• Journal of the Korean Ceramic Society
• /
• v.30 no.12
• /
• pp.1029-1038
• /
• 1993

The microstructures of aluminas, included of dissolved CaO as $\alpha$-alumina seeded pseudo-boehmite hydrosol was gelled in plaster mold and doped of MgO as dipping of calcines(120$0^{\circ}C$-2h) into Mg-nitrate solution, were compared to the one of which additives are excluded during the gellation. It was formed the boundary layer of 300~350${\mu}{\textrm}{m}$ distance from surface to the inside, containing of approximately 500ppm CaO by dissolved Ca from plaster mold. As the MgO addition to the boundary layer with dissolved CaO, the microstructure of the layer was uniformed and inhibited the grian growth, compared to one of that additives be excluded specimen and of MgO doped-inside region. This result was considered as abnormal grain growth and effect of flat boundary formation be appeared by effects of dissolved CaO, were decreased by MgO co-doping.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.7
• /
• pp.641-646
• /
• 2005

To fabricate a single layer white organic light emitting diode (OLED), a novel non-conjugated blue emitting material PPPMA-co-DTPM copolymer was synthesized containing a perylene moiety unit with hole transporting and blue emitting ability and a triazine moiety unit with electron transporting ability. The devices were fabricated using PPPMA-co-DTPM $(PPPMA[70\;wt\%]:DTPM[30\;wt\%])$ copolymer by varying the doping concentrations of each red, green and blue fluorescent dye, by molecular-dispersing into Toluene solvent with spin coating method. In case of ITO/PPPMA-co-DTPM:TPB$(3\;mol\%):C6(0.04\;mol\%):NR(0.015\;mol\%)/Al$ structure, as they were molecular-dispersing into 30 mg/ml Toluene solvent, nearly-pure white light was obtained both (0.325, 0.339) in the CIE coordinates at 18 V and (0.335, 0.345) at 15 V. The turn-on voltage was 3 V, the light-emitting turn-on voltage was 4 V, and the maximum external quantum efficiency was $0.667\%$ at 24.5 V. Also, in case of using 40 mg/ml Toluene solvent, the CIE coordinate was (0.345, 0.342) at 20 V.

• Korean Journal of Materials Research
• /
• v.8 no.6
• /
• pp.526-531
• /
• 1998

A hydride vapor phase epitaxy (HVPE) method was performed to grow the $10~240\mu{m}$ thick GaN films on (111) spinel $MgAl_2O_4$ substrate. The GaN films on $MgAl_2O_4$ substrate revealed a photoluminescence (PL) characteristics of the impurity doped GaN by the out-diffusion and auto-doping of Mg from $MgAl_2O_4$ substrate during GaN growth. The PL spectrum measured at 10K consists of free and bound excitons related recombination transitions and impurity-related donor-acceptor pair recombination and its phonon replicas. However, the deep-level related yellow band emission was not observed. The peak energy of neutral donor bound excitonic emission and the frequency of Raman $E_2$ mode were exponentially decreased with increasing the GaN thicknesses. and the frequency of E, Raman mode was shifted with the relation of $\Delta$$\omega$=3.93$\sigma$($cm^{-1}$/GPa), where l1 (GPa) is the residual strain in the GaN epilayers.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2006.08a
• /
• pp.1093-1095
• /
• 2006

An orange-emitting phosphor for inorganic electroluminescent device has been studied. Cu and Cl were co-doped in Mn-doped ZnS for a high-performing phosphor. The effect of $Mn^{2+}-doping$ concentration as well as $Mg^{2+}-sensitizer$ addition on the luminescence characteristics has been investigated.

• Journal of the Korean Ceramic Society
• /
• v.44 no.3 s.298
• /
• pp.147-151
• /
• 2007

An improvement for the efficiency of the $Sr_{2}SiO_{4}:Eu$ yellow phosphor under the $450{\sim}470\;nm$ excitation range have been achieved by adding the co-doping element ($Mg^{2+}\;and\;Ba^{2+}$) in the host. White LEDs were fabricated through an integration of an blue (InGaN) chip (${\lambda}_{cm}=450\;nm$) and a blend of two phosphors ($Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor) in a single package. The InGaN-based two phosphor blends ($Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor) LEDs showed three bands at 450 nm, 550 nm and 640 nm, respectively. The 450 nm emission band was due to a radiative recombination from an InGaN active layer. This 450 nm emission was used as an optical transition of the $Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor. As a consequence of a preparation of white LEDs using the $Mg^{2+},\;Ba^{2+}\;co-doped\;Sr_{2}SiO_{4}:Eu$ yellow phosphor+CaS:Eu red phosphor yellow phosphor and CaS:Eu red phosphor, the highest luminescence efficiency was obtained at the 0.03 mol $Ba^{2+}$ concentration. At this time, the white LEDs showed the CCT (5300 K), CRI (89.9) and luminous efficacy (17.34 lm/W).

• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.541-548
• /
• 1991

Sinterability and stability of TZP ceramics co-stabilized by 12 mol% CeO2 and divalent or trivalent oxides less than 1 mol% were investigated. Divalent and trivalent oxides increased stability of tetragonal ZrO2. 100% tetragonal ZrO2 phase was obtained by doping 12 mol% CeO2 and 0.2 mol% CaO and MgO respectively when sintering was carried out at 1500$^{\circ}C$ for 2 hours. Divalent and trivalent oxides improved sinterability and inhibit grain growth of ZrO2. And it was found that CaO was the most effective sintering aid and grain growth inhibitor for ZrO2 in this study. Incorporation of divalent and trivalent oxides into 12Ce-TZP increased the strength of 12Ce-TZP and particulary 12Ce, 0.4Ca-TZP exhibited a flexural strength of about twofold greater than 12Ce-TZP.

• Current Photovoltaic Research
• /
• v.4 no.4
• /
• pp.150-154
• /
• 2016

Mg and In co-doped ZnO (MIZO) thin films with transparent conducting characteristics were successfully prepared on glass substrates by RF magnetron sputtering technique. The Influence of different substrate temperature (from RT to $400^{\circ}C$) on the structural, morphological, electrical, and optical properties of MIZO thin films were investigated. The MIZO thin film prepared at the substrate temperature of $350^{\circ}C$ showed the best electrical characteristics in terms of the carrier concentration ($4.24{\times}10^{20}cm^{-3}$), charge carrier mobility ($5.01cm^2V^{-1}S^{-1}$), and a minimum resistivity ($1.24{\times}10^{-4}{\Omega}{\cdot}cm$). The average transmission of MIZO thin films in the visible range was over 80% and the absorption edges of MIZO thin films were very sharp. The bandgap energy of MIZO thin films becomes wider from 3.44 eV to 3.6 eV as the substrate temperature increased from RT to $350^{\circ}C$. However, Band gap energy of MIZO thin film was narrow at substrate temperature of $400^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.212-212
• /
• 2010

Recently, lithium transition metal phosphates with an ordered olivine-type structure, $LiMPO_4$ (M=Fe, Mn, Ni, and Co), have attracted extensive attention due to a high theoretical specific capacity (170 mAh/g). The $LiMPO_4$ is the most attractive because of its high stability, low cost, high compatibility with environment. However, it is difficult to attain its full capacity because its electronic conductivity is very low, and diffusion of Li-ion in the olivine structure is slow and the supervalue cation doping was used. In this research, we are used the supervalue cation doping methode such as Cu, Ti, and Mg were partially replace the Fe. The cycling performance resulted of the used $LiM_xFe_{1_x}PO_4$ cathode materials for lithium batteries exhibit excellent high capacity than $LiFePO_4$/Li cells.

• Journal of the Korean Ceramic Society
• /
• v.55 no.2
• /
• pp.166-173
• /
• 2018

In order to investigate the effect of Mn on the dielectric and piezoelectric properties of PMN-PT [$Pb(Mg_{1/3}Nb_{2/3})O_3-PbTiO_3$], four different types of 71PMN-29PT samples were prepared using the solid-state single crystal growth (SSCG) method: (1) Undoped single crystals, (2) undoped polycrystalline ceramics, (3) Mn-doped single crystals, and (4) Mn-doped polycrystalline ceramics. In the case of single crystals, the addition of 0.5 mol% Mn to PMN-PT decreased the dielectric constant ($K_3{^T}$), piezoelectric charge constant ($d_{33}$), and dielectric loss (tan ${\delta}$) by about 50%, but increased the coercive electric field ($E_C$) by 50% and the electromechanical quality factor ($Q_m$) by 500%, respectively. The addition of Mn to PMN-PT induced an internal bias electric field ($E_I$) and thus specimens changed from piezoelectrically soft-type to piezoelectrically hard-type. This Mn effect was more significant in single crystals than in ceramics. These results demonstrate that Mn-doped 71PMN-29PT single crystals, because they are piezoelectrically hard and simultaneously have high piezoelectric and electromechanical properties, have great potential for application in fields of SONAR transducers, high intensity focused ultrasound (HIFU), and ultrasonic motors.

• Journal of the Korean Ceramic Society
• /
• v.55 no.3
• /
• pp.290-298
• /
• 2018

In order to investigate the effect of thickness on the dielectric and piezoelectric properties of (001) PMN-29PT single crystals, three different types of PMN-29PT samples were prepared using the solid-state single crystal growth (SSCG) method: high density crystal [99%], low density crystal [95%], and high density crystal doped with Mn [98.5%]. When their thickness decreased from 0.5 mm to 0.05 mm, their dielectric constant ($K_3{^T}$), piezoelectric constants ($d_{33}$ and $g_{33}$), and electromechanical coupling factor ($k_t$) decreased continuously. However, their dielectric loss (tan ${\delta}$) increased. The addition of Mn to PMN-PT induced an internal bias electric field ($E_I$), increased the coercive electric field ($E_C$), and prevented local depoling. Therefore, Mn-doped PMN-PT crystals show high stability as well as high performance, even in the form of very thin plates (< 0.2 mm), and thus are suitable for application to high frequency composites, medical ultrasound probes, non-destructive testing devices (NDT), and flexible devices.