• Journal of Korean Society on Water Environment
• /
• v.26 no.3
• /
• pp.454-459
• /
• 2010

This study investigated the applicability of manganese coated media such as manganese coated sand (MCS), manganese coated sericite (MCSe) and manganese coated starfish material calcined at $550^{\circ}C$ (MCSf) to remove Mn(II) in synthetic wastewater. Manganese coated media prepared at different pH was applied in the treatment of soluble Mn(II) in batch and column experiments at various Mn(II) concentrations. The amount of Mn coated on three different media was approximately 800~1100 mg/kg. From the stability test, negligible dissolution of Mn was observed above pH 3.0. In batch test, more than 40% of Mn(II) was removed by all sand media at various manganese concentrations. In order to see the effect of additional oxidant for the removal of Mn(II), 4 mg/L of hypochlorite was added in Mn(II) solution during column experiment. Breakthrough of Mn(II) was greatly retarded in the presence of hypochlorite in all column reactors packed with different media. Among the manganese coated media, MCSf prepared at pH 4 indicated the highest removal capacity. The removal efficiency of Mn(II) was also increased in the multi-layer system (0.5 g of MCS, MCSe, and MCSf each).

• Journal of Korean Society of Environmental Engineers
• /
• v.28 no.1
• /
• pp.54-60
• /
• 2006

[ $MnO_2$ ]-Coated Sand(MCS) was prepared with variation of coating temperature, coating time, and dosage of initial Fe(III) with two kinds of sands such as Joomoonjin and quartz sand. An optimum condition for the preparation MCS was determined from the coating efficiency as well as the oxidation efficiency of As(III). Coating efficiency of Mn was strongly dependent on the coating temperature but quite similar over the investigated coating time, showing an increased coating efficiency at higher coating temperature. In contrast to coating efficiency, the oxidation efficiency of As(III) by MCS was severely reduced as increase of coaling temperature. By considering these results, an optimum coating temperature and time for the preparation of MCS was selected as $150^{\circ}C$ and 1-hr, respectively. Coating efficiency increased as the dosage of initial Mn(II) increased, while As(III) oxidation was maximum at 0.8 Mn(II) mol/kg sand. The solution pH was identified as an important parameter affecting stability of MCS, and dissolution of Mn from MCS increased as pH decreased. Oxidation rate of As(III) increased as the dosage of MCS increased as well as solution pH decreased.

• Journal of Korean Society of Environmental Engineers
• /
• v.32 no.2
• /
• pp.193-200
• /
• 2010

This study evaluated treatability of soluble Mn(II) using multifunctional sand media simultaneously coated with iron and manganese. In the preparation of IMCS(Iron and Manganese Coated Sand), 0.05 M Mn(II) solution and Fe(III) solution was mixed with sand at pH 7. The mineral type of IMCS was identified as the mixture of ${\gamma}-MnO_2$, goethite and magnetite($F_{e3}O_4$). The contents of Mn and Fe coated onto sand were 826 and 1676 mg/kg, respectively. The $pH_{pzc}$ of IMCS was measured as 6.40. The removal of soluble Mn(II) using IMCS and oxidants such as NaOCl and $KMnO_4$ was investigated with variation of the solution pH, reaction time and Mn(II) concentration in a batch test. The removal of Mn(II) on IMCS was 34% at pH 7.4 and the removals of Mn(II) on IMCS in the presence of NaOCl(13.6 mg/L) at pH 7 and $KMnO_4$(4.8 mg/L) at pH 7.6 were 96% and 89%, respectively. The removal of Mn(II) using IMCS and oxidants followed a typical cationic type, showing a gradual increase of removal as the solution pH increased. The removal of Mn(II) was rapid in the first 6 hrs and then a constant removal was observed. The maximum removed amount of Mn(II) on IMCS-alone and IMCS in the presence of oxidants such as NaOCl(13.6 mg/L) and $KMnO_4$(4.8mg/L) were 833.3, 1428.6 and 1666.7 mg/kg, respectively. Mn(II) removal onto the IMCS in the presence of oxidants was well described by second-order reaction and Langmuir isotherm expression.

