• 한국정밀공학회지
• /
• 제22권10호
• /
• pp.129-136
• /
• 2005

The demand on thermos furnace of Al molten metal has recently been getting higher and higher according to the increase in use of Al and Al alloys. This study considers the estimation of the thermal and mechanical stability in the thermos furnace for Al casting. It is executed through the analysis of heat transfer on the refractory material and heat stress on each steel shell. Also, the estimation of structural stability was appraised through the strength analysis of the lower structure. In result, the temperature of steel shell rose to 320.15K and its elastic deformation was about 1.5mm. The elastic deformation of the lower structure was about 0.66mm. As a result of it, the data obtain from the analysis in this study are regarded as stable value on considering that the size of the furnace is 2500mm.

• Metals and materials international
• /
• 제24권6호
• /
• pp.1241-1248
• /
• 2018

The reactive wetting behaviors of molten Zn-Al-Mg alloys on MnO- and amorphous (a-) $SiO_2$-covered steel sheets were investigated by the sessile drop method, as a function of the Al and Mg contents in the alloys. The sessile drop tests were carried out at $460^{\circ}C$ and the variation in the contact angles (${\theta}_c$) of alloys containing 0.2-2.5 wt% Al and 0-3.0 wt% Mg was monitored for 20 s. For all the alloys, the MnO-covered steel substrate exhibited reactive wetting whereas the $a-SiO_2$-covered steel exhibited nonreactive, nonwetting (${\theta}_c>90^{\circ}$) behavior. The MnO layer was rapidly removed by Al and Mg contained in the alloys. The wetting of the MnO-covered steel sheet significantly improved upon increasing the Mg content but decreased upon increasing the Al content, indicating that the surface tension of the alloy droplet is the main factor controlling its wettability. Although the reactions of Al and Mg in molten alloys with the $a-SiO_2$ layer were found to be sluggish, the wettability of Zn-Al-Mg alloys on the $a-SiO_2$ layer improved upon increasing the Al and Mg contents. These results suggest that the wetting of advanced high-strength steel sheets, the surface oxide layer of which consists of a mixture of MnO and $SiO_2$, with Zn-Al-Mg alloys could be most effectively improved by increasing the Mg content of the alloys.

• Tribology and Lubricants
• /
• 제16권1호
• /
• pp.15-21
• /
• 2000

Radiation of Nd-YAG laser changes and refines the surface microstructure of steels, which gives rise to enhancement of hardness and resulting wear resistance. In the present work, the effect of processing parameters during the surface modification with laser on the wear behavior of the SM45C steel was studied by means of wear testing. The counter material was alumina ceramics. The microstructure observation revealed the dependence of molten depth and width on the defocusing distance. The laser modification of steel surface give rise to improved wear resistance in the testing speed range of either <0.2 m/s or >0.9 m/s Material transfer from steel was wear observated the surface of counter material when testing speed was lower than 0.7 m/s.

• 한국세라믹학회지
• /
• 제19권1호
• /
• pp.24-34
• /
• 1982

The effect of the several variables on wetting of AISIB1113 steel by molten glass was studied by Sessible-drop method. Experimental variables were temperature, firing atmospheres, Fe2O3 addition to the sealing glass and steel surface conditions. The degree of wetting in terms of contact angles between molten glass and metal tested at different test conditions was analyzed by using Young's equation. The results showed that contact angles in H2 atmosphere in the glass metal systems were high but in N2 atmosphere, were small for studied glass metal systems. Especially, when the glass drop was in contact with oxidized steel in N2 atmosphere, The best adherence with contact angle of approximately 9°was obtained. In the case of Fe2O3 addition in glass contact angles subtantially increased due to the increase of surface tension of glass. Wetting phenomena were also discussed under the basis of these experimental results.

• 한국표면공학회지
• /
• 제30권3호
• /
• pp.159-166
• /
• 1997

The metalliding technique was adopted to obtain the diffusion coating of zirconium on AISI 304 Stainless Steel in molten mixed chlorides (32.9wt.%LICl-34.8wt.%NaCl-32.3wt.%). Experiments were carried out in argon gas atmosphere. The electrolytic cell was consisted of a AISI 304 Stainless steel cathode and a consumable zirconium anode. The quality of deposit was analysed by SEM, Optical Microscope, EDS, and also examined by the Micro-Vickers hardness and corrosion tests. Interface of deposit layer was identified as zirconium-iron alloy layer caused by diffusion process at elevated temperatures. The optimum condition for the metalliding was found to be the bath temperature of $550^{\circ}C$, the concentration of $K_2ZrF_6$ ,5wt.%, cathodic current derrent density of 7.0 to 10.0mA/$\textrm{cm}^2$ , and anodic current density of 2.0mA/$\textrm{cm}^2$.

• 한국표면공학회지
• /
• 제26권4호
• /
• pp.183-191
• /
• 1993

Diffusion coating(metalliding) of aluminium on steel from molten fluorides(29.2wt.% LiF-11.7wt.% NaF-59.1wt.% KF, FLINAK) was studied. The electrolytic cell consists of a steel cathode and a consumable aluminium anode. Effects of manganese on the aluminium deposition were also investigated. The quality of the deposit was analyzed by SEM, OM, EPMA, EDXA, and also examined by means of Micro-Vickers hardness and corrosion tests. Deposit layer was identified as an aluminium-rich iron alloy caused by diffusion process. The optimum condition for the metalliding was found to be the current density, 50 to $150mA/\textrm{cm}^2$, the bath tem-perature, $57.5^{\circ}C$, and the amount of AlF3, 10wt.%. Addition of manganese fluoride (up to 5wt.%) as a co-de-posit element improved significantly the quality of the deposit layer.

