• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.536-537
• /
• 2006

In the present work, the sintering behavior of high strength Al-5.6Zn-2.5Mg-1.6Cu (in wt.%) alloy compacts prepared from elemental powders was investigated. Microstructural evaluation was accompanied by XRD and DSC methods in order to determine the temperature and chemical composition of the liquid phases formed during sintering. It was found that three transient liquid phases are formed at 420, 439 and 450 $^{\circ}C$. Microstructural study revealed the progressive formation of sintered contacts due to the presence of the liquid phases, although the green compact expands as a result of the melt penetration along the grain boundaries. While Zn melts at ${\sim}420\;^{\circ}C$, the intermetallic phases formed between Al and Mg were found to be responsible for the formation of liquid phase and the dimensional change at higher temperatures.

• 소성∙가공
• /
• 제12권6호
• /
• pp.588-596
• /
• 2003

The relationships between evolution of microstructure and mechanical properties of porous Al-3Si-2Mg-2Cu alloy after the foaming and various heat treating were investigated. The foamed alloy having various densities were manufactured by powder compact foaming and heat treated. Then compression test was performed with deformation rate of 0.5/s. The ultimate compression strength was not changed after solution heat treatment but the flow curve after ultimate strength showed very smooth and uniform plateau region. This change of flow curve means that the deformation mechanism is altered from brittle fracture to ductile deformation and the energy absorption property of Al foam is dramatically improved. The improvement of energy absorption without any detriment of mechanical properties is due to that the very brittle precipitation like Al-Cu and Al-Mg was uniformly dissolved in Al matrix after solution heat treatment. And various mechanical properties of Al alloy porous material were improved by 40% with aging of $200^{\circ}C$ and 50min. These improvements are ascribe to the various fine precipitates like $\Omega$ and $\theta$'.

• 한국자동차공학회논문집
• /
• 제22권4호
• /
• pp.30-35
• /
• 2014

According to weight lightning trend of automobile body, necessity of resistance spot welding (RSW) of Mg alloy on automobile industry is increasing rapidly because of the highest specific strength among commercial metals. Mg alloy has low electric resistance and high thermal conductivity like as Al alloy, so that needs applying high current in short time when welding. Thick oxide film of Mg alloy pollutes the electrodes and makes partial current carrying paths when on welding. Partial current carrying paths signify excessive concentration of current. There can initiate expulsion easily and reduces electrode life rapidly. Generating partial current carrying paths and expulsions are influenced by shapes of electrode. Therefore, electrode life also influenced by shape. In this study, we perform life test of RSW electrode of radius type. Measure tensile shear load and nugget size every spot alternately. As a result, radius type electrode can extend life over twice as dome type electrode.

• 한국주조공학회지
• /
• 제20권1호
• /
• pp.29-37
• /
• 2000

The purpose of this study is to investigate the effect of misch metal addition on the microstructure and mechanical property of rapidly solidified AZ91 alloy by melt spinning process. As the contents of misch metal(rare earth element:Ce,La, Nd, Pr)was increased, the microstructure of RS ribbons and extrudates became finer than those of AZ91, and RE related phases($Al_{11}RE_3$, $Al_2RE$) were formed. At room temperature, the rapidly solidified AZ91+1 wt%Mm alloy showed the highest tensile strength, 430 MPa due to precipitation strengthening of${\beta}(Mg_{17}Al_{12})$ phase and Al11RE3 phase. At the elevated temperature, the mechanical property of AZ01+3 wt%Mm alloy was higher than those of other Mg alloys. The reasons were that $Al_{11}La_3$ phase was thermally stable and suppressed the grain growth. In contrast with $Al_{11}La_3$ phase, ${\beta}$ phase was thermally unstable and could not suppress the grain growth at the elevated temperature. Therefore, Al11RE3 phase contributed to improve the thermal stability of RS AZ91 Alloy.

• 한국재료학회지
• /
• 제27권11호
• /
• pp.597-602
• /
• 2017

In this study, an Al-0.7wt%Fe-0.2wt%Mg-0.2wt%Cu-0.02wt%B alloy was designed to fabricate an aluminum alloy for electrical wire having both high strength and high conductivity. The designed Al alloy was processed by casting, extrusion and drawing processes. Especially, the drawing process was done by severe deformation of a rod with an initial diameter of 12 mm into a wire of 2 mm diameter; process was equivalent to an effective strain of 3.58, and the total reduction in area was 97 %. The drawn Al alloy wire was then annealed at various temperatures of 200 to $400^{\circ}C$ for 30 minutes. The mechanical properties, microstructural changes and electrical properties of the annealed specimens were investigated. As the annealing temperature increased, the tensile strength decreased and the elongation increased. Recovery or/and recrystallization occurred as annealing temperature increased, and complete recrystallization occurred at annealing temperatures over $300^{\circ}C$. Electric conductivity increased with increasing temperature up to $250^{\circ}C$, but no significant change was observed above $300^{\circ}C$. It is concluded that, from the viewpoint of the mechanical and electrical properties, the specimen annealed at $350^{\circ}C$ is the most suitable for the wire drawn Al alloy electrical wire.

