• Korean Journal of Materials Research
• /
• v.23 no.4
• /
• pp.246-249
• /
• 2013

Nano-sized ${\beta}$-SiC nanoparticles were synthesized combined with a sol-gel process and a carbothermal process. TEOS and carbon black were used as starting materials for the silicon source and carbon source, respectively. $SiO_2$ nanoparticles were synthesized using a sol-gel technique (Stober process) combined with hydrolysis and condensation. The size of the particles could be controlled by manipulating the relative rates of the hydrolysis and condensation reactions of tetraethyl orthosilicate (TEOS) within the micro-emulsion. The average particle size and morphology of synthesized silicon dioxide was about 100nm and spherical, respectively. The average particles size and morphology of the used carbon black powders was about 20nm and spherical, respectively. The molar ratio of silicon dioxide and carbon black was fixed to 1:3 in the preparation of each combination. $SiO_2$ and carbon black powders were mixed in ethanol and ball-milled for 12 h. After mixing, the slurries were dried at $80^{\circ}C$ in an oven. The dried powder mixtures were placed in alumina crucibles and synthesized in a tube furnace at $1400{\sim}1500^{\circ}C$ for 4 h with a heating rate of $10^{\circ}C$/min under flowing Ar gas (160 cc/min) and furnace cooling down to room temperature. SiC nanoparticles were characterized by XRD, TEM, and SAED. The XRD results showed that high purity beta silicon carbide with excellent crystallinity was synthesized. TEM revealed that the powders are spherical shape nanoparticles with diameters ranging from 15 to 30 nm with a narrow distribution.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.560-565
• /
• 2010

Nano laminated bulk $Ti_3SiC_2$ was synthesized by hot press process using TiCx/Si powder mixture at the temperature range of $1300^{\circ}C\sim1500^{\circ}C$. pure $Ti_3SiC_2$ was synthesized by a hot pressing above $1400^{\circ}C$, while unreacted TiCx were remained in bulk $Ti_3SiC_2$ which synthesized below $1400^{\circ}C$. The sintering density of bulk $Ti_3SiC_2$ were varied with the amount of TiCx. It was found that the mechanical properties and micro structures of bulk $Ti_3SiC_2$ were closely related to the amounts of TiCx which was controlled by the hot pressing temperature. The TiCx increase the flexural strength of bulk $Ti_3SiC_2$, while the fracture toughness and thermal shock resistance of bulk $Ti_3SiC_2$ were decreased with the content of TiCx. The plastic deformations of bulk $Ti_3SiC_2$ were appeared above $1000^{\circ}C$.