• 한국표면공학회지
• /
• 제44권2호
• /
• pp.44-49
• /
• 2011

The films formed on AZ31B magnesium alloy were prepared from alkaline solution composed of potassium permanganate and sodium hydroxide. The immersion tests were carried out at the different concentration of sodium hydroxide and pre-treatment method in 5 minute. The morphology and the phase composition of the film were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The corrosion behavior of the film in 5.0% NaCl solution was evaluated using potentiodyanmic polarization. Open circuit potential in developing film was examined with time. The thin and transparent film was mainly composed of MgO and $Mg(OH)_2$. The film with the best corrosion resistance was obtained at $70^{\circ}C$ bath temperature, 1.6 M concentration of sodium hydroxide and chemical pre-treatment.

• Journal of Electrical Engineering and Technology
• /
• 제13권2호
• /
• pp.892-901
• /
• 2018

Because of excellent electrical properties, epoxy resin is widely used in packaging and casting power equipment. Moisture and temperature in the environment are inclined to seriously affect the insulation tolerance of epoxy resin. This work focuses on the aging characteristics of epoxy resin in hygrothermal environment. Scanning electron microscopy images show that there are micro-crack, micro-slit and holes inside aged samples. The moisture absorption process undergoes three equilibrium stages and it does not follow the Fick's second law. Observing the change of hydrogen bonds in the infrared spectra of the dried samples, it is found that chemically moisture absorption immerges when the physical moisture absorption entered the third equilibrium stage. By Debye equation to fit the imaginary part of the dielectric constant, it is concluded that the uniformity of water molecule has a great influence on the electrical conductivity loss. Furthermore, the polarization loss can be more easily affected by water molecules than small free molecules. After the aged samples being dried, their real and imaginary part of the dielectric constant descend, but their original electrical properties cannot completely restored. After chemical moisture absorption appears inside the material, the residual space charges increase significantly and the charge dissipation rate slow down obviously.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.105-106
• /
• 2006

The ferroelectric materials of the PZT, SBT attracted much attention for application to ferroelectric random access memory (FRAM) devices. Through the last decade, the lead zirconate titanate (PZT) is one of the most attractive perovskite-type materials for the ferroelectric products due to its higher remanant polarization and the ability to withstand higher coercive fields. FRAM has been currently receiving increasing attention for one of future memory devices due to its ideal memory properties such as non-volatility, high charge storage, and faster switching operations. In this study, we first applied the damascene process using chemical mechanical polishing (CMP) to the fabricate the $Pb_{1.1}(Zr_{0.52}Ti_{0.48})O_3$ thin film capacitor in order to solve the problems of plasma etching such as low etching profile and ion charging. The structural characteristics were compared with specimens before and after CMP process of PZT films. The scanning electron microscopy (SEM) analysis was performed to compare the morphology surface characteristics of $Pb_{1.1}(Zr_{0.52}Ti_{0.48})O_3$ capacitors. The densification by the vertical sidewall patterning and charging-free ferroelectric capacitor could be obtained by the damascene process without remarkable difference of the characteristics.

• Corrosion Science and Technology
• /
• 제19권1호
• /
• pp.8-15
• /
• 2020

In this paper, the efficiency and the inhibition mechanisms of cobalt salts (cobalt nitrate and cobalt-exchange silica Co/Si) for the corrosion protection of AA2024 were investigated in a neutral aqueous solution by using the electrochemical impedance spectroscopy (EIS) and polarization curves. The experimental measurements suggest that cobalt cation plays a role as a cathodic inhibitor. The efficiency of cobalt cation was important at the concentration range from 0.001 to 0.01 M. The formation of precipitates of oxides/hydroxides of cobalt on the surface at low inhibitor concentration was confirmed by the Scanning Electron Microscopy/Energy Dispersive X-Ray Spectroscopy (SEM/EDS) analysis. EIS measurements were also conducted for the AA2024 surface covered by water-based epoxy coating comprising Co/Si salt. The results obtained from exposure in the electrolyte demonstrated the improvement of the barrier and inhibition properties of the coating exposed in the electrolyte solution for a lengthy time. The SEM/EDS analysis in artificial scribes of the coating after salt spray testing revealed the release of cobalt cations in the coating defect to induce the barrier layer on the exposed AA2024 substrate.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.200-203
• /
• 2003

Ferroelectric europium-substitution $Bi_4Ti_3O_{12}$ thin films were fabricated by spin-coating onto a Pt/Ti/$SiO_2$/Si substrate. The $Bi_{3.25}Eu_{0.75}Ti_3O_{12}$ (BET) films have polycrystalline structure annealed at 700 C. We investigated that the influence of $Bi_4Ti_3O_{12}$ thin films by substituting for Bi ions with Bi ions using X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). From the XPS measurement, it was suggested that the stability of the metal-oxygen octahedral should be related to substitute for Bi ions with Eu ions at annealed $800^{\circ}C$. The BET thin films showed a large remanent polarization (2Pr) of $60.99C/cm^2$ at an applied voltage of 10 V. The BET thin films exhibited no significant degradation of switching charge at least up to $5{\times}10^9$ switching cycles at a frequency of 50 kHz.

