Electron field emission properties from various CVD diamond films were studied. Diamond films were synthesized by microwave plasma CVD at 1173K and at 673K substrates temperature and pulse microwave plasma CVD at 1173K. B-doped diamond film was synthesized by microwave plasma CVD at 1173K also. Estimation by SEM, both the non-doped diamond film and B-doped diamond film which were synthesized at 1173K substrate temperature were $2~3\mu\textrm{m}$ in diameter and nucleation densities were $10^{8}{\;}numbers/\textrm{cm}^2$ order. The diamond film synthesized at 673K was $0.2\mu\textrm{m}$ in diameter and nucleation densities was 109 numbers/cm2 order. The diamond film synthesized by pulse microwave plasma CVD at 1173K was $0.2\mu\textrm{m}$ in diameter and nucleation density was $10^{9}{\;}numbers/\textrm{cm}^2$ order either. From the result of electron field emission measurement, electron field emission at $20V/\mu\textrm{m}$ from CVD diamond film synthesized by pulse microwave plasma CVD was $37.3\mu\textrm{A}/\textrm{cm}^2$ and the diamond film showed the best field emission property comparison with other CVD diamond.

• 한국결정성장학회지
• /
• 제15권1호
• /
• pp.10-15
• /
• 2005

Microwave plasma CVD 다이아몬드/Ti 박막 성장 시 CH₄/H₂ 가스의 유량비율, chuck bias, microwave power 등이 다이아몬드 박막의 구조적 특성과 입자밀도에 미치는 영향에 대하여 조사하였다. 2∼3 CH₄ Vol.% 조건일 때 sp³-결합성의 탄소 neutral 들이 우선적으로 형성되고 sp²-결합성의 탄소 neutral 들이 선택적으로 제거됨에 따라 양질의 다이아몬드 박막을 얻을 수 있었으며, 다이아몬드 입자 증착 기구를 해석하였다. Ti 기판에 걸어준 negative chuck bias가 증가함에 따라 다이아몬드 핵생성이 증진되어 다이아몬드 입자 밀도가 증가하였고, 임계 전압은 약 -50V 임을 확인하였다. 또한, microwave power가 증가함에 따라 미세결정질(micro-crystalline) graphite 층 생성이 제어되고 다이아몬드 층이 형성됨을 확인하였다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1993년도 추계 학술발표 강연 및 논문 개요집
• /
• pp.142-142
• /
• 1993

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2003년도 춘계학술발표회 초록집
• /
• pp.66-67
• /
• 2003

• 한국표면공학회지
• /
• 제29권5호
• /
• pp.487-493
• /
• 1996

Diamond films were grown at lower temperatures (630-813K) on Si, Al (1100P), and Al-Si(8A, 8B, BC) alloy substrates using improved microwave plasma CVD apparatus in a mixed methane and hydrogen plasma. Improved microwave plasma CVD apparatus equipped water cooled substrate holder and the substrates were set up lower position than bottom line of the applicator waveguide. When the methane concentration was high and growth was conducted at lower pressures the diamond films were synthesized. Moreover the deposits on the scratched substrates formed flat surfaces consisting of fine grains. XRD results, the deposits were identified to cubic diamond. An analysis using Raman spectroscopy, further confirmed that diamond films deposited on the Si substrates were high quality. The deposits on the Al substrates, in contrast, contained amorphous carbon. While the quality of the deposits on the Al-Si substrates were differed with the substrate alloys.

• 한국표면공학회지
• /
• 제29권5호
• /
• pp.540-544
• /
• 1996

To apply the CVD diamond film to coated tools, it is necessary to make adhesion strength between diamond film and substrate stronger. So adhesion strength of diamond coated WC-Co tools using Microwave Plasma CVD and cutting test of Al-18mass%Si alloy using diamond cutting tools were studied. Diamond coating was carried out using Microwave Plasma CVD apparatus. Reaction gas was used mixture of methane and hydrogen. Substrate temperature were varied from 673K to 1173K by control of microwave output power and reaction pressure. By observation of SEM, grain size became larger and larger as substrate temperature became higher and higher. Also all deposits were covered with clear diamond crystals. XRD results, the deposits were identified to cubic diamond. An analysis using Raman spectroscopy, the deposit synthesized at lower substrate temperature (673K) showed higher quality than deposit synthesized at higher substrate temperature (1173K). As a result of scratch adhesion strength test, from 873K to 1173K adhesion strength decreased by rising of substrate temperature. The deposit synthesized at 873K showed best adhesion strength. In the cutting test of Al-18mass%Si alloy using diamond coated tools and the surface machinability of Al-Si works turned with diamond coating tools which synthesized at 873K presented uniform roughness. Cutting performance of Al-18mass%Si alloys using diamond coated WC-Co tools related to the adhesion strength.

• 반도체디스플레이기술학회지
• /
• 제3권3호
• /
• pp.45-50
• /
• 2004

Highly oriented diamond (HOD) films in polycrystalline can be grown on the (100) silicon substrate by microwave plasma CVD. Bias enhanced nucleation (BEN) method was adopted for highly oriented diamond deposition with high nucleation density and uniformity. The substrate was biased up to -250[Vdc] and bias time required for forming a diamond film was varied up to 25 minutes. Diamond was deposited by using $\textrm{CH}_4$/CO and $H_2$ mixture gases by microwave plasma CVD. Nucleation density and degree of orientation of the diamond films were studied by SEM. Thermal conductivity of the diamond films was ∼5.27[W/cm.K] measured by $3\omega$ method.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1994년도 춘계 학술발표 강연 및 논문 개요집
• /
• pp.131-131
• /
• 1994

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제25회 춘계학술대회
• /
• pp.69-73
• /
• 1997

Microwave Plasma assisted CVD (Chemical Vapor Deposition) and DC Plasma CVD were used to prepare thin and thick diamond film, respectively. Diamond coated silicon nitride and fiee standing diamond thick film were eroded by silicon carbide particles. The velocity of the solid particle was about 220m/sec. Phase transformation and the other crack formation were investigated by using Raman spectroscopy and microscopy.

• The Korean Journal of Ceramics
• /
• 제2권4호
• /
• pp.212-215
• /
• 1996

This paper focuses the strength and wear resistance of CVD diamond films. The strength of free-standing CVD diamond films synthesized by microwave plasm CVD, DC plasma CVD, RF plasma CVD and arc discharge plasma jet CVD has been measured by three-point bending test. The wear resistance of CVD diamod films has been evaluated by the pin-on-disk type testing. diamond films coated on the base of sintered tungsten carbide pin by hot filament CVD have been rubbed with a sintered diamond disk in muddy water. Volume removed wear of CVD diamond has been compared with stellite, WC alloy and bearing steel.