• Journal of the Korean Ceramic Society
• /
• v.32 no.7
• /
• pp.769-776
• /
• 1995

Infrared radiators of a cordierite system [cordierite (2MgO.2Al2O3.5SiO2)＋30wt% clay＋X wt% MnO2 (X=0, 0.1, 0.25, 0.5, 1.0, 1.5, 2.0, 2.5)] were manufactured by a slurry casting method. Thermal and physical properties of these infrared radiators were studied by the measurement of spectra emissivity, thermal expansion coefficient and apparent density, SEM and EPMA analyses were also carried out. The thermal expansion coefficient and apparent density were decreased with increasing amouonts of MnO2 additives. On the other hand, the spectral emissivity was increased in the wavelength below 4.5${\mu}{\textrm}{m}$. Also, infrared radiators of the cordierite system, of which the spectral emisivity was 0.8, could be attainable in the wavelength above 4.5${\mu}{\textrm}{m}$. The infrared radiator of the cordierite system with 2.0wt% MnO2, of which the spectral emissivity was approximately 1.0, could be attainable in the wavelength between 4.5${\mu}{\textrm}{m}$ and 8${\mu}{\textrm}{m}$. The spectral emissivity of the specimen containing 2.0wt% MnO2 was higher than others in the wavelength between 8${\mu}{\textrm}{m}$ and 14${\mu}{\textrm}{m}$.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.41 no.5
• /
• pp.508-516
• /
• 1992

In this study, dielectric and piezoelectric properties of 0.05Pb(AlS12/3TWS11/3T)OS13T-0.95Pb(ZrS10.52TTiS10.48T)OS13T system ceramics were investigated with respect to the variations of MnOS12T and FeS12TOS13T additions amounts. The results obtained in this study are summarized as follows: 1. As the amounts of MnOS12T and FeS12TOS13T are increased, tetragonality(c/a) and apparent density were decreased but grain size was increased, also the limits of solubility were revealed because pores were formed at the amounts of 0.3wt% MnOS12T and 0.5wt% FeS12TOS13T. 2. AS the increasing of amounts of MnOS12T and FeS12TOS13T, the temperature of phase transition(TS1cT) was decreased, and pemeability had maximum value at the amount of 0.3wt% MnOS12T but were sharply decreasd for the increasing FeS12TOS13T amounts. 3. As the amounts of MnOS12T and FeS12TOS13T are increased, the electro-mechanical coupling factor(kS1pT) was decreased from 60% to 41%, 19% respectively, but mechanical quality factor(QS1mT) had maximum values 720 for amount of 0.3wt% MnOS12T and 320 the amount of 0.5wt% FeS12TOS13T.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.257-264
• /
• 1997

The aim of this study was to investigate the degradation of piezoelectric properties with compressive cy-clic loading, the change in bending strength before and after poling treatment and fracture strength in MPB depending on the amount of MnO2 addition. The MPB with 0.25 wt.% MnO2 showed the best resistance against the piezoelectric degradation with compressive cyclic loading. Bending strength increased when pol-ing and loading directions are parallel, however decreased when poling and loading directions are per-pendicular each other. Because, during poling treatment, compressive residual stress is generated in the pol-ing direction but tensile residual stress in the perpendicular direction to poling direction.

• Journal of the Korean Ceramic Society
• /
• v.40 no.7
• /
• pp.637-643
• /
• 2003

In order to improve the photoluminescent properties and crystallinity, Zn$_2$SiO$_4$:Mn, M(M=Cr, Ti) phosphors were synthesized by the sol-gel method. The willemite single phase was obtained at 110$0^{\circ}C$, which is lower temperature than that of the conventional solid-state reaction (130$0^{\circ}C$). The characteristics of fired samples were obtained by a 147 nm excitation source under VUV (Vacuum Ultraviolet). To investigation the effect of co-dopant, the content of Mn and the ratio of $H_2O$ to TEOS was fixed as 2 ㏖% and 36. 1, respectively. The highest emission intensity was obtained when the concentration of Cr and Ti was 0.1 ㏖% relative to Zn$_2$SiO$_4$:Mn. While the emission intensity decrease continuously the decay time improved as increased the Cr concentration. In the case of Ti added samples, however, the emission intensity increase up to 2 ㏖％ concentration.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.4
• /
• pp.316-322
• /
• 2001

Cathode materials $LiMn_{2-y}$$M_{y}$ $O_4$(M=Zn and Mg) were obtained by reacting the mixture of LiOH.$H_2O$, Mn $O_2$ and MgO ar ZnO at 80$0^{\circ}C$ for 36h in an air atmosphere. These materials showed an extended cycle life in lithium-anode cells working at room temperatue in a 3.0 to 4.3V potential window. Among these materials, LiM $n_{1.9}$M $g_{0.1}$ $O_4$ showed the best cycle performance in terms of the capacity and cycle life. The discharge capacities of the cathode for the Li/LiM $n_{1.9}$ $M_{0.1}$ $O_4$ cell at the 1st cycle and at the 70th cycle were about 120 and 105mAh/g, respectively. This cell capacity is retained by 88% after 70th cycle. In cyclic voltammetry measurement, all cells revealed tow oxidation peaks and reduction peaks. However, Li/$LiMn_{2-y}$$M_{y}$ $O_4$ cell substituted with Zn and Mg showed new reaction peak during reduction reaction.eaction.ion.ion.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.8
• /
• pp.663-669
• /
• 2001

