• Corrosion Science and Technology
• /
• 제15권3호
• /
• pp.120-124
• /
• 2016

The effect of alloying element Ca (0, 1, and 2 wt%) on corrosion resistance and bioactivity of the as-received and anodized surface of rolled plate AM60 alloys was investigated. A plasma electrolytic oxidation (PEO) was carried out to form anodic oxide film in $0.5mol\;dm^{-3}\;Na_3PO_4$ solution. The corrosion behavior was studied by polarization measurements while the in vitro bioactivity was tested by soaking the specimens in Simulated Body Fluid (1.5xSBF). Optical micrograph and elemental analysis of the substrate surfaces indicated that the number of intermetallic particles increased with Ca content in the alloys owing to the formation of a new phase $Al_2Ca$. The corrosion resistance of AM60 specimens improved only slightly by alloying with 2 wt% Ca which was attributed to the reticular distribution of $Al_2Ca$ phase existed in the alloy that might became barrier for corrosion propagation across grain boundaries. Corrosion resistance of the three alloys was significantly improved by coating the substrates with anodic oxide film formed by PEO. The film mainly composed of magnesium phosphate with thickness in the range $30-40{\mu}m$. The heat resistant phase of $Al_2Ca$ was believed to retard the plasma discharge during anodization and, hence, decreased the film thickness of Ca-containing alloys. The highest apatite forming ability in 1.5xSBF was observed for AM60-1Ca specimens (both substrate and anodized) that exhibited more degradation than the other two alloys as indicated by surface observation. The increase of surface roughness and the degree of supersaturation of 1.5xSBF due to dissolution of Mg ions from the substrate surface or the release of film compounds from the anodized surface are important factors to enhance deposition of Ca-P compound on the specimen surfaces.

• 소성∙가공
• /
• 제33권3호
• /
• pp.178-184
• /
• 2024

In this study, we investigated the effects of extrusion ratio and extrusion temperature on the microstructure and tensile properties of extruded Mg-6Al-0.3Mn-0.3Ca-0.2Y (SEN6) alloy. As the extrusion ratio and temperature increase, dynamic recrystallization during extrusion is promoted, leading to the formation of a fully recrystallized microstructure with increased grain size. Additionally, the increases in extrusion ratio and temperature lead to texture strengthening, exhibiting a higher maximum texture intensity. The extruded materials contain three types of secondary phases, i.e., Al₈Mn₄Y, Al₂Y, and Al₂Ca, with irregular or polygonal shapes. The quantity, size, distribution, and area fraction of the second-phase particles are nearly identical between the two materials. Despite its larger grain size, the tensile yield strength of the material extruded at 450 ℃ and an extrusion ratio of 25 (450-25) is higher than that of the material extruded at 325 ℃ and an extrusion ratio of 10 (325-10), which is mainly attributed to the stronger texture hardening effect of the former. The ultimate tensile strength is similar in the two materials, owing to the higher work hardening rate in the 325-10 extrudate. Despite differences in grain size and recrystallization fraction, numerous twins are formed throughout the specimen during tensile deformation in both materials; consequently, the two materials exhibit nearly the same tensile elongation.

• 한국주조공학회지
• /
• 제9권6호
• /
• pp.474-482
• /
• 1989

The aim of this research is to investigate the effects of gas bubbles on the formation of spheroidal graphite in cast iron, Fe-Si-8%Mg alloy, mischmetal hydride($MmH_2$) and $CaCO_3$, which discharge various amounts of Mg, $H_2$ and $Co_2$, gases, were added to Fe-3.9% C-2.0%Si melt and the melt was innoculated with 0.3wt% of 75%Fe-Si. The spheroidal graphites and/or compacted vermicular graphites were produced with more than 0.625cc/g of Mg gas or more than 0.3125cc/g of $H_2$ gas while $CO_2$ gas did not contribute to graphite spheroidization. Nodule counts increased with the amount of Fe-Si-Mg added ; but they decreased with the amount of $MmH_2$ added because the number of effective gas bubbles decrease with the increase in Mm residual. The bull's eye structure was revealed with 0.625cc/g, 1.25cc/g of Mg and 0.3125cc/g of $H_2$ ; the ledeburite structure was revealed with more than 0.625cc/g of $H_2$.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.75-75
• /
• 2018

