• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.297-298
• /
• 2005

We have fabricated twisted nematic (TN) liquid crystal cells doped by carbon nanotubes (CNTs) with different CNT wt. %. With a minute amount doping, multi-walled CNTs did not perturb the liquid crystal orientations at the off- and on-state. The hysteresis studies of voltage-dependent capacitance (V-C) under the influence of electric field generated by ac and dc voltage show that the residual do, which is tightly related to image sticking problem in liquid crystal displays, is greatly reduced due to ion trapping by CNTs. Also, the V-C hysteresis shows dependency of capacitance on concentration of multi-walled CNTs.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 Techno-Fair 및 합동춘계학술대회 논문집 전기물성,응용부문
• /
• pp.159-160
• /
• 2008

본 논문에서는 변압기 절연유 상태를 측정하여 변압기 열화정도를 분석할 수 있는 CNT센서를 개발하였다. 센서의 감지막 형성을 위해 MWCNT(multi walled carbon nanotube)로 CNT paste를 제작하고 이를 프린팅공정을 이용하여 그 규격을 최적화하였다. 제작된 CNT 센서를 이용하여 절연유 상태를 분석하고 이를 전기 화학적 분석을 통하여 변압기 열화 정도를 확인하였다. 변압기 사용 여부에 따른 센서의 특성과 절연유의 산가, 절연파괴전압 등 기타 특성과 비교하여 변압기 절연유의 열화정도를 확인하였다. 변압기 과부화 및 과전류에 의해 열화가 진행되어 전산가가 높아지면 이를 CNT 감지막의 전기적 특성 변화로 확인 할 수 있다. 개발된 IT 센서를 이용하면 변압기 열화 정도를 실시간으로 확인 할 수 있어 변압기 사용에 있어서 안정성 확보 및 유지관리에 경제성을 높일 수 있다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2003년도 International Meeting on Information Display
• /
• pp.849-851
• /
• 2003

After multi-walled carbon nanotubes (MWNT) powder was crushed with ball milling process, it was mixed with organic vehicles. And then CNT paste was printed on ITO coated glass substrate. The field emission characteristics of CNT pastes fired in air atmosphere was better than that of CNT paste fired in Ar ambient due to less organic residues after firing.

• 한국산학기술학회:학술대회논문집
• /
• 한국산학기술학회 2010년도 춘계학술발표논문집 2부
• /
• pp.1127-1130
• /
• 2010

본 연구에서는 CNT의 분산성을 개선하고자 다중벽 탄소나노튜브(multi-walled carbon nanotube, MWNT)에 butyllithium solution 및 hexyllithium solution을 이용하여 표면을 화학적으로 개질하였다. 개질된 MWNT는 적외선 분광 분석 및 Raman spectrophotometer를 이용하여 MWNT에 작용기가 도입되었는지를 확인하였다. 또한, 열중량분석기(Thermogravimetric analysis, TGA)를 이용하여 작용기가 도입된 MWNT의 열적 성질을 측정하였으며, MWNT 및 개질된 MWNT를 다양한 용매에 따른 분산성을 확인하였다.

• 대한기계학회논문집B
• /
• 제36권1호
• /
• pp.25-29
• /
• 2012

탄소나노튜브의 기계적 특성과 금속의 전기적 특성을 이용할 수 있는 나노 복합구조체의 특성은 두 재료 사이의 계면이 중용한 역할을 한다. 본 연구에서는 나노임프린트 패터닝을 이용하여 촉매금속을 패턴하고 이를 이용한 개별 성장된 탄소나노튜브 위에 증기증착법을 이용하여 니켈을 증착한 나노구 조체의 계면을 조사하였다. 이를 위하여 고해상의 투사전자현미경과 3 차원 원자 프로브 분석기를 이용하였다. 탄소나노튜브 위에서 성장된 나노결정의 경우 준 안정 상태인 조밀입방구조의 $Ni_3C$ 를 형성하는 것으로 나타났다. 이러한 특성을 이용한 나노복합체의 응용가능성을 살펴보았다.

