• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.843-853
• /
• 1997

The effect of dopant on microwave dielectric properties of (1-x)MgTiO3-xCaTiO3 ceramics, known to be used as microwave dielectric resonators for global positioning system and personal communication system, has been analyzed in terms of variations in defect concentrations and microstructural features with its addition. The addition of dopants was revealed to result in a significant change in the microstructure as well as defect concentration of the ceramics. For instance, the quality factor is proportional to sintered density of the ceramics by inversely proportional to grain size as well as vacancy concentration. Accordingly, it is believed that the dopant effect on the microwave dielectric properties should be separately analyzed with either microstructural change or the change in vacancy concentration.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.8
• /
• pp.335-339
• /
• 2002

Ba(Mgl-xCox)TaO3[BMCT] ceramics were prepared by the conventional mixed oxide method. The ceramics were sintered at the temperature of 1525~$1625^{\circ}C$ for 5hr. in air. The crystal structure of BMCT ceramics was investigated by the XRD. The microstructure of the specimens were observed by SEM. The Microwave dielectric properties of BMCT specimens were investigated as a function of composition and sintering temperature. All BMCT ceramics sintered over 1575$^{\circ}C$ were showed a polycrystalline complex perovskite structure. The density of BMCT (90/10) specimen sintered at $1575^{\circ}C$ was 7.75g/㎤. As the Co contents decreased, the ordering parameter of B-site in BMCT increased. In the case of the BMCT(90/10) ceramics sintered at $1575^{\circ}C$ for 5 hours, dielectric constant, quality factor and temperature coefficient of resonant frequency for microwave dielectrics application were a good value o( 25, 17, 845 at 10㎓ and +2.4 ppm/${\circ}$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.40 no.4
• /
• pp.340-345
• /
• 2003

B $i_2$ $O_3$-Ti $O_2$ composite dielectric ceramics have been prepared by a conventional solid state ceramic route. The composite ceramics were prepared with starting materials of different origin and the microwave dielectric properties were investigated. The sintered ceramics were characterized by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray microanalysis, Raman and microwave methods. Structural and microstructural analyses identified two separate phases: Ti $O_2$(rutile) and B $i_2$ $Ti_4$0$_{11}$. The separate grains of titania and bismuth titanate were distributed uniformly in the ceramic matrix. The composition 0.88Ti $O_2$-0.12B $i_2$ $Ti_4$ $O_{11}$ was found to have a Q$\times$f of 9300 GHz (measured at a frequency of 3.9 GHz), a temperature coefficient of frequency, $\tau$$_{cf}$ near zero and a high relative permittivity, $\varepsilon$r of 83. The microwave dielectric properties were measured down to 20$^{\circ}$K K. The quality factor increased on cooling the ceramic samples.les.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.10
• /
• pp.870-875
• /
• 2002

Ba(Zn$_1$-xCox)TaO$_3$[BZCT] ceramics were Prepared by the conventional mixed oxide method. The ceramics were sintered at the temperature of 1450∼1550$\^{C}$ for 5 hr in air. The crystal structure of BZCT ceramics was investigated by the XRD. The microstructure of the specimens were observed by SEM. The structural properties of BZCT specimens were investigated as a function of composition and sintering temperature. All BZCT ceramics sintered over 1550$\^{C}$ were showed a polycrystalline complek perovskite structure without second phases and any unreacted materials. The density of BZCT (70/30) specimen sintered at 1550$\^{C}$ was 6.31g/㎤. In the case of the BZCT(70/30) ceramics sintered at 1550$\^{C}$ for 5 hours, dielectric constant, qualify factor and temperature coefficient of resonant frequency for microwave dielectrics application were a good value of 29, 16,468 at 10㎓ and -4.4 ppm/$\^{C}$, respectively.

• Korean Journal of Crystallography
• /
• v.12 no.2
• /
• pp.81-87
• /
• 2001

We have studied the effect of sintering temperature and time on the cation ordering and second phase formation in Ba(Mg/sub 1/3/Nb/sub 2/3/)O₃(BMN) microwave ceramics by using transmission electron microscopy. The relationship between the structural-chemical behavior arid microwave dielectric properties has also been investigated. It is revealed that according to the sintering conditions the BMN ceramics show very diverse local ordering behavior, such as the development of domain twinning and "core-shell"-structured grains and the formation of local disordered domains, though having 1 : 2 cation ordering structure basically. The disordered structure is found in Mg-excess region. Such local chemical variation seems to be caused by the formation of BaNb₂O/sub 6/-like second phase in its neigh-boring grain boundary. The microwave dielectric quality factor of the ceramics decreases greatly with the increase of the structural-chemical inhomogeneity and diversity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.84-87
• /
• 2000

The microwave dielectric properties of complex perovskite-structured $Ba(Mg_{1/3}Ta_{2/3})O_3$ ceramics were investigated with calcining condition. The BMT ceramics were prepared by conventional mixed oxide method. Calcining conditions were $1200^{\circ}C$ for 10hr., $1300^{\circ}C$ for 2hr., and 5hr., respectively. And the specimens were sintered at $1650{\mu}m$. The structural and microwave properties of BMT ceramics were investigated by XRD, SEM and network analyzer. In the case of BMT ceramics calcined at $1300^{\circ}C$ for 5 hr., dielectric constant, quality factor and temperature coefficient of resonant frequency were 20.26, 31,144(at 1GHz), 6.11[ppm/$^{\circ}C$], respectively.

