• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.1
• /
• pp.76-84
• /
• 2013

In this study, some engineering properties of OPC and GGBFS shotcrete mortars with alkali-free or aluminate accelerator were experimentally examined. As a result, GGBFS mortars with alkali-free accelerator were significantly similar to OPC mortars with same accelerator with respect to both setting time and compressive strength. Comparatively, GGBFS mortars with aluminate accelerator showed a good performance with an increased replacement of GGBFS. Furthermore, when replaced with GGBFS over 50%, the mortars exhibited superior performances of electrical resistivity and chloride ions penetration resistance. Accordingly, it is suggested that GGBFS has a beneficial effect as shotcreting materials in the condition of proper replacement levels.

• Explosives and Blasting
• /
• v.27 no.1
• /
• pp.32-37
• /
• 2009

To look over the effect of mixed proportion of cement, sand and water on strength, 162 tests were made for 9 mix proportions. It was observed that strength increased as water in the mixture is reduced. As a result of the control of sand ratio by 50%, the execution strength increased when the sand ratio is raised. Strength was consistent during curing period on each mix proportion, but there were sections where it suddenly increased. Poisson's ratio widely ranged from 0.13 to 0.27, and Young's modulus also broadly ranged from 13.79MPa to 33.25MPa. Poisson's ratio had nothing to do with uniaxial compressive strength, wheras Young's modulus was concerned with it. Young's modulus from theory and experiment showed similar outcome on the 3rd curing day, however, the strength from theory was higher than that from test after 3rd day. In consequence, there was a great change of strength between 3rd and 7th curing day. In addition, it is more efficient to use field strength value between the 3rd and 7th day and to apply Young's modulus on it for determining the exact time.

• Korean journal of food and cookery science
• /
• v.33 no.2
• /
• pp.181-189
• /
• 2017

Purpose: This study was conducted to examine the effects of the starch concentration of filled hydrogel and the addition of ${\alpha}-amylase$ and simulated mastication processing in an oral phase on lipid digestion and ${\beta}-carotene$ bioaccessibility of filled hydrogels. Methods: Lipid digestion and ${\beta}-carotene$ bioaccessibility of the filled hydrogels were measured after the samples were passed through an in vitro gastrointestinal tract model consisting of oral, gastric, and small intestinal phases. Results: The initial rate and final extent of lipid digestion were higher in the filled hydrogels than in the emulsion when the filled hydrogels were treated in an oral phase without simulated mastication processing and addition of ${\alpha}-amylase$, regardless of starch concentration. However, when the filled hydrogels were minced using mortar and pestle for 2 min and were exposed to ${\alpha}-amylase$, the filled hydrogel fabricated with 5% starch showed the lowest lipid digestion rate and extent compared to the emulsion and other filled hydrogels. Bioaccessibility of ${\beta}-carotene$ was higher in the filled hydrogels than in the emulsion, regardless of the digestion method performed in an oral phase and starch concentration. However, there were appreciable differences in bioaccessibility of the filled hydrogels depending on whether or not simulated mastication and addition of ${\alpha}-amylase$ were employed. Conclusion: These results suggested that the rheological properties of initial filled hydrogels and simulated mastication processing in an oral phase plays an important role in determining the lipid digestion and ${\beta}-carotene$ bioacccessibility entrapped within filled hydrogels.

• Journal of the Korea Concrete Institute
• /
• v.23 no.6
• /
• pp.817-826
• /
• 2011

Concrete using eco-cement has a problem with long-term strength development. However, currently, a long-term strength development mechanism is not confirmed, resulting in a lack of application of eco-cement in construction fields. In this study, the curing humidity influence on development in long-term strength of concrete using eco-cement and the relationship between strength and pore structure were examined. The results showed that wet cured eco-cement with a high water/cement ratio showed serious long-term strength reduction due to non-reduction of pore volume (pore size over 10 nm) in mortar caste with eco-cement. Also, the study results on improvement of long-term strength of eco-cement by partial replacement with ordinary portland cement and finely-ground fly ash showed that both of these alternatives improved long-term strength of concrete caste with eco-cement due to gradual refinement of their micro-structure.

