• Journal of the Korean Society for Heat Treatment
• /
• v.35 no.2
• /
• pp.74-81
• /
• 2022

This study aims to mitigate the microstructural heterogeneity arising from the manufacture of magnesium alloy plates using the twin roll casting (TRC) process. Homogenization was introduced through hot rolling and heat treatment, followed by confirmation of observed changes in the microstructure. Following the TRC process, the hot rolled 2mm plate exhibited a dendritic cast structure tilted in the roll rotation direction, while central segregation were developed. This nonuniform structure and central segregation disappeared upon heat treatment, followed by recrystallization to form uniform and fine grains. Abnormal grain growth (AGG) was observed over the course of heat treatment; grains exhibiting AGG occupied up to 75% of the total area after having held the sample at 400℃ for 64 h. The formation of coarse grains was also observed during heat treatment at 340℃ over a relatively long duration, though the maximum grain size was significantly smaller than that corresponding to the heat treatment at 400℃. AGG in the 400℃ heat treatment occurred because of movement of the grain boundary, which had been fixed prior as a result of the grain boundary fixing effect of the precipitation phase. The re-dissolution of the Ca₂Mg₅Zn₅ precipitated phase over the long duration of the high-temperature annealing process caused the surrounding grains to disappear and regrow.

• Journal of Welding and Joining
• /
• v.30 no.6
• /
• pp.56-61
• /
• 2012

Magnesium alloy sheet which is commercially available in the market presently is AZ31B, a Mg-Al-Zn three elements alloy. AZ31B is used by being classified into AZ31B-H24 and AZ31B-O depending on temper designation. In this study, AZ31B-H24 and AZ31B-O alloy sheets with 1.25mm thickness were butt-welded using CW Nd:YAG laser. And the effect of materials on mechanical properties was investigated by tensile and hardness tests. As a result of this study, regardless of materials, the butt-welded joint did not show a significant difference in tensile strength and hardness values. However, compared with the basemetal, the AZ31B-O showed more outstanding mechanical properties than AZ31B-H24, and that is because H24 material lost the effect of work hardening during welding.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.378-381
• /
• 2009

In this study, the repetitive loading-unloading tensile tests with AZ31B magnesium sheet metal have been conducted under various elevated temperatures to check out how the Young's moduli of the sheets evolve during the plastic deformation. The loading-unloading tests have been carried out at every 1% of strain increment. With the tested results, some damage parameters of magnesium sheets based on the Lemaitre's continuum damage theory could be calculated at room temperature, $100^{\circ}C$, $150^{\circ}C$, $200^{\circ}C$ and $250^{\circ}C$. It has been shown that the critical damage parameters obtained in all temperature conditions are within the range of 0.12 to 0.18.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.1000-1009
• /
• 2008

Hydro-mechanical forming process has numerous advantages compared to those of a conventional deep drawing process such as an excellent surface quality and low costs of dies. In fact, Hydro-mechanical forming is a desirable forming process for producing complex parts in automotive body components, and it is an excellent candidate for the forming process of aluminum panels. In this research, Hydro-mechanical forming process with a cross shape punch has been studied for Al-Si-Mg alloy sheets. Finite element analysis by LS-Dyna has predicted the deep drawing depth of the aluminum sheets, and the experiment has confirmed that result. Put Abstract text here.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.69-72
• /
• 2005

The crystal structure of magnesium is hexagonal close-packed (HCP), so its formability is poor at room temperature. But formability is improved in high temperature with increasing of the slip planes. Purpose of this paper is to know about the mechanical properties of magnesium alloy (AZ31B), before warm and hot forming process. The mechanical properties were defined by the tension and compression tests in various temperature and strain-rate. As the temperature is increased, yield${\cdot}$ultimate strength, K-value, work hardening exponent (n) and anisotropy factor (R) are decreased. But strain rate sensitivity (m) is increased. As strain-rate increased, yield${\cdot}$ultimate strength, K-value, and work hardening exponent (n) are increased. Also, microstructures of grains fine away at high strain-rate. These results will be used in simulations and manufacturing factor for warm and hot forming process.

• Transactions of Materials Processing
• /
• v.30 no.1
• /
• pp.35-42
• /
• 2021

Magnesium alloys are used in electronic devices such as laptops due to their lightweight features as well as vibration absorption and electromagnetic shielding properties. However, the precision of electronics is limited by the large number of small and precise ribs, the cost-effective manufacture of which requires appropriate technology. Plate forging is an efficient manufacturing process that can address these challenges. In this study, plate forging of magnesium alloys was investigated specifically for the fabrication of laptop cover. The plate forging process with back-pressure was used for near-net shape formation. Finite element analysis was used to select appropriate variables for back-pressure formation to generate ribs of various sizes and shapes without defects. The reliability of the analysis was verified to manufacture the prototype. The effect of back-pressure can be verified via fabrication of prototypes as well as structure and forming analysis based on finite element method. The process design factor of back-pressure increases formability without defects of under-filling and flow-through. Moreover, the tensile strength was maintained even after high temperature plate forging at 370 ℃, and the elongation was improved.

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.3
• /
• pp.122-129
• /
• 2021

This study focuses on the microstructural development of 99% magnesium alloy sheet manufactured using twin roll casting (TRC) process. Herein, a plate with a thickness of 5 mm was manufactured using the TRC process, homogenization heat treatment was performed at 400℃ for 2-32 h, and finally, the change in microstructure was evaluated via optical microscopy and textural analysis. The results suggest that the plate manufactured using the TRC process was not destroyed and was successfully rolled into a plate. Microscopic observation suggested that the dendritic cast structure was arranged along the rolling direction. And the central layer of the rolled plate, where was present in a liquid state at the beginning of rolling, solidified later during the TRC process to form central segregation. The initial cast structure and inhomogeneous structure of the plate were recrystallized by homogenization heat treatment for only 2 h, and it was confirmed that the segregated part of the central layer became homogeneous and recrystallization occurred. Grain growth occurred as the heat treatment time increased, and secondary recrystallization occurred, wherein only some grains were grown. The textural analysis, which was conducted via X-ray diffraction, confirmed that the relatively weak basal plane texture developed using the TRC process was formed into a random texture after heat treatment.

