• 펄프종이기술
• /
• 제41권5호
• /
• pp.26-32
• /
• 2009

As a part of utilizing the nanocellulose (NC) from lignocellulosic components of wood biomass, this paper reports preliminary results on the products of sulfuric acid hydrolysis. The purpose of this study was to investigate the morphology of both NC and micro-sized cellulose fiber (MCF) isolated by acid hydrolysis from commercial microcrystalline cellulose (MCC). Field emission.scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM) were employed to observe the acid hydrolysis suspension, NC, and MCF. The electron microscopy observations showed that the acid hydrolysis suspension, before separation into NC and MCF by centrifugation, was composed of nano-sized NCs and micro-sized MCFs. The morphology of isolated NCs was a whisker form of rod-like NCs. Measurements of individual NCs using TEM indicated dimensions of 6.96$\pm$0.87 nm wide by 178$\pm$55 nm long. Observations of the MCFs showed that most of the MCC particles had de-fibered into relatively long fibers with a diameter of 3-9 ${\mu}m$, depending on the degree of acid hydrolysis. These results suggest that proper technologies are required to effectively realize the potentials of both NCs and MCFs.

• Journal of the Korean Wood Science and Technology
• /
• 제52권3호
• /
• pp.205-220
• /
• 2024

Various polylactic acid (PLA) blends were reinforced with untreated or silane-treated micro-sized cellulose fiber (MCF), successfully prepared as 3D printing filaments and then printed using a fused filament fabrication (FFF) 3D printer. In this study, we focused on developing 3D-printed MCF/PLA composites through silane treatment of MCF and investigating the effect of silane treatment on the various properties of FFF 3D-printed composites. Fourier transform infrared spectra confirmed the increase in hydrophobic properties of silane-treated MCF by showing the new absorption peaks at 1,100 cm^-1, 1,030 cm^-1, and 815 cm^-1 representing C-NH₂, Si-O-Si, and Si-CH₂ bonds, respectively. In scanning electron microscope images of silane-treated MCF filled PLA composites, the improved interfacial adhesion between MCF and PLA matrix was observed. The mechanical properties of the 3D-printed MCF/PLA composites with silane-treated MCF were improved compared to those of the 3D-printed MCF/PLA composites with untreated MCF. In particular, the highest tensile and flexural modulus values were observed for S-MCF10 (5,784.77 MPa) and S-MCF5 (2,441.67 MPa), respectively. The thermal stability of silane-treated MCF was enhanced by delaying the initial thermal decomposition temperature compared to untreated MCF. The thermal decomposition temperature difference at T₉₅ was around 26℃. This study suggests that the effect of silane treatment on the 3D-printed MCF/PLA composites is effective and promising.