• Journal of the Korea Concrete Institute
• /
• v.24 no.2
• /
• pp.121-127
• /
• 2012

Cement has been traditionally used as a main binding material of high ductile fiber reinforced cementitious composites. The purpose of this paper is to investigate the feasibility of using alkali-activated slag and polyvinyl alcohol (PVA) fibers for manufacturing high ductile fiber reinforced cementless composites. Two mixture proportions with proper flowability and mortar viscosity for easy fiber mixing and uniform fiber dispersion were selected based on alkali activators. Then, the slump flow, compression, uniaxial tension and bending tests were performed on the mixes to evaluate the basic properties of the composites. The cementless composites showed an average slump flow of 465 mm and tensile strain capacity of approximately 2% of due to formation of multiple micro-cracks. Test results demonstrated a feasibility of manufacturing high ductile fiber reinforced composites without using cement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.677-680
• /
• 2008

The surface of particles was energetically modified by inter-grinding OPC and BFS in vibration mill for improvement of the early strength and low-heat evolution of concretes. BFS was pre-grinding in ball-mill to 2535(BS2) and 3245 $cm^2/g$(BS3), in blaine surface area. The inter-grinding time in vibration mill was changed from 10 minutes to 30 minutes. And Mixing ration of BFS to OPC was changed in 60, 70, 80%. After inter-grinding, the change of specific surface area, particle size distribution, hydration heat of cement and compressive strength of mortar were measured. As the result of comparison test with LHC, it was found that the mixture and inter-grinding time satisfying the value of over 100% of compressive strength for 7 days and under 170J/g of heat of hydration for 72 hours. and it was confirmed that the possibility of low heat slag cement utilizing blast furnace slag(BS2, BS3) with the low fineness in high volumes.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.1
• /
• pp.27-34
• /
• 2020

In the industry, due to the carbon dioxide gas produced during cement production is increasing, research on recycling by-products has been actively conducted. In the industrial by-products, the high calcium fly ash(HCFA) produced by the blast-furnace in the circulating fluidized bed combustion method has a high ratio of CaO and CaSO4. In view of this, the purpose of this is to use high calcium fly ash(HCFA) as a stimulant in blast furnace slag powder and use it as a cement substitute. As a result, it is judged that the substitution ratio of HCFA should be 15% or less. In addition, although durability and strength are relatively lower than of OPC, it is considered that it can be utilized as an environmentally building material.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.4
• /
• pp.145-151
• /
• 1998

The vertical tensile stress, ${\sigma}_y$, in the contact zone between the overlay (mortar layer) and substratum (base concrete) can be the main cause of the failure phenomenon of overlaid concrete structures. The development of tensile stress, ${\sigma}_y$, due to external rainy condition was analytically investigated using finite element method. Rainfall intensity $(n_R\;=\;1/a,\;t_R\;=\;10min,\;60min)$, thickness of overlay (do=1,2,4,10 cm) and overlay material (CM,ECM,EM) were the main variables in the analyses. An equation was suggested with which the development of vertical tensile stress, ${\sigma}_y$, in the rainy condition could be determined. Using this equation, it is possible to select proper material properties and overlay thicknesses to prevent failure in the contact zone due to thermally transient condition caused by rainfall.

• Journal of the Korea Concrete Institute
• /
• v.13 no.4
• /
• pp.406-413
• /
• 2001

Up to this day, reinforced spun concrete pipes have been widely used as drain pipes. However, many reinforced spun concrete pipes are exposed to the deteriorated environment such as freezing-thawing damage and chemical attack by the growth of a sulfur-oxidizing bacterium isolated from corroded concrete. The purpose of this study is to evaluate the effects of lining by polymer-modified mortar using polymer dispersions as cement modifier on the development in durability of reinforced spun concrete pipe. The polymer-modified mortars were prepared with various polymer types and polymer-cement ratios, and tested for compressive and flexural strengths, acid, freezing-thawing, and heat resistances. And then, the reinforced spun concrete pipe product lined by polymer-modified mortars was tested for adhesion in tension and surface conditions according to curing temperatures in the field. From the test results, it is apparent that the polymer-modified mortars have good mechanical properties and durability as a lining material. In practice, all polymers can be used as lining the materials for reinforced spun concrete pipe, and types of polymer, and polymer-cement ratio and curing conditions are controlled for a good lining product.

• Resources Recycling
• /
• v.22 no.3
• /
• pp.36-42
• /
• 2013

According to the recent community-based structures enlargement, specification, and diversification. It needs appropriate construction materials in terms of intensity and environmental aspects. Thus, in manufacturing the cement using micro limestone powder which is main material. It is also expected to save energies and reduces $CO_2$, by using the blast furnace slag and fly ash which are mitigated environmental load construction materials that emerged. In this research, The durability aspect tries to be grasped considering the chemical property according to the coherence of the hydration product. Consequently, The compressive strength was measured over 30 Mpa on 3rd. In addition, according to the content of the limestone powder, the setting time is promoted. It has the feature expanded in the length change. And it is determined because the possibility of replacing the existing for construction material such as it is measured compared with the time to use the portland cement usually that flexural strength is high with the age 7 days ago, so it is sufficient.