• Journal of Korean Society of Environmental Engineers
• /
• v.29 no.5
• /
• pp.571-576
• /
• 2007

Manganese-Coated Sand(MCS) prepared with three different methods were applied in the treatment of soluble $Mn^{2+}$ in batch and column experiments. In the bench-scale MCS preparation, the coating efficiency of manganese on the surface of sand increased as the dosage of initial Mn(II) increased. The removed amount of the soluble $Mn^{2+}$ by MCS increased as the solution pH increased, following a typical anionic-type adsorption. The removed amounts of the soluble $Mn^{2+}$ through adsorption was quite similar over the entire pH range, without depending on the contents of Mn on the surface of sand as well as coating methods. When NaClO was used an oxidant, the removed amount of the soluble $Mn^{2+}$ by MCS increased as the concentration of NaClO increased, This trend might be explained by the increased removal efficiency through coating of manganese oxides produced from oxidation of the soluble $Mn^{2+}$ by NaClO on the surface of MCS. From the bench-scale column experiments, the breakthrough of $Mn^{2+}$ occurred after 4,100 bed volume without presence of NaClO while 1.6-times delayed breakthrough of $Mn^{2+}$ was observed in the presence of NaClO. This result also supports that the removal efficiency of the soluble $Mn^{2+}$ could be enhanced by using NaClO.

• Environmental Engineering Research
• /
• v.14 no.2
• /
• pp.134-139
• /
• 2009

In this study, oxidation of As (III) as well as removal of total arsenic by adsorbents coated with single oxides or multi-oxides (Fe (III), Mn (IV), Al (III)) was investigated. In addition, multi-functional properties of adsorbents coated with multi-oxides were evaluated. Finally, application of activated carbon impregnated with Fe or Mn-oxides on the treatment of As (III) or As (V) was studied. As (V) adsorption results with adsorbents containing Fe and Al shows that adsorbents containing Fe show a greater removal of As (V) at pH 4 than at pH 7. In contrast adsorbents containing Al shows a favorable removal of As (V) at pH 7 than at pH 4. In case of iron sand, it has a negligible adsorption capacity for As (V) although it contains 217.9 g-Fe/kg-adsorbent, Oxidation result shows that manganese coated sand (MCS) has the greatest As (III) oxidation capacity among all metal oxides at pH 4. Oxidation efficiency of As (III) by IMCS (iron and manganese coated sand) was less than that by MCS. However the total removed amount of arsenic by IMCS was greater than that by MCS.

• Journal of Korean Society of Environmental Engineers
• /
• v.31 no.7
• /
• pp.541-548
• /
• 2009

Iron coated media (activated carbon, sand and starfish) were prepared at pH 4 and applied for the treatment of landfill leachate containing organic compounds and soluble metal ions such as $Zn^{2+},\;Cu^{2+},\;Mn^{2+}$ in batch and column experiment. The amount of iron coated in media was analyzed with EPA 3050B method. The removal efficiency of metal ions and phenol was compared with iron coated media. The amount of iron coated in Fe-AC and ICS(iron coated sand) were 1,612 mg/kg and 1,609 mg/kg, respectively, while it was higher with 1,768 mg/kg in ICSF(iron coated starfish). The result of batch study represent the highest removal efficiency in the treatment of wastewater using iron coated starfish. In column study, the removal efficiency of phenol and metal ions was higher in multi-layered system of ICS, Fe-AC and ICSF compared to single layered system. Breakthrough time in the effluent was relatively enhanced for $Cu^{2+}$ and $Zn^{2+}$ in multi-layered system while the removal efficiency of $Mn^{2+}$ were not varied much. Therefore, multi-layered system was identified as the better system for the treatment of wastewater containing of metal ions and organic compound.

• Journal of Korean Society of Environmental Engineers
• /
• v.31 no.7
• /
• pp.473-482
• /
• 2009

In this study, iron and manganese coated sand (IMCS) was prepared by mixing Joomoonjin sand with solutions having different molar ratio of manganese ($Mn^{2+}$) and iron ($Fe^{3+}$). Mineral type of IMCS was analyzed by X-ray diffraction spectroscopy. Removal efficiency of arsenic through As(III) oxidation and As(V) adsorption by IMCS having different ratio of Mn/Fe was evaluated. The coated amount of total Mn and Fe on all IMCS samples was less than that on sand coated with iron-oxide alone (ICS) or manganese-oxide alone (MCS). The mineral type of the manganese oxide on MCS and iron oxides on ICS were identified as ${\gamma}-MnO_2$ and mixture of goethite and magnetite, respectively. The same mineral type was appeared on IMCS. Removed amount As(V) by IMCS was greatly affected by the content of Fe rather than by the content of Mn. Adsorption of As(V) by IMCS was little affected by the presence of monovalent and divalent electrolytes. However a greatly reduced As(V) adsorption as observed in the presence of trivalent electrolyte such as $PO_4\;^{3-}$. As(III) oxidation efficiency by MCS in the presence of NaCl or $NaNO_3$ was two times greater than that in the presence of $PO_4\;^{3-}$. Meanwhile a greater As(III) oxidation efficiency was observed by IMCS in the presence of $PO_4\;^{3-}$. This was explained by the competitive adsorption between phosphate and arsenate on the surface of IMCS.

