• Journal of the Korean Society of Safety
• /
• v.18 no.3
• /
• pp.64-68
• /
• 2003

ITO_{(n)}/Si_{(p)}$ solar cell is fabricated by vaccum deposition method under the resistance heating with substrate temperature kept about 200[$^{\circ}C$] and than their properties are investigated. The maximum output of fabricated solar cell is obtained when the composition of the thin film is consisted of indium oxide 91[mole %] and tin oxide 9(mole %). The solar cell electrical charateristics can be improved by annealing but are deteriorated at temperature above 600[$^{\circ}C$] for longer than 15[min].

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.479-483
• /
• 2002

Silicon dioxide thick film using silica optical waveguide cladding was fabricated by Plasma Enhanced Chemical Vapor Deposition(PECVD) method, at a low temperature ($320^{\circ}$C) and from $(SiH_4+N_2O)$ gas mixtures. The effects of deposition parameters on properties of $SiO_2$ thick films were investigated by variation of $N_2O/SiH_4$ flow ratio and RF power. After the deposition process, the samples were annealed in a furnace at $1150^{\circ}$C, in N2 atmosphere, for 2h. As the $N_2O/SiH_4$ flow ratio increased, deposition rate decreased from 9.4 to 2.9 ${\mu}m/h$. As the RF power increased, deposition rate increased from 4.7 to 6.9 ${\mu}m/h$. The thickness and the refractive index measurements were measured by prism coupler. X-ray Photoelectron Spectroscopy(XPS) and Fourier Transform-infrared Spectroscopy(FT-IR) were used to determine the chemical states. The cross-section of films was observed by Scanning Electron Microscopy(SEM).

• Korean Journal of Materials Research
• /
• v.28 no.4
• /
• pp.241-246
• /
• 2018

$TaN_x$ film is grown by plasma enhanced atomic layer deposition (PEALD) using t-butylimido tris(dimethylamido) tantalum as a metalorganic source with various reactive gas species, such as $N_2+H_2$ mixed gas, $NH_3$, and $H_2$. Although the pulse sequence and duration are the same, aspects of the film growth rate, microstructure, crystallinity, and electrical resistivity are quite different according to the reactive gas. Crystallized and relatively conductive film with a higher growth rate is acquired using $NH_3$ as a reactive gas while amorphous and resistive film with a lower growth rate is achieved using $N_2+H_2$ mixed gas. To examine the relationship between the chemical properties and resistivity of the film, X-ray photoelectron spectroscopy (XPS) is conducted on the ALD-grown $TaN_x$ film with $N_2+H_2$ mixed gas, $NH_3$, and $H_2$. For a comparison, reactive sputter-grown $TaN_x$ film with $N_2$ is also studied. The results reveal that ALD-grown $TaN_x$ films with $NH_3$ and $H_2$ include a metallic Ta-N bond, which results in the film's higher conductivity. Meanwhile, ALD-grown $TaN_x$ film with a $N_2+H_2$ mixed gas or sputtergrown $TaN_x$ film with $N_2$ gas mainly contains a semiconducting $Ta_3N_5$ bond. Such a different portion of Ta-N and $Ta_3N_5$ bond determins the resistivity of the film. Reaction mechanisms are considered by means of the chemistry of the Ta precursor and reactive gas species.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.11 no.11
• /
• pp.2095-2099
• /
• 2007

In this paper, the optimum amorphous silicon nitride thin film is deposited using plasma enhanced chemical vapor deposition(PECVD). Amorphous silicon nitride is deposited using $SiH_4$ and $NH_3$ gas. At this time, electrical and optical characteristics of amorphous silicon nitride and deposition rate are changed under deposition condition such as $SiH_4$, $NH_3$ and $N_2$ gas flow rate, chamber pressure, rf power and substrate temperature. From the experimental results, we can estimate that the deposition condition makes a good electrical characteristic of amorphous silicon nitride thin film.

• The Journal of the Institute of Internet, Broadcasting and Communication
• /
• v.15 no.6
• /
• pp.231-238
• /
• 2015

In this paper, we have studied a sheet resistance property of N- and P-type thin films deposited on ITO glass by use of RF magnetron sputtering. The N-type samples which has the deposition condition of 150W RF power, shows the highest current value, and the samples deposited for 15 minutes shows a better Ohmic contact property. As the substrate temperature, RF power and deposition time are increased, the sheet resistance of the samples is increased, and the low sheet resistance sample shows a better I-V property. The P-type samples shows the highest current value by 150W RF power condition as similar as N-type samples. and the samples deposited for 20 minutes shows a better ohmic contact property. The sheet resistance of the both types samples is increased as increasing RF power and deposition time.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.429-429
• /
• 2012

To investigate the gettering effect of B-doped n-type monocrystalline silicon wafer, we made the p-n junction by diffusing boron into n-type monocrystalline Si substrate and then oxidized the boron doped n-type monocrystalline silicon wafer by in-situ wet and dry oxidation. After oxidation, the minority carrier lifetime was measured by using microwave photoconductance and the sheet resistance by 4-point probe, respectively. The junction depth was analyzed by Secondary Ion Mass Spectrometry (SIMS). Boron diffusion reduced the metal impurities in the bulk of silicon wafer and increased the minority carrier lifetime. In the case of wet oxidation, the sheet resistance value of ${\sim}46{\Omega}/{\Box}$ was obtained at $900^{\circ}C$, depostion time 50 min, and drive-in time 10 min. Uniformity was ~7% at $925^{\circ}C$, deposition time 30 min, and drive-in time 10 min. Finally, the minority carrier lifetime was shown to be increased from $3.3{\mu}s$ for bare wafer to $21.6{\mu}s$ for $900^{\circ}C$, deposition 40 min, and drive-in 10 min condition. In the case of dry oxidation, for the condition of 50 min deposition, 10 min drive-in, and O2 flow of 2000 SCCM, the minority carrier lifetime of 16.3us, the sheet resistance of ${\sim}48{\Omega}/{\Box}$, and uniformity of 2% were measured.

