• 소성∙가공
• /
• 제21권5호
• /
• pp.324-329
• /
• 2012

Mg-(9-x)Sn-xAl-1Zn (x=1, 2, 3 and 4 wt.%) alloys were subjected to indirect extrusion, and the microstructure and mechanical properties of the as-extruded Mg-Sn-Al-Zn (TAZ) alloys were investigated. The TAZ 811 alloy exhibited a finer grain structure than the TAZ 541 alloy due to a larger number of Mg2Sn particles, which pinned the grain boundaries and prevented growth of recrystallized grains. The TAZ alloys showed an unusual yield asymmetry behavior. The tension-compression yield asymmetry increased with decreasing average grain size. The TAZ 811 alloy with a small grain size exhibited a larger yield asymmetry than that of the TAZ 541 alloy having a relatively large grain size, which is mainly attributed to the low Al content and large number of second phase particles in the TAZ 811 alloy.

• 한국주조공학회지
• /
• 제24권6호
• /
• pp.340-346
• /
• 2004

초정 $Mg_2Si$와 미세한 $MgZn_2$ 석출상을 갖는 고강도 내마모 Al합금을 개발하기 이하여 Al-l2wt%Mg-5.5wt%Zn합금에 0-5wt%까지 Si을 첨가 시켰으며, 미세조직 및 기계적 성질에 미치는 영향을 조사하였다. Si의 함량이 증가함에 따라 형성되는 $Mg_2Si$상의 양이 증가하였으며, 동시에 고강선 온도가 점차적으로 증가함에 따라 효과적인 열처리가 가능해지는 것을 관찰할 수 있었다. 5wt%Si이 첨가된 합금의 경우 적절한 열처리를 통해 미세한 $MgZn_2$ 석출상이 기지에 균일하게 분포한 미세조직을 얻을 수 있었고 이를 통해 인장강도를 현저하게 증가시킬 수 있었다. 또한 Si이 첨가된 Al-Mg-Zn합금은 유동도 및 열간 균열저항성과 같은 주조성면에서도 다른 고강도 Al합금에 비하여 월등히 우수한 것으로 나타났다.

• 열처리공학회지
• /
• 제36권4호
• /
• pp.223-229
• /
• 2023

This work was intended to investigate the effects of Zn content on microstructure and hardness of discontinuous precipitates (DPs) produced by continuous cooling (CC) in Mg-8%Al-X%Zn alloys with 0%, 0.5% and 1% of Zn contents (wt%). The DPs in the alloys possessed a wide range of (α+β) interlamellar spacings, which is attributed to the different transformation temperatures during CC. The higher Zn content resulted in the lower level of interlamellar spacings of the DPs, along with thinner and larger volume fraction of β phase layer in the DPs. It is noted that the DPs in the alloy with higher Zn content exhibited higher hardness, and that the ratio of increase in hardness of the DPs to that of the as-cast state was also increased with increasing Zn content. The reason was discussed on the basis of microstructural differences of the DPs in the Mg-8%Al-X%Zn alloys.

• 열처리공학회지
• /
• 제12권1호
• /
• pp.1-8
• /
• 1999

This study has investigated the effect of aging treatment on the microstructure and mechanical properties of Mg-6Al-xZn(x = 1.5, 2.5) alloys fabricated by the squeeze casting process. The microstructures of as-squeeze cast were composed of pro-eutectic ${\alpha}$, super saturated ${\alpha}$ and ${\beta}(Mg_{17}Al_{12})$ compound. Aged at both $200^{\circ}C$ and $240^{\circ}C$, Mg-6Al-xZn alloys showed the peak hardness due to the formation of ${\beta}(Mg_{17}Al_{12})$ precipitates. The discontinuous precipitates of the lamella type are predominant at $200^{\circ}C$ aging treatment, while the finely dispersed continuous precipitates were dominant at $240^{\circ}C$ aging treatment. Mg-6Al-xZn alloys fabricated by the squeeze casting process had the better combination of tensile strength and elongation compared to the conventionally cast alloys. As zinc contents increased, the tensile strength was increased by the solid solution strengthening effect of zinc.

• 열처리공학회지
• /
• 제28권3호
• /
• pp.126-133
• /
• 2015

The aim of this study is to investigate the effect of solution treatment on the corrosion behavior of Mg-8%Al-(0-1)%Zn casting alloys in 1M NaCl aqueous solution. After the solution treatment, all alloys showed single ${\alpha}$-(Mg) phase microstructure by dissolution of ${\beta}(Mg_{17}Al_{12})$ phase into the ${\alpha}$-(Mg) matrix. The $H_2$ evolution volume decreased with an increase in Zn content, which indicates that the addition of Zn plays a beneficial role in decreasing corrosion rate of the Mg-Al-Zn alloy in solution-treated state. The microstructural evaluations on the corrosion products and corroded surfaces after the immersion test in 1 M NaCl solution revealed that the incorporation of more $Al_2O_3$ and ZnO into the corrosion product, by which the penetration of $Cl^-$ ions is impeded, are thought to be responsible for the better corrosion resistance in relation with the Zn addition.

