• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.4
• /
• pp.264-270
• /
• 2013

$CaMoO_4:Tb^{3+}$ green phosphor powders and thin films were successfully prepared by using the solid-state reaction method and the radio-frequency magnetron sputtering technique, respectively. The crystalline structure of all phosphor powders with different $Tb^{3+}$ ion concentrations was found to be a tetragonal system with the maximum diffraction intensity at $28.58^{\circ}$, while that of the phosphor thin films, irrespective of the type of substrate, was amorphous. As for the phosphor powders, the grain particles showed the chain-like patterns with inhomogeneous size distribution, the excitation spectra were composed of a broad band peaked at 307 nm and two small narrow bands centered at 381 and 492 nm, and the highest green emission spectrum was observed at 0.01 mol of $Tb^{3+}$ ions. As for the phosphor thin films, the average transmittance exceeding 85% was measured in the 400~1,100 nm range and the optical band gap showed a significant dependence on the type of substrate.

• Journal of the Korean Magnetics Society
• /
• v.9 no.4
• /
• pp.203-209
• /
• 1999

Effects of Mo and Si addition in Cr underlayer on magnetic properties of CoCrTa/CrMo and CoCrTa/Si thin films media were investigated. Thin films were prepared with DC magnetron sputtering system. The thickness of CoCrTa magnetic layer and Cr underlayer were fixed at 300 $\AA$ and 700 $\AA$, respectively. The substrate heating temperature was kept constant at 26$0^{\circ}C$ for both magnetic layer and underlayer preparation. The coercivity increase of CoCrTa film was realized due to Mo addition in Cr underlayer. Si addition made a small decrease in coercivity. Coercivity increase seems to be attributed by the improvement of preferred orientation of Cr(200) plane. It is found that lattice fit between Cr(200) and CoCrTa(1120) of CrMo underlayer is better than that of CrSi underlayer. This small misfit may also contribute coercivity increase.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1542-1545
• /
• 2005

Transparent conducting aluminum-doped zinc oxide (AZO) thin films have been deposited on corning 1737 glass by DC magnetron sputter. The structural, electrical and optical properties of the films were investigated as a function of various substrate temperatures. AZO thin films were fabricated by dc magnetron sputtering with AZO ceramic target $(Al_2O_3: 2wt %)$. The obtained films were poly crystalline with a hexagonal wurtzite structure and preferentially oriented in the (002) crystallographic direction. The lowest resistivity is $6.0{\times}10^{-4}$ Ocm with the carrier concentration of $2.694{\times}10^{20}\;cm^{-3}$ and Hall mobility of $20.426cm^2/Vs$. The average transmittance in the visible range was above 90%.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.158-158
• /
• 2011

$Cu(In_xGa_{1-x})Se_2$ (CIGS) thin film solar cell is one of the most promising solar cells in photovoltaic devices. CIGS has a direct band gap which varied from 1.0 to 1.26 eV, depending on the Ga to In ratio. Also, CIGS has been studying for an absorber in thin film solar cells due to their highest absorption coefficient which is $1{\times}10^5cm^{-1}$ and good stability for deposition process at high temperature of $450{\sim}590^{\circ}C$. Currently, the highest efficiency of CIGS thin film solar cell is approximately 20.3%, which is closely approaching to the efficiency of poly-silicon solar cell. The deposition technique is one of the most important points in preparing CIGS thin film solar cells. Among the various deposition techniques, the sputtering is known to be very effective and feasible process for mass production. In this study, CIGS thin films have been prepared by rf magnetron sputtering method using a single target. The optical and structural properties of CIGS films are generally dependent on deposition parameters. Therefore, we will explore the influence of deposition power on the properties of CIGS films and the films will be deposited by rf magnetron sputtering using CIGS single target on Mo coated soda lime glass at $500^{\circ}C$. The thickness of CIGS films will be measured by Tencor-P1 profiler. The optical properties will be measured by UV-visible spectroscopy. The crystal structure will be analyzed using X-ray diffraction (XRD). Finally the optimal deposition conditions for CIGS thin films will be developed.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.433-439
• /
• 1999

In this study, the diffusion barrier properties of $1000\AA$ thick molybdenum compounds (Mox=1-5 Si) were investigated using sheet resistance measurements, X-ray diffractometry (XRD), and Rutherford back scattering spectrometry (RBS). Each barrier material was deposited by the de and rf magnetron co-sputtering of Mo and Si, respectively, and annealed at $500-700^{\circ}C$ for 30 min in vacuum. Each barrier material was failed at low temperatures due to Cu diffusion through grain boundaries and defects of barrier thin films or through the reaction of Cu with Si within Mo-barrier thin films. It was found that Mo rich thin films were less effective than Si rich films to Cu penetration activating Cu reaction with the substrate at a temperature higher than $500^{\circ}C$.

