• 한국주조공학회지
• /
• 제13권1호
• /
• pp.50-61
• /
• 1993

Retained austenite in matrix of austempered ductile iron has been well-known as a parameter in controlling mechanical properties, but investigation to obtain quantitative relationship with mechanical properties lack. Therefore, this study executed austempering treatment at various temperatures on ductile iron alloyed with Mo, Ni, Cu. In consequence, microstructure of retained austenite transformed coarse, and quantity increased according as austempering temperature increased. After heat-treatment, microstructure of specimen alloyed with Ni was fine, and toughness improved. At austempering temperature up to $400^{\circ}C$, carbide precipitation started in retained austenite. In consequence, afforded cause of hardness increase, a lot of increase did not arise for coarse structure.

• 동력기계공학회지
• /
• 제14권2호
• /
• pp.84-89
• /
• 2010

The effect of forging condition on the microstructure and mechanical properties of 9Cr-1Mo heat-resisting steel was investigated. Microstructure of centrifugal casted 9Cr-1Mo heat resisting steel and forged heat resisting steel are consisted of martensite. With the increase of forging ratio, tensile strength and hardness increased, while elongation and impact value decreased. By increasing of forging starting temperature and finishing temperature, tensile strength and hardness increased, while elongation and impact value decreased. We obtained the optimum forging conditions as follow, forging ratio is 30%, forging starting temperature is $1200^{\circ}C$ and forging finishing temperature is $950^{\circ}C$.

• Steel and Composite Structures
• /
• 제17권6호
• /
• pp.825-834
• /
• 2014

This manuscript presents an experimental investigation on the effect of Multi-walled carbon nanotubes (MWCNTs) addition on the tensile, flexural and impact properties of woven Kevlar fabric reinforced epoxy composites. MWCNTs were dispersed in the epoxy resin by sonication technique and the samples were fabricated by hand layup laminating procedure. Scanning electron microscopy (SEM) was used to characterize the microstructure of produced samples. The effects of adding small amounts (${\leq}1%$) of MWCNT on the tensile, flexural and impact (Izod) behaviors of laminated composites were analyzed. Results revealed that MWCNTs enhanced the Young's modulus up to 20%, bending modulus up to 40%, and impact strength up to 45% in comparison with woven Kevlar fabric/epoxy composites. It was found that the maximum improvements in mechanical properties were happened for 0.5 wt.% MWCNT.

• 한국분말재료학회지
• /
• 제30권3호
• /
• pp.242-248
• /
• 2023

The Ag/WC electrical contacts were prepared via powder metallurgy using 60 wt% Ag, 40 wt% WC, and small amounts of Co₃O₄ with varying WC particle sizes. After the fabrication of the contact materials, microstructure observations confirmed that WC-1 had an average grain size (AGS) of 0.27 ㎛, and WC-2 had an AGS of 0.35 ㎛. The Ag matrix in WC-1 formed fine grains, whereas a significantly larger and continuous growth of the Ag matrix was observed in WC-2. This indicates the different flow behaviors of liquid Ag during the sintering process owing to the different WC sizes. The electrical conductivities of WC-1 and WC-2 were 47.8% and 60.4%, respectively, and had a significant influence on the Ag matrix. In particular, WC-2 exhibited extremely high electrical conductivity owing to its large and continuous Ag-grain matrix. The yield strengths of WC-1 and WC-2 after compression tests were 349.9 MPa and 280.7 MPa, respectively. The high yield strength of WC-1 can be attributed to the Hall-Petch effect, whereas the low yield strength of WC-2 can be explained by the high fraction of high-angle boundaries (HAB) between the WC grains. Furthermore, the relationships between the microstructure, electrical/mechanical properties, and deformation mechanisms were evaluated.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.375-379
• /
• 2014

Nanocrystalline TiAlN coatings were prepared by reactively sputtering TiAl metal target with $N_2$ gas. This was done using a magnetron sputtering system operated in DC and ICP (inductively coupled plasma) conditions at various power levels. The effect of ICP power (from 0 to 300 W) on the coating microstructure, corrosion and mechanical properties were systematically investigated using FE-SEM, AFM and nanoindentation. The results show that ICP power has a significant influence on coating microstructure and mechanical properties of TiAlN coatings. With increasing ICP power, the coating microstructure evolved from the columnar structure typical of DC sputtering processes to a highly dense one. Average grain size of TiAlN coatings decreased from 15.6 to 5.9 nm with increasing ICP power. The maximum nano-hardness (67.9 GPa) was obtained for the coatings deposited at 300 W of ICP power. The smoothest surface morphology (Ra roughness 5.1 nm) was obtained for the TiAlN coating sputtered at 300 W ICP power.

