• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2007년도 춘계학술대회 논문집
• /
• pp.265-266
• /
• 2007

• Design & Manufacturing
• /
• 제18권3호
• /
• pp.22-29
• /
• 2024

Steel is one of the most widely used metals for various industries in the world. Over 95% of steels in the world is manufactured from continuous casting processes. During continuous casting, there are many phenomena including fluid flow, heat transfer, solidification, particle transport, etc. in mold regions. Molten steel continuously flows into the mold through the nozzle, and generates asymmetric flow pattern. The asymmetry of flow behaviors affects the behavior of surface slag/molten steel interface on the top of molten steel pool. These phenomena are influential on the quality of final steel products. This work investigates the asymmetric flow and the top surface behaviors in mold region with a slide-gate nozzle during continuous casting of steel slabs, by applying lab-scale water model experiments.

• 열처리공학회지
• /
• 제25권4호
• /
• pp.196-205
• /
• 2012

The purpose of this study is to enhance the hardenability and the mechanical properties by the addition of alloying elements such as Ni, Cr, Mo and B for the development of Cr-Mo plastic mold steel with uniform hardness and microstructure. The ingots were prepared by vacuum induction melting and forged to ${\Phi}35mm$ round bar. Forged bars were quenched and tempered at $200{\sim}600^{\circ}C$ for 1.5 hour. Jominy test, boron distribution observation, microstructual observation, tensile test and charpy impact test were conducted. It was confirmed that the hardenablity of these steels was improved by increasing of alloying elements and further promoted by the addition of boron. The critical rate of cooling required to obtain the bainitic structure for 0.27C-1.23Cr-0.28Mo-B steel was $0.5^{\circ}C/sec$. Hardness and strength of Cr-Mo steels decreased with increasing tempering temperature, but elongation and reduction of area increased with increasing tempering temperature. However, impact energy tempered at $400^{\circ}C$ showed the lowest value in the range $200{\sim}600^{\circ}C$ due to the temper embrittlement.

• 열처리공학회지
• /
• 제23권4호
• /
• pp.191-197
• /
• 2010

Zr addition is known as effective method to improve the anisotropy of steel due to the elongated MnS inclusions which are observed in hot forged steels. The aim of this research is to investigate the effect of Zr addition on the mechanical properties and manganese sulphide morphology of 0.27%C-Cr-Mo plastic mold steel. The ingots were prepared by vacuum induction melting and forged to ${\Phi}35mm$ round bar. Forged bars were quenched and tempered at $560{\sim}640^{\circ}C$ for 1 hour. Jominy test, microstructual observation, tensile test and Charpy impact test were conducted. The morphology of MnS inclusions was changed by Zr addition. The shape of MnS inclusions was not so much lengthened and controlled not to be elongated by Zr inclusions which surround the MnS inclusions. Tensile strength and yield strength of the tempered steels were not nearly affected by the addition of Zr, but elongation and reduction of area were decreased. Especially, the toughness of Zr added steels was deteriorated with increasing of Zr content. From the results of this study, it is assumed that anisotropy of steels was improved by the addition of Zr. However, impact toughness of the steel was significantly decreased by the excessive Zr addition (over 0.066%).

• 열처리공학회지
• /
• 제21권5호
• /
• pp.265-273
• /
• 2008

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.123-123
• /
• 2015

0.087 wt.% Gd-lean duplex stainless steels were inert arc-melted and cast in a mold. The micro-hardnesses of the rolling, transverse, short transverse directions were 258.5, 292.3, 314.7 HV, respectively. The 33% cold rolled specimen had the crystallographic texture that mainly (100) pole was concentrated to normal direction and (110) pole was concentrated in the center of normal and rolling directions. The corrosion potential and corrosion rate in artificial sea water were in the range of $105.6-221.6mV_{SHE}$, $0.59-1.06mA/cm^2$, respectively. The friction coefficient and wear loss of the 0.087 wt.% Gd-lean duplex stainless steels in artificial sea water were about 67% and 65% lower than in air, whereas, the wear efficiency was 22% higher. The corrosion and wear behaviors of the 0.087 wt.% Gd-lean duplex stainless steels significantly depended on the gadolinium phases.