• Journal of the Korean Ceramic Society
• /
• v.44 no.5 s.300
• /
• pp.173-178
• /
• 2007

The microstructure and microwave dielectric properties of dolomite type borates, $CaZr(BO_3)_2$ ceramics prepared by conventional mixed oxide method were explored. The sintering temperature of $CaZr(BO_3)_2$ ceramics could be reduced from $1150^{\circ}C\;to\;925^{\circ}C$ with little amount of sintering additives. Microwave dielectric properties of 3 wt% $Bi_2O_3-CuO$ added $CaZr(BO_3)_2$ ceramics sintered at $925^{\circ}C$ were $K{\approx}10.4,\;Q{\times}f{\approx}80,000GHz\;and\;TCF{\approx}+2ppm/^{\circ}C$. Thus obtained LTCC tape was co-fired with Ag paste for compatibility test and revealed no sign of Ag reaction with the ceramics. Therefore, $CaZr(BO_3)_2$ ceramics is considered as a possible candidate material for low temperature co-fired multilayer devices.

• Proceedings of the KIEE Conference
• /
• 1993.11a
• /
• pp.181-184
• /
• 1993

Microwave characteristics of the system (Zr, Sn)$TiO_4$, ceramics within composition range X between 0.2 and 0.35 were investigated at 8GHz. For the improvement properties of (Zr, Sn)$TiO_4$, system, $Ta_2O_5$ and $WO_3$ addition in the range of 0.5 to 2.0wt% were investigated.

• Journal of Electrochemical Science and Technology
• /
• v.13 no.3
• /
• pp.390-397
• /
• 2022

The use of microwaves as the energy source for synthesis and sintering of ceramics offers substantial advantages compared to conventional gas-fired and electric resistance furnaces. Benefits include much shorter processing times and reaching the sintering temperature more quickly, resulting in superior final product quality. Most oxide ceramics poorly interact with microwave irradiation at low temperatures; thus, a more complex setup including a susceptor is needed, which makes the whole process very complicated. This investigation pursued a new approach, which enabled us to use microwave irradiation directly in poorly coupled oxides. In many solid-state electrochemical devices, the support is either metal or can be reduced to metal. Metal powders in the support can act as an internal susceptor and heat the entire cell. Then sufficient interaction of microwave irradiation and ceramic material can occur as the sample temperature increases. This microwave heating and exothermic reaction of oxidation of the support can sinter the ceramic very efficiently without any external susceptor. In this study, yttria stabilized zirconia (YSZ) and a Ni-YSZ cermet support were used as an example. The cermet was used as the support, and a YSZ electrolyte was coated and sintered directly using microwave irradiation without the use of any susceptor. The results were compared to a similar cell prepared using a conventional electric furnace. The leakage test and full cell power measurement results revealed a fully leak-free electrolyte. Scanning electron microscopy and density measurements show that microwave sintered samples have lower open porosity in the electrode support than conventional heat treatment. This technique offers an efficient way to directly use microwave irradiation to sinter thin film ceramics without a susceptor.

• Advances in materials Research
• /
• v.3 no.2
• /
• pp.105-116
• /
• 2014

The microwave dielectric properties of $CeO_2$ nanoparticles (0.5, 1.0 & 1.5wt%) doped $Mg_2TiO_4$ (MTO) ceramics have been investigated at cryogenic temperatures. The XRD patterns of the samples were refined using the full proof program reveal the inverse spinel structure without any secondary phases. The addition of $CeO_2$ nanoparticles lowered the sintering temperature with enhancement in density and grain size as compared to pure MTO ceramics. This is attributed to the higher sintering velocity of the fine particles. Further, the microwave dielectric properties of the MTO ceramics were measured at cryogenic temperatures in the temperature range of 6.5-295 K. It is observed that the loss tangent ($tan{\delta}$) of all the samples increased with temperature. However, the $CeO_2$ nanoparticles doped MTO ceramics manifested lower loss tangents as compared to the pure MTO ceramics. The loss tangents of the pure and MTO ceramics doped with 1.5 wt% of $CeO_2$ nanoparticles measured at 6.5K are found to be $6.6{\times}10^{-5}$ and $5.4{\times}10^{-5}$, respectively. The addition of $CeO_2$ nanoparticles did not cause any changes on the temperature stability of the MTO ceramics at cryogenic temperatures. On the other hand, the temperature coefficient of the permittivity increased with rise in temperature and with the wt% of $CeO_2$ nanoparticles. The obtained lower loss tangent values at cryogenic temperatures can be attributed to the decrease in both intrinsic and extrinsic losses in the MTO ceramics.