• Journal of the Korea Institute of Building Construction
• /
• v.3 no.1
• /
• pp.93-105
• /
• 2003

The Precast Concrete(PC) method was developed for a large production of a structure in Europe. Afterwards, this PC method has been applied to a structure and an outside Coating of buildings extensively. The outside Coating of the building applied this PC method is a method to put tiles or stones to base concrete. And there is a method to use paints for, so the expression of various patterns is possible. The Multi-Layer Coating is one of the methods to use paints. This Multi-Layer Coating method can show various designs of external appearance with Foam when it is made with the PC panel. Also, the paint film of the PC panel enables a splendid appearance, and a protective function of concrete is possible, too. Therefore, it makes good durability of the PC. Besides, maintenance is easy to manage because it is free from pollution when it uses metallic materials, stones, or any other materials. You might have no trouble in applying the Multi-Layer Coating method in order to save a merit of an outside Coating on the PC panel. However, the Multi-Layer Coating method used as a current outside Coating method has pollution and bad working environment because Oil Epoxy Resins have toxicity and flammability. Therefore, a lot of warnings are required for coating work in order to have appropriate quality because working hours are short, and production efficiency is low too. These reasons make the cost of construction of the Multi-Layer Coating method increase. And employers or designers may have problems in selecting this Multi-Layer Coating method. Therefore, the purpose of this study is to get activation of the Multi-Layer Coating method by offering improvement measures about the problems of the existing Multi-Layer Coating method.

• Korean Journal of Materials Research
• /
• v.31 no.6
• /
• pp.331-338
• /
• 2021

Ti-Al-Si target and Cr-Si target are sputtered alternately to develop a multi-layered nitride coating on a steel mold to improve die-casting lifetime. Prior to the multi-layer deposition, a CrN layer is developed as a buffer layer on the mold to suppress the diffusion of reactive elements and enhance the cohesive strength of the multi-layer deposition. Approximately 50 nm CrSiN and TiAlSiN layers are deposited layer by layer, and form about three ㎛-thickness of multi-layered coating. From the observation of the uncoated and coated steel molds after the acceleration experiment of liquid metal injection casting, the uncoated mold is severely eroded by the adhesion of molten metallic glass. On the other hand, the multi-layer coating on the mold prevents element diffusion from the metallic glass and mold erosion during the experiment. The multi-layer structure of the coating transforms the nano-composite structured coating during the acceleration test. Since the nano-composite structure disrupts element diffusion to molten metallic glass, despite microstructure changes, the coating is not eroded by the 1,050 ℃ molten metallic glass.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.1 no.1
• /
• pp.33-36
• /
• 2000

Auto DOME-reversing system had been installed in a vacuum coating chamber which decreased the coating time, the electric energy spending and the contamination by rotating and revilving substance. Auto multi coating with dual electron beam was accomplished and effective coating area was increased. The coating duration was decreased with 30%. the production efficiency were increased with 50%. Also the surface conductivity the coated film uniformity and anti-reflection capablity were also improved.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.211-217
• /
• 2016

Boride coating applied on steam turbine parts of power plants has provided good particle erosion resistance under temperature of $550^{\circ}C$, but it isn't able to protect the parts effectively any more in ultra super critical (USC) steam turbine which is being operated up to temperature of $650^{\circ}C$. To ensure stable durability for USC steam turbine parts, an alternative coating replacing boride coating should be developed. In this study, multi-component boride coatings containing elements such as chromium (Cr) and vanadium (V) were formed on base metal (B50A365B) using thermochemical treatment method called by pack cementation. The thermochemical treatments involve consecutive diffusion of boron(B) and Cr or/and V using pack powders containing diffusion element sources, activators and diluents. The top layer of Cr-boride coating is primarily consisted of $Cr_2B_3$ and $Cr_5B_3$, while that of V-boride coating is mostly consisted of $VB_2$ and $V_2B_3$. The (Cr,V)-boride coating is consisted of $Cr_2B_3$, $Cr_5B_3$ and $V_2B_3$ mostly. The top surfaces of 3 multi-component boride coatings show hardness of $3200-3400H_v$, which is much higher than that of boride, about $1600-2000H_v$. In 5 wt.% NaCl solution immersion tests, the multi-component boride coatings show much better corrosion resistance than boride coating.