• 한국정보전자통신기술학회논문지
• /
• 제1권2호
• /
• pp.27-32
• /
• 2008

A current research basically diverted towards an increase in the operational output with the minimization of the materials used, which ultimately scaled down the dimensions of ceramic electronic components. In this direction the nano-technology pave the revolutionary changes in particular the electronic industries. The applications of nano-sized particles or nano-sized materials are hence, playing a significant role for various purposes. The PZT(lead, zirconium, titanium) based ceramics which, are reported to be ferroelectric materials have their important applications in the areas of surface acoustic waves (SAW), filters, infrared detectors, actuators, ferroelectric random access memory, speakers, electronic switches etc. Moreover, these PZT materials possess the large electro mechanical coupling factor, large spontaneous polarization, low dielectric loss and low internal stress etc. Hence, keeping in view the unique properties of PZT piezoelectric ceramics we also tried to synthesize indigenously the small sized PZT ceramic powder in the laboratory by using the modified sol-gel approach. In this paper, propyl alcohol based sol-gel method was used for preparation of PZT piezoelectric ceramic. The powder obtained by this sol-gel process was calcined and sintering to reach a pyrochlore-free crystal phase. The characterization of synthesized material was carried out by the XRD analysis and the surface morphology was determined by high resolution scanning electron microscopy.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.290-291
• /
• 2006

The effect of praseodymium substitution on the ferroelectric properties of $Bi_4Ti_3O_{12}$ thin films have been investigated. Ferroelectric Pr-substituted $Bi_4Ti_3O_{12}$ thin films were fabricated by chemical solution deposition onto Pt/Ti/$SiO_2$/Si substrates. The structure and morphology of the films were analyzed using Xray diffraction, and scanning electron microscopy, respectively. About 200-nm-thick BPT films grown at $720^{\circ}C$ exhibited a polycrystalline structure and showed excellent ferroelectric properties with a remanent polarization ($2P_r$) of $28.21\;{\mu}C/cm^2$ at an applied voltage of 5 V. The films a1so demonstrate fatigue-free behavior up to $10^{11}$ read/write switching cycles with 1 MHz bipolar pulses at an electric field of ${\pm}5\;V$.

• 한국재료학회지
• /
• 제18권1호
• /
• pp.22-25
• /
• 2008

In this study, calcium titanate $(CaTiO_3)$ gel was prepared by mixing calcium nitrate and titanium isopropoxide in 2-methoxy-ethanol. $CaTiO_3$ gel was single-layer coated on Ti-6Al-4V using a sol-gel dip-coating technique. The coating was calcined at $750^{\circ}C$ in air by utilizing a very slow heating rate of $2^{\circ}C/min$. The crystalline phases of the coating were characterized by x-ray diffraction using a slow scan rate of $1^{\circ}/min$. The morphology of the coating was analyzed by scanning electron microscopy. The corrosion behavior of Ti-6Al-4V samples coated with $CaTiO_3$ films were tested in an artificial saliva solution by potentiodynamic polarization and were quantified by the Tafel extrapolation method. The electrochemical parameters showed a considerable increase in the corrosion resistance for the $CaTiO_3$-coated Ti-6Al-4V samples compared to bare substrates.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.177-178
• /
• 2012

In this experiment, post-nitriding treatment has been performed at $400^{\circ}C$ on AISI 316 stainless steel which is plasma carburized previously at $430^{\circ}C$ for 15 hours. Plasma nitriding was implemented on AISI 316 stainless steel at various gas compositions (25% N2, 50% N2 and 75% N2) for 4 hours. Additionally, during post nitriding Ar gas was used with H2 and N2 to observe the improvement of treatment. After treatment, the behavior of the hybrid layer was investigated by optical microscopy, X-ray diffraction, and micro-hardness testing. Potentiodynamic polarization test was also used to evaluate the corrosion resistance of the samples. Meanwhile, it was found that the surface hardness increased with increasing the nitrogen gas content. Also small percentage of Ar gas was introduced in the post nitriding process which improved the hardness of the hardened layer but reduces the corrosion resistance compared with the carburized sample. The experiment revealed that AISI 316L stainless steel showed better hardness and excellent corrosion resistance compared with the carburized sample, when 75% N2 gas was used during the post nitriding treatment. Also addition of Ar gas during post nitriding treatment were degraded the corrosion resistance of the sample compared with the carburized sample.

• 대한금속재료학회지
• /
• 제48권3호
• /
• pp.218-224
• /
• 2010

Direct copper electroplating on Mg alloy AZ31B was carried out in a traditional pyrophosphate copper bath containing potassium fluoride. Electrochemical impedance spectroscopy and polarization methods were used to study the effects of added potassium fluoride on electrochemical behavior. The chemical state of magnesium alloy in the electroplating bath was analyzed by X-ray photoelectron spectroscopy. Adhesion of the copper electroplated layer was also tested. Due to the added potassium fluoride, a magnesium fluoride film was formed in the pyrophosphate copper bath. This fluoride film inhibits dissolution of Mg alloy and enables to electroplate copper directly on it. A dense copper layer was formed on the Mg alloy. Moreover, this copper layer has a good adhesion with Mg alloy substrate.