와 FT-IR을 통하여 알아보았고, 열안정성은 TGA와 DSC를 통하여 알아보았으며, SEM을 이용하여 복합재료의 모폴로지를 관찰하였다. 복합재료의 기계적 물성은 UTM을 사용하여 측정하였다. 실험 결과, MMT를 충전한 나노복합재료의 층간거리가 $7.5{\AA}$ 증가하였고, Silica 내 Si-O기에 의해 $1038cm^{-1}$에서 새로운 피크가 나타났다. 또한 열안정성과 기계적 물성도 폴리우레탄 매트릭스보다 향상된 것을 확인할 수 있었다.