• 한국재료학회지
• /
• 제30권10호
• /
• pp.542-549
• /
• 2020

Effects of Sc addition on microstructure, electrical conductivity, thermal conductivity and mechanical properties of the as-cast and as-extruded Al-2Zn-1Cu-0.3Mg-xSc (x = 0, 0.25, 0.5 wt%) alloys are investigated. The average grain size of the as-cast Al-2Zn-1Cu-0.3Mg alloy is 2,334 ㎛; however, this value drops to 914 and 529 ㎛ with addition of Sc element at 0.25 wt% and 0.5 wt%, respectively. This grain refinement is due to primary Al₃Sc phase forming during solidification. The as-extruded Al-2Zn-1Cu-0.3Mg alloy has a recrystallization structure consisting of almost equiaxed grains. However, the as-extruded Sc-containing alloys consist of grains that are extremely elongated in the extrusion direction. In addition, it is found that the proportion of low-angle grain boundaries below 15 degree is dominant. This is because the addition of Sc results in the formation of coherent and nano-scale Al₃Sc phases during hot extrusion, inhibiting the process of recrystallization and improving the strength by pinning of dislocations and the formation of subgrain boundaries. The maximum values of the yield and tensile strength are 126 MPa and 215 MPa for the as-extruded Al-2Zn-1Cu-0.3Mg-0.25Sc alloy, respectively. The increase in strength is probably due to the existence of nano-scale Al₃Sc precipitates and dense Al₂Cu phases. Thermal conductivity of the as-cast Al-2Zn-1Cu-0.3Mg-xSc alloy is reduced to 204, 187 and 183 W/MK by additions of elemental Sc of 0, 0.25 and 0.5 wt%, respectively. On the other hand, the thermal conductivity of the as-extruded Al-2Zn-1Cu-0.3Mg-xSc alloy is about 200 W/Mk regardless of the content of Sc. This is because of the formation of coherent Al₃Sc phase, which decreases Sc content and causes extremely high electrical resistivity.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1996년도 재료학회 춘계학술발표회
• /
• pp.88-89
• /
• 1996

• 열처리공학회지
• /
• 제18권1호
• /
• pp.12-17
• /
• 2005

Effects of Zn and Zr additions on the microstructure and mechanical properties of Al-5%Mg-1%Mn alloys were investigated. As Zn content increased in the Al-Mg-Mn-Zn alloys, the tensile strength and ductility of as-cast alloys rather decreased while the tensile strength of the heat-treated alloys significantly increased mainly due to the precipitation of fine $MgZn_2$ phases. Small amount of Zr was added to the 3%Zn alloy to further enhance the mechanical properties, and it appeared to increase the strength and ductility, especially in as-cast state.

• 한국재료학회지
• /
• 제31권12호
• /
• pp.704-709
• /
• 2021

In the flux used in the batch galvanizing process, the effect of the component ratio of NH₄Cl to ZnCl₂ on the microstructure, coating adhesion, and corrosion resistance of Zn-Mg-Al ternary alloy-coated steel is evaluated. Many defects such as cracks and bare spots are formed inside the Zn-Mg-Al coating layer during treatment with the flux composition generally used for Zn coating. Deterioration of the coating property is due to the formation of AlCl_x mixture generated by the reaction of Al element and chloride in the flux. The coatability of the Zn-Mg-Al alloy coating is improved by increasing the content of ZnCl₂ in the flux to reduce the amount of chlorine reacting with Al while maintaining the flux effect and the coating adhesion is improved as the component ratio of NH₄Cl to ZnCl₂ decreases. Zn-Mg-Al alloy-coated steel products treated with the optimized flux composition of NH₄Cl·3ZnCl₂ show superior corrosion resistance compared to Zn-coated steel products, even with a coating weight of 60 %.

• 한국주조공학회지
• /
• 제26권1호
• /
• pp.34-39
• /
• 2006

In the present study, the possibility of Mg-Zn-Y alloys as high temperature casting alloys has been investigated. The fluidity of alloys containing yttrium were better than that of commercial AZ91 alloy because the oxide layer on the surface reduced the reaction between melt, and air and mold, which would reduce the resistance during the process of filling the mold. However, this oxide film reduced the hot-tearing resistance. In the case of ZAW942, this alloy exhibited fluidity and hot-tearing resistance better than AZ91 alloy. Because of thermally stable quasicrystal and other phases obstructed the movement of grains, the creep resistance of alloys containing rare earth elements more than 2 wt% was better than that of AZ91 alloy.