• 자원리싸이클링
• /
• 제28권4호
• /
• pp.44-50
• /
• 2019

국내 전기로 공정에서 산화 반응열 및 탄소 연소열 등으로 인한 화학에너지는 전체 투입 에너지 대비 30%정도로 알려져 있다. 전기로에서 $CO_2$를 저감하기 위해서는 전기로 용해 구간 중에 사용되는 전력에너지를 줄이고 화학에너지 사용을 높여야 한다. 일반적으로 용강 중 탄소를 단독으로 투입할 경우, 탄소가 용강에 용해되기 전 낮은 밀도로 인해 슬래그 층으로 부유한다. 용강 중 탄소 농도가 높을 시 취입하는 산소와 용강 중 탄소의 연소반응으로 인해 전력에너지를 낮추며 화학에너지 사용량을 높일 수 있다. 따라서 탄소 연소열의 효율을 높이기 위해서는 용강 중 새로운 탄재 장입 조건이 필요하다. 한편, Al 제련 후의 부산물로 알려져 있는 Al 드로스는 금속성 Al을 25 mass% 이상 함유하고 있으며 Al은 탄소와 비교하여 높은 산화열을 가지고 있다. 그러나 Al 드로스는 재활용이 어려워 거의 매립하고 있으며, Al 드로스 내 Al의 산화열을 효과적으로 활용하기 위해서는 철강 공정 적용에 대한 연구가 필요하다. 본 연구에서는 화학 에너지의 활용 증대를 위한 기반연구로서, 분코크스와 Al 드로스를 화학에너지 연료로서 활용하여 다양한 배합비 및 반응 온도에서 용강 중 탄소 및 알루미늄의 용해 농도와 용해효율을 조사하였다.

• 한국표면공학회지
• /
• 제31권1호
• /
• pp.3-11
• /
• 1998

Molten Carbonate Fuel cell is a promising new type electric power generation system which can achieve high efficiency, lower matrrial cost and high operating temperature Making internal reforming possible. Although the development of the MCEC is progressing rapidly toward commercialization, two important tchological problems such as dissolution of NiO cathode and not corrosion of metallic separator plate must be resolved. Because MCFC is operated at $650^{\circ}C$ and the electrolyte is very corrosive, corrosion-resistance of separator plated against oxidation abd molten carbonate is required. Al-coating on separator material for corrosion-resistance was carried out by painting, thermal spraying. hot dipping and vacuum vapour deposition. The corrosion of Al-coated STS 316S and 316L in molten carbonate at $700^{\circ}C$was studied. Vacuum vapour deposition and thermal spraing for Al-coating on STS 310S and 316L were the most effective methods for protecting thestainless steel corrosion in molten carbonate.

• 대한금속재료학회지
• /
• 제46권5호
• /
• pp.289-295
• /
• 2008

The effect of the alloy elements(Si/Mn) ratio on the coating quality including wettabilty with molten zinc, galvannealing kinetics and crater has been investigated in interstitial-free high strength steel(IFHSS) containing Si and Mn. When the Si/Mn ratio was below 0.75, IF-HSS exhibited a good wettability leading to a good galvannealed coating quality after annealing at $800^{\circ}C$ for 40s in $15%H_2-N_2$ mixed gas with dew point $-60^{\circ}C$. In contrast, the wettability and galvannealed coating quality were deteriorated in the Si/ Mn ratio above 0.75. It is shown that they have relevance to oxides forms by selective oxidation on the steel surface. The oxide particles dispersed on the steel surface with a surface coverage of below 40% resulted in good wettability and galvannealed coating quality. The oxide particle is mainly consisted of $Mn_2SiO_4$ with low contact angle in molten zinc. On the other hand, the continuous oxide layer on the steel surface, such as network- and film-type,caused to poor wettability and galvannealed coating quality. The coverage of oxide layer was above 80%, and its chemical species was $SiO_2$ with high contact angle in molten zinc. Consequently, the Si/Mn alloy ratio played an importance role in galvannealed coating quality of IF-HSS.

• 한국재료학회지
• /
• 제9권2호
• /
• pp.211-216
• /
• 1999

LiCl 및 $LiCl/Li_2O$ 용융염분위기에서 오스테나이트 스테인레스강, SUS 316L과 SUS 304L의 부식특성을 650­~$850^{\circ}C$ 온도범위에서 조사하였다. SUS 316L과 304L의 부식층은 외부 $Li(CrFe)O_2와 내부 Cr_2O_3$의 2층 구조를 형성하였다. LiCl 용융염중에서는 균일한 부식충이 형성되지만, $LiCl/Li_2O$ 혼합용융염중에서는 균일한 부식충 형성외에 업계부식이 발생되는 것을 알 수 있었다. $750^{\circ}C$까지 온도 증가에 따른 부식속도의 증가속도는 느리고, $750^{\circ}C$ 이상에서는 부식속도가 급격히 증가하였다. 용융염분위기에서 SUS 316L은 SUS 304L에 비하여 부식속도가 느려셔 보다 좋은 내식성을 나타내였다.