• Journal of the Korea institute for structural maintenance and inspection
• /
• v.2 no.2
• /
• pp.170-176
• /
• 1998

The team mixed PbO, $ZrO_2$, $TiO_2$, $Nb_2O_5$ and $MnCO_3$, to make $Pb[(Zr_{0.54}\;Ti_{0.46})\;Nb_{0.005}]O_3+4%MnCO_3$. The electroded PZT ceramics were poled by 3 kV/mm at $110^{\circ}C$ for 600 s. We assembled the 0.4mm thick PZT slices into ultrasonic transducers. Central frequency of the probe is 5 MHz, which is proper to the thickness gauge for steel pipes and for flaw detector. The probe can detect a disk shape defect of 1mm diameter at 15cm deep in steel block. The new probe's Fresnel zone that the ultrasonic beam do not broaden is 13mm. Over the Fresnel zone, the ultrasonic beam spreads. Half of the beam spread angle of the probe is $4.3^{\circ}-4.6^{\circ}$. This probe can be used for the ultrasonic transducers for non-destructive testing of steel bridges.

• Journal of the Korean Ceramic Society
• /
• v.23 no.3
• /
• pp.15-20
• /
• 1986

Formation of powders and electromechanical coupling factor of $Pb(Mn_{1/3} Sb_{2/3})_{0.08} Ti_{0.495}Zr_{0.425}O_3$ by hydro-thermal synthesis are described. The hydrothermal reactions each were accomplished at 12$0^{\circ}C$~25$0^{\circ}C$ for 5hours and sintering was accomplished at 1, .20$0^{\circ}C$ for 1hours. The PZT powders by hydrothermal synthesis were formed above 16$0^{\circ}C$ and the forms were cubic types. The ratio of grain size of sintered sample to powder was slowly decreased with the rising of hydrothermal reactino temperature but decreased rapidly above 22$0^{\circ}C$ Sintering density was decreased with the rising of hydrothermal reaction temperature above 16$0^{\circ}C$ but dielectric constant was increased. Electromechanical coupling factor $K_P$ was almost constant at 16$0^{\circ}C$~24$0^{\circ}C$ range and the value of $K_P$ was about 0.43-0.45.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.1
• /
• pp.390-395
• /
• 2011

In order to develope piezoelectric transformer for the ballast of fluorescent lamp, the composition of piezoelectric ceramics was 0.95Pb($Zr_xTi_{1-x}$)O3+yPb($Mn_{1/3}Nb_{2/3}$)$O_3$+(0.05-y)Pb($Sb_{1/2}Nb_{1/2}$)$O_3$. PMN compound was selected to improve mechanical quality factor and PSN to prevent the decrease of dielectric constant and electromechanical coupling coefficient. Dielectric and piezoelectric characteristics in the region of MPB of 0.95Pb($Zr_xTi_{1-x}$)$O_3$+yPb($Mn_{1/3}Nb_{2/3}$)$O_3$+(0.05-y)Pb($Sb_{1/2}Nb_{1/2}$)$O_3$ ceramics was discussed both quantatively and qualitatively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.12S
• /
• pp.1195-1199
• /
• 2003

In this study, in order to develop the low temperature sintering ceramics for multilayer piezoelectric transformer, dielectric and piezoelectric properties of PSN-PZT[0.91Pb(Sb$\sub$1/2/Nb$\sub$1/2/)$\sub$0.03/(Zr$\sub$0.495/Ti$\sub$0.505/)$\sub$0.97/O$_3$-0.04Pb(Ni$\sub$1/2/W$\sub$1/2/)O$_3$+0.05BiFeO$_3$+0.3wt％MnO$_2$+0.6wt％CuO〕 ceramics were investigated according to Zr/Ti ratio. As Zr/Ti ratio is increased, electromechanical coupling factor(k$\sub$p/) and dielectric constant increased and then decreased after the ratio of Zr/Ti=50/50. Also, mechanical qualify factor(Q$\sub$m/) decreased and then increased after the ratio of Zr/Ti=50/50.

• Electrical & Electronic Materials
• /
• v.4 no.3
• /
• pp.220-228
• /
• 1991

본 연구에서는 핫프레스법으로 제작된 0.05Pb(Sn$_{1}$2/Sb$_{1}$2/)O$_{3}$-0.60PbZrO$_{3}$-0.35PbTiO$_{3}$+x[wt%]MnO$_{2}$ 세라믹스에 대해 구조적, 전기적 특성 및 탄성 표면파 특성을 조사하였다. x가 0.4인 조성을 1150[.deg.C]에서 45분간 소성한 시편의 경우 탄성표명파의 전기 기계 결합 계수 k$_{s}$ $^{2}$가 2.8[%], 기계적 품질 계수 Q$_{m}$ 이 1976으로 탄성 표면파 소자용 기판으로서 응용 가능함을 보였다.

