• Elastomers and Composites
• /
• v.44 no.2
• /
• pp.134-142
• /
• 2009

Organo bifunctional silane (TESPD) is added into silica containing NR and its effects are investigated with respect to the vulcanization properties, the processability, and the physical properties. The addition of the TESPD into silica filled NR compound increases the degree of crosslinking by formation of a strong 3-dimensional network structure with silica surface via coupling reaction, which results in an improved mechanical property. It also improves the processabilities compared to the Control compound.

• Elastomers and Composites
• /
• v.7 no.2
• /
• pp.183-192
• /
• 1972

As a series of tile studies of EPDM-Polymer blends, tile experiment are concentrated to the investigation of the physical properties of tile EPDM-NR-SBR blends. The results are shown as follows: 1. In blending, tensile strength decreased with increase in EPDM contents, especially the ratio of EPDM/NR-SBR is 75/25. 2. Elongation and tear strength were much influenced by blending, especially the ratio of EPDM/NR-SBR is 50/50. 3. Ozone resistance is much improved after blending. It was effective more than tile ratio of EPDM/NR-SBR is 25/75. 4. Aging resistance is much improved after blending. It was effective more than the ratio of EPDM/NR-SBR is 50/50. 5. Hardness increased with increase in EPDM contents and on the other hand, abrasion resistance decreased.

• Elastomers and Composites
• /
• v.56 no.1
• /
• pp.12-19
• /
• 2021

The abrasion behaviors of NR/BR blend vulcanizates were investigated using NR/BR = 100/0, 80/20, and 60/40 compounds. The abrasion test was performed using a laboratory abrasion tester (LAT) at slip angles of 1° and 7°. The size distributions of the wear particles and the abrasion rates were examined according to the rubber compositions and slip angles. The most abundant wear particles at the slip angle of 1° were sizes above 1,000 ㎛, irrespective of the rubber composition. The most abundant wear particles at 7° slip angle had sizes in the range of 212-500 ㎛, except for the NR = 100 sample. The wear particle size distribution shifted to a smaller size as the slip angle and BR content increased. The abrasion rate at 7° was much larger than that at 1° slip angle. Furthermore, the abrasion rate was notably increased by adding BR to NR.

• Elastomers and Composites
• /
• v.48 no.3
• /
• pp.181-189
• /
• 2013

Unfilled, carbon black-filled, and silica-filled natural rubber (NR) composites were aged with a circular deformation at $60-90^{\circ}C$ and the recovery behaviors were investigated. The samples were aged under the altering aging medium systems of air and distilled water every day for 10 days. The order of the recoveries according to the filler systems was unfilled > silica > carbon black. The recoveries of the samples aged in the air to water altering system were greater than those of the samples aged in the water to air altering system. The initial aging medium dominantly influenced the deformation level.

• Macromolecular Research
• /
• v.16 no.6
• /
• pp.561-566
• /
• 2008

NR composites with different curing systems were aged thermally at 60, 70, 80, and $90^{\circ}C$ for 2-185 days in a convection oven, and the changes in the crosslink density were investigated as a function of the accelerated thermal aging. The overall crosslink densities increased with increasing aging time irrespective of the aging temperatures and curing systems. The changes in crosslink density were enhanced by increasing the aging temperature. The degree of the increased crosslink density was in the following order: "the conventional cure system > the semi-EV system > the EV system". For short term thermal aging, the change in crosslink density with the aging time was complicated, particularly for low temperature aging. The activation energies of the change in crosslink density with thermal aging using the conventional and semi-EV cure systems increased and then remained relatively constant with increasing aging time, whereas that of the specimen with an EV cure system tended to increase linearly. The experimental results were explained by the dissociation of the existing polysulfidic linkages and the formation of new cross links through the crosslinking-related chemicals remaining in the sample.

• Journal of Adhesion and Interface
• /
• v.8 no.2
• /
• pp.15-21
• /
• 2007

To prepare a natural rubber-based pressure-sensitive adhesive (PSA) for protection film of opto- functionalized sheet, natural rubber (NR) was blended with a DCPD type tackifier and three types of aliphatic hydrocarbon resins, respectively. Also, to supply low cohesion strength of NR, in the fixed ratio of tackifier, synthetic rubber, styrene-isoprene-styrene (SIS) block copolymer was blended with NR as a function of SIS contents. PSA performance of prepared PSAs was evaluated using probe tack and peel strength. Probe tack of NR/tackifier blends was increased with increasing tackifier contents, and showed maximum peak. In addition, probe tack of NR/tackifier blends slightly increased with increasing softening point of aliphatic hydrocarbon resins. Their peel strength increased up to 50 wt% of tackifier contents, but in the over contents of tackifier, they showed stick-slip failure mode. Finally, probe tack of NR/SIS/tackifier blends showed the maximum values at 20~40 wt% of tackifier contents, but at 20 wt% of tackifier contents, they showed fibrillation. For this reason, peel strength showed maximum values at 40 wt% of tackifier contents.