Commercially pure titanium (CP-Ti) and Ti-6Al-4V alloys have been widely used in implant materials such as dental and orthopedic implants due to their corrosion resistance, biocompatibility, and good mechanical properties. However, surface modification of titanium and titanium alloys is necessary to improve osseointegration between implant surface and bone. Especially, when titanium oxide nanotubes are formed on the surface of titanium alloy, cell adhesion is greatly improved. In addition, plasma electrolytic oxide (PEO) coatings have a good safety for osseointegration and can easily and quickly form coatings of uniform thickness with various pore sizes. Recently, the effects of bone element such as magnesium, zinc, strontium, silicon, and manganese for bone regeneration are researching in dental implant field. The purpose of this study was researched on the surface morphology of PEO-treated Ti-6Al-4V alloy after anodic titanium oxide treatmentusing various instruments. Ti-6Al-4V ELI disks were used as specimens for nanotube formation and PEO-treatment. The solution for the nanotube formation experiment was 1 M $H_3PO_4$ + 0.8 wt. % NaF electrolyte was used. The applied potential was 30V for 1 hours. The PEO treatment was performed after removing the nanotubes by ultrasonics for 10 minutes. The PEO treatment after removal of the nanotubes was carried out in the $Ca(CH_3)_2{\cdot}H_2O+(CH_3COO)_2Mg{\cdot}4H_2O+Mn(CH_3COO)_2{\cdot}4H_2O+Zn(CH_3CO_2)_2Zn{\cdot}2H_2O+Sr(CH_2COO)_2{\cdot}0.5H_2O+C_3H_7CaO_6P$ and $Na_2SiO_3{\cdot}9H_2O$ electrolytes. And the PEO-treatment time and potential were 3 minutes at 280V. The morphology changes of the coatings on Ti-6Al-4V alloy surface were observed using FE-SEM, EDS, XRD, AFM, and scratch tester. The morphology of PEO-treated surface in 5 ion coating solution after nanotube removal showed formation or nano-sized mesh and micro-sized pores.

• 한국주조공학회지
• /
• 제5권3호
• /
• pp.5-12
• /
• 1985

Many researchers have studied the eutectic solidification of CV Graphite Cast Iron qualitatively. However quantative studies have not been done. The type of eutectic solidification of CV Graphite Cast Iron treated with CG Alloy (Fe-Si-Mg-5Ti-Ca-Ce) was studied quantitatively through M.D.E. value (Mushy Degree of Eutectic Solidification) = $t_2/t_1)$, where $t_1$ is the difference of the eutectic solidification starting time between surface and center part of the casting sample, and $t_2$ is the time of eutectic solidification of the center part. Following results were obtained. (1) The M.D.E. value of CV graphite cast iron lies between that of spheroidal graphite and that of flake graphite cast iron but is closer to that of Flake graphite cast iron. (2) The M.D.E. value of CV graphite cast iron depends upon CV ratio. (3) The time required for eutectic solidification increases as graphite form is changed from Flake, CV. to spheroidal graphite. (4) The M.D.E. value increases as cooling rate increases.

• 한국표면공학회지
• /
• 제34권4호
• /
• pp.281-288
• /
• 2001

Phosphating treatments have been performed to improve paint adhesion and corrosion resistance of zinc and zinc alloy coated steels for a long time. In this work, the effects of the addition of chelate compound were studied to improve the stability of surface conditioning solution and properties of zinc phosphate films. The coalescence of colloidal Ti-compound and extraneous charged particles (alkaliearth metal cation such as $Mg^{2+}$ , $Ca^{2+}$ ) were suppressed by using a surface conditioning solution with chelate compound. Therefore, after surface conditioning solution containing chelate compound was left standing for one week at room temperature, the formation of a white sediment was decreased comparing to surface conditioning solution without chelate compound. The crystal size of phosphate film was fine and the whiteness value of phosphated zinc coated steel sheets was also high without the decrease of corrosion resistance and anti-patina. It was very effective to use chelate compound improving the stability of surface conditioning solution.

• Journal of Advanced Marine Engineering and Technology
• /
• 제30권1호
• /
• pp.157-168
• /
• 2006

Recently, interest in using Al alloys in ship construction instead of fiber-reinforced plastic (FRP) has increased because of the advantages of A) alloy ships over FRP ships, including high speed, increased load capacity. and ease of recycling. This paper investigated the mechanical and electrochemical properties of Al alloys in a slow strain rate test under various potential conditions. These results will provide reference data for ship design by determining the optimum protection potential regarding hydrogen embrittlement and stress corrosion cracking. In general, Al and Al alloys do not corrode on formation of a film that has resistance to corrosion in neutral solutions. In seawater, however, $Cl^-$ ions lead to the formation and destruction of a Passive film. In a potentiostatic experiment. the current density after 1200 sec in the Potential range of $-0.68\~-1.5\;V$ was low. This low current density indicates the protection potential range. Elongation at an applied potential of 0 V was high in this SSRT. However, corrosion protection under these conditions is impossible because the mechanical properties are worse owing to decreased strength resulting from the active dissolution reaction in parallel parts of the specimen. A film composed of $CaCO_3\;and\;Mg(OH)_2$ confers corrosion resistance. However, at potentials below -1.6 V forms non-uniform electrodeposition coating, since there is too little time to form a coating. Therefore, we concluded that the mechanical properties are poor because the effect of hydrogen gas generation exceeds that of electrodeposition. Comparison of the maximum tensile strength, elongation, and time to fracture indicated that the optimum protection potential range was from -1.45 to -0.9 V (SSCE).

