• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.210-215
• /
• 2001

The ferritic 2.25CrMo steel has been used for high temperature structure applications such as turbine rotors, boilers and pressure vessels in fossil plant and petroleum chemical facilities. However, this steel is known to result in aging degradation due to temper embrittlement, carbide induced brittleness and softening of matrix after long time exposure to high temperature. This research investigated the microstructural and mechanical changes after artificial degradation treatment and evaluated the degree of degradation by several nondestructive methods. The decrease of electrical resistivity and increase of magnetic Barkhausen noise(RMS voltage) with increasing aging time were observed. The change of electrical resistivity and Barkhausen noise showed a good correlation with the ductile-brittle transition temperature.

• Korean Journal of Materials Research
• /
• v.3 no.2
• /
• pp.111-120
• /
• 1993

Abstract In this study, the Mo-Hf-O ingots containing 0.31-1.14at % Hf and 0.08-1.00at % 0 were prepared by plasma arc melting. The change of microstructure depending on the condition of heat treatmen~ was analysed by optical microscophy, auger electron microscophy, and transmission electron microscophy. Molybdenum powder with the oxygen content of 830ppm was compacted, and then melted. The oxygen content of molybdenum ingots was detected to be 40 -130ppm. As the contents of Hf and 0 increased, the grain size of ingots decreased. When molybdenum igot containing l.14at % Hf and 1.00at % C was heat treated, p-molybdenum carbide in grains was transformed into ${\alpha}$-molybdenum carbide at 130$0^{\circ}C$. Between 140$0^{\circ}C$ and 150$0^{\circ}C$, the precipitation of hafnium carbide was due to the reaction of solute Hf and C, and the hafnium carbide was saturated at grain boundaries at 150$0^{\circ}C$. When the sample was heat treated from 150$0^{\circ}C$ to 170$0^{\circ}C$, Hafnium oxide more stable thermodynamically precipitated both at grain boundaries and in grains after hafnium carbide had been dissolved at grain boundaries.

• Corrosion Science and Technology
• /
• v.5 no.4
• /
• pp.123-128
• /
• 2006

It was analyzed the causes of boiler tube rupture due to a degradation and corrosion on the boiler tubes in fossil power plant. The experiments were carried out among samples taken from the operating facilities. The result were analyzed based on experimental results from mechanical strength, microstructure observation, and hardness measurement in order to determine the cause of local rupture on boiler tubes. In general, 2.25Cr-1Mo steel generates carbides, it is coarsened, its ductility and strength abruptly decreased as degradation is in progress, In order to confirm this phenomenon, we observed changes of the mount of Cr and Mo of carbide by carrying out EDX chemical composition analysis. The amount of Cr and Mo in the degraded material or service exposed material gradually increased the amount of Mo but initially they were almost maintained at the same amount. Furthermore, we observed that the carbide become coarsened both in the grain and at the grain boundary. Tensile test was carried out to measure a material hardness and to recognize a drop-off of hardness. Overall result for tensile strength and hardness turned out to be lower than new material and mechanical strength and hardness was degraded as the material degradation was in progress.

• Korean Journal of Materials Research
• /
• v.11 no.6
• /
• pp.472-476
• /
• 2001

Type and three-dimensional morphology of carbides precipitated in the X(X= 1.70, 1.92, 2.21, 2.50, 2.86)%C-5%Cr-5%V-5%Mo-5%W-5%Co multi-component white cast iron were investigated using an optical microscope and SEM. The types of carbides precipitated were MC, M$_2$C and M$_{7}$C$_{3}$. Morphology of the MC carbide took three forms, that it petal-like, nodular and coral-like. MC carbide seemed to change its morphology from petal-like through nodular, and finally to coral-like with an increase in carbon content. M7C carbide was classified into lamellar and plate-like type. The lamellar M$_2$C arbide precipitated in the iron with low molybdenum and tungsten contents, and higher contents of both elements in the iron were needed to form the plate-like M$_2$C carbide. The morphology of M$_{7}$C$_{3}$ was rod-like similar to that observed in high chromium white cast iron. However, cobalt does not affect the type and morphology of precipitated carbides.des.

• Korean Journal of Metals and Materials
• /
• v.48 no.7
• /
• pp.589-597
• /
• 2010

In the present study, the effect of variation in alloying elements on the carbide formation behavior during casting and homogenization treatment of M2 high speed steels was investigated. M2 high speed steels of various compositions were produced by vacuum induction melting. Contents of C, Cr, W, Mo, and V were varied from the basic composition of 0.8C, 0.3Si, 0.2Mn, 4.0Cr, 6.0W, 5.0Mo, and 2.0V in weight percent. Homogenization treatment at $1150^{\circ}C$ for 1.5 hr followed by furnace cooling was performed on the ingots. Area fraction and chemical compositions of eutectic carbide in as-cast and homogenized ingots were analyzed. Area fraction of eutectic carbide appeared to be higher in the ingots with higher contents of alloying elements the area fraction of eutectic carbide also appeared to be higher on the surface regions than in the center regions of ingots. As a result of the homogenization treatment, $M_2C$ carbide, which was the primary eutectic carbide in the as-cast ingots, decomposed into thermodynamically stable carbides, MC and $M_6C$. The latter carbide was found to be the main one after homogenization. Fine carbides uniformly distributed in the matrix was found to be MC type carbide and coarsened by homogenization.

