• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.4
• /
• pp.154-159
• /
• 2001

(Li,Al)$MnO_2(OH)_2$:Co compound was synthesized by hydrothermal method. $MnO_2$, LiOH.$H_2$O, $Co_3O_4$ and $Al(OH)_3$ were used as starting materials and the optimum conditions for synthesis of monolithic (Li,Al)$MnO_2(OH)_2$:Co compound were as follows : reaction temperature; $200^{\circ}C$, reaction time; 3 days, hydrothermal solvent; 3M-KOH solution, reaction apparatus; seesaw type, atomic ratio of Li:Al:Mn;Co = 1:2.1:2.5~2:0.5~1. Monolithic(Li,Al)$MnO_2(HO)_2$:Co compound synthesized in this work had a god crystallinity and excellent color forming effect as a blue pigment compatible with natural mineral. The particles of the synthesized (Li,Al)$MnO_2(OH)_2$:Co compound have hexagonal plate shape with the size of 0.5~1 $\mu\textrm{m}$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.4
• /
• pp.172-179
• /
• 2006

When $Al_2O_3-MoO_3$ mixture is reduced, $MoO_3$ is only reduced to Mo at $900^{\circ}C$. But a compound between $Al_2O_3$ and Mo is not formed up to $1300^{\circ}C$. In the case of $Al_2O_3-MoO_3-MnO_2$ mixture, an intermediate compound $Mn_2Mo_3O_8$ is firstly formed at $900^{\circ}C$ and changes to $MnAl_2O_4$ at $1100^{\circ}C{\sim}1300^{\circ}C$. $Al_2O_3/Mo/MnO_2$ composite are manufactured by a selective reduction process in which Mo is only reduced in the powder mixture of $Al_2O_3,\;MoO_3\;and\;MnO_2$ oxide. For $Al_2O_3/Mo$ composite, the average grain size was not changed with increasing Mo content because of inhibition of grain growth of $Al_2O_3$ matrix in the presence of Mo particles. Fracture strength increased with increasing Mo content due to phenomenon of grain growth inhibition of $Al_2O_3$ matrix. Hardness decreased because of a lower hardness value of Mo, whereas fracture toughness increased. For $Al_2O_3,\;Mo\;and\;MnO_2$ composite, grain growth was facilitated by MnOB and it showed a lower fracture strength because of grain growth effect with increasing Mo and $MnO_2$ content. Hardness decreased because of the grain growth of matrix and coalesced Mo particles to be located in grain boundary, whereas fracture toughness increased.

• Korean Chemical Engineering Research
• /
• v.56 no.3
• /
• pp.349-355
• /
• 2018

$BaMnAl_{11}O_{19}$ was prepared by urea-induced homogeneous precipitation and characterized by X-ray diffraction and scanning electron microscopy. At increased precipitant concentrations, AlOOH replaced $Al(OH)_3$ as an Al precursor. $BaMnAl_{11}O_{19}$ exhibited enhanced catalytic combustion performance and inhibited CO generation. Catalytic performance was also enhanced by the presence of $BaAl_2O_4$ and $BaMnAl_{11}O_{19}$. Compared to $BaAl_2O_4$, $BaMnAl_{11}O_{19}$ exhibited superior catalytic combustion activity.

• Applied Chemistry for Engineering
• /
• v.35 no.1
• /
• pp.1-7
• /
• 2024

Mn-M/Al₂O₃ (M = Cu, Fe, Co, and Ce) catalysts were prepared for simultaneous oxidation of NO, CO, and CH₄, and their oxidation activities were compared. The Mn-Cu/ Al₂O₃ catalyst with the best simultaneous oxidation activity was characterized by XRD, Raman, XPS, and O₂-TPD analysis. The result of XRD indicated that Mn and Cu existed as complex oxides in the Mn-Cu/Al₂O₃ catalyst. Raman and XPS results showed that electron transfer between Mn ions and Cu ions occurred during the formation of the Mn-O-Cu bond in the Mn-Cu/Al₂O₃ catalyst. The XPS O 1s and O₂-TPD analyses showed that the Mn-Cu/Al₂O₃ catalyst has more adsorbed oxygen species with high mobility than the Mn/Al₂O₃ catalyst. The high simultaneous oxidation activity of the Mn-Cu/Al₂O₃ catalyst is attributed to these results. Gas-phase NO promotes the oxidation reactions of CO and CH₄ in the Mn-Cu/Al₂O₃ catalyst while suppressing the NO oxidation reaction. These results were presumed to be because the oxidized NO was used as an oxidizing agent for CO and CH₄. On the other hand, the oxidation reactions of CO and CH₄ competed on the Mn-Cu/Al₂O₃ catalyst, but the effect was not noticeable because the catalyst activation temperature was different.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.4
• /
• pp.156-159
• /
• 2007

