• Journal of the Korean Ceramic Society
• /
• v.36 no.10
• /
• pp.1108-1114
• /
• 1999

Microstructure and electrical properties of ZnO-doped (0-5 mol%) 0.05 Pb(Mn1/3Sb2/3)O3-0.95 PZT ceramics were investigated. Sintering temperature was decreased to 100$0^{\circ}C$ due to eutetic reaction between PbO and ZnO. Grain-size increased up to adding 1mol% ZnO and then decreased. Compositions of grain and grain-boundary were investigated by WDS. Lattice parameter was decreased with ZnO addition. Density increased with ZnO addition and reached to the maximum of 7.84(g/cm2) at 2 mol% ZnO. The effect of ZnO on electrical properties of PMS-PZT was investigated. At 3mol% ZnO addition electromechanical coupling factor(kp) was about 50% and relative dielectric constant($\varepsilon$33/$\varepsilon$0) was 997 Mechanical quality factor(Qm) decreased with ZnO addition. Lattice parameters and tetragonality(c/a) were measured to investigate relationship between the electric properties and substitution of Zn2+. At 3 mol% ZnO tetragonality was maximiged at c/a=1.0035 Curie temperature (Tc) decreased slightly with ZnO addition.

• Journal of the Korean Ceramic Society
• /
• v.39 no.10
• /
• pp.903-906
• /
• 2002

Nanosized $Mn_xFe_2O_4$ powders were prepared in ethylene glycol solution under mild temperature and pressure conditions by precipitation from metal nitrates with aqueous potassium hydroxide. The average size and distribution of the synthesized $Mn_xFe_2O_4$ powders was about 20 nm and broad, respectively. The phase of synthesized particles was crystalline reacted at 200${\circ}C$ for 6h. The magnetic properties of the synthesized $Mn_xFe_2O_4$ powders were about 35-60 (emu/g) with superparamagnetic character.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.271-278
• /
• 2006

Green light emitting $Zn_2SiO_4$Mn and Al co-doped $Zn_2SiO_4$:Mn phosphor were synthesized by a sol-gel method combined with a furnace firing. The luminescent properties of the sample have been investigated. We have found that the phosphor powder with uniform shape show the maximum luminescent intensity when it is prepared with sol-gel method and fired at relatively high temperature ($1100{\sim}1300^{\circ}C$).

• Korean Journal of Crystallography
• /
• v.15 no.1
• /
• pp.44-50
• /
• 2004

Spinel structured lithium managanese oxide $(LiMn_2O_4)$ powder with well defined facetted morphology was prepared by precipitation-evaporation method. {111}, {110}, and {100} planes are mainly observed in the $LiMn_2O_4$ powder. And powder shape of tetradecahedron and octahedron was observed depending on the calcinations temperature. The observed powder morphology observed seemed to be related to the nonstoichiometry of the oxygen in the $LiMn_2O_4$ spinel structure. Oxygen nonstoichiometry might be responsible for the Jahn-teller effect and structure transition which in turn affects the surface energy of the {111}, {110}, and {100} planes. Powder shape transition from tetradecahedron to octahedron seemed to be related to the surface energy of the {111}, {110}, and {100} planes with oxygen nonstoichiometry.

• Journal of the Korean Ceramic Society
• /
• v.37 no.6
• /
• pp.564-568
• /
• 2000

Spinel LiMn2O4 catalyst with submicron and single phase particles was synthesized at 48$0^{\circ}C$ for 12 hr in air by a sol-gel method. The spinel LiMn2O4 was deoxidized by hydrogen at various temperatures. Effects of physiochemical properties of the catalyst reduced by hydrogen were examined with X-ray diffractometer, thermogravimetric analysis and scanning electron microscope. The decomposition rate of carbon dioxide was measrued using the catalyst deosidized at 35$0^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.196-199
• /
• 2000

Since the reports of CMR(colossal magnetoresistance) effects in some single crystal R-P phase $La_{1+x}Sr_{2-x}Mn_2O_7$, considerable researches have been carried out to find optimum composition and to understand the role of dimensionality in the CMR mechanism of this system. In this study, layered perovskite $Ln_xCa_{1-x}MnO_{4}$ (x=0.5, Ln=Pr, Nd, Sm, Gd) phases were synthesized by solid state reaction and their structures were refined by Rietveld method. Electrical and magnetic properties were measured between room temperature and liquid helium temperature and compared with those of two dimensional $La_{1.4}Sr_{1.6}Mn_2O_7$ phase.

• Transactions on Electrical and Electronic Materials
• /
• v.8 no.3
• /
• pp.121-124
• /
• 2007

The $Zn_2SiO_4:Mn$ phosphors were prepared using polymer matrix technique in order to improve the performance of green emitting phosphors for plasma display panel(PDP). $Zn_2SiO_4:Mn$ phosphor exhibits a strong green emission around 520-530 nm. The emission intensity and particle size of powders were controlled by sintering temperature and raw material composition. The zinc silicate $Zn_2SiO_4:Mn$ single phase were obtained at lower temperature than prepared by solid-state reaction method. PL luminance of $Zn_2SiO_4:Mn$ phosphor was similar to the commercial material.

• Proceedings of the KIPE Conference
• /
• 1998.10a
• /
• pp.934-937
• /
• 1998

Charge/discharge property of LiMn2O4 was investigated with LiMn2O4/Li cell for use of lithium ion battery in electric vehicle. LiMn2O4 calcined at $800^{\circ}C$ for 36hr show high charge/discharge capacity and excellent cycle stability than that of others. This is found to be in agreement with expectation in the X-ray diffraction analysis. In addition, the kind and volume of conductive agent involved in LiMn2O4 cathode is excellent at super-s-black and 20wt%, respectively.

• Journal of Surface Science and Engineering
• /
• v.30 no.1
• /
• pp.57-62
• /
• 1997

Green-emitting $ZnGa_2O_4$ : Mn phosphors were synthesized by a thermal method and their low-voltage cathodoluminescent characteristics were examined for the field emitter display (FED) application. Low efficiency of $ZnGa_2O_4$ : Mn phosphors could be ascribed to the low penetration depth of into phosphors, which might results in charge accumulation on the phosphors screen. For increasing cathodoluminescent of $ZnGa_2O_4$ : Mn under low voltage excitation, wide band-gap oxide materials were added to the $ZnGa_2O_4$: Mn powder. It is found that the luminance can be increased by 20%. Measurement of leakage current on the phosphor screen shows that the enhancement of low-voltage cathodoluminescent by additive materials is mainly due to the consumption of surface charges on the phosphor.

• Proceedings of the KIEE Conference
• /
• 2006.10a
• /
• pp.83-84
• /
• 2006

Chemical mechanical polishing (CMP) process has been attracted as an essential technology of multi-level interconnection. However, the COO (cost of ownership) is very high, because of high consumable cost. Especially, among the consumables, slurry dominates more than 40 %. So, we focused how to reduce the consumption of raw slurry. In this paper, $MnO_2$ abrasives were added de-ionized water (DIW) and pH control as a function of KOH contents. Also, the addition effects of $MnO_2$ abrasives and the diluted silica slurry (DSS) on CMP performances were evaluated. Finally, we have investigated the possibility of new abrasive for the oxide CMP application.