• Journal of the Korea Institute of Building Construction
• /
• v.17 no.3
• /
• pp.261-268
• /
• 2017

Red mud is an inorganic by-product obtained from the mineral processing of alumina from Bauxite ores. A highly alkali inorganic waste product with a pH level over 11, red mud in its original state negatively impacts the ecosystem, so appropriate treatment is necessary. The development of alkali activated slag-red mud cement can be a representative study aimed at recycling the strong alkali of the red mud as a construction material. However, Alkali-activated binders that use sodium activators have been reported to be more vulnerable to efflorescence. Therefore, in this study, the compressive strength, pore characteristics, water absorption, elution characteristics, and efflorescence properties of alkali-activated slag cement mortar were assessed according to their red mud substitution ratio.

• Korean Journal of Materials Research
• /
• v.16 no.12
• /
• pp.754-760
• /
• 2006

Mercaptoundecanoic acid (MUA) has been used to enhance the dispersity of Au nanoparticles in organic solvent and the affinity between the Au nanoparticles surface and titanium dioxide shell in the synthesis of $Au/TiO_2$ core-shell composite nanoparticles. The dispersity of the MUA-coated Au nanoparticles in ethanol aqueous solution with different concentration of $H_2O$ was investigated by UV-Vis. absorption spectrum and the coating amount of MUA was varied from 0.02 mM to 1.0 mM. The MUA-coated Au nanoparticles were highly dispersed in pure $H_2O$ in the wide range of the coating amount of MUA. On the contrary, the MUAcoated Au nanoparticles showed an enhanced stability in the ethanol/$H_2O$=8/2 mixed solution only when the coating amount of MUA was 0.05 mM, and in the ethanol/$H_2O$=7/3 mixed solution when the coating amount of MUA was in the range from 0.02 mM to 0.17 mM. From this systematic study, it can be inferred that the stability and the dispersibility of Au nanoparticles in organic solvents are highly sensitive towards the amount of MUA coating.

• Resources Recycling
• /
• v.21 no.2
• /
• pp.17-33
• /
• 2012

In order to review the recent technological progress and issues on the urban mine resources recycling in Japan and Korea, recycling process of the ELV(End of Life Vehicles) and E-waste(WEEE) were studied. Although technological level for processing of the ELV and E-waste is almost similar in both countries, the treatment of hazadous materials of ELV such as freon, air bag and ASR is unsufficient in Korea. In the E-waste recycling, the technological level is deeply different according to the enterprise size in Korea. Finally, the big R&D project on recycling of urban mine resources sponsored by government in both countries were discussed.

• Korean Journal of Remote Sensing
• /
• v.21 no.2
• /
• pp.135-143
• /
• 2005

RPC(Rational Polynomial Camera) models have become the replacement model of choice for a number of high resolution satellite imagery providers. RPCs(Rational Polynomial Coefficients) provide a compact accurate representation of the ground to image geometry, allowing users to perform full photogrammetric processing of satellite imagery including block adjustment, 3D feature extraction and orthorectification. This paper presents an algorithm for 3D feature extraction using downhill simpler method which requires only function evaluations, not derivatives. The algorithm was implemented as an executable software program and tested using stereo IKONOS images of Seoul city. The results showed that the proposed algorithm was fast and accurate enough to be used as a practical method for the 3D feature extraction from stereo images with RPCs.

• Korean Journal of Remote Sensing
• /
• v.17 no.2
• /
• pp.165-181
• /
• 2001

Using a field spectrometer having a spectral range of 0.4$\mu\textrm{m}$~2.5$\mu\textrm{m}$ with a spectral resolution of 1nm, the researchers measured the reflectance of granite, andesitic rocks, sedimentary rocks, and pyrophyllite ore in the Ungsang area, Kyungsang Basin, South Korea. Spectral characteristics of the geological media were investigated from the analysis. The in-situ measured sites were selected in well exposed rock outcrops. In case of unfavorable weather conditions, rocks were sampled and remeasured under natural solar condition. The reflectance of field data was measurd at three sistes for granite, six sites for andesitic rock three sites for sedimentary rocks, and two sites for pyrophyllite ore. The vibrational absorption bands for pyrophyllite are detected in the spectral range of 2.0$\mu\textrm{m}$~2.5$\mu\textrm{m}$. The absorption band for granites in study area is not distinctive. The reflectance measured under normal field conditions showed strong absorption at wavelengths of 1.4$\mu\textrm{m}$ and 1.9$\mu\textrm{m}$ due to the effect of moisture in the atmosphere. After the bands of 1.4$\mu\textrm{m}$ and 1.9$\mu\textrm{m}$ were removed, Hull Quotient method was applied to characterize absorption bands. The reflectances of field data were calculated to estimate the band ratio corresponding to the Landsat TM and EOS Terra ASTER. The researchers suggest here that the TM band2, band3, band4, and band7 or ASTER band2, band3, band4, and band9 are the best combination for discriminating outcrops. The researchers tested and demonstrated using a Landsat TM image in the study area. For geologic applications, decorrelation stretch is also an effective tool to enhance the exposed rock mass in images.

