• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.7 s.238
• /
• pp.1022-1027
• /
• 2005

In this study, ball milling process was applied to reduce the particle size of bio-material down to submicron size. The material used was Ibuprofen. The ball milling was performed at low temperature of about $-180^{\circ}C$. The effect of processing conditions (milling time, milling speed) on the particle size was determined. The results showed that the degree of crystallite of Ibuprofen was slightly reduced by the ball milling process. The results also showed that the size of Ibuprofen was significantly reduced by the ball milling process. The effect of milling time was significant within the milling time of six hours while it was small thereafter.

• Carbon letters
• /
• v.26
• /
• pp.11-17
• /
• 2018

Milled carbon fiber (mCF) was prepared by a ball milling process, and X-ray diffraction (XRD) diffractograms were obtained by a $2{\theta}$ continuous scanning analysis to study mCF crystallinity as a function of milling time. The raw material for the mCF was polyacrylonitrile-based carbon fiber (T700). As the milling time increased, the mean particle size of the mCF consistently decreased, reaching $1.826{\mu}m$ at a milling time of 18 h. The XRD analysis showed that, as the milling time increased, the fraction of the crystalline carbon decreased, while the fraction of the amorphous carbon increased. The (002) peak became asymmetric before and after milling as the left side of the peak showed an increasingly gentle slope. For analysis, the asymmetric (002) peak was deconvoluted into two peaks, less-developed crystalline carbon (LDCC) and more-developed crystalline carbon. In both peaks, Lc decreased and $d_{002}$ increased, but no significant change was observed after 6 h of milling time. In addition, the fraction of LDCC increased. As the milling continued, the mCF became more amorphous, possibly due to damage to the crystal lattices by the milling.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.5
• /
• pp.129-133
• /
• 2007

Focused Ion Beam(FIB) systems is a useful tool for the fabrication of micro-nano scale structures. In this study, the effects of FIB etching on the Au microstructure are systematically investigated. As the fabrication parameters, ion dose, dwell time and beam overlap ratio are studied. First, the increases of Ga ion dose makes the milling yield higher and the sidewall of milling profile steeper. Dwell time is found to have little effects on the milling profile due to the relatively large milling area of $1\times1{\mu}m^2$ used in this study. However, beam overlap significantly affects not only milling rate but also milling profile. As the beam overlap ratio changes from positive to negative, the development of regular cross-stripe patterns at the bottom with low milling rate is observed.

• Transactions of the Korean hydrogen and new energy society
• /
• v.17 no.4
• /
• pp.418-424
• /
• 2006

In order to improve the activation properties of the $AB_2$ type hydrogen storage alloys for Ni-MH battery, the alloy surface was modified by employing high energy ball milling. The $Zr_{0.54}Ti_{0.45}V_{0.54}Ni_{0.87}Cr_{0.15}Co_{0.21}Mn_{0.24}$ alloy powder was ball milled for various period by using the high energy ball mill. As the ball milling time increased, activation of the $AB_2$ type composite powder electrodes were enhanced regardless of additives. When the ball milling time was small discharge capacities of the $AB_2$ type composite powder electrodes increased with the milling time. On the other hand for large milling time it decreased with increasing milling time. The maximum discharge capacity was obtained by ball milling for 3-4 min.

• Journal of Powder Materials
• /
• v.17 no.3
• /
• pp.242-250
• /
• 2010

In this research, the optimal manufacturing conditions of fine Si powders from Si scrap were investigated as a function of different initial powder size using the high-energy ball milling equipment, which produces the fine powder by means of an ultra high-energy within a short duration. The morphological change of the powders according to the milling time was observed by Scanning electron microscopy (SEM). With the increasing milling time, the size of Si powder was decreased. In addition, more energy and stress for milling were required with the decreasing initial powder size. The refinement of Si scrap was rapidly carried out at 10min ball milling time. However, the refined powder started to agglomerate at 30 min milling time, while the powder size became uniform at 60 min milling time.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.234-237
• /
• 2000

