• 한국주조공학회지
• /
• 제17권5호
• /
• pp.502-509
• /
• 1997

The mechanical behavior and microstructural evolution in the ignition-proof Mg-Zn-Ca-Zr alloy produced by the semisolid squeeze casting are clarified and the mechanical properties are also compared with those of squeeze cast Mg-Zn-Ca-Zr alloy. The tensile strength and elongation increase slightly as the solid fraction depending on temperature decreases, while the 0.2% proof stress decreases. The size of primary crystal increases with increasing holding time. The tensile strength and 0.2% proof stress of the semi-solid squeeze cast Mg-Zn-Ca-Zr alloy decrease as the size of primary crystal increases, indicating the dependence of strength on the size of primary crystal. The elongation of the semi-solid squeeze cast Mg-Zn-Ca-Zr alloy is two times as large as the squeeze cast Mg-Zn-Ca-Zr alloy and the tensile strength is unchanged despite the growth of primary crystal, resulting from the refining of the melted ${\alpha}Mg$ phase and the brittle eutectic compound as well as the reduction of solidification shrinkage and porosities.

• 한국주조공학회지
• /
• 제29권5호
• /
• pp.213-219
• /
• 2009

Optimum conditions for production of semi-solid Al-Zn-Mg alloy billets was carried out by the Taguchi design method. And, Al-Zn-Mg alloy billets contained Sc (free, 0.1 and 0.3 mass %) were fabricated at optimum conditions. Evolution of microstructure in semi-solid state was investigated through various liquid fractions, holding times and holding temperatures. The Al-Zn-Mg alloy billets reheated at $615^{\circ}C$ during 30min are grain growth and it was fractured due to increasing liquid fraction before quenching. And, during reheating up to $600^{\circ}C$, grain growth of Al-Zn-Mg alloy billets contained Sc (0.1 and 0.3 mass %) was not occurred in comparison with those of Al-Zn-Mg alloy without Sc. It was thought that $Al_3Sc$ phases have a pinning effect in grain boundary and Sc content of 0.1 mass% is able to inhibit grain growth effectively through reheating process.

• 열처리공학회지
• /
• 제19권5호
• /
• pp.257-261
• /
• 2006

Scandium(Sc) in Al-Zn-Mg-Cu based Al alloy on precipitation phenomenon was compared to a 7001(Al-7.2%Zn-3.2%Mg-1.8%Cu) Al alloy. GP zone and ${\eta}^{\prime}$ phases were the main strengthening phases at low aging temperature under $100^{\circ}C$, but ${\eta}^{\prime}$ and $Al_3Sc$ phases were the main strengthening phases at high aging temperature above $1600^{\circ}C$ in Sc added 7000(Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr) Al alloy. With the addition of 0.1%Sc in 7000 Al alloy, the activation energy for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phase decreased compared to the 7001 Al alloy. This result indicates that the Sc accelerated the precipitation for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phases in 7000 Al alloy. Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr-0.1 Sc alloy has higher strength than 7001 Al alloy, which has high strength.

• 한국정밀공학회지
• /
• 제19권10호
• /
• pp.77-83
• /
• 2002

Magnesium alloys casting are gaining increased acceptance in the automotive and electronic industeries and die casting is the most efficient method of manufacturing such mass produced parts. This study has been investigated the microstructures and mechanical properties of Mg-9Al-lZn alloy fabricated by die casting process for development of air bag case. The microstructure of die casted specimen were composed of pro-eutectic magnesium solid solution and $\beta$(Mg17Al12) precipitates. The tensile strength of as-fabricated Mg-9Al-lZn alloy revealed 231.4MPa. It was found that Mg-9Al-lZn alloy have good corrosion resistance in electrochemical polarization test.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1043-1044
• /
• 2006

Compositional dependence of corrosion behavior of rapidly solidified Mg-rich Mg-Zn-Y alloys in NaCl aqueous solution has been investigated. Mg-Zn-Y ternary alloys containing small amounts of Zn exhibited low corrosion rate, although the $Mg_{98}Y_2$ (at. %) binary alloy showed severe corrosion with violet evolution of hydrogen. The alloy with highest corrosion-resistance was $Mg_{97.25}Zn_{0.75_Y_2$, its corrosion rate was about 1 mm year-1 in 0.17 M (1.0 wt. %) NaCl solution. $Mg_{97.25}Zn_{0.75}Y_2$ alloy exhibited passive region in anodic polarization curves when immersed in NaCl solution. Rapidly solidification and small amount of Zn addition may bring about an increase in electrochemical homogeneity of Mg-Zn-Y alloys, resulting in enhancement of corrosion resistance.