• Journal of Fisheries and Marine Sciences Education
• /
• v.23 no.4
• /
• pp.709-722
• /
• 2011

This study was investigated to obtain basic data which can be applied to processing of retort pouched seasoned sea mussel. Shell was washed and steamed before shucking. Sea mussel meat was seasoned in boiled and mixed seasoning sauce(soy sauce 23%, monosodiun glutamate 2%, sorbitol 2%, sesame oil 1%, vinegar 2%, starch syrup 15%, water 55%) for 30 min. The seasoned sea mussel was vacuum packed in plastic film bag and sterilized for various Fo values(Fo 7~13 min.) in a hot water circulation system retort at $121^{\circ}C$. The chemical composition such as pH, VBN, amino-N, total amino acid, free amino acid, color value (L, a, b), texture profile, TBA value, mineral, sensory evaluation and viable cells count of the retort pouched seasoned sea mussels sterilized with various conditions(Fo 7~13 min.) were measured. The same experimental items were also measured during storage. There was no remarkable difference between sterilization conditions and sensual characteristics. The results showed that the product sterilized at Fo 7 min. was the most desirable because this condition is most economical.

• Journal of Fisheries and Marine Sciences Education
• /
• v.23 no.4
• /
• pp.662-672
• /
• 2011

This study was investigated to obtain basic data which can be applied to processing of canned seasoned kwamaegi. Commercial Kwamaegi was cut into $2{\times}3cm$ lengths, filled 90 g into can (301-3) and added with 60 g water before precooking for 10 min. at $100^{\circ}C$. The precooked Kwamaegi was packed into the can, and added with 60 g seasoning sauces, which was prepared by mixing soy sauce 23%, monosodium glutamate (MSG) 2%, sorbitol 2%, sesame oil 1%, vinegar 2%, starch syrup 17%, sake 5%, water 48%. The cans were sealed using a vacuum seamer and then sterilized for various Fo values (Fo 8~12 min.) in a steam system retort at $121^{\circ}C$. The factors such as pH, VBN, amino-N, total amino acid, free amino acid, color value (L, a, b), texture profile, TBA value, mineral, sensory evaluation and viable bacterial count of the canned seasoned Kwamaegi produced with various sterilization condition(Fo 8~12 min.) were measured. There was no remarkable difference between sterilization conditions and sensual characteristics. The results showed that the product sterilized at Fo 8 min. was the most desirable because this condition is most economical.

• Journal of the Korean Society for Environmental Technology
• /
• v.19 no.6
• /
• pp.543-549
• /
• 2018

In this study, the treatment efficiency of inorganic membrane according to the flux that blending raw water was investigated at the laboratory level. Based on the results of each blending and flux, we obtained the best efficiency according to each measurement item. The treatment efficiencies were different depending on the raw water and treatment amount of the treated water. Especially, turbidity removal efficiency was high. In the case of $UV_{254}$, the removal efficiency according to the concentration of the raw water and the removal efficiency according to the flux of the treated water showed a maximum of 69 % to minimum of 48 %. In the case of TOC and DOC, the processing efficiency was 22 % and 28 %, respectively, because the organic value of the raw water was low. These results suggest that there is an optimal process to effectively remove contaminants from the inorganic membrane process, and it is necessary to optimize it according to operating conditions.

• Resources Recycling
• /
• v.30 no.5
• /
• pp.17-24
• /
• 2021

Natural aggregate regular exploitation has led to environmental and resource depletion issues; consequently, construction waste has become an important raw material in the supply of aggregate smoothly. The recycled aggregate produced in the most of recycled aggregate processing company in Korea has a high adhesion ratio of cement paste and mortar, which affects the water absorption ratio and density. Therefore, the quality of recycled aggregate needs to be improved. In this study, we improved the quality of recycled aggregate through the use of a multistage separation ball mill. This ball mill has a sieve which protects the ball mix and improves the motion. Products produced by using multistage separation ball mill were compared with various quality standard for utilization as recycle aggregate. Finally, we confirmed that the multistage separation ball mill can efficiently separate cement paste and mortar from natural aggregate and that it is suitable for the production of recycled aggregates.

• Journal of the Korean Society of Industry Convergence
• /
• v.23 no.6_2
• /
• pp.1043-1050
• /
• 2020

In this study, a study was presented on the monitoring technique of landslide area using UAV. In the case of disaster investigation using drone mapping, it can be used at various disaster sites. The mission can be carried out at various disaster sites, including surveys of damage to mountainous areas caused by landslides, building collapses surveys of flood damage, typhoons, earthquakes. The damage investigation plan using drone mapping is expected to be highly utilized at disaster sites where investigators cannot access it like in mountainous areas and where it is difficult to conduct direct damage investigations at the site. Drone mapping technology has many advantages in terms of disaster follow-up, such as recovery. Compared to the existing survey system, which was mainly carried out manually, the investigation time can be drastically reduced, and it can also respond to disaster sites that are difficult to carry out or are difficult to access directly. In addition, it is possible to establish and guide spatial data at the disaster site based on accurate mapping data from the time of the disaster, which has considerable strength in managing the situation of the disaster site, selecting priority areas for recovery, and establishing recovery plans. As such, drone mapping is a technology that can be used in a wide range of sites along with natural disasters and social disasters. If a damage investigation system is established through this, it is believed that it will contribute significantly to the rapid establishment of recovery plans along with the investigation of disaster response time and extent of damage recovery.