The red emission properties of $Mn^{4+}$ doped $SrAl_{12}O_{19}$ prepared by the solid-state reaction was investigated, in order to verify its potential to act as the red emitting phosphor of white LEDs. The emission spectrum exhibits a narrow band between $600{\sim}700 nm $ with four sharp peaks occurring at about 643, 656, 666, 671 nm due to the $^2E\to^4A_2$ transition of $Mn^{4+}$. The excitation spectrum exhibits a broad band between $200{\sim}500 nm$ with three peaks occurring at about 338, 398 and 468 nm, respectively. Moreover, the relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ with or without $CaF_2$ and MgO fluxes measured at excitation source 390 nm. The relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ containing 0.67mol% MgO was approximately 30% higher than that of the base composition sample. Strontium hexa-aluminate measured at room temperature as a function of the substituted Mg concentration. MgO was added to replace part of the $Al_2O_3$. Also, the relative emission intensity of $SrAl_{12}O_{19}:Mn^{4+}$ containing 0.67 mol% MgO and 0.67 mol% $CaF_2$ was approximately about 48% higher than that of the base composition $SrAl_{12}O_{19}:Mn^{4+}$.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.2
• /
• pp.401-410
• /
• 2016

The $Pt-Sn/Al_2O_3$ catalysts mixed with metal oxides for propane dehydrogenation were studied. $Cu-Mn/{\gamma}-Al_2O_3$, $Ni-Mn/{\gamma}-Al_2O_3$, $Cu/{\alpha}-Al_2O_3$ was prepared and mixed with $Pt-Sn/Al_2O_3$ to measure the activity for propane dehydrogenation. As standard sample, $Pt-Sn/Al_2O_3$ catalyst mixed with glassbead was adopted. In the case of catalytic activity test after non-reductive pretreatment of catalyst and metal oxide, $Pt-Sn/Al_2O_3$ mixed with $Cu-Mn/{\gamma}-Al_2O_3$ showed higher conversion of 15% and similar selectivity at $576.5^{\circ}C$, compared to conversion of 8% in standard sample. In the case of catalytic activity test after reductive pretreatment of catalyst and metal oxde, $Cu/{\alpha}-Al_2O_3$ showed higer yield than standard sample. But, increase of yield of most of samples after reductive pretreatment was not significant, so it was found that lattice oxygen of $Cu-Mn/{\gamma}-Al_2O_3$ is effective to propane dehydrogenation.

• Korean Journal of Plant Resources
• /
• v.20 no.1
• /
• pp.12-21
• /
• 2007

Ginsengs (1,2 3 years) from the Keumsan are analysed for the inorganic compounds and compared with the their soils from the granite, phyllite and shale areas. In the soils, the granite areas show high $Al_2O_3\;and\;Na_2O$ contents while the phyllite areas have high $Fe_2O_3,\;MnO\;and\;MgO$ contents. Positive correlations are shown in the $Al_2O_3-K_2O\;and\;Fe_2O_3-MgO$ pairs while negative correlations are shown in the $SiO_2-CaO$ pair. In the ginsengs, the shale areas are high in the most of the elements, but low in the granite areas. Compared with same soils of different ages, Al, Na and Ti contents of the ginsengs are high in the all areas. The shale areas are mainly high in the upper parts while the granite areas are mainly high in the root parts. Regardless of the localities, Fe, Mn and Ca contents are high in the upper parts while Ti contents are high in the root parts with differences of several times. Relative ratios between field soils and ginsengs (field soil/ginseng) suggest that the ginsengs show high Ca contents with differences of several ten times whereas the soils have high Na, Fe, Ti and Al contents with differences of several times. Regardless of the localities, the ratios of the Al, Mn and Na are high in the 2 year relative to the 3 year. Overall ratios between field soils and ginsengs are mainly big in the 2 year area relative to the 3 year area. It suggests that contents of the 3 year ginsengs are more similar to those of their soils relative to the 2 year and the ginsengs may absorpt eligible element contents with increasing ages.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.9
• /
• pp.539-545
• /
• 2016