• Elastomers and Composites
• /
• v.35 no.3
• /
• pp.215-226
• /
• 2000

Cure characteristics of carbon black-filled rubber compounds with different rubber composition were studied using a rheometer. The carbon black-filled rubber compounds with single, binary, and ternary rubber compositions of natural rubber (NR), styrene-butadiene rubber (SBR), and butadiene rubber (BR) were used. Delta-torques of the NR/BR- and SBR/BR-based compounds with a high BR content were higher than those of the single rubber-based compounds. For ternary rubber-based compounds, the delta-torques of the compounds were lower when the difference in the rubber content ratios was small than when it was big. Scorch and optimum cure times of the rubber compounds became shorter by increasing the content of NR in the compounds while those became longer by increasing the SBR content. Cure rates of the rubber compounds increased with a decrease of the SBR content in the rubber compounds. Reversion ratios decreased with an increase of the SBR content in the rubber compounds.

• Elastomers and Composites
• /
• v.58 no.3
• /
• pp.128-135
• /
• 2023

To improve the adhesive strength of natural rubber (NR) for a seismic isolation damper, citraconic acid-g-NR (CCA-g-NR) was synthesized via the melt grafting of citraconic acid (CCA) onto NR using an azobisisnomerobutyronitrile (AIBN) initiator. Subsequently, the influence of CCA and AIBN concentrations on the graft ratio G/R (%) and graft efficiency G/E (%) of the CCA-g-NR was investigated. The optimum CCA and AIBN concentrations required to achieve the desired G/R (3.49%) and G/E (49.8%) were found to be 7 phr and 0.13 phr, respectively. Additionally, we studied the influence of CCA-g-NR concentration on the mechanical properties (tensile strength, elongation at break, and modulus at 300%), adhesive strength, and cure characteristics of the rubber compound in the seismic isolation damper. As the concentration of CCA-g-NR increased, the elongation at break and adhesive strength of the compound increased, whereas its tensile strength and modulus at 300% decreased. Moreover, as the concentration increased, the maximum torque decreased and the scorch time was delayed to obtain an optimal vulcanization time.

• Elastomers and Composites
• /
• v.3 no.1
• /
• pp.32-38
• /
• 1968

The physical properties of NR-SBR and NR-BR blends were studied. 1. In blending, tensile strength decreased with increase in synthetic rubber contents. It was most effective when the ratio of NR/Syn. R is 75/25. 2. Tensile strength decreased with order of NR, SBR and BR and modulus after aging is proportional of synthetic rubber contents. 3. Elongation is less influenced by synthetic rubber ratio that on the other hand, the decrease of elongation is proportional to synthetic rubber contents after aging. 4. Hardness decreased with increase in the synthetic rubber contents and on the other hand, the hardness increased after aging.

• Elastomers and Composites
• /
• v.34 no.4
• /
• pp.332-340
• /
• 1999

Hydrogenations of BR and NR performed by a noncatalytic method using p-toluenesulphonylhydrazide were carried out by reactive processing. The experimental procedures for carrying out the reaction were established. Two steps comprising premixing of the rubber with TSH followed by hydrogenation in compression mould were proved to be suitable. The percentages of hydrogenation attained by reactive processing were higher than those of the reaction carried out in solution at the same [TSH]/[C=C] ratio, reaction temperature and time. In-creasing the reaction temperature and reaction time resulted in increases of the percentage of hydrogenation. For BR, the maximum percentage of hydrogenation obtained was 36% at [TSH]/[C=C]=1/1.5. For NR, the highest percentage of hydrogenation was 34% at [TSH]/[C=C]=1/1.5. Cis-trans isomerisation was also observed to occur during hydrogenation of both BR and NR. Thermal stabilities of the hydrogenated BR and NR were shown to improve over those or the unhydrogenated counterparts.