Spinel LiM $n_2$ $O_4$ and LiM $n_{1.9}$M $g_{0.1}$ $O_4$ power was synthesized with solid-state method by calcining the mixture of LiOH.$H_2O$, Mn $O_2$ and MgO at 80$0^{\circ}C$ for 36 h in an air atmosphere. To investigate the effect of temperature on he cycle performance of cathode material during cycling, charge-discharge experiments and ac impedance measurement were performed. Initial discharge capacity was gradually increased with the increase of charge-discharge temperature. Discharge capacity at high temperature was suddenly decreased during cycling. On the other hand, discharge capacity at low temperature was almost constant during cycling. It confirmed that Mn dissolution is serious at high temperature than at low temperature. LiM $n_2$ $O_4$ and LiM $n_{1.9}$M $g_{0.1}$ $O_4$ showed the best capacity and stability at room temperature.ure.ure.

• Journal of the Korean Magnetics Society
• /
• v.19 no.2
• /
• pp.57-61
• /
• 2009

$MnFe_2O_4$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by XRD, SEM, and $M{\ddot{o}}ssbauer$ spectroscopy, VSM. $MnFe_2O_4$ powder that was annealed at $250^{\circ}C$ has spinel structure and behaved superparamagnetically at room temperature. $MnFe_2O_4$ annealed at 400 and $500^{\circ}C$ has a typical spinel structure and is ferrimagnetic in nature. The estimated size of superparammagnetic $MnFe_2O_4$ nanoparticle is around 17 nm. The hyperfine fields of the A and B patterns at 4.2 K were found to be 508 and 475 kOe, respectively. The blocking temperature ($T_B$) of superparammagnetic $MnFe_2O_4$ nanoparticle is about 120 K. The magnetic anisotropy constant and relaxation time constant of $MnFe_2O_4$ nanoparticle were calculated to be $4.9{\times}10^5erg/cm^3$.

• Electrical & Electronic Materials
• /
• v.1 no.4
• /
• pp.311-318
• /
• 1988

초음파센서(수신기)에 응용가능한 압전세라믹스를 제조하기 위하여 Ba변조된 Pb(ZR, Ti)O$_{3}$계 세라믹스에 MnO$_{2}$를 첨가하여 첨가량과 소성온도에 따른 영향을 조사하였다. 또한 제조된 압전세라믹스를 이용하여 초음파 수신기를 제작하여 수신특성을 확인하여 보았다. 그 겨로가 MnO$_{2}$가 0.4(wt%)첨가되었을 때 압전 g정수가 가장 크고 수신감도가 우수한 것으로 밝혀졌다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.4
• /
• pp.154-158
• /
• 2021

The optical transmittance of Mn-doped SnO₂ monolayer film increased gradually from 80.9 to 85.4 % at 550 nm wavelengths upon increasing the O₂/Ar+O₂ concentration rate from 0 to 7.9 % and the band gap energy changed from 3.0 to 3.6 eV. The resistivity tended to decrease from 3.21 Ω·cm to 0.03 Ω·cm, reaching a minimum at 2.7 %, and then gradually increased from 0.03 to 52.0 Ω·cm at higher O₂/Ar+O₂ gas concentration ratio. Based on XPS spectra analysis, the Sn 3d_5/2 peak of Mn-doped SnO₂ single layer shifted slightly from 486.40 to 486.58 and O_1s peak also shifted from 530.20 to 530.33 eV with increase the O₂/Ar+O₂ concentration ratio. Therefore, the XPS spectra results indicate that a multiphase with SnO and SnO₂ coexisted in the sputtered Mn-doped SnO₂ monolayer film.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2006.05a
• /
• pp.898-901
• /
• 2006

In this paper, effect of ceramic processing was investigated on the magnetic properties of low loss Mn-Zn ferrite. High frequency characteristics, high saturated magnetic flux density and high magnetic permeability and low magnetism loss are required for the development of Mn-Zn ferrite, which is parts in the communication. therefore, in order to improve Mn-Zn ferrite with a high frequency , it is important to have a minimal change of particles and to control the eddy current loss caused by high resistance of the stratum of particles and to reduce the hysteresis loss by uniform change of detailed structure. In this paper, we added $V_2O_5\;and\;CaCo_3$ to Mn-Zn Ferrite to achieve a high efficiency, low loss core material. The compositions are MnO : ZnO : $Fe_2O_3$ = 21 : 10 : 69 mol%. They were sintered at $1250^{\circ}C$ for Three hours. Initial permeability was measured at 0.1MHz. At 50mT, Power loss was measured by temperature changing at 100kHz.