• Journal of Korea Foundry Society
• /
• v.30 no.2
• /
• pp.60-65
• /
• 2010

In this study, we investigate the effects of austempering heat treatment on the processing window and mechanical properties in cast and hot-rolled Fe-0.7 C-2.3 Si-0.3 Mn steel. Each specimens were austenitised at $900^{\circ}C$ for 7 min, and austempered at $260^{\circ}C,\;320^{\circ}C$, and $380^{\circ}C$ for the various periods of time from 2 min to 240 min. After heat treatment, the evaluation of stage I and stage II as performed by optical metallography, XRD, hardness test. Both cast and hot rolled specimens had similar processing window. So grain size effect is not important to the austempered high carbon high silicon cast steel. When the austempering temperature was $260^{\circ}C$, the microstructure consisted of the lower ausferrite while the upper ausferrite structure was formed at $380^{\circ}C$. As the austempering temperature increases from 260 to $380^{\circ}C$, the strength and hardness decreased, elongaton and volume fraction of austenite increased. In addition, there was no change of mechanical properties between cast and hot-rolled specimens.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.2
• /
• pp.145-156
• /
• 1999

The distribution of the second phase, the change of transformation temperature and mechanical properties with thermomechanical treatment conditions were investigated by metallography, calorimetry, EDS, tensile test and fractography in a Cu-Al-Ni-Ti-Mn alloy. The cast structure revealed Ti-rich precipitates($X_L$ phase) between dendrite arms, which have been identified as $(Cu,Ni)_2TiAl$ intermetallic compounds. By homogenizing above $900^{\circ}C$, the $X_L$ phase was melted in the matrix, while the Xs phase was precipitated in matrix and the volume fraction of it was increased. When hot-rolled specimen was betatized below $750^{\circ}C$, recrystallization could not be observed. However, the specimen betatized above $800^{\circ}C$ was recrystallized and the grain size was about $50{\mu}m$, while Xs phase was precipitated in matrix. With raising betatizing temperature, $M_s$ and $A_s$ temperatures were fallen and transformation hysteresis became larger. The strain of the specimen betatized at $800^{\circ}C$ was 8.2% as maximum value. The maximum shape recovery rate could be obtained in the specimen betatized at $800^{\circ}C$ but it was decreased due to the presence of Xs phase with increasing betatizing temperature.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.5
• /
• pp.215-221
• /
• 2017

The effect of austenitizing temperature on the degree of carbides re-solutionizing, mean graine size, hardness and the volume fraction of retaind austenite ($V_{\gamma}$) etc., has been studied by means of metallography, X-ray diffractometry and hardness measurement in STD 11 tool steel. As austenitizing temperature increases, the amount of alloying elements which is re-dissolved into matrix increases, resulting in increase of $V_{\gamma}$, due to the chemical stabilization of austenite. The Vickers hardness value decreases with increasing austenitizing temperature, which is attributed to grain size as well the volume fractions of $V_{\gamma}$ and carbides. Theoretical diffraction intensity of (200) ${\alpha}^{\prime}$, (211) ${\alpha}^{\prime}$ (200) ${\gamma}$ and (220) ${\gamma}$ peaks obtained by $CuK_{\alpha}$ chracteristics X-ray (${\lambda}=0.15429nm$) was calculated, and quantitative analysis of $V_{\gamma}$ could be carried out by X-ray diffraction method. The resultant value is well coincided with the value obtained by image analysis method. When the quenched specimen is tempered above $200{\sim}400^{\circ}C$ for 30 min, the transition carbides i.e., MC and $M_2C$ in the size of about 20 nm begin to precipitate at $300^{\circ}C$.