• 소성∙가공
• /
• 제8권3호
• /
• pp.295-295
• /
• 1999

In the present study, the corrosion behavior of AZ91D as-cast alloy was investigated form the viewpoint of the distribution aspect of precipitate ($Mg_{17}Al_{12}$) and the variation of Al concentration in the Mg-rich matrix. The dendrite arm spacing (DAS) of an as-cast specimen was measured as a function of degree which describes the distribution aspect of the precipitate, and the salt spray test was conducted for various grain-sired specimens fur 20 days. The dendrite arm spacing increased as the grain size increased to about 150㎛, but a constant value is indicated when the grain size exceeds that range. Although the relationship between the corrosion rate and grain size is of a nonlinear type, the linear trend between the corrosion rate and the dendrite arm spacing is maintained for the overall range of dendrite arm spacing. Since the precipitate in the as-cast alloy is discontinuously distributed, this linear relationship means that the variation of Al-solute concentration in the Mg-rich matrix has a more potent effect than the protective action of the precipitate on the corrosion behavior of an as-cast alloy.

• 한국주조공학회지
• /
• 제33권1호
• /
• pp.22-31
• /
• 2013

In order to develop an aluminum alloy, that can combine high thermal conductivity and good castability and anodizability, aluminum alloys with low Si content, such as Al-(0.5~1.5)Mg-1Fe-0.5Si and Al-(1.0~1.5)Si-1Fe-1Zn, were designed. The developed aluminum alloys exhibited 170~190% thermal conductivity (160~180 W/mK), 60~85% fluidity, and equal or higher ultimate tensile strength compared with those of the ADC12 alloy. In each developed alloy system, the thermal conductivity decreased and the strength increased with the increment of Mg and Si, which are the significant alloying elements. The fluidity was in reverse proportion to the Mg content and in proportion to the Si content. The Al-(0.5~1.5)Mg-1Fe-0.5Si alloys exhibited better fluidity in thick-wall castings, while the Al-(1.0~1.5)Si-1Fe-1Zn alloys were better in thin-wall castability due to their lower surface energies. The fluidity behavior was complexly affected by the heat release for the solidification, viscosity, solidification range, and the type, quantity, and formation juncture of the main secondary phase.

• 한국주조공학회지
• /
• 제11권3호
• /
• pp.208-216
• /
• 1991

The solidification behavior of the squeeze cast composites of aluminum alloys reinforced with boron fiber($100{\mu}m$) and silicon carbide fibers($140{\mu}m$ and $15{\mu}m$) were investigated. Al-4.5wt%Cu and Al-l0wt%Mg were chosen for the matrix phase of the composites. In the squeeze cast specimen with high thermal difference between fiber and melt, the average secondary dendrite arm spacing(DAS) in reinforced alloy is smaller than that in unreinforced alloy. It was also observed that primary ${\alpha}$ and non-equilibrium eutectic, which seems to be penetrated and solidified at the final stage of the solidification of the matrix, are irregularly distributed around fibers. It is considered that cold fibers serve as heterogeneous nucleation site. While in the remelted and resolidified specimen without temperature difference, the DAS was not changed with reinforcement and microstructure reveals non-equilibrium eutectic with relatively uniform thickness around fibers. It might be evident the nucleation starts at interfiber region. Microsegregation decreases with the decrease in cooling rate and with reinforcement in the as-squeeze cast specimen. Al-10wt% Mg alloy shows less microsegregation than Al-4.5wt%Cu alloy.

• 한국주조공학회지
• /
• 제20권6호
• /
• pp.386-394
• /
• 2000

In the present study, the effect of yttrium addition on the microstructure and mechanical property of rapidly solidified AZ91 alloy by melt spinning process is estimated. As yttrium was added, the microstructure of RS ribbons and extrudates became finer than those of AZ91, and RE related phases $(Al_2RE)$ were formed. In the case of the addition of 3wt%Y, the microstructure of extrude showed the finest grain size. At room temperature, the AZ91 + 3wt%Y alloy showed the highest tensile strength, 352 MPA due to precipitation of ${\beta}(Mg_{17}Al_{12})$ phase and $Al_2RE$ phase. At the elevated temperature, the mechanical property of AZ91 + 3wt%Y alloy was higher than those of other Mg alloys. The reasons were that $Al_2Y$ compound was thermally stable and suppressed the grain growth. In contrast with $Al_2Y$ compounds, ${\beta}$ phase was thermally unstable and could not suppress the grain growth at the elevated temperature. Therefore, $Al_2Y$ phase contributed to improve the thermal stability of RS AZ91 alloy.

• 한국주조공학회지
• /
• 제37권5호
• /
• pp.148-156
• /
• 2017

The effects of minor additives on the casting properties of AC4A aluminum alloys were investigated. Measurements of the cooling curve and microstructure observations were conducted to analyze the effects of Ti-B and Sr minor elements during the solidification process. A fine grain size and an increase in the crystallization temperature for the ${\alpha}-Al$ solution were evident after the addition of 0.1wt% Al-5%Ti-1%B additive. The modification effect of the eutectic $Mg_2Si$ phase with the addition of 0.05% Al-10%Sr additive was prominent. A fine eutectic $Mg_2Si$ phase and a decrease in the growth temperature of the eutectic $Mg_2Si$ phase were evident. Fluidity, shrinkage and solidification-cracking tests were conducted to evaluate the castability of the alloy. The combined addition of Al-5%Ti-1%B and Al-10%Sr additives showed the maximum filling length owing to the effect of the fine ${\alpha}-Al$ grains. The macro-shrinkage ratio increased, while the micro-shrinkage ratio decreased with the combined addition of Al-5%Ti-1%B and Al-10%Sr additives. The macro-shrinkage ratio was nearly identical, while the micro-shrinkage ratio increased with the addition of the Al-10%Sr additive. The tendency of the occurrence of solidification cracking decreased owing to the effect of the fine ${\alpha}-Al$ grains and the modification of the $Mg_2Si$ phase with the combined addition of Al-5%Ti-1%B and Al-10%Sr additives.