In this paper, the structural, dielectric and piezoelectric properties of the Pb[(S $b_{1}$2/N $b_{1}$2/)$_{0.035}$- $_Mn_{1}$3/N $b_{2}$3/)$_{0.065}$-(Z $r_{0.49}$, $Ti_{0.51}$)$_{0.90}$] $O_3$ ceramics were investigated with respect to the variation of the milling time. Grain size was decreased as the increase of milling time. As the milling time is increased, the particle size of the powder was decreased. Dielectric constant and electromechanical coupling factor (Qm)were slowly increased with the increase of milling time. The highest value of Qm was 1,497 at milling time 8 hour. Temperature coefficient of resonant frequency(TC $F_{r}$) was moved to positive side with the increase of milling time.e.e.e.e.e.e.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.7
• /
• pp.49-54
• /
• 2010

The cryogenic ball milling was performed on carbon nanotubes (CNTs) at an extremely low temperature to increase the dispersion of CNTs. The effects of milling speed and time on the deagglomeration and structural changes of CNTs were studied. FESEM was used to analyze the dispersion and the change of particle size before and after milling process. Transmission electron microscopic (TEM) analysis was also investigated the effect of cryogenic ball milling on the morphological characteristics of CNTs. The structural changes by the cryogenic ball milling process were further confirmed by x-ray diffraction (XRD) and Raman spectroscopic analysis. The results showed that the agglomeration of CNTs was significantly reduced and amorphous structure was observed at high milling speed. However, the milling time has no great effect on the dispersion property and structural change of CNTs compared with milling speed.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.12
• /
• pp.1039-1043
• /
• 2007

In this paper, in order to develop low temperature sintering ceramics for multilayer piezoelectric actuator application, PMN-PZN-PZT ceramics were fabricated using $LiCO_3,\;Bi_2O_3$ and CuO as sintering aids. And also, their piezoelectric and dielectric properties were investigated according to the milling time. All the specimens sintered at $930\;^{\circ}C$ showed tetragonal phases without secondary phases. With increasing milling time, piezoelectric and dielectric characteristic of specimens increased up to 60 hours milling time and then decreased due to the agglomeration of fine particle. Accordingly, it seems that 60 hour is optimum milling condition. At the sintering temperature of $930\;^{\circ}C$ and milling time of 60 hour, density, dielectric constant(${\varepsilon}_r$), electromechanical coupling factor (kp), mechanical quality factor (Qm), piezoelectric d constant showed the optimum value of $7.95\;g/m^3$, 1382, 0.546, 1749, 330 pC/N, respectively for multilayer piezoelectric actuator application.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1298-1299
• /
• 2006

In the present work, the influence of the ball-milling time, milling atmosphere and weight ratio of ball to powder on characteristics of $WO_3-CuO$ was studied. Results show that, the grain sizes of the $WO_3$ and CuO in the ball-milled powder mixture were significantly decreased with increasing the milling time. Those of each oxide ball-milled in Argon and Hexane atmosphere for 30 and 20 hour were about 98 and 84 nm, respectively. After milling of 20 hour in Hexane as PCA, the powder had a homogeneously mixed structure and the average size of $WO_3-CuO$ powders was determined to about 230nm.

• Transactions on Electrical and Electronic Materials
• /
• v.2 no.3
• /
• pp.18-23
• /
• 2001

For the piezoelectric transformer application, Pb(Sb$\_$1/2/ Nb$\_$1/2/)O$_3$-Pb(Zr,Ti)O$_3$ ceramics were produced by attrition milling. Microstructural, dielectric and piezoelectric characteristics of the ceramics were investigated as a function of milling time. The particle size and grain size decreased while dielectric constant, density and mechanical quality factor (Q$\_$m/) increased with milling time. Temperature coefficient of resonant frequency (TCf$\_$r/) was shifted to positive side with increasing milling time. The attrition milling process proved to be one of the effective routes to produce transformers for high power application.