• Electrical & Electronic Materials
• /
• v.1 no.2
• /
• pp.162-167
• /
• 1988

본 논문에서는 Pb(Sn$_{1}$7/Mn$_{2}$7/Nb$_{4}$7/)O$_{3}$- Pb(Zr, Ti)O$_{3}$계에 La$_{2}$O$_{3}$를 첨가하여 그양에 따른 압전일 전기력 성질의 변화를 고찰하였다. La$_{2}$O$_{3}$ 첨가량의 증가에 따라 유전상수, 압전 d상수, 유전손실, 비저항 등은 증가하였으나 경시 변화량은 오히려 감소하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1994.11a
• /
• pp.13-16
• /
• 1994

In this paper, xPb(Zn$_{1/3}Nb_{2/3}$)$O_3$-yPbTiO$_3$-zPbZrO$_3$-(0.5wt%)MnO$_2$ ceramics were fabricated by the mixed oxide method sintered at $1250^{\circ}C$ for 2[hr] and then the deielectric, electromechanical coupling factor($K_{p}$ and mechanical coupling factor(Qm) properties were investigated. In 0.1PZN-0.45PT-0.45PZsample, dielectric properties and electromechanical coupling factor were 829 and 29%. In the case of 0.5PZN-0.45PT-0.50PZ sample, that was 101 according to mechanical quality facotr. molphotropic phase boundary(MPB) certained area which $PbTiO_3$addition quatity 40∼50[㏖%].

• Fire Science and Engineering
• /
• v.9 no.2
• /
• pp.29-36
• /
• 1995

In this study, the effect of Mn $O_2$ additive on the electrical characteristics of PZN-PSS-PZT Pyroelectric materials for the fire detactor was studies. PZT ceramics used this experimental is 4 composite system $[$Pb(Z $n_{1}$3/ N $b_{2}$3/) $O_3$＋Pb(S $n_{1}$3/ S $b_{2}$3/) $O_3$＋PbTi $O_3$＋PbZr $O_3$$]$The dielectric constants and dissipation factors decreases as to Mn $O_2$ concentration increases. At the Mn $O_2$ 0.5($\omega$t%), Pyroelectric coefficient shows 8(10$^{-8C}$$\textrm{cm}^2$$^{\circ}C$) which have the highst value among other additive contents. It is found that output voltage shows maximum peck at Mn $O_2$0.7($\omega$t％) is associated with the higher pyroelectric coefficient and Lowered dielectric constant.t.

• Corrosion Science and Technology
• /
• v.5 no.2
• /
• pp.45-51
• /
• 2006

Properties of the anode for cathodic protection need low overvoltage for oxygen evolution and high corrosion resistance. It is well known that DSA (Dimensionally Stable Anode) has been the best anode ever since. DSA is mainly composed of $RuO_2$, $IrO_2$, $ZrO_2$, $Co_2O_3$, and also $Ta_2O_5$, $TiO_2$, $MnO_2$ are added to DSA for better corrosion resistance. The lifetime of DSA for cathodic protection is also one of the very important factors. $RuO_2$, $IrO_2$, $RhO_2$, $ZrO_2$ are well used for life extension, and many researches are focused on life extension by lowering oxygen evolution potential and minimizing dissolution of oxide coatings. This work aims to evaluate the influence of constituents of MMO and coating cycles and $ZrO_2$ coating on the electrochemical properties and lifetime of DSA electrodes. From the results of lifetime assessment in the anodes coated with single component, $RuO_2$ coating was more effective and showed longer lifetime than $IrO_2$ coating. Also, an increased coating cycle and an electrochemically coated $ZrO_2$ could enhance the lifetime of a DSA.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.257-264
• /
• 1997

The aim of this study was to investigate the degradation of piezoelectric properties with compressive cy-clic loading, the change in bending strength before and after poling treatment and fracture strength in MPB depending on the amount of MnO2 addition. The MPB with 0.25 wt.% MnO2 showed the best resistance against the piezoelectric degradation with compressive cyclic loading. Bending strength increased when pol-ing and loading directions are parallel, however decreased when poling and loading directions are per-pendicular each other. Because, during poling treatment, compressive residual stress is generated in the pol-ing direction but tensile residual stress in the perpendicular direction to poling direction.