• Journal of the Korean Ceramic Society
• /
• v.33 no.5
• /
• pp.495-506
• /
• 1996

Monodispersed colloidaly yttria(Y2O3) can be used in a variety of applications such as phosphors. IR transparent materials and fine ceramics. For preparing monodispersed yttria homogeneous precipitation has been regarded as a fovorable method that is monodispersed yttria can be obtained through calcining monodispersed colloidal compound of yttrium (eg:Y(OH)CO3.nH2O)which can be prepared by homogeneous precipitation with urea. It is however still required to find out the quantitative effects of important variables of precipitation such as concentration of yttrium and urea reaction temperature and initial pH of reactant even though homogeneous precipitation of Y3+ with urea has been studied extensively. Among the effects of these variables we investiga-ted 1) the effect of yttrium concentration on the shape and size of precipitate and the reation rate 2) range of yttrium concentration required to make monodispersed colloidal particles 3) the reason for limited concentra-tion range of yttrium and 4) the effect of ultrasonic radiation on the limited concentration.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.981-987
• /
• 2002

Monodispersed colloidal silica was prepared by Stober process. We have synthesized monodispersed colloidal silica of carious sizes (100 nm, 200 nm, 300 nm) by controlling volume ratios of TEOS(Tetraethylorthosilicate), $NH_4OH$, Ethanol and D. I. water. Shape and monodispersity of the synthesized colloidal particles were observed by Scanning Electron Microscopy(SEM) and laser light scattering particle analyzer. Self-assembled monolayer of monodispersed colloids was achieved by dipping Si substrate into a well-dispersed silica suspension. It was determined that uniformity and spatial extent of the self-assemble monolayer of monodispersed colloids are significantly influenced by the experimental parameters such as concentration, pH and surface tension of the colloidal suspension. We have observed a hexagonally well-ordered packing colloidal monolayer in a relatively large area (1.5 mm ${\times}$ 1.5 mm) as confirmed by SEM.

• KSTLE International Journal
• /
• v.6 no.1
• /
• pp.28-32
• /
• 2005

The electrorheoloRical (ER) fluids are composed of a colloidal dispersion of polarizable particles in insulating oil, and it's the rheological property changes by the applied electric field. These changed are reversible and occur fast within a fewmilliseconds. The ER properties of the ER fluid such as increment of viscosity and yield stress come from the particle chain structure induced by electric fleld. When formulating the ER fluid for a speciflc application, some requirement must besatisfled, which are high yield stress under electric field, rapid response, and dispersion stability. While this characteristic makes valuable ER fluids in valious industrial applications, their lung term and quiescent application has been limited because ofproblems with particle sedimentation. In an effort to overcome sedimentation problem of ER fluids, the anhydrous ER materials of monodispersed hollow polyaniline (PANI) and adipate derivative respectively with submicron-sized suspension providing wide operating temperature range and other advantage were synthesized in a four-step procedure. The ER fluidswere characterized by FT-lR, TGA, DLS, SEM, and TEM. Stability of the suspensions was examined by an UV spectroscopy.The rheological and electrical properties of the suspension were investigated Couette-type rheometer with a high voltagegenerator, current density, and conductivity. And the behavior of ER suspensions was observed by a video camera attached toan optical microscope under 3kV/mm. The suspensions showed good ER properties, durability, and particle dispersion.