• 한국재료학회지
• /
• 제13권3호
• /
• pp.137-143
• /
• 2003

The air gap between the metal and mold, formed by shrinkage during solidification, causes surface and subsurface cracks in the continuous casting process. Molten crack on the surface might also occur due to improper heat transfer between them. In order to compensate the air gap in mold design, the thermal contraction is an essential factor. In this study, the thermal contraction and expansion behaviors were examined from the ($\alpha$ and pearlite)/${\gamma}$ to ${\gamma}$/$\delta$ transformations in continuous casting steels by the commercial dilatometer and the self- assembled dilatometer with laser distance measurement. It was found that the thermal contraction and expansion behaviors were very dependant on the phase transformation of the ${\gamma}$/$\delta$ as well as ($\alpha$ and pearlite)/${\gamma}$. The sudden volume change from $\delta$ to ${\gamma}$ which might cause cracks in the continuous casting process, was observed on cooling just below the melting temperature by the self-assembled dilatometer.

• 한국생산제조학회지
• /
• 제18권6호
• /
• pp.629-635
• /
• 2009

In this research, KP-4, one of the plastic mold steels, was coated with the AlTiN from one layer to four layers by the PVD method in the $\Phi$ 8mm cemented carbide ball end mill. Coated KP-4 was processed with various conditions. For example, slope of $15^{\circ}$, $30^{\circ}$ and $45^{\circ}$ the spindle rotation speed was changed from 10,000rpm to 16,000rpm, the tool feeding speed was changed from 1,300mm/min to 1,700mm/min, the depth of cut was also changed from 0.3mm to 0.9mm, and etc. Cutting component force according to the coating layer number, and surface roughness were studied. The cutting component force showed a good agreement better the up ward direction than the down ward direction under all experimental conditions. In case of the condition per the material shape, it was lessen when the tool have larger angle because the average effective diameter of the tool is larger. The surface roughness showed good condition in case of the up ward than the down ward direction. And, in the 3rd layer of AlTiN coating, it showed the most suitable condition.

• 대한금속재료학회지
• /
• 제48권7호
• /
• pp.651-659
• /
• 2010

When high-speed interrupted cutting is carried out for die and mold steels with high hardness, CBN tools manifested a significantly longer wear life than carbide, ceramic, or cermet tools in an experiment of face milling characteristics. In addition, it was also found that they secured a stable surface roughness within a range of 1.6 S~6.3 S, an acceptable range for precision machining for polished machining parts. And it makes them acceptable in the precision machining field, except in industries where very high machining accuracy is required. In the high hardness interrupted cutting, it was advantageous to perform a negaland treatment and a honning treatment on the tools' cutting edge to extend tool life and surface roughness. Also, severe crater development was found on the sloped face in CBN tools following high-speed machining. This caused the cutting edge to be weakened and damaged, and ultimately resulted in a shorter tool life. Finally, as a result of EDX mapping inspection, Cr component was detected evenly on the entire crater wear area, which can be included only in STD 11.

• Design & Manufacturing
• /
• 제16권1호
• /
• pp.9-14
• /
• 2022

A lot of research is being done on metal materials to improve the lifespan of molded parts. As a result, excellent mold materials have been developed that withstand high hardness at high temperatures and frictional heat generated from high-speed cutting. In this study, the press mold life of powder high-speed tool steel and general high-speed tool steel was compared. Powdered high-speed steel is composed of alloying elements such as tungsten, maldividene, cobalt, chromium, and vanadium in steel, which improves wear resistance compared to high-hardness and high-speed tool steels. The mold parts of both steel types were manufactured in the same way from heat treatment to machining, and the powder high-speed tool steel was 66HRC and the high-speed tool steel was 61HRC. As a result of the experiment, it was observed that the number of punching of powder high-speed tool steel was improved by 40-50%, and powder high-speed tool steel had fewer impurities, uniform texture, and excellent surface structure. It has a microscopic structure.