• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.194.1-194.1
• /
• 2016

The present study investigated the effect of zincate treatment time on the dissolution behavior and the deposition of copper by immersion process and electroplating process on AZ31 Mg alloy substrate in a copper pyrophosphate bath. Without zincate pretreatment, the AZ31 Mg substrate quickly dissolved in the copper pyrophosphate solution although an external cathodic current was applied. The copper layers deposited on non-zincate treated AZ31 Mg alloy substrate by both immersion and electroplating processes showed very porous structure and very poor adhesion. With increasing zincate treatment time up to 2 min, the dissolution of AZ31 substrate in pyrophosphate solution rapidly decreased and the deposited copper layer was less porous and exhibited stronger adhesion. The immersion of AZ31 Mg sample in zincate solution for 5 min was found as a critical time for producing a non-porous and adherent electrodeposited copper layer on AZ31 Mg alloy. The optimum zincating time can be determined by observing the open circuit potential (OCP) of AZ31 Mg alloy samples in a copper pyrophosphate electroplating bath. The OCP reached a stable value of about -0.10 V (vs. SCE) after 5 min of immersion in the copper pyrophosphate electroplating solution.

• Korean Journal of Materials Research
• /
• v.31 no.11
• /
• pp.642-648
• /
• 2021

The precipitation effect of Al-6%Si-0.4%Mg-0.9%Cu-(Ti) alloy (in wt.%) after various heat treatments was studied using a laser flash device (LFA) and differential scanning calorimetry (DSC). Solid solution treatment was performed at 535 ℃ for 6 h, followed by water cooling, and samples were artificially aged in air at 180 ℃ and 220 ℃ for 5 h. The titanium-free alloy Al-6%Si-0.4%Mg-0.9%Cu showed higher thermal diffusivity than did the Al-6%Si-0.4%Mg-0.9%Cu-0.2%Ti alloy over the entire temperature range. In the temperature ranges below 200 ℃ and above 300 ℃, the value of thermal diffusivity decreased with increasing temperature. As the sample temperature increased between 200 ℃ and 400 ℃, phase precipitation occurred. From the results of DSC analysis, the temperature dependence of the change in thermal diffusivity in the temperature range between 200 ℃ and 400 ℃ was strongly influenced by the precipitation of θ'-Al₂Cu, β'-Mg₂Si, and Si phases. The most important factor in the temperature dependence of thermal diffusivity was Si precipitation.

• Journal of Powder Materials
• /
• v.12 no.4 s.51
• /
• pp.303-308
• /
• 2005

Various kinds of Mg-Zn-Ca base alloys were rapidly quenched via melt spinning process. The meltspun ternary and quaternary alloy ribbons were heat-treated, and then the effects of additional elements on age hardening behavior and phase change of precipitates were investigated using Vickers hardness tester, XRD, and TEM equipped with EDS system. In ternary alloys, age hardening was mostly due to the distribution of $Mg_6Ca_2Zn_3$ and $Mg_2Ca$. The stable phases of precipitates were varied according to the aging temperature and the alloy composition. With the increase of Ca content, $Mg_2Ca$ precipitates were detected more than $Mg_6Ca_2Zn_3$ precipitates. In quaternary alloys, the precipitates taken from Mg-Zn-Ca-Co were identified as new quaternary phase, whereas those taken from Mg-Zn-Ca-Zr as MgZnCa containing Zr. In general, the ternary alloy showed higher peak hardness and thermal stability than the quaternary considering the total amounts of the solutes. It implies that the structure of precipitate should be controlled to have the coherent interface with the Mg matrix.