• Transactions on Electrical and Electronic Materials
• /
• 제1권2호
• /
• pp.32-37
• /
• 2000

Effect of alloying element additions to Ag on thermal conductivity and electrical conductivity of sheath materials for Bi-Pb-Sr-Ca-Cu-O(BSCCO) tapes has been characterized. The thermal conductivity at low temperature range (10~300K) of Ag and Ag alloys were evaluated by both direct and indirect measurement techniqueas and compared with each other, It was observed that the thermal conductivity decreases with increasing the content of alloying element such as Au, Pd and Mg. Thermal conductivity of pure Ag at 3 0K was measured to be 994.0 W(m.K) on the other hand, the corresponding values of $Ag_{0.9995}Mg_{0.0005}$, $Ag_{0.974}$, $Au_{0.025}$, $Mg_{0.001}$, $Ab_{0.973}$, $Au_{0.025}$, $Mg_{0.002}$ and $Ag_{0.92}$, $Pb_{0.06}$, $Mg_{0.02}$ were 342.6, 62.1, 59.2 and 28.9 W(m.K), respectively, indicating 3 to 30 times lower than that of pure Ag. In addition, the thermal conductivity of pure Ag measured by direct and indirect measurement techniques was 303.2 and 363.8 W(m.K) The difference in this study is considered to be within an acceptable error range compared to the reference data.

• 해양환경안전학회:학술대회논문집
• /
• 해양환경안전학회 2005년도 춘계학술발표회
• /
• pp.161-165
• /
• 2005

Recently, it is on the increase interest for Al alloy with new material for ship application to substitute for FRP ship. The reason is thatAl alloy ship has beneficial characteristics such as high sea speed, increase of loadage and easy to recycle compared with FRP ship. In this paper, mechanical and electrochemical properties are investigated by slow strain rate test experiment in various applied potential condition. These results will provide as reference data to design ship by deciding optimum protection potential regard to hydrogen embrittlement and stress corrosion cracking. In general, Al and Al alloys are not corroded with forming film which has the corrosion resistance property in neutral solution. However, it was observed that formation and destruction of passive film by $Cl^-$ ion in sea water environment. At comparison of current density after 1200 sec in potentiostatic experiment, the current density in the potential range of -0.68 $\~$-1.5 V is shown low value. The low current density means protection potential range. Elongation in applied potential of 0 V was high. However, the corrosion protection application in this condition is impossible potential because the toughness is low value by decreasing strength by active dissolution reaction at parallel part of specimen. The film composed with $CaCO_3$ and $Mg(OH)_2$ has a corrosion resistance property. However, the uniform electrodeposition coating at below -1.6 V potential is not formed since the time to form the uniform electrodeposition coating is short. Therefore, it is concluded that mechanical property is poor because effect by hydrogen gas generation is larger than that of electrodeposition coating. It is concluded that the optimum protection potential range from comparison of_maxim urn tensile strength, elongation and time to fracture is -1.3$\~$0.7 V (SSCE).

• 한국세라믹학회지
• /
• 제43권10호
• /
• pp.646-652
• /
• 2006

Several oxynitride glasses were fabricated by means of adding $Si_3N_4$ powders as nitrogen source to Ca-Al-Si-O-N (CAS) and Mg-Al-Si-O-N (MAS) glass powders, and heat-treated in graphite crucible at 1600$^{\circ}C$ for 1 h. The physical and mechanical properties as well as impact resistance were generally increased and compared with each other. The impact resistance properties of those manufactured glasses were evaluated by DOP (depth of penetration) method which is a way to analyze armor materials. There were two means to be used herein; the copper jet impacted at hyper velocity by exploding K2l5 warhead and tungsten heavy alloy (WHA) impact bar at high velocity by firing in 30 mm solid propellent gun. The impact resistance properties against copper jet were increased and then decreased with increasing nitrogen content, while those against WHA bar were not changed apparently with nitrogen content.