• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.231-231
• /
• 2009

In this work, we prepared the Ni-loaded porous SBA-15 (SBA-15) by a depositionprecipitation (D-P) method, in order to enhance the hydrogen storage capacity. The structure and morphology of the Ni/SBA-15 were characterized by X-ray diffraction (XRD) and field emission transmission electron microscopy (FE-TEM). The results showed that, at the Ni loading used at the DP times in the range of 0-120 min, SBA-15 preserved the well-ordered hexagonal porous arrangement. The textural properties of the Ni/SBA-15 were analyzed using N2 adsorption isotherms at 77 K. Specific surface area and mesopore volume of the samples were determined from the Brunauer-Emmett-Teller (BET) equation and Barrett-Joiner-Halenda (BJH) method, respectively. The hydrogen storage capacity of the Ni/SBA-15 was evaluated at 298 K/10 MPa. The hydrogen storage capacity of the Ni/SBA-15 was increased in accordance with Ni content. Consequently, it was found that the presence of Ni on mesoporous SBA-15 created hydrogen-favorable sites which enhanced the hydrogen storage capacity by spillover effect.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.3
• /
• pp.179-184
• /
• 2018

In this study, Ni and tungsten carbide (WC) nanoparticles are simultaneously synthesized with the mesoporous carbon nanoparticles (CNP) using a solution plasma processing (SPP) in the benzene. The Ni and WC nanoparticles were formed through the sputtering effect of electrodes during discharge, and mean time CNP were formed through reduction reaction. TEM observation showed that loaded Ni and WC nanoparticles were evenly dispersed on the CNP. The results of electrochemical analysis demonstrated that an introduction of Ni nanoparticles promoted to improve catalytic activity for oxygen reduction reaction (ORR). Moreover, Ni-WC/CNP lead to fast electron transfer process compared to that of WC/CNP. Therefore, the inexpensive Ni-WC/CNP might be a promising as catalytic material for cathodes in fuel cell applications.

• Korean Chemical Engineering Research
• /
• v.59 no.2
• /
• pp.269-275
• /
• 2021

In this study, ordered mesoporous silica-supported Ni catalysts were prepared for catalytic partial oxidation of methane (CPOM) by using electroless nickel plating method. Unlike conventionally impregnated catalysts, the electrolessly-plated nickel catalyst showed that nickel was highly dispersed and formed stably on silica-supported surface. It was verified by TEM-EDS analysis. During the activity tests, the electrolessly-plated nickel was barely sintered and the amount of carbon deposition was very small. Consequently, the catalyst was far less deactivated, while the sintering was significantly observed in the cases of the catalysts prepared by the conventional impregnation method. Regarding the palladium-promoted catalysts, the reducibility of nickel was increased, and the reaction performances were enhanced in terms of CH4 conversion and H2/CO ratio of produced syngas.