• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.7
• /
• pp.549-554
• /
• 2009

Al thin films were synthesized on TiN/Si substrate by MOCVD using N-methylpyrrolidine alane (MPA) precursor. Effects of substrate temperature, reaction pressure on the deposition rate, surface roughness and electrical resistivity were investigated. The early stage of Al thin film formation was analyzed by in-situ surface reflectivity measurement with a laser and photometer apparatus. From the Arrhenius plot of deposition rate vs. substrate temperature, it was found that the activation energy of surface reaction was 91.1kJ/mole, and the transition temperature from surface-reaction-limited region to mass-transfer-limited region was about $150^{\circ}C$. The growth rate increased with the reaction pressure, and average growth rates of $200{\sim}1,200nm/min$ were observed at various experimental conditions. Surface roughness of the film increased with the film thickness. The electrical resistivity of Al film was about $4{\mu}{\Omega}{\cdot}cm$ in the case of optimum condition, and it was close to the value of the bulk Al, $2.7{\mu}{\Omega}{\cdot}cm$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.2
• /
• pp.104-108
• /
• 2015

Al thin films were deposited on TiN/Si(100) via metal-organic chemical vapor deposition using N-methylpyrrolidine alane as a precursor. Characterization of the deposited films were investigated with SEM, XRD, ${\alpha}$-step, AFM, 4-point probe. The early stage of Al thin film deposition was analyzed by in-situ surface reflectance measurement with laser and photometer apparatus. The surface reflectance were changed greatly during the initial 30~40 seconds. There were two increases and two decreases in the surface reflectance, thus the sequence of Al films were deposited at 8 significant points of the surface reflectance change. Surface topograph and cross-sectional view of each film were analyzed with SEM. Al films were grown in the complex mechanism of Volmer-Weber and Stranski-Krastanov process.

• Journal of the Korean Solar Energy Society
• /
• v.39 no.1
• /
• pp.33-40
• /
• 2019

Al-doped ZnO (AZO) thin films were synthesized on Si(100) wafers via plasma enhanced metal organic chemical vapor deposition (PE-MOCVD) method using diethyl zinc (DEZ) and N-methylpyrrolidine alane (MPA) as precursors. Effects of Al/Zn mixing ratio, plasma power on the surface morphology, crystal structure, and electrical property were investigated with SEM, XRD and 4-point probe measurement respectively. Growth rate of the film decreased slightly with increasing the Al/Zn mixing ratio, however electrical property was enhanced and resistivity of the film decreased greatly about 2 orders from $9.5{\times}10^{-1}$ to $8.0{\times}10^{-3}{\Omega}cm$ when the Al/Zn mixing ratio varied from 0 to 9 mol%. XRD analysis showed that the grain size increased with increasing the Al/Zn mixing ratio. Growth rate and electrical property were enhanced in a mild plasma condition. Resistivity of AZO film decreased down to $7.0{\times}10^{-4}{\Omega}cm$ at an indirect plasma of 100 W condition which was enough value to use for the transparent conducting oxide (TCO) material.