• Journal of Powder Materials
• /
• v.14 no.6
• /
• pp.372-379
• /
• 2007

The microstructure, mechanical and electrochemical properties of plasma electrolytic coatings (PEO) coatings on Mg-4.3 wt%Zn-1.0 wt%Y and Mg-1.0 wt%Zn-2.0 wt%Y alloys prepared by gas atomization, followed by compaction at 320 for 10 min under the pressure of 700 MPa and sintering at 380 and 420 respectively for 24 h, were investigated, which was compared with the cast Mg-1.0 wt%Zn alloy. All coatings consisting of MgO and $Mg_2SiO_4$ oxides showed porous and coarse surface features with some volcano top-like pores distributed disorderly and cracks between pores. In particular, the surface of coatings on Mg-1.0 wt%Zn-2.0 wt%Y alloy showed smaller area of pores and cracks compared to the Mg-4.3 wt%Zn-1.0 wt%Y and Mg-1.0 wt%Zn alloys. The cross section micro-hardness of coatings on the gas atomized Mg-Zn-Y alloys was higher than that on the cast Mg-1.0 wt%Zn alloy. Additionally, the coated Mg-1.0 wt%Zn-2.0 wt%Y alloy exhibited the best corrosion resistance in 3.5%NaCl solution. It could be concluded that the addition of Y has a beneficial effect on the formation of protective and hard coatings on Mg alloys by plasma electrolytic oxidation treatment.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.1327-1328
• /
• 2013

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.142-142
• /
• 2007

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.577-582
• /
• 2002

The solidification cracking susceptibilities of AI-Mg-Si alloy laser welds were assessed using the self-restraint tapered specimen crack test. The cracking susceptibility of 6061 and 6082 Al-Mg-Si alloy laser welds was substantially reduced when the filler wire containing high Si such as Al-12 wt.% Si (4047A) was used. The amount of eutectic was observed to affect the solidification cracking of Al-Mg-Si alloy laser welds. Abundant eutectic seems to heal the cracking and reduces the cracking susceptibility, while an initial increase in eutectic liquid leads to the increased cracking tendency.

• Journal of Power System Engineering
• /
• v.5 no.4
• /
• pp.74-81
• /
• 2001

The infiltration behavior of molten Al-alloy, microstructures, hardness, and the interfacial reactions of $SiC_p/Al$ composites fabricated by the pressureless infiltration technique were investigated. It was made clear that both the weight fraction of SiC reinforcement and additive Mg content considerably influenced on the infiltration behavior of the molten Al-alloy matrix. Complete infiltration of molten Al-alloy achieved under the conditions that weight fraction of SiC content is more than 30wt%, and additive Mg content is more than 9wt%. Interfacial region of Al-alloy matrix and SiC reinforcement phase, $Mg_2Si$ was formed by the reaction between Mg and SiC. Another reaction product AlN was also formed by the reaction between Al-alloy matrix and gas atmosphere nitrogen.

• Laser Solutions
• /
• v.17 no.1
• /
• pp.7-12
• /
• 2014

The dissimilar welding between magnesium alloy and steel sheet was required in automobile industry to increase the strength of the dissimilar joints. Laser brazing is one of the good joining processes for Mg- steel dissimilar joint. In this study, AZ31 magnesium alloy and Zn coated steel dissimilar joint was brazed using diode direct laser with Mg600 filler wire and Superior #21 flux. The wetting of Mg filler wire on Zn coating was very good because of the formation of eutectic phase with low melting temperature. The strength of the brazed joint between AZ31 magnesium alloy and Zn coated steel was 131.3N/mm. The fracture occurred at brazement.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1264-1265
• /
• 2006

Study about the feasibility and effect of high-energy ball milling on a specific Mg alloy under protection medium of alcohol was presented via comparing with conventional vacuum milling. More fine particles with wider powder size distribution but more irregular shape were shown of the powder milled under alcohol. No obvious oxide was revealed from the two kinds of Mg alloy powders with limited milling time. And since slip induced in a preferential direction, the (002) texture was formed in the Mg alloy powders at the initial stage of alcohol milling. More O and Fe contaminants were introduced into the powders milled under alcohol according to the EDS analysis.