• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.81-84
• /
• 2005

In order to effectively resist seismic loads, coupling beams must be sufficiently stiff, strong and posses a stable load-deflection hysteretic response. This paper reports experimental data on the seismic performance of precast HPFRCC coupling beams with variable details. Precast HPFRCC coupling beam was tested to evaluate their failure modes. shear behavior, micro crack pattern and energy dissipation. Based on the experimental results, precast coupling beam with diagonal and rhombic details offer greater performance and ductility than coupling beam with normal detail.

• Journal of the Korea Concrete Institute
• /
• v.12 no.3
• /
• pp.67-75
• /
• 2000

It was well recognized that the damages associated mainly with the aging of civil infrastructures were one of very serious problems for assurance of safety and reliability. Recently carbon fiber sheet(CFS) has been widely used for reinforcement and rehabilitation of damaged concrete beam. However, the fundamental mechanism of load transfer and its load-resistant for carbon fiber sheet reinforced concrete are not fully understood. In this study, three point bending test has been carried out to understand the damage progress and the micro-failure mechanism of CFS reinforced mortars. For this purpose, four different types of specimens are used, that is, mortar, steel bar reinforced mortar, CFS reinforced mortar, and steel bar and CFS reinforced morter. Acoustic Emission(AE) technique was used to evaluate the characteristics of damage progress and the failure mechanism of specimens. in addition, two-dimensional AE source location was also performed to monitor crack initiation and propagation processes for these specimens.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.68-68
• /
• 2010

To reduce PV manufacturing costs, the thickness of solar cell is getting thinner. Bow is shown after cooling down the temperature of solder cell. It happens because of different thermal expansion coefficients of different metals. Bowed cell can make micro crack while module processing and it can drop off efficiency of PV module. As thinner solar cell is produced, the thickness of ribbon should be concerned to prevent extra bow. In this paper we investigate the contrast of deflection when we solder different thickness of ribbons on same solar cell. This approach would help to find out the optical thickness of ribbon for particular thickness of solar cell later on.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.1136-1141
• /
• 2003

Among various methods to manufacture the PDP barrier ribs, the pressing and the roll forming methods are simple and economical because they form the ribs by utilizing the plastic flow of the green tape in a relatively short time without generating air-polluting dusts. In the present study, the roll forming method was investigated by experiments as well as numerical analyses and in result the groove roll and the preform were designed. The effect of draft angle, comer radius, and initial thickness of the green tape on the plastic flow was examined by a series of parametric studies. The preform was recommended to ease the plastic flow into the grooves and to avoid the occurrence of crack during rolling and sintering processes.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.1349-1354
• /
• 2003

Ultrasonic Machining process is an efficient and economical means of precision machining on glass and ceramic materials. However, the mechanics of the process with respect to crack initiation and propagation, and stress development in the ceramic workpiece subsurface are still not well understood. In this research, we investigate the basic mechanism of chemical assisted ultrasonic machining(CUSM) of glass through the experimental approach. For the purpose of this study, we designed and fabricated the desktop micro ultrasonic machine. The feed is controlled precisely by using the constant load control system. During the machining experiment, the effects of HF(hydrofluoric acid) characteristics and machining condition on the surface roughness and the material removal rate are measured and compared.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.1
• /
• pp.80-85
• /
• 2007

High speed cutting is a machining process which cuts materials with the fast movement and rotation of a spindle in a machine tool. High speed cutting leaves a plastically deformed layer on the machined surface. This deformed layer affects in various forms to the surface roughness of machined parts such as the dimensional instability, the micro crack. The surface roughness is called surface integrity which is very important in precision cutting. This paper aims to study on the machined surfaces characteristics of aluminum alloy and brass by AFM(Atomic force microscope) measurement. The objective is contribution to ultra- precision cutting by exhibit foundation data of surface roughness and tool wear when parts are cutting with diamond tool at the factory.

• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.6
• /
• pp.724-730
• /
• 2006

Fracture behavior of brittle solids is closely related to microcracking. A meso-scale analysis method using the natural element method is proposed for the analysis of brittle microcracking solids. The microcracking is assumed to occur along Voronoi edges in the Voronoi diagram generated using the nodal points as the generators. The mechanical effect of microcracks is considered by controlling the material constants in the neighborhood of the microcracks. The meso-analysis method is applied to the simulation of the microcracking behaviors of brittle solids subjected to tensile macrostress. The method is also applied to the analysis of the propagation of a macrocrack accompanied by the coalescence with microcracks formed near the macrocrack-tip.

• Computers and Concrete
• /
• v.1 no.4
• /
• pp.371-388
• /
• 2004

Our objective is to model static multi-cracking processes in concrete. The explicit dynamic relaxation (DR) method, which gives the solutions of non-linear static problems on the basis of the steady-state conditions of a critically damped explicit transient solution, is chosen to deal with the high geometric and material non-linearities stemming from such a complex fracture problem. One of the common difficulties of the DR method is its slow convergence rate when non-monotonic spectral response is involved. A modified concept that is distinct from the standard DR method is introduced to tackle this problem. The methodology is validated against the stable three point bending test on notched concrete beams of different sizes. The simulations accurately predict the experimental load-displacement curves. The size effect is caught naturally as a result of the calculation. Micro-cracking and non-uniform crack propagation across the fracture surface also come out directly from the 3D simulations.

• 제어로봇시스템학회:학술대회논문집
• /
• 1995.10a
• /
• pp.142-145
• /
• 1995

It is important from prevention of the malfunction and an important accident by the failuer, to detect a failuer in revolution devices. The acoustic emission(AE) method is expected as means that defects an abnormal phenomenon of revolution devices earlily and utilized. Although a research example by the AE method is reported regarding a gears, little reserch has been conducted using the AE method for running gears in a bending fatigue process of spur gear teeth. Therefore, in this report, with two micro AE sensors attached to the side of the gear, AE was measured in a bending fatigue process of a carburizing gear by using the power circurating-type machine and AE source location in gear teeth were required. By various analysis in these data, the AE characteristics in the fatigue damaging process of the gear tooth were determined.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.265-271
• /
• 1998

High temperature wear behavior of plasma sprayed zirconia based coating sealing with zirconia sol were investigated for high temperature wear resistance application. The zirconia powders containing 2.5, 5.0, 7.5, 10.0 mol% of MoS$_2$, $Fe_2O_3$ for plasma spray were made by spray drying method. As-sprayed coating was sealed by zirconia-sol to fill up the pore and crack in coating. wear test were performed at temperature ranges from room temperature to 600$\circ$C. The microstructural changes of before and after sealing process were examined by SEM, XRD and EPMA. After sealing process, the porosity was decreased and micro-hardness was increased. The wear properties of coating after sealing process were improved by sealing of pores and cracks. The behavior of wear amount and coefficient of friction were same tendency to before sealing process.