• Tribology and Lubricants
• /
• v.25 no.1
• /
• pp.7-12
• /
• 2009

Coating brittle intermetallic compounds on metal can enlarge the range of their use. It is found that intermetallic compound coating layers made by only combustion synthesis in an electric furnace have porous multi-phase structures containing several intermediate phases, even though the coating layers show good wear resistance. In this study, dense $Ni_{3}Al$ single phase layer corresponding to the initial composition of the mixed powder is coated on two different ferrous materials by the diffusing treatment after combustion synthesis. After- ward, sliding wear behaviors of the coating layer are evaluated in comparison with that of the coating layer with porous multi-phase structure made by only combustion synthesis. As a result, the wear properties of the coating layer composed of dense $Ni_{3}Al$ single phase are considerably improved at the range of low sliding speed com- pared with that of the coating layer with porous multi-phase structure, particularly in the running-in wear region. This is attributed to the fact that wear of the coating layer is progressed by shearing as a sequence of adhesion, not by occurring of pitting on the worn surface due to having dense structure without pores.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.5
• /
• pp.848-854
• /
• 2012

SCM420 steel cutting gear to improve the durability is quenched. When quenching, increases surface hardness, a change of the physical properties and machinability or fall. This study, using a solid carbide hobs skiving hobbing gear cutting finishing. And cutting tool solid carbide TiAlN coating hove when TiAlN coating on the surface of multi-con polishing hob conducted aero lap nano polishing for each cutting. Experimental results conducted aero lap nano coating on the surface polishing tool machinability was excellent. And aero lap nano polishing tool results were reduced 2.5 times the tool wear compared to TiAlN coated tools. Excellent results were 1.42 times longer tool life.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.6
• /
• pp.1665-1669
• /
• 2014

Four multialkoxy-functionalized siloxane base-polymers (BP-1~4) were synthesized through either hydrosilylation or condensation reactions in order to prepare multi-networked siloxane polymers having appropriate physical properties for protective coating in fabrications of electronics. Formulations of 4 base-polymers gave coating materials A and B. Product A showed well-controlled flowing and leveling properties, and product A-2 was successfully applied to protective insulating coating for junction areas of connectors and chips in PDP controller. Tack free time, extrusion rate, dielectric breakdown voltage, hardness, thermal stability, water resistance and flame resistance of products A and B were examined.

• Journal of Korean Ophthalmic Optics Society
• /
• v.2 no.1
• /
• pp.31-43
• /
• 1997

In this paper, the rate of transmittance regarding the home -and foreign-made lens that have been treated with multi coating and no coating has been studied in the range of the visible ray. The lens that were treated with No Coating turned out to be about 93% of the rate of transmittance, but those treated with Coating turned out to be over 98%. Especially, the rate of transmittance of product made by a company in a foreign country turned out to be homogeneous in the whole range.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.3
• /
• pp.138-143
• /
• 2007

The effects of texturing and anti-reflection coating on the reflection properties of multi-crystalline silicon solar cell have been investigated. The chemical solutions of alkaline and acidic etching solutions were used for texturing at the surface of multi-crystalline Si wafer. Experiments were performed with various temperature and time conditions in order to determine the optimized etching condition. Alkaline etching solution was found inadequate to the texturing of multi-crystalline Si due to its high reflectance of about 25%. The reflectance of Si wafer texturing with acidic etching solution showed a very low reflectance about 10%, which was attributed to the formation of homogeneous. Also, deposition of ITO anti-reflection coating reduced the reflectance of multi-crystalline si etched with acidic solution($HF+HNO_3$) to 2.6%.

• Journal of the Korean Applied Science and Technology
• /
• v.26 no.4
• /
• pp.467-472
• /
• 2009

Ultraviolet curable coating solution was prepared with poly(ethylene glycol) acrylate oligomer and various mono and multi-functional acrylate monomers. The optical properties of UV cured coating layer on PET film with acrylate coating solution containing metal oxides, such as fumed silica and alumina, were also investigated to reduce light reflection on films. Poly(ethylene glycol) diacrylate which has 575 of average molecular weight was used as oligomer acrylate, and pentaerythritol triacrylate and dipentaerythritolpenta-/hexa acrylate were used as multi-functional acrylate monomers. Also, butyl acrylate was used to improve the adhesion as well as to reduce glass transition temperature to give a better flexability. 1-hydroxy cyclohexyl phenyl ketone was used as photoinitiator. We found out the metal oxides in acrylate coating solution showed a homogeneous dispersion from energy dispersive spectroscopy data. Transmittance and light reflection of coated PET film was measured with UV/vis spectrometer and gloss meter, respectively. When 1.00 g of both metal oxides was added into coating solution, the transmittance and the glossiness were reduced from 90% to 30% and from 190 GU to 35 GU, respectively. However, adding up to 1.00 g of the metal oxide into coating solution did not affect on the hardness of coating layer and adhesion between coated layer and PET film. Conclusively, we can control transmittance and light reflection of coated film by adjusting the amounts of metal oxide in coating solution.