Alumina added with Mn3O4 up to 7.5 cat% of Mn was prepared by conventional ceramic processing, and the sintering behavior and the optical properties of which were studied as functions of Mn content. Densification and grain growth of alumina were enhanced by Mn addition up to 0.75 cat% but was leveled off at higher concentrations. XRD revealed that $Al_2MnO_4$(galaxite) was formed as a second phase in the specimens with more than 0.75 cat% of Mn. Thus it is believed that either the solid solution effect of Mn or the Zener effect of $Al_2MnO_4$ becomes predominant in the sintering of Mn-added $Al_2O_3$ according to the additive concentration. UV-VIS reflectivity(SCI) spectra of Mn-added $Al_2O_3$ consisted of smooth bottoms in 300~550 nm wavelength range and plateaus at wavelengths longer than 650 nm. The reflectivity spectrum continuously moved downward, and the specimen color became darker and thicker with increasing Mn content. The CIELAB color change with respect to standard white was also dependent on the amount of Mn added: ${\Delta}L^*$(D65) negatively increased and ${\Delta}E_{ab}^*$(D65) positively increased with increasing Mn content, probably due to Mn substitution to Al and/or the mixing effect of black $Al_2MnO_4$ as a second phase.

• The Korean Journal of Ceramics
• /
• v.4 no.4
• /
• pp.297-303
• /
• 1998

The effect of aliovalent dopants, $ Nb_2O_5$ and MnO, on the phase stability of 12 mol% ceria partially-stabilized zirconia (Ce-TZP) polycrystals was studied. Both dopants (MnO and $ Nb_2O_5$) significantly increased the stability of the tetragonal zirconia phase (Mb temperature lower than liquid nitrogen temperature). The enhancement of the stability of the tetragonal phase in Ce-TZP doped with 1 mol% of Mno(Ce-TZP/MnO) andCe-TZP doped with 1 mol% of $ Nb_2O_5$(Ce-TZP/$ Nb_2O_5$) were explained by the significant reduction of the driving force, -${\Delta}$Gchem, for the tetragonal-to-mono-clinic phase transformation caused by the addition of MnO and $ Nb_2O_5$. The enhanced stability of the tetragonal phase in the Ce-TZP and Al2O3 composite (Ce-TZP/$Al_2O_3$) is believed to be caused by smaller grain size, moderate reduction in the chemical driving force and increase in the strain energy barrier to the transformation. Mechanical properties of the Ce-TZP and the Ce-TZP/$Al_2O_3$ with (i) the same grain size and (ii) the same Mb temperature were examined by measuring stress-strain behavior in 3 point bending. The Ce-TZP/$Al_2O_3$ composite doped with 1.3w% MnO (Ce-TZP/$Al_2O_3$/MnO), which had the same grain size as the Ce-TZP and De-TZP/$Al_2O_3$ showed more transformation plasticity than either the Ce-TZP or the Ce-TZP/$Al_2O_3$ composite. The Ce-TZP wihch had the same Mb temperature as that of the Ce-TZP/$Al_2O_3$/MnO did not show any transformation plasticity.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.2 no.2
• /
• pp.71-76
• /
• 1992

Piezoceramic filters were fabricated by adding $MnO_2 and FeZ0_3$ to the $0.05Pb(Al_{2/3}W_{1/3})O_3-0.95Pb(Zr_{0.52}Ti0.48)O_3$ system using photolithography method. As the amounts of $MnO_2$ increased, the electro-mechanical coupling factor(Kp) decresed. On the other hand, for $Fe_2O_3$ added samples, Kp was 57%, but mechanical quality factor(Qm) showed relatively low value. The passband widths were 155kHz for 0.3wt % $MnO_2$ addition and 260kHz for 0.1 wt % $Fe_2O_3$ addition, and were inversely propotional to Qm values. Group delay time characteristics showed Gausian for $MnO_2$ additions and Butterworth for$Fe_2O_3$ additions.