• 한국재료학회지
• /
• 제26권11호
• /
• pp.628-634
• /
• 2016

The cold rolling workability and mechanical properties of two new alloys, designed and cast Al-5.5Mg-2.9Si and Al-7Mg-0.9Zn alloys, were investigated in detail. The two alloy sheets of 4 mm thickness, 30 mm width and 100 mm length were reduced to a thickness of 1 mm by multi-pass rolling at ambient temperature. The rolling workability was better for the Al-7Mg-0.9Zn alloy than for the Al-5.5Mg-2.9Si alloy; in case of the former alloy, edge cracks began to occur at 50% rolling reduction, and their number and length increased with rolling reduction; however, in the latter alloy, the sheets did not have any cracks even at higher rolling reduction. The mechanical properties of tensile strength and elongation were also better in the Al-7Mg-0.9Zn alloy than in Al-5.5Mg-2.9Si alloy. Work hardening ability after cold rolling was also higher in the Al-7Mg-0.9Zn alloy than in the Al-5.5Mg-2.9Si alloy. At the same time, the texture development was very similar for both alloys; typical rolling texture developed in both alloys. These differences in the two alloys can primarily be explained by the existence of precipitates of $Mg_2Si$. It is concluded that the Al-7Mg-0.9Zn alloy is better than the Al-5.5Mg-2.9Si alloy in terms of mechanical properties.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 추계총회 및 학술대회 논문집
• /
• pp.15-15
• /
• 2012

Mg(1-4)Zn 이원계 압출재 및 Mg5Sn(1-4)Zn 삼원계 압출재의 부식거동을 3.5 % NaCl 용액에서 다양한 전기화학기법을 이용하여 평가하였다. 이원계 합금에 대한 연구결과, Zn 함량 증가에 따라 Mg 모재의 부동태화가 촉진되었고 동시에 수소발생속도가 증가하였으며 그 결과 부식전위의 상승이 관찰되었다. 그러나 Zn 함량 증가에 따른 부동태화 효과보다 수소발생 증가 효과가 우세하므로 결과적으로 Zn 함량 증가에 따라 부식속도는 증가하였다. Mg5Sn(1-4)Zn 삼원계 합금에 대한 부식시험 결과, Mg5Sn2Zn 합금이 가장 낮은 부식속도 및 우수한 부동태화를 나타내었으며 이는 합금원소 Sn의 수소발생속도 감소효과와 합금원소 Zn의 부동태화 효과의 상호작용에 의한 것으로 사료된다.

• 한국주조공학회지
• /
• 제29권6호
• /
• pp.265-269
• /
• 2009

The optimum RRA heat treating conditions and SCC (stress corrosion cracking) resistance of semi-solid Al-Zn-Mg-Cu alloy fabricated by inclined cooling plate were compared with those of conventional mould cast alloys. The non-stirring method characterized by using a cooling plate can effectively eliminate dendritic structure and form a fine globular semisolid microstructure in as-cast Al-Zn-Mg-Cu alloy and the SCC resistance of semi-solid Al-Zn-Mg-Cu alloy was higher than that of conventional mold cast alloy. Also, after retrogressed treatment at RRA heat treatment of semi-solid Al-Zn-Mg-Cu alloy, retrogressed treatment time has increased more than 10 minutes at $180^{\circ}C$ to recovery the T6 heat treatment strength.

• 한국재료학회지
• /
• 제5권6호
• /
• pp.682-689
• /
• 1995

Mg-Zn합금계의 입자미세화를 위하여 0.5-6 wt.% 조성범위의 Cu 및 Si를 첨가하였다. 합 잉곳트는 4 $\times$ $10^{-4}$ Torr의 진공의 BN을 내벽에 바른 석영관내에서 제조하였다. 제조된 합금을 435$^{\circ}C$에서 8시간 용체화처리한 후 결정립크기와 경도를 측정하였다. 측정결과 Mg-6wt.%Zn합금의 입자미세효과는 Cu가 2wt.%첨가될때, Si은 1.5wt.%가 첨가될 때가 최적의 조건이었다. Mg-6wt.% Zn과 Mg-6wt.%Zn-2wt.%Cu 및 Mg-6wt.%Zn-1.5wt.%Si합금을 시효열처리하여 시효거동을 조사하였다. 입자미세화에 의한 경도증가효과는 Mg-Zn-Cu합금계에서 크게 나타났으며 시효에 의한 경도증가 효과는 Mg-Zn-또합금계에서 크게 나타났다.

• 한국기계기술학회지
• /
• 제20권6호
• /
• pp.818-823
• /
• 2018

In this study, the effect of pre-aging treatment for inhibition of natural aging of Al-4.8Zn-1.3Mg alloy by extrusion process was investigated. Firstly, the as-cast microstructure of Al-4.8Zn-1.3Mg alloy billet and its evolution during homogenization($460^{\circ}C$, $4h+510^{\circ}C$, 5h) were investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), hardness analysis. The as-cast microstructures of Al-4.8Zn-1.3Mg alloy reveal $Mg_2Zn$, $Al_5Cu$, $Al_{13}Cu$ formed between dendrities. After homogenization, MgZn, $Al_4Cu$, $Al_{13}Cu$ phases precipitated into the matrix. In addition, standard deviation of homogenized billet was improved than as-cast billet from 2.62 to 0.99. According to pre-aging($100^{\circ}C$, 1h) Al-4.8Zn-1.3Mg alloy by extrusion process, yield strength and tensile strength deviation improved more than condition by natural aging.