• 한국표면공학회지
• /
• 제56권5호
• /
• pp.335-340
• /
• 2023

Quinary component of 3㎛ thick Ti-Al-Si-Cu-N films were deposited onto WC-Co and Si wafer substrates by using an arc ion plating(AIP) system. In this study, the influence of copper(Cu) contents on the mechanical properties and microstructure of the films were investigated. The hardness of the films with 3.1 at.% Cu addition exhibited the hardness value of above 42 GPa due to the microstructural change as well as the solid-solution hardening. The instrumental analyses revealed that the deposited film with Cu content of 3.1 at.% was a nano-composites with nano-sized crystallites (5-7 nm in dia.) and a thin layer of amorphous Si₃N₄ phase.

• 한국분말재료학회지
• /
• 제2권1호
• /
• pp.36-43
• /
• 1995

Rapidly solidified and mechanically alloyed Al-Ti base alloys were prepared by gas atomization and attritor milling separately. The gas atomized and the mechanically alloyed powders were consolidated after preheating at $450^{\circ}C$, and then heat treated isochronally for 1 hour to observe the microstructures and to investigate the mechanical properties. Stable phases of precipitates in the Al-Ti-Si and the Al-Ti-Zr alloys were identified as DO22-$(Al,Si)_3Ti$ and $Do_{23}-Al_3(Ti, Zr)$ each. Among the alloys, the mechanically alloyed Al-l0Ti-2Si alloy showed superior thermal stability and mechanical properties at elevated temperature. The additions of third elements, such as Si and Zr, to Al-Ti alloys seemed to improve the mechnical properties remarkably by stabilizing the microstructure and the precipitate phases in the consolidated alloys.

• 한국세라믹학회지
• /
• 제43권8호
• /
• pp.469-471
• /
• 2006

The effects of $Cr_2O_3$ on the microstructural evolution and mechanical properties of $Al_2O_3$ polycrystalline were investigated. The microstructure of $Al_2O_3-Cr_2O_3$ composites (ruby) was carefully controlled in order to obtain dense and fine-grained ceramics, thereby improving their properties and reliability with respect to numerous applications related to semiconductor bonding technology. Ruby composites were produced by Ceramic Injection Molding (CIM) technology. Room temperature strength, hardness, Young's modulus and toughness were determined, as well as surface strengthening induced by thermal treatment and production of a fine-grained homogenous microstructure.

• 한국표면공학회지
• /
• 제45권3호
• /
• pp.123-129
• /
• 2012

Nanocrystalline CrN coatings were fabricated by DC and ICP (inductively coupled plasma) assisted magnetron sputtering techniques. The effect of ICP power, ranging from 0 to 500 W, on coating microstructure, preferred orientation mechanical properties were systematically investigated with HR-XRD, SEM, AFM and nanoindentation. The results show that ICP power has an significant influence on coating microstructure and mechanical properties of CrN coatings. With the increasing of ICP power, coating microstructure evolves from the columnar structure of DC process to a highly dense one. Grain size of CrN coatings were decreased from 11.7 nm to 6.6 nm with increase of ICP power. The maximum nanohardness of 23.0 GPa was obtained for the coatings deposited at ICP power of 500 W. Preferred orientation in CrN coatings also vary with ICP power, exerting an effective influence on film nanohardness.

• 한국생산제조학회지
• /
• 제7권3호
• /
• pp.61-67
• /
• 1998

To find out the reason of fracture, specimens were made from the fractured winding shaft and the mechanical properties as well as their microstructures were investigated. Several heat treatments. including caburizing and tempering were carried out to improve the microstructure, mechanical properties, fatigue crack propagation and rotating bending fatigue characteristics. Through these experiments, following conclusions were obtained. (1) Carburized and tempered specimens showed greatly improved mechanical properties including impact energy, hardness and strength. (2) The fatigue strength of the carburized and tempered specimens increased more than twice than that of the original fractured winding shaft. (3) Crack propagation of the carburized and tempered specimens were faster than that of the original fractured speciens under the same △K. However, it is believed that, in the early stage, the fatigue crack initiation and growth for the carburized and tempered specimen is more difficult.