• 한국분말재료학회지
• /
• 제21권1호
• /
• pp.50-54
• /
• 2014

A powder-in-sheath rolling method was applied to a fabrication of a carbon nano tube (CNT) reinforced aluminum composite. A STS304 tube with an outer diameter of 34 mm and a wall thickness of 2 mm was used as a sheath material. A mixture of pure aluminum powders and CNTs with the volume contents of 1, 3, 5 vol was filled in the tube by tap filling and then processed to 73.5% height reduction by a rolling mill. The relative density of the CNT/Al composite fabricated by the powder-in-sheath rolling decreased slightly with increasing of CNTs content, but exhibited high value more than 98. The grain size of the aluminum matrix was largely decreased with addition of CNTs; it decreased from $24{\mu}m$ to $0.9{\mu}m$ by the addition of only 1 volCNT. The average hardness of the composites increased by approximately 3 times with the addition of CNTs, comparing to that of unreinforced pure aluminum. It is concluded that the powder-in-sheath rolling method is an effective process for fabrication of CNT reinforced Al matrix composites.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2007년도 추계학술발표대회 및
• /
• pp.137.2-137.2
• /
• 2007

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2005년도 International Meeting on Information Displayvol.II
• /
• pp.1459-1461
• /
• 2005

Carbon nanotube -copper composite structures were fabricated using composite plating method and their field emission characteristics were investigated. Multi-walled carbon nanotubes synthesized by chemical vapor deposition were used in the present study. It was revealed that turn-on field of the structures was about 3.0 $V/{\mu}m$ at the current density of 0.1 ${\mu}A/cm^2$. We observed relatively uniform emission characteristics as well as stable emission currents. CNT-Cu composite plating method is efficient and it has no intrinsic limit on the plating area. Moreover, it gives strong adhesion between emitters and an electrode. The refore, we expect that CNT-Cu composite plating method can be applied to fabricate electron field emitters for large area FEDs and large area vacuum lighting sources.

• 공업화학
• /
• 제19권2호
• /
• pp.161-167
• /
• 2008

다층카본나노튜브(MWCNT)가 강화된 폴리에틸렌에틸아크릴레이트(EEA) 나노복합체를 용융혼합법과 용액혼합법으로 제조하였다. 카본나노튜브의 형태 및 함량변화에 따른 기계적, 열적, 전기적 특성을 조사하였다. MWCNT의 함량이 증가함에 따라 인장강도, 모듈러스는 증가하였고, 파단신장률은 감소하였다. 할로우 형태의 MWCNT가 일반적인 MWCNT에 비해 우수한 인장강도 및 파단신장률을 나타내었다. MWCNT 함량이 증가함에 따라 약 $40^{\circ}C$의 열분해온도의 향상을 보였다. 전기적 특성은 용융혼합법의 경우가 가장 높은 전기저항 특성을 나타내었고, 용액혼합법의 경우 일반형 MWCNT가 할로우 MWCNT보다 낮은 체적저항을 보였다. MWCNT의 함량이 증가할수록 파단면 위로 돌출되는 CNT 수가 증가하였고, 인장변형을 가하면 표면 위로 돌출되는 CNT 수와 길이가 크게 증가하였다. 용융혼합된 시편이 용액혼합에 비해 돌출된 CNT의 수와 길이가 현격히 낮았다.

• 폴리머
• /
• 제37권4호
• /
• pp.526-532
• /
• 2013

라텍스 기법으로 제조한 폴리스티렌(PS)/탄소나노튜브(CNT) 나노복합재료의 CNT 분산 방법에 따른 유변물성과 전기 전도도를 비교하였다. PS/CNT 나노복합재료는 PS 입자와 CNT를 분산시킨 후 동결건조하여 제조하였다. 본 연구에서는 화학적 개질시 나타나는 CNT의 고유 물성 저하를 방지하기 위하여 sodium dodecylsulfate(SDS)를 첨가하는 방법과 polyvinyl pyrrolidone(PVP)으로 CNT를 감싸는 방법의 물리적 분산법을 적용하였다. 라텍스 기법에 적용한 물리적 분산 방법은 CNT의 분산에 매우 효과적이었다. SDS를 첨가한 경우는 PVP로 감싼 CNT를 사용하여 제조한 경우에 비해 나노복합재료의 유변물성의 증가폭이 낮은데 이는 저분자량인 SDS를 첨가로 인해 매트릭스의 물성이 감소하기 때문이다. CNT를 SDS로 분산시킨 나노복합재료와 PVP로 감싼 CNT를 사용한 나노복합재료의 전기적 임계점은 각각 0.23과 0.90 wt%로 나타났다. PVP로 CNT를 감싼 경우가 전기 전도도 향상 효과가 낮은데 이는 감싸고 있는 절연성의 PVP가 CNT간의 전기적 연결을 억제하기 때문이다.