• 한국세라믹학회지
• /
• 제32권1호
• /
• pp.63-70
• /
• 1995

A crack-free ceramic composite membrane with micropores has been synthesized by the pressurized sol-gel coating technique using the mixed Al2O3-SiO2 sols. The mixed sols were prepared by mixing nanoparticulate SiO2 and boehmite sols. These sols were more stable at lower pH, but very unstable when their copositions were in the range of 50~75mol% of SiO2 at the same pH. The mixed Al2O3-SiO2 membrane prepared from the mixed sol (0.2mol/$\ell$ of solid content and pH=2) containing 40mol% of SiO2 had the mean pore radius of 0.80nm and the specific surface area of 280$m^2$/g. The nitrogen permeability through the coated Al2O3-SiO2 layer was 42$\times$107mol/$m^2$.s.Pa. It was found that the thermal stability of aluminosilicate membranes, even through similar to that of SiO2 membranes, was much improved in comparison with ${\gamma}$-alumina membranes.

• 한국세라믹학회지
• /
• 제30권7호
• /
• pp.535-542
• /
• 1993

It was investigated in this study that a preparation method, activation energy, surface area, pore volume, pore size distribution and DTA analysis of the dry gel in process of producing monolithic porous gel in Li2O-Al2O3-TiO2-SiO2 system by the sol-gel technique using metal alkoxides. Activation energy for gellation according to the variation of water concentration and the kind of catalysts ranged from 10 to 20kcal/mole. Monolithic dry gels were prepared after drying at 9$0^{\circ}C$ when the amount of water for gellation was 4~8 times more than the stoichiometric amount, that was necessary for the full hydrolysis of the mixed metal alkoxide. The specific surface area, the pore volume, the average pore radius of the dried gel at 18$0^{\circ}C$ according to the various kinds of catalyst were about 348~734$m^2$/g, 0.35~0.70ml/g and 10~35$\AA$, respectively. It showed that the dry gels were porous body. As a result ofthe analysis of DTA, it was confirmed that the exothermaic peaks at 715$^{\circ}C$ and 77$0^{\circ}C$ was clue to the crystallization of dried gel.

• 한국세라믹학회지
• /
• 제28권7호
• /
• pp.503-508
• /
• 1991

High pure and fine mullite powders were synthesized from Al-secbutoxide[Al(OC4H9)3] and TEOS[Si(OC2H5)4] (SiO2/Al2O3=2/3 mole). Sol-Gel process by partial hydrolysis technique, as it were, first, TEOS was partially hydrolysized and then mixed with Al-secbutoxide for complete hydrolysis was used. The mullite precursor was synthesized within 30 hrs, which was reduced about a half of synthetic time in comparison with the other's study. Al-Si spinel was formed at 980℃ and mullite crystal was formed at 1200℃. Mullite powders synthesized in this study was spherical type like those of the other studies and particle sizes were very fine. Also mullite powders calcined at 1,600℃ had a stoichiometric composition (3Al2O3·2SiO2) and lattice constants were coincided with known theoretical values.

• 한국재료학회지
• /
• 제16권12호
• /
• pp.719-724
• /
• 2006

Ultrafine mullite powder was prepared from aluminium-secbutoxide and tetraethyl orthosilicate(TEOS) in the molar $Al_2O_3/SiO_2$=3/2. Sol-gel method by partial hydrolysis technique, as it were, first, TEOS was partially hydrolysized and then mixed with Al-secbutoxide for complete hydrolysis was used. X-ray diffraction, infrared spectroscopy and transmission electron microscopy, etc. confirmed that the mullite powder prepared by this method is in the stoichiometric $Al_2O_3/SiO_2$ ratio. Al-Si spinel was formed at $980^{\circ}C$ and ultrafine mullite powder with about 20 nm particle size was obtained above $1,200^{\circ}C$. Also mullite powders calcined at $1,600^{\circ}C$ had a stoichiometric composition, $3Al_2O_3{\cdot}2SiO_2$ and the lattice constants of the mullite powders calcined above $1,200^{\circ}C$ were almost coincided with theoretical values.

• 공업화학
• /
• 제18권6호
• /
• pp.568-574
• /
• 2007

투명결정화 유리의 전구체로서 균열이 없는 $Li_2O1{\cdot}7Al_2O_3{\cdot}8.6SiO_2$ 조성인 다공성 괴상 겔을 formamide를 첨가한 알콕시드 용액으로부터 sol-gel방법으로 합성하였다. 겔 합성에서 겔화 활성화 에너지, 비표면적, 습윤겔의 완전 탈수에 필요한 온도, 기공의 부피 및 기공크기와 분포를 측정하였고, 겔의 결정화온도를 검토하고자 시차열분석을 실시하였다. 겔화의 활성화에너지는 가수분해에 필요한 물의 첨가량에 따라 13~14 kcal/mol 범위를 나타내고, 물의 첨가량이 가수분해시 필요한 이론량의 3배 이상일 경우, $70{\sim}75^{\circ}C$, 건조속도 0.1~0.3 %/h에서는 겔의 균열을 방지할 수 있어 안정한 괴상 겔을 제조할 수 있었다. $180^{\circ}C$에서 건조한 겔체는 비표면적, 기공부피 및 기공크기분포는 $239.40m^2/g$, 0.001~0.03 mL/g 그리고 1~122 nm 반지름의 미세구조로 된 투명 겔체로서 다공질 물질임이 확인되었고, 건조겔의 시차열분석 결과 $800^{\circ}C$ 부근에서 1차 발열피크, $980^{\circ}C$ 부근에서가 2차 발열피크가 확인되어 결정화가 일어남을 알 수 있었다.

• The Korean Journal of Ceramics
• /
• 제4권4호
• /
• pp.323-330
• /
• 1998

Mixed oxide compounds of potential usefulness for fibre coatings (hexagonal celsian, $BaAl_2Si_2O_8$ and lanthanum hexaluminate, $LaAl_{11}O_{18}$) or for matrix materials (yttrium aluminium garnet, $Y_3Al_5O_{12}$) were prepared by hybrid sol-gel synthesis and their thermal crystallisation was monitored by thermal analysis, X-ray diffraction and multinuclear solid state MAS NMR. All the gels convert to the crystalline phase below about $12200^{\circ}C$, via amorphous intermediates in which the Al shows and NMR resonance at 36-38 ppm sometimes ascribed to Al in 5-fold coordination. Additional information about the structural changes during thermal treatment was provided by $^{29}Si$, $^{137}Ba$ and $^{89}Y$ MAS NMR spectroscopy, showing that the feldspar framework of celsian begins to be established by about $500^{\circ}C$ but the Ba is still moving into its polyhedral lattice sites about $400^{\circ}C$ after the sluggish onset of crystallization. Lanthanum hexaluminate and YAG crystallise sharply at 1230 and $930^{\circ}C$ respectively, the former via $\gamma-Al_2O_3$, the latter via $YAlO_3$. Yttrium moves into the garnet lattice sites less than $100^{\circ}C$ after crystallisation.