• Journal of the Korean institute of surface engineering
• /
• v.46 no.3
• /
• pp.116-119
• /
• 2013

To improve the corrosion resistance of an electrogalvanized steel sheet, we deposited magnesium film on it using a vacuum evaporation method and annealed the films at $250-330^{\circ}C$. The zinc-magnesium alloy is consequently formed by diffusion of magnesium into the zinc coating. From the anodic polarization test in 3% NaCl solution, the films annealed at $270-310^{\circ}C$ showed better corrosion resistance than others. In X-ray diffraction analysis, $ZnMg_2$ was detected through out the temperature range, whereas $Mg_2Zn_{11}$ and $FeZn_{13}$ were detected only in the film annealed at $310^{\circ}C$. The depth composition profile showed that the compositions of Mg at $270-290^{\circ}C$ are evenly and deeply distributed in the film surface layer. These results demonstrate that $270-290^{\circ}C$ is a proper temperature range to produce a layer of $MgZn_2$ intermetallic compound to act as a homogeneous passive layer.

• Journal of the Korean Society for Heat Treatment
• /
• v.36 no.4
• /
• pp.198-205
• /
• 2023

We investigated the effects of Al and Mg on the microstructure and hardness of the coating layer of galvanized steel sheets, by thermodynamic calculations, X-ray diffraction, scanning electron microscopy, and Vickers hardness tests of Zn-0.2Al, Zn-6Al-2Mg, and Zn-10Al-5Mg coating layers. Regardless of the alloy composition of the galvanizing bath, a Fe-Al layer was observed between the coating layer and steel sheet. The Zn-0.2Al coating layer consists of major h.c.p. Zn phase and minor f.c.c. Al phase. The fraction of f.c.c. Al phase (containing a significant amount of Zn) of the coating layer increases with increasing the chemical composition of Al of the galvanizing bath. The h.c.p. MgZn₂ phase was formed in the Al/Mg-containing Zn-6Al-2Mg and Zn-10Al-5Mg coating layers, forming Zn-Al-MgZn₂ eutectic microstructure. The primary MgZn₂ phase was additionally formed in the Zn-10Al-5Mg coating layers containing high concentrations of Al and Mg. The Vickers hardness values of Zn-0.2Al, Zn-6Al-2Mg, and Zn-10Al-5Mg coating layers were 59.1 ± 1.2 HV, 161.2 ± 5.7 HV, and 215.5 ± 40.3 HV, respectively. The addition of Al and Mg increased the hardness of the coating layer by increasing the fraction of the Al phase (containing Zn) and MgZn₂ intermetallic compound, which were harder than the Zn phase.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.44-44
• /
• 2018

칼라도장강판은 금속 제품의 제품화 공정 중에 도장 공정을 생략함으로 경제적이며, 제조공정 중 발생할 수 있는 VOCs(Volatile Organic Compounds)의 배출 염려가 없어 건축 및 가전 산업에 다용되고 있다. 칼라도장강판은 용융아연도금강판(GI), 전기아연도금강판(EGI), 용융알루미늄아연합금도금강판 등이 기재로 적용되고 있으며, 최근 마그네슘 성분이 첨가되는 고내식 도금강판 개발과 함께 고내식 도금강판을 이용한 칼라도장강판의 개발 및 수요 발굴을 위한 연구가 활발하게 진행 중에 있다. 칼라강판의 구성은 일반적으로 도막 밀착성 확보를 위한 화성처리층, 기재와 도막간의 밀착성과 내식성 개선을 위한 하도층(primer layer), 가공성, 내오염성, 의장성 등의 기능성 부여를 위한 상도층(top layer)의 구조로 도장되어 있다. 도료는 가공성, 내오염성, 경도 등의 기능성이 우수한 폴리에스테르 수지계가 가장 폭넓게 사용되고 경화제로는 멜라민 화합물과 이소시아네이트 화합물이 널리 사용되고 있다. 칼라도장 강판은 1970년대 이후 본격적으로 보급되어 사용되기 시작하였으며, 화성처리층은 밀착성과 내식성이 우수한 크로메이트처리가 널리 사용되고, 하도층은 방청성이 우수한 크로메이트계 방청 안료를 함유시킨 도료가 일반적이다. 그러나, 전기전자 제품에 적용되는 칼라도장강판은 2006년에 RoHS 규제의 시행과 더불어 6가 크롬 사용 제한의 영향으로 크롬프리 화성처리가 일반화되어 적용되고 있으며, 그 동안 6가 크롬 제안이 유보적이었던 건축용 칼라도장강판 또한 크롬프리 화성처리층 및 크로메이트계 방청 안료의 하도층 적용을 회피하고 있는 추세이다. 이에 따라, 고내식 합금도금강판을 기재로 사용하고 기존의 화성처리층과 하도층에 크롬프리 수지를 적용하는 연구개발이 활발하게 진행 중에 있다. 본 연구에서는 마그네슘이 첨가된 고내식 합금도금강판으로 Al-Mg-S i강판과 용융 Zn-Al-Mg 합금도금강판에 기존의 상용화 공정에서 사용되는 크롬계 및 크로프리 화성처리 적용 칼라도장강판에 대한 내식성 등 칼라도장강판의 특성에 대해 발표한다.