• Journal of Integrative Natural Science
• /
• v.13 no.3
• /
• pp.87-91
• /
• 2020

Molybdenum carbide (MoC_x) thin films (TFs) were deposited by reactive radio frequency (rf) magnetron co-sputtering in high vacuum chamber. We compared the properties of MoC_x thin films as the rf power changed on C target. The result of alpha step measurement showed that the thickness of the MoC_x TFs varied from163.3 to 194.86 nm as C power was increased from 160 to 200 W. The crystallinity of MoC_x such as b-Mo₂C, Mo₂C, and diamond like carbon (DLC) structures were observed by XRD. The oxidation states of Mo and C were determined using high resolution XPS spectra of Mo 3d and C 1s were deconvoluted. Molybdenum was consisted of Mo, Mo⁴⁺, and Mo⁶⁺ species. And C was deconvoluted to C-Mo, C, C-O, and C=O species.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.176-176
• /
• 2010

전자기술이 발전함에 따라 전자부품 소자는 소형화, 다기능화, 고집적화, 대용량화 되고 있다. 그에 따른 부품들의 고밀도화는 높은 열을 발생시켜 각종 전자부품을 기판으로부터 단락 시키거나 기능을 상실하게 하는 문제점이 발생된다. 이와 같은 문제점을 해결하기 위해서는 발생된 열을 가능한 빠르게 방열 시켜주는 것이 대단히 중요하고 높은 방열 특성을 가지는 금속 PCB기판의 중요성이 높아지고 있다. 하지만 금속을 PCB에 적용하기 위해서는 금속기판과 회로전극사이에 절연층이 반드시 필요하다. 본 실험에서는 RF-Magnetron Sputtering 방법을 이용하여 AlN(질화알루미늄)을 절연물질로 사용, Aluminum기판위에 후막을 제작하여 열적 전기적 구조적 특성을 분석 하였다. 스퍼터링시 아르곤과 질소 분압비에 따른 특성과 후막의 두께에 따른 열적, 전기적, 구조적 특성을 측정 분석하였고, 후열처리를 통하여 AlN 후막의 특성 측정 결과 $200^{\circ}C$로 후열처리 했을 경우 절연파괴전압이 후열처리 전 0.56kV보다 1.125kV로 높아지고 SEM 이미지 상의 AlN 입자 밀도가 더욱 조밀해지는 것으로 확인 하였다. 결론적으로 AlN를 RF-Magnetron Sputtering 방법으로 증착 금속 PCB의 절연물질로 적용하기 위해서는 적정한 가스분압비와 후열처리가 필요하며 이를 통하여 금속 PCB의 절연층으로 응용 가능성이 높을 것으로 사료된다. 본 연구는 한국 산업기술 진흥원의 사업화 연계 연구개발(R&BD)사업의 연구비 지원에 의한 것입니다.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.6
• /
• pp.269-276
• /
• 2011

Phase evolution and tribological behavior of Cr-Mo-N multi compositional films with different interlayer were investigated. The films were deposited by hybrid PVD (Physical Vapor Deposition) system consisted of dc unbalanced magnetron (UBM) sputtering and arc ion plating (AIP) sources. A pure molybdenum (Mo) was used as sputtering target and also a pure Cr was used as AIP target to form the Cr-Mo-N films. Various growth planes were found, no textured surface, in all of the multi composition films. Maximum value of microhardness was measured in Cr-Mo-N film with Mo interlayer as 29 GPa. Composition film was mainly showed the aspect of the adhesive wear than CrN film. The friction coefficient was decreased from 0.6 for pure CrN coating to 0.35 for Cr-Mo-N film with Mo interlayer. This result may come from the formation of metal oxide tribo-layer which is known as solid lubricant during the wear test.

• Current Photovoltaic Research
• /
• v.4 no.1
• /
• pp.25-29
• /
• 2016

$Eu^{3+}$-activated $MgMoO_4$ phosphor thin films were grown at $400^{\circ}C$ on quartz substrates by radio-frequency magnetron sputter deposition from a 15 mol% Eu-doped $MgMoO_4$ target. After the deposition, the phosphor thin films were annealed at several temperatures for 30 min in air. The influence of thermal annealing temperature on the structural and optical properties of $MgMoO_4:Eu^{3+}$ phosphor thin films was investigated by using X-ray diffraction (XRD), photoluminescence (PL), and ultraviolet-visible spectrophotometry. The transmittance, optical band gap, and intensities of the luminescence and excitation spectra of the thin films were found to depend on the thermal annealing temperature. The XRD patterns indicated that all the thin films had a monoclinic structure with a main (220) diffraction peak. The highest average transmittance of 91.3% in the wavelength range of 320~1100 nm was obtained for the phosphor thin film annealed at $800^{\circ}C$. At this annealing temperature the optical band gap energy was estimated as 4.83 eV. The emission and excitation spectra exhibited that the $MgMoO_4:Eu^{3+}$ phosphor thin films could be effectively excited by near ultraviolet (281 nm) light, and emitted the dominant 614 nm red light. The results show that increasing RTA temperature can enhance $Eu^{3+}$ emission and excitation intensity.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1546-1549
• /
• 2005

Al-doped ZnO (ZnO:Al) thin films were grown on corning 1737 glass substrates by dc magnetron sputtering. The structural, electrical and optical properties of the films were investigated as a function of various discharge power. The obtained films were polycrystalline with a hexagonal wurtzite structure and preferentially oriented in the (002) crystallographic direction. The lowest resistivity is $6.0{\times}10^{-4}$ Ocm with the carrier concentration of $2.694{\times}10^{20}$ $cm^{-3}$ and Hall mobility of $20.426cm^2/Vs$. The average transmittance in the visible range was above 90%.