• Journal of Integrative Natural Science
• /
• v.13 no.3
• /
• pp.87-91
• /
• 2020

Molybdenum carbide (MoC_x) thin films (TFs) were deposited by reactive radio frequency (rf) magnetron co-sputtering in high vacuum chamber. We compared the properties of MoC_x thin films as the rf power changed on C target. The result of alpha step measurement showed that the thickness of the MoC_x TFs varied from163.3 to 194.86 nm as C power was increased from 160 to 200 W. The crystallinity of MoC_x such as b-Mo₂C, Mo₂C, and diamond like carbon (DLC) structures were observed by XRD. The oxidation states of Mo and C were determined using high resolution XPS spectra of Mo 3d and C 1s were deconvoluted. Molybdenum was consisted of Mo, Mo⁴⁺, and Mo⁶⁺ species. And C was deconvoluted to C-Mo, C, C-O, and C=O species.

• Journal of Welding and Joining
• /
• v.15 no.1
• /
• pp.101-108
• /
• 1997

In repaired weldment of ASTM A-470 class 8 high pressure stream turbine rotor steel, creep rupture life was studied in relation with carbide morphology. Carbides were identified using carbide extraction replica method. A retired rotor has molybdenum rich carbide $M_2C$, lndacochea vanadium rich carbide $M_4C_3$, and chromium rich carbides $M_{23}C_6$and $M_7C_3$. Weldments ruptured at ICHAZ showed that some of carbides have been transformed into spherical types of coarsened carbides at ruptured area. Those carbides were revealed as molybdenum rich $M_6C$ carbide and they provided cavitation sites due to molybdenum depletion around $(M_6C)$ carbide. However coarsened $M_6C$ and $M_{23}C_6$ carbides were observed at ruptured area in case of ruptured at CGHAZ.

• Journal of the Korean Society for Heat Treatment
• /
• v.14 no.6
• /
• pp.323-329
• /
• 2001

Artificial aging was performed to simulate the microstructural degradation in 2.25CrMo steel arising from long time exposure at $540^{\circ}C$. The carbide morphologies were classified as acicular, pipe and globular type, and the number of carbides per unit area was measured for each type of carbides. The fine acicular carbides were found to diminish drastically in the initial stage of aging. An attempt was made to evaluate the microstructural degradation in artificially aging heat treated 2.25CrMo steel by the magnetic property measurements such as saturation magnetization, coercivity and remanence. The saturation magnetization showed no distinct trend with aging time. However, the coercivity and remanence were observed to decrease rapidly in initial 920 hours of aging time and then decrease slowly afterwards.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.627-628
• /
• 2006

The present work is a study on the argon gas pressure effects of Sinter/HIP sintering on microstructure and strength of different grades of TiC-NiMo cermets. Titanium carbide in the composition of different grades of TiC-NiMo cermets was ranged from 40 to 80 wt.% and the ratio of nickel to molybdenum in the initial powder composition was 1:1, 2:1 and 4:1 respectively. On the sintered alloys, the main strength characteristic, transverse rupture strength (TRS) was measured. Furthermore, the microstructure parameters of some alloys were measured and the pressure effect on pore elimination was evaluated. All the results were compared with common, vacuum sintered alloys. The TRS values of TiC-NiMo cermets could be considerably improved by using Sinter/HIP technique, for high-carbide fraction alloys and for alloys sintered at elevated temperatures.

• International Journal of Precision Engineering and Manufacturing
• /
• v.5 no.1
• /
• pp.19-26
• /
• 2004

The growth of solid particles in TiC-XC-2vo1.% and TiC-XC-30vo1.% Ni alloys, (where X=Zr, W or Mo) was fitted to the equation of the form $d^3$-${do}^3$=Kt during the liquid phase sintering at 1,673K. Also, the grain growth behavior decreased markedly with the addition of ${MO}_2$C or WC and increased with the addition of zrC. The contiguity was greater in the alloys with a smaller growth rate constant and especially, decreased by increasing the Ni content in the TiC-${MO}_2$C-Ni alloy. In addition, the effect of the addition of carbide on the grain growth of 2 vo1.% Ni alloys was found to be similar to that of 30vo1.% Ni alloys. Consequently, the grain growth mechanism cannot be explained by the usual solution / reprecipitation process, but can be explained in terms of a new growth velocity equation, which includes the effects of contiguous carbide grain boundaries in restricting the overall grain growth, as well as the area of the solid / liquid interface in the alloy.