• Journal of the Korean Magnetics Society
• /
• v.17 no.2
• /
• pp.81-85
• /
• 2007

MnTe layers of high crystalline quality were successfully grown on Si(100) : B and Si(111) substrates by molecular beam epitaxy (MBE). Under tellurium-rich condition and the substrate temperature around $400^{\circ}C$, a layer thickness of $700{\AA}$ could be easily obtained with the growth rate of $1.1 {\AA}/s$. We investigated the structural, magnetic and transport properties of MnTe layers by using x-ray diffraction (XRD), superconducting quantum interference device (SQUID) magnetometry, and physical properties measurement system (PPMS). Characterization of MnTe layers on Si(100) : B and Si(111) substrates by XRD revealed a hexagonal structure of polycrystals with lattice parameters, ${\alpha}=4.143{\pm}0.001{\AA}\;and\;c=6.707{\pm}0.001{\AA}$. Investigation of magnetic and transport properties of MnTe films showed anomalies unlike antiferromagnetic powder MnTe. The temperature dependence of the magnetization data taken in zero-field-tooling (ZFC) and field-cooling (FC) conditions indicates three magnetic transitions at around 21, 49, and 210 K as well as the great irreversibility between ZFC and FC magnetization in the films. These anomalies are attributable to a magnetic-elastic coupling in the films. Magnetization measurements indicate ferromagnetic behaviour with hysteresis loops at 5 and 300 K for MnTe polycrystalline film. The coercivity ($H_c$) values at 5 and 300 K are 55 and 44 Oe, respectively. In electro-transport measurements, the temperature dependence of resistivity revealed a noticeable semiconducting behaviours and showed conduction via Mott variable range hopping at low temperatures.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.1
• /
• pp.126-131
• /
• 1999

$Cd_{1-x}Mn_xTe$ thin films were grown on GaTs (100) substrates by hot-wall epitaxy method. From the XRD measurements, it was found that CdTe/GaAs (100)film was grown as a single crystal with the same growth plane of (100) and $Cd_{1-x}Mn_xTe$film as a poly crystal as Mn content was increased, and the lattice constant was decressed with the similar gradient of bulk crystal as x was increased. From the PL measurements, $L_1$line due to the exciton trapped on an acceptor and $L_2$line due to an exciton trapped on a shallow potential fluctuation were observed, and $L_1$line was observed only in $Cd_{0.91}Mn_{0.09}$te but it was disappeared probably due to a stronger lacalization of excitons with increasing alloy fluctuation.$L_2$line was dominant in case of $x{\ge}0.2$and for higher Mn contents the broad transition about 2.0eV associated to the 3d levels of the $Mn^{2+}$ ion dominated the PL spectrum, and the $L_2$ transition become weaker and weaker. For$x{\ge}0.4$, the transition line about 2.0eV due to $Mn^{2+}$ion showed no shift.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.53.2-53.2
• /
• 2008

• Proceedings of the Korean Magnestics Society Conference
• /
• 2007.05a
• /
• pp.50.1-50.1
• /
• 2007