• Korean Journal of Materials Research
• /
• v.21 no.5
• /
• pp.268-272
• /
• 2011

Due to their novel properties, GaN based semiconductors and their nanostructures are promising components in a wide range of nanoscale device applications. In this work, the gallium nitride is deposited on c-axis oriented sapphire and porous SWCNT substrates by molecular beam epitaxy using a novel single source precursor of $Me_2Ga(N_3)NH_2C(CH_3)_3$ with ammonia as an additional source of nitrogen. The advantage of using a single molecular precursor is possible deposition at low substrate temperature with good crystal quality. The deposition is carried out in a substrate temperature range of 600-750$^{\circ}C$. The microstructural, structural, and optical properties of the samples were analyzed by scanning electron microscopy, X-ray diffraction, Raman spectroscopy, and photoluminescence. The results show that substrate oriented columnar-like morphology is obtained on the sapphire substrate while sword-like GaN nanorods are obtained on porous SWCNT substrates with rough facets. The crystallinity and surface morphology of the deposited GaN were influenced significantly by deposition temperature and the nature of the substrate used. The growth mechanism of GaN on sapphire as well as porous SWCNT substrates is discussed briefly.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.455-460
• /
• 2005

Deposition of TiN$_{x}$ film was conducted with a DC sputtering technique. The effect of the processing parameters such as substrate temperature, deposition time, working pressure, bias power, and volumetric flowing rate ratio of Ar to N$_{2}$ gas on the resistivity of TiN$_{x}$ film was systematically investigated. Three kinds of substrates, soda-lime glass, (100) Si wafer, and 111m thermally grown (111) SiO$_{2}$ wafer were used to explore the effect of substrate. The phase of TiN$_{x}$ film was analyzed by XRD peak pattern and deposition rate was determined by measuring the thickness of TiNx film through SEM cross-sectional view. Resistance was obtained by 4 point probe method as a function of processing parameters and types of substrates. Finally, optimum condition for synthesizing TiN$_{x}$ film having lowest resistivity was discussed.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.37 no.3
• /
• pp.27-33
• /
• 2000

The selective chemical vapor deposition techniques for Cu metallization were studied. For enhancing the selectivity, furnace annealing and N$_{2}$ plasma were treated on patterned TiN/BPSG prior to the copper deposition. As a result, Cu did not deposited lead to suppressing the nucleation on BPSG singificantly. With the increasement the plasma treatment temperature, copper nucleation on BPSG was suppressed mote effectively, From TOF-SIMS(Time-of-Flight Secondary ion Mass Spectrometry), it is considered that annealing and N$_{2}$ plasma treatment remove hydroxyl(0-H) group so that eliminating the nucleation site for copper precursor enhance the selectivity.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.179-179
• /
• 2010

다양한 분야에서 확산 방지막은 소자의 신뢰성 향상에 중요한 역할을 하고 있다. 최근 반도체에 적용되기 시작한 구리 배선 형성 공정에서도 실리콘이나 실리콘 산화막으로 구리가 확산하는 것을 방지하는 기술이 중요한 부분을 차지하고 있다. 기존 physical vapor deposition (PVD)법을 이용한 $TaN_x$ 확산 방지막 형성 기술이 성공적으로 적용되고 있으나 반도체의 최소선폭이 지속적으로 감소함에 따라 한계에 다다르고 있다. 20 nm 급과 그 이하의 구리 배선을 위해서는 5 nm 이하의 매우 얇고 높은 피복 단차율을 가진 확산 방지막 형성 기술이 요구된다. 또한, 요구 두께의 감소에 따라 더 우수한 확산 방지 특성이 요구된다. Atomic layer deposition (ALD)은 박막의 정교한 두께 조절이 가능하며 높은 종횡비를 가지는 구조에서도 균일한 박막 형성이 가능하다. 이번 연구에서는 다른 질소 함량을 가진 $TaN_x$ 박막을 Tertiarybutylimido tris (ethylamethlamino) tantalum (TBITEMAT) 전구체와 $H_2+N_2$ 반응성 플라즈마를 사용하여 plasma enhanced atomic layer deposition (PEALD) 법으로 형성하였다. 박막 내질소 함량에 따라 $TaN_x$의 상 (phase)과 미세구조 변화가 관찰되었고, 이러한 물성의 변화는 확산 방지 특성에 영향을 주었다. TEM (Transmission electron microscopy)과 SEM (scanning electron microscope), XPS (x-ray photoelectron spectroscopy)를 통해 $TaN_x$의 물성을 분석하였고, 300 도에서 700 도까지 열처리 후 XRD (x-ray deffraction)와 I-V test를 통해 확산 방지막의 열적 안정성이 평가되었다. PEALD를 통해 24 nm 크기의 trench 기판 위에 약 4 nm의 $TaN_x$ 확산 방지막이 매우 균일하게 형성할 수 있었으며 향후 구리 배선에 효과적으로 적용될 것으로 예상된다.