• Journal of Conservation Science
• /
• v.28 no.3
• /
• pp.257-264
• /
• 2012

Ancient mirrors are generally made of bronze, and it is very rare to find cases of iron mirrors excavated domestically. In this study, the unidentified ferrous artifact was treated for conservation, and was identified as a mirror. In this process, the sample was taken and analyzed for microstructure, and the manufacturing technology was studied. Analysis involved optical microscope, micro-hardness tester, and SEM-EDS. As the result of analysis, iron mirror structure exist not almost non-metallic inclusions, and partially network cementite was observed. This appears to have been caused by reduced carbon content due to decarburizing the cast iron in the solid state mirror which was created by cast iron. The ledeburite structure of the casting has difficult to cut or polish because has great hardness by high carbon content. Thus, the cast iron mirror was decarburized at a temperature under $850^{\circ}C$ with CO or $CO_2$ blocked, which reduced the hardness of the iron mirror and made it possible to polish the mirror surface. This deformation of structure according to carbon content results from such manufacturing technology.

• Nuclear Engineering and Technology
• /
• v.52 no.8
• /
• pp.1756-1763
• /
• 2020

The paper studies spark plasma sintering (SPS) of industrially used UO₂-based fuel containing integral fuel burnable absorber (IFBA) of neutrons Gd₂O₃. Densification dynamics of pristine UO₂ powder and the one added with 2 and 8 wt% of Gd₂O₃ under ultrasonication in liquid has been studied under SPS conditions at 1050, 1250, and 1450 ℃. Effect of sintering temperature on phase composition as well as on O/U stoichiometry has been investigated for UO₂ SPS ceramics. Sintering of uranium dioxide added with Gd₂O₃ yields solid solution (U,Gd)O₂, which is isostructural to UO₂. SEM with EDX and metallography were implemented to analyze the microstructure of the obtained UO₂ ceramics and composite UO₂-Gd₂O₃ one, particularly, open porosity, defects, and Gd₂O₃ distribution were studied. Microhardness, compressive strength and density were shown to reduce after addition of Gd₂O₃. Obtained results prove the hypothesis on formation of stable pores in the system of UO₂-Gd₂O₃ due to Kirkendall effect that reduces sintering efficiency. The paper expands fundamental knowledge on pros and cons of fuel fabrication with IFBA using SPS technology.

• Restorative Dentistry and Endodontics
• /
• v.8 no.1
• /
• pp.89-96
• /
• 1982

The purpose of this study is to identify the phases of four different types, low-copper lathe cut (Type II, class 1) and spherical (Type II, class 2) amalgam alloys which are made by Caulk company and high copper Dispersalloy (Type II, class 3) made by Johnson & Johnson and Tytin (Type I, class 2) made by S.S. White and to determine the Vickers hardness number on the individual phase and four different types of dental amalgam. After each amalgam alloy and Hg measured exactly by the balance was triturated by the mechanical amalgamator (De Trey), the triturated mass was inserted into the cylindrical metal mold which was 4 mm in diameter and 12mm in height and was pressed by the Instron Universal Testing machine (Model 1125) at the speed of 1mm/minute with 143$kg/cm^2$ according to the A.D.A. Specification No. 1. The Specimen removed from the mold, mounted and stored in the room temperature for 7 days. The speciman was polished with the emery paper from #220 to #1200 and finally on the polishing cloth with 0.3 and 0.05 um $Al_2O_3$ powder suspended in water. And then each specimen was etched by Allan's method and washed with Sodium Bisulfinite for 30 seconds. Finally differentiation and metallography on each phase were obtained by using metallographical microscope (Versamet, Union) and microhardness was obtained by using microhardness tester (MVH-2, Torsee). The results were as follows: 1. In the low-copper amalgam, the ${\gamma}$, ${\gamma}_1$ and ${\gamma}_2$ phase were observed and in the high-copper amalgam, the ${\gamma}$, ${\gamma}_1$. ${\epsilon}$ and ${\eta}$ phases were observed but ${\gamma}_2$ phase was not observed. 2. Among the microhardness of each amalgam phase measured under pressing a vickers diamond indenter with 2.0gm load for 30 seconds, e phase has the highest V.H.N (314 ${\pm}$ 20), and in low-copper amalgam 12 phase has the lowest V.H.N. (29${\pm}$1) and ${\eta}$ phase which was observed in high-copper amalgam has 230${\pm}$13 V.H.N and this phase is considerd to contribute to strengthen the handness in amalgam. 3. The V.H.N. measured under pressing a Vickers diamond indenter with 300.0gm load for 30 seconds in low-copper amalgam was lower than that of high-copper amalgam.