• Current Photovoltaic Research
• /
• v.2 no.4
• /
• pp.168-172
• /
• 2014

Under concentrated illuminations, the solar cells show higher efficiencies mainly due to an increase of the open circuit voltage. In this study, InGaP/InGaAs/Ge triple-junction solar cells have been grown by a low pressure metalorganic chemical vapor deposition. Photovoltaic characteristics of the fabricated solar cells are investigated with a class A solar simulator under concentrated illuminations from 1 to 100 suns. Ideally, the open circuit voltage should increase with the current level when maintained at the same temperature. However, the fabricated solar cells show degraded open circuit voltages under high concentrations around 100 suns. This means that the heat sink design is not optimized to keep the cell temperature at $25^{\circ}C$. To demonstrate the thermal degradation, changes of the device performance are investigated with different bonding conditions and heat sink materials.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.6
• /
• pp.114-119
• /
• 1996

The use of holographic interference lithography and removal techniques to corrugate GaAs substrate have been studied. The periodic photoresist structure, which serves as a protective mask during etching, is holographically prepared. Subsequently periodic V-grooved pattern is formed on the GaAs substrate by conventional a H$_{2}$SO$_{4}$-H$_{2}$O$_{2}$-H$_{2}$O wet etching. The linewidth of a GaAs pattern is about 0.4$\mu$m and the depth is 0.5$\mu$m A quantum wires(QWRs) array is well formed on the V-grooved substrate by MOCVD (metalorganic chemical vapor deposition) growth of GaAs/Al$_{0.5}$Ga$_{0.5}$As (50$\AA$/300$\AA$) quantum wells. The formation of QWR array is confirmed by the temperature dependent photoluminescence (PL) measurement. The intensive PL peak with a FWHM of 6meV at 21K shows the high quality of the QWR array.

• Journal of the Korean Vacuum Society
• /
• v.12 no.2
• /
• pp.118-122
• /
• 2003

Using low pressure metalorganic chemical vapor deposition (MOCVD), we have developed selectively area epitaxy (SAE). Using the developed SAE technology, we have grown AlGaAs/GaAs multi layers and InGaAs/GaAs quantum wire structures on the selectively $SiO_2$ masked GaAs substrates. We have obtained triangular shaped AlGaAs/GaAs and InGaAs/GaAs structures with sharp tips and smooth sidewalls. To rod the optimum conditions, several growth parameters such as growth rate, V/III ratio, growth temperature, and direction of the opening stripes were investigated. The emission peak from quantum wires was observed at 975 nm. With increasing of temperature the emission intensity from side wall quantum wells decreased abruptly. But the intensity from Quantum wires decreased slowly compared to that of side wall quantum wells and it became even stronger from above 50 K.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.246-246
• /
• 2010

As the trench width in the interconnect technology decreases down to nano-scale below 50 nm, superconformal gap-filling process of Cu becomes very critical for Cu interconnect. Obtaining superconfomral gap-filling of Cu in the nano-scale trench or via hole using MOCVD is essential to control nucleation and growth of Cu. Therefore, nucleation of Cu must be suppressed near the entrance surface of the trench while Cu layer nucleates and grows at the bottom of the trench. In this study, suppression of Cu nucleation was achieved by treating the Ru barrier metal surface with capacitively coupled hydrogen plasma. Effect of hydrogen plasma pretreatment on Cu nucleation was investigated during MOCVD on atomic-layer deposited (ALD)-Ru barrier surface. It was found that the nucleation and growth of Cu was affected by hydrogen plasma treatment condition. In particular, as the plasma pretreatment time and electrode power increased, Cu nucleation was inhibited. Experimental data suggests that hydrogen atoms from the plasma was implanted onto the Ru surface, which resulted in suppression of Cu nucleation owing to prevention of adsorption of Cu precursor molecules. Due to the hydrogen plasma treatment of the trench on Ru barrier surface, the suppression of Cu nucleation near the entrance of the trenches was achieved and then led to the superconformal gap filling of the nano-scale trenches. In the case for without hydrogen plasma treatments, however, over-grown Cu covered the whole entrance of nano-scale trenches. Detailed mechanism of nucleation suppression and resulting in nano-scale superconformal gap-filling of Cu will be discussed in detail.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.111-111
• /
• 2000

최근 질화물 반도체를 이용한 단파장 laser diode (LD)와 ultraviolet light emitting diode (LED)에 관한 관심의 증가로 인하여 AlGaN의 성장에 관한 연구가 많이 진행되고 있다. Metalorganic chemical vapor deposition (MOCVD)법을 이용한 AlGaN 성장에 있어서는 Al의 전구체로 널리 사용되고 있는 trimethylaluminum (TMAl)과 암모니아와의 기상에서의 adduct 형성을 억제하기 위하여 주로 저압에서 성장을 하거나 원료 가스의 유속을 증가시키는 방법으로 연구가 되고 있다. 또한, AlN의 경우 GaN보다 녹는점이 매우 높기 때문에 일반적으로 Al을 포함하는 질화물 반도체의 성장에 있어서는 GaN보다 녹는점이 매우 높기 때문에 일반적으로 Al을 포함하는 질화물 반도체의 성장에 있어서는 GaN 성장 시보다 높은 온도에서 성장이 이루어지고 있다. MOCND법을 이용하여 AlGaN를 성장시키는 대부분의 연구들은 100$0^{\circ}C$ 이상의 고온에서의 성장 온도가 AlGaN특성에 미치는 영향에 대한 것으로 국한되고 있다. 그러나, InGaN/GaN multiple quantum wells (MQWs) 구조의 LD나 LED를 성장시키는 경우 In의 desorption을 억제하기 위하여 MQWs층 위에 저온에서 AlGaN를 성장하는 데 있어서 AlGaN의 성장 온도를 500-102$0^{\circ}C$로 변화시키면서 AlGaN의 성장거동을 고찰하였다. GaN는 사파이어 기판을 수소분위기하에서 고온에서 가열한 후 저온에서 GaN를 이용한 핵생성층을 성장하고 102$0^{\circ}C$의 고온에서 1.2$\mu\textrm{m}$정도의 두께로 성장하였다. AlGaN는 고온에서 성장된 GaN 위에 200Torr의 성장기 압력 하에서 trimethylgallium (TMGa)과 TMAl의 유속을 각각 70 $\mu$mol/min 으로 고정한 후 성장온도만을 변화시키며 증착하였다. 성장 온도가 낮아짐에 따라 AlGaN의 표면거칠기가 증가하고, 결함과 관련된 포토루미네슨스가 현저히 증가하는 것이 관찰되었다. 그러나, 성장온도가 50$0^{\circ}C$정도로 낮아진 경우에 있어서는 표면 거칠기가 다시 감소하는 것이 관찰되었다. 이러한 현상은 저온에서 표면흡착원자의 거동에 제한이 따르기 때문으로 생각되어진다. 또한, 성장 온도가 낮아짐에 따라 AlGaN의 성장을 저해하기 때문으로 판단된다. 성장 온도 변화에 따라 성장된 V의 구조적 특성 및 표면 거칠기 변화를 관찰하여 AlGaN의 성장 거동을 논의하겠다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.147-147
• /
• 2011

High crystalline nonpolar a-plane (11-20) nitride light emitting diodes (LEDs) have been fabricated on r-plane (1-102) sapphire substrates by metalorganic chemical-vapor deposition (MOCVD). The multi-quantum wells (MQWs) active region is consists of 4 periods the nonpolar a-plane InGaN/GaN(a-InGaN/GaN) on a high quality a-plane GaN (a-GaN) template grown by using the multibuffer layer technique. The full widths at half maximum (FWHMs) of x-ray rocking curve (XRC) obtained from phiscan of the specimen that was grown up to nonpolar a-plane GaN LED layers with double crystal x-ray diffraction. The FWHM values were decreased down to 477 arc sec for $0^{\circ}$ and 505 arc sec for $-90^{\circ}$, respectively. After fabricating a conventional lateral LED chip which size was $300{\times}600{\mu}m^2$, we measured the optical output power by on-wafer measurements. N-electrode was made with Cr/Au contact, and ITO on p-GaN was formed with Ohmic contact using Ni/Au followed by inductively coupled plasma etching for mesa isolation. The optical output power of 1.08 mW was obtained at drive current of 20 mA with the peak emission wavelength of 502 nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.144-144
• /
• 2008

Blue light emitting diode structures consisting of the InGaN/GaN multiple quantum wells were grown by metalorganic chemical vapor deposition at different growth temperatures for the p-GaN contact layers and the influence of growth temperature on the emission and microstructural properties was investigated. The I-V and electroluminescence measurements showed that the sample with a p-GaN layer grown at $1084^{\circ}C$ had a lower electrical turn-on voltage and series resistance, andenhanced output power despite the low photoluminescence intensity. Transmission electron microscopy (TEM) revealed that the intense electro luminescence was due to the formation of a p-GaN layer with an even distribution of Mg dopants, which was confirmed by TEM image contrast and strain evaluations. These results suggest that the growth temperature should be optimized carefully to ensurethe homogeneous distribution of Mg as well as the total Mg contents in the growth of the p-type layer.

• Journal of the Korean Vacuum Society
• /
• v.7 no.2
• /
• pp.104-111
• /
• 1998

The InGaAs/InP quantum wells(QWs) were grown by low pressure metalorganic chemical vapor deposition and the effects of growth interruption steps on their interfacial structures were investigated by measuring photoluminescence spectra. When InP or InGaAs surface was treated under the same group V ambient, the full width at half maximum (FWHM) of the QW peak increased possibly due to the incorporation of impurities during the growth interruption time. When InP surface was treated under $AsH_3$, howerer, the PL peak showed red-shift due to the As-P exchange reaction and the change of FWHM was not remarkable. The effective thickness of InAs interfacial layer formed during $AsH_3$, treatment on the InP surface was calculated to be 1~2 monolayers. In the case of InGaAs treatment under $PH_3$, the PL peak energy and the FWHM increasied. This results suggest that $PH_3$ treatment on the InGaAs surface suppresses the incorporation of As into the subsequent InP layer and the local replacement of As by P occurs simultaneously.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.171-171
• /
• 2010

GaN 기반 Light emitting diodes(LEDs)의 p-type doping layer는 일반적으로 hole을 발생시키는 acceptor로 Mg이 사용하되고 있다. 보통 Mg이 도핑된 p-type GaN은 >$1\;{\Omega}{\cdot}cm$의 저항이 존재하는데 그 이유는 Mg의 열적 이온화를 위한 activation 에너지가 높아서 상온에서 valence band의 hole concentration는 전체 억셉터 농도의 1%가 되지 않기 ��문이다. 본 논문에서는 높은 hole 농도를 얻기 위해서 metalorganic chemical-vapor deposition (MOCVD)를 장비를 사용하여 사파이어 기판의 misorientation-angle에 따른 p-type a-plane(11-20) GaN 특성을 분석하였다. misorientation-angle은 c축 방향으로 $+0.15^{\circ}$, $-0.15^{\circ}$, $-0.2^{\circ}$, $-0.4^{\circ}$ off된 r-plane(1-102) 사파이어 기판 을 사용하였다. p-type 도핑물질로 bis-magnesium (Cp2Mg) 소스를 사용하였고 성장 과정중 발생하는 hydrogen passivation으로 인한 Mg-H complexes현상을 해결하기위해 conventional furnace annealing (CFA)와 rapid thermal annealing (RTA)를 이용하여 열처리 공정을 진행하였다. 열처리 공정은 Air와 N2 분위기에서 $650^{\circ}C$에서 $900^{\circ}C$ 사이의 다양한 온도에서 수행하였고 Hall 측정을 위해 Ni을 전극 물질로 사용하였다. 상온에서 Accent HL5500IU Hall system을 사용하여 hole concentration, mobility, specific resistance을 측정하였다. 열처리 공정 후 Hall측정 결과 $+0.15^{\circ}$, $-0.15^{\circ}$, $-0.2^{\circ}$, $-0.4^{\circ}$ off된 각 샘플들은 온도, 시간, 분위기에 따라 hole concentration ($7.4{\times}10^{16}cm^{-3}{\sim}6{\times}10^{17}cm^{-3}$), mobility(${\mu}h=\;1.72\;cm^2/V-s\;{\sim}15.2\;cm^2/V-s$), specific resistance(4.971 ohm-cm ~8.924 ohm-cm) 가 변화됨을 확인 할 수 있었다. 또한 광학적 특성을 분석하기 위해 Photoluminescence (PL)을 측정하였다.

• Applied Science and Convergence Technology
• /
• v.26 no.4
• /
• pp.79-85
• /
• 2017

The crack-free AlGaN template has been successfully grown by using selective area growth with triangular GaN facet. The triangular GaN stripe structure was obtained by vertical growth rate enhanced mode with low growth temperature of $950^{\circ}C$ and high growth pressure of 500 torr. The lateral growth rate enhanced mode of AlGaN for crack-free and flat surface was also investigated. Low pressure of 30 torr and high V/III ratio of 4400 were favorable for lateral growth of AlGaN. It was confirmed that the $4{\mu}m$ -thick $Al_{0.2}Ga_{0.8}N$ was crack-free over entire 2-inch wafer. The dislocation density of $Al_{0.2}Ga_{0.8}N$ was as low as ${\sim}7.6{\times}10^8/cm^2$ measured by cathodoluminescence. Based on the high quality AlGaN with low dislocation density, the ultraviolet laser diode epitaxy with cladding, waveguide and GaN/AlGaN multiple quantum well (MQW) was grown by metalorganic chemical vapor deposition. The stimulated emission at 349 nm with full width at half maximum of 1.8 nm from the MQW was observed through optical pumping experiment with 193 nm KrF laser. We also have fabricated the deep ridge type ultraviolet laser diode (UV-LD) with $5{\mu}m-wide$ and $700{\mu}m-long$ cavity for electrical properties. The turn on voltage was below 5 V and the resistance was ${\sim}55{\Omega}$ at applied voltage of 10 V. The amplified spontaneous emission spectrum of UV-LD was also observed from pulsed current injection.