• Journal of Korean Society of Water and Wastewater
• /
• v.24 no.3
• /
• pp.341-349
• /
• 2010

It is well known that manganese is hard to oxidize under neutral pH condition in the atmosphere while iron can be easily oxidized to insoluble iron oxide. The purpose of this study is to identify removal mechanism of manganese in the D water treatment plant where is treating bank filtered water in aeration and rapid sand filtration. Average concentration of iron and manganese in bank filtered water were 5.9 mg/L and 3.6 mg/L in 2008, respectively. However, their concentration in rapid sand filtrate were only 0.11 mg/L and 0.03 mg/L, respectively. Most of the sand was coated with black colored manganese oxide except surface layer. According to EDX analysis of sand which was collected in different depth of sand filter, the content of i ron in the upper part sand was relatively higher than that in the lower part. while manganese content increased with a depth. The presence of iron and manganese oxidizing bacteria have been identified in sand of rapid sand filtration. It is supposed that these bacteria contributed some to remove iron and manganese in rapid sand filter. In conclusion, manganese has been simultaneously removed by physicochemical reaction and biological reaction. However, it is considered that the former reaction is dominant than the latter. That is, Mn(II) ion is rapidly adsorbed on ${\gamma}$-FeOOH which is intermediate iron oxidant and then adsorbed Mn(II) ion is oxidized to insoluble manganese oxide. In addition, manganese oxidation is accelerated by autocatalytic reaction of manganese oxide. The iron and manganese oxides deposited on the surface of the sand and then are aged with coating sand surface.

• Environmental Analysis Health and Toxicology
• /
• v.17 no.4
• /
• pp.333-339
• /
• 2002

Yellow sand (YS) storms were observed about ten times in the Korean peninsula during March and April in 2002. Twenty four hour fine particle (PM$\_$2.5/) samples were collected onto the 47 mm Teflon - coated quartz filters over 9 days during and after the events using the MiniVol Portable Air Sampler at a flow rate of 5 liters per minute. The highest PM$\_$2.5/ concentration measured during the YS period was 289 $\mu\textrm{g}$/㎥, which is 13 times higher than the lowest of the values for the samples collected during the non-yellow sand period. The filter samples were analyzed for inorganic ions using the IC, AAS and Autoanalyzer, and for metals using the ICP-MS. The results showed that the concentrations of some inorganic ions (e.g., Ca$\^$2+/ and SO$_4$$\^$2-/) and metals (e.g., Fe, Mn) of soil origin were elevated during the yellow sand events.

• Journal of Soil and Groundwater Environment
• /
• v.13 no.2
• /
• pp.62-69
• /
• 2008

In this study physicochemical characteristics and stability of various manganese coated sands (MCS) prepared with different methods were evaluated. In addition, removal efficiencies of As(III) by each MCS were compared. Four different MCSs were used; B-MCS prepared by baking method, W&D-MCS prepared by wetting and dry method, NMCS prepared during the water treatment process and Birm which is a commercial MCS widely used for the removal iron and manganese. The manganese content in each MCS was following order: Birm (63,120 mg/kg) > N-MCS (10,400 mg/kg) >W&D-MCS (5,080 mg/kg) > B-MCS (2,220 mg/kg). Birm showed the least solubility (% basis) in acidic conditions. As(III) oxidation efficiency of B-MCS was continuously increased as the solution pH decreased. While As(III) oxidation efficiency of N-MCS and Birm was minimum around neutral pH. The increased As(III) oxidation efficiency above neutral pH for N-MCS and Birm could be due to the competitive adsorption of $Mn^{2+}$, which was produced from reduction of $MnO_